• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 1998.04b
• /
• pp.23-23
• /
• 1998

• Journal of Powder Materials
• /
• v.13 no.5 s.58
• /
• pp.351-359
• /
• 2006

Ni based($Ni_{57}Zr_{20}Ti_{18}Si_2Sn_3$) bulk metallic glass(BMG) powders were produced by a gas atomization process, and ductile Cu powders were mixed using a spray drying process. The Ni-based amorphous powder and Cu mixed Ni composite powders were compacted by a spark plasma sintering (SPS) processes into cylindrical shape. The relative density varied with the used SPS mold materials such as graphite, hardened steel and WC-Co hard metal. The relative density increased from 87% to 98% when the sintering temperature increased up to $460^{\circ}C$ in the WC-Co hard metal mold.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.83-84
• /
• 2006

Processing of W-Cu graded materials from attritor-milled W-CuO mixtures is described. The powder reduction steps are investigated by TG and XRD analyses and by microstructural observations (SEM, TEM). Sintering of reduced powder with different compositions is analysed by dilatometry. Sintering behaviour of the graded component processed by co-compaction of a 10/20/30wt%Cu multi-layer material is briefly discussed. Liquid Cu migration is observed and smooths the composition gradient. Perspectives to control this migration are discussed.

• Progress in Superconductivity and Cryogenics
• /
• v.11 no.2
• /
• pp.7-10
• /
• 2009

Effects of $BaCO_3$ purity on the superconducting properties of top seeded melt growth (TSMG) processed $Y_{1+x}Ba_2Cu_3O_{7-y}$ (Y1+x, x=0.1 and 0.2) superconductors were investigated. $YBa_2Cu_3O_{7-y}$ (Y123) powder prepared using $BaCO_3$ with 99.75% purity and commercially available Y123 powder of 99.9% were used for the fabrication of single Y123 grain superconductors. $T_c$ values of the Y1+x samples prepared using low purity Y123 powder were slightly lower than those of the samples prepared using a high purity powder. In addition to the lower $T_c$, an anomalous peak effect in the intermediate magnetic fields was observed in Y1+x samples prepared using the low purity $BaCO_3$ powder. The slight decrease in $T_c$ and the anomalous peak effect are ascribed to the possible incorporation of a Y123 phase with impurity elements such as strontium and calcium included in the $BaCO_3$powder of 99.7%. The result suggests that the low purity $BaCO_3$ powder of a low price can be used as a raw power for the fabrication of single grain YBCO bulk superconductors.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2003.10a
• /
• pp.91-91
• /
• 2003

• Journal of Powder Materials
• /
• v.26 no.2
• /
• pp.112-118
• /
• 2019

Infiltration is a popular technique used to produce valve seat rings and guides to create dense parts. In order to develop valve seat material with a good thermal conductivity and thermal expansion coefficient, Cu-infiltrated properties of sintered Fe-Co-M(M=Mo,Cr) alloy systems are studied. It is shown that the copper network that forms inside the steel alloy skeleton during infiltration enhances the thermal conductivity and thermal expansion coefficient of the steel alloy composite. The hard phase of the CoMoCr and the network precipitated FeCrC phase are distributed homogeneously as the infiltrated Cu phase increases. The increase in hardness of the alloy composite due to the increase of the Co, Ni, Cr, and Cu contents in Fe matrix by the infiltrated Cu amount increases. Using infiltration, the thermal conductivity and thermal expansion coefficient were increased to 29.5 W/mK and $15.9um/m^{\circ}C$, respectively, for tempered alloy composite.

• Journal of Powder Materials
• /
• v.10 no.2
• /
• pp.136-141
• /
• 2003

In the present study, $TiO_2$ imbedded copper matrix powders have been successfully prepared from the ($CuSO_4+TiO_2+Zn$) composite salt solution. The composite $Cu/TiO_2$ powders were formed by drying the solution at $200{\sim}~400^{\circ}C$ in the hydrogen atmosphere. Photocatalytic characteristics was evaluated by detecting TOC (total organic carbon) amount with TOC analyzer (model 5000A Shimadzu Co). Phase analysis of $Cu/TiO_2$ composite powders was carried out by XRD, DSC and powder size was measured with TEM. The mean particle size of composite powders was about 100 nm and a few zinc and copper oxide phases was included. The reduction ratio of TOC amount was 60% by the composite $Cu/TiO_2$ powders under the UV irradiation for 8 hours.

• Journal of Powder Materials
• /
• v.19 no.4
• /
• pp.264-270
• /
• 2012

In this study, we mainly focus on the study of densification of gas-atomized Cu-50 wt.%In-13 wt.%Ga alloy powder without occurrence of crack during the forming process. Cu-50 wt.%In-13 wt.%Ga alloy powder was consolidated by sintering and rolling processes in order to obtain high density. The phase and microstructure of formed materials were examined by X-ray diffraction (XRD), scanning electron microscopy (SEM) and optical microscopy (OM), respectively. Warm rolling using copper can result in the improvement of density. The specimen obtained with 80% of rolling reduction ratio at $140^{\circ}C$ using cooper can have the highest density of $8.039g/cm^3$.

• Journal of the Korean institute of surface engineering
• /
• v.54 no.3
• /
• pp.144-151
• /
• 2021

In the present work, planar-type ZnO powder of [0001] plane with a high aspect ratio range of 20:1 to 50:1 was synthesized. Ag or CuO could be coated on the planar-type ZnO powder by wet methods such as centrifugation or ball milling. During the coating, the average size of the powder was slightly increased while maintaining the shape and XRD pattern of ZnO. When Ag or CuO was coated, the absolute value of the zeta potential, as well as the concentration of oxygen vacancy, was increased. Ag or CuO coated planar-type ZnO power exhibited excellent antibacterial performance, which seems to be related to their high electrostatic attraction force. They could be made into a masterbatch by mixing with ABS resin, and their applicability to antibacterial substances was confirmed by manufacturing the caps of a keyboard.

• Bulletin of the Korean Chemical Society
• /
• v.30 no.7
• /
• pp.1607-1610
• /
• 2009

The carbon-coated Si/Cu powder has been prepared by mechanical ball milling and hydrocarbon gas decomposition methods. The phase of Si/Cu powder was analyzed using X-ray diffraction (XRD), dispersive Raman spectroscopy, electron probe microanalysis (EPMA) and transmission electron microscope (TEM). The carbon-coated Si/Cu powders were used as anode active material for lithium-ion batteries. Their electrochemical properties were investigated by charge/discharge test using commercial LiCo$O_2$ cathode and lithium foil electrode, respectively. The surface phase of Si/Cu powders consisted of carbon phase like the carbon nanotubes (CNTs) with a spacing layer of 0.35 nm. The carbon-coated Si/Cu/graphite composite anode exhibited a higher capacity than commercial graphite anode. However, the cyclic efficiency and the capacity retention of the composite anode were lower compared with graphite anode as cycling proceeds. This effect may be attributed to some mass limitations in LiCo$O_2$ cathode materials during the cycling.