• Journal of Welding and Joining
• /
• v.17 no.2
• /
• pp.61-65
• /
• 1999

Because of the need for packages which accommodate high pin count, high density and high speed device, PBGA(plastic ball grid array) package gets more spotlight. But the substrate material which is used for PBGA package is in nature susceptible to moisture penetration. The objective of the study is to find out the path of delamination in the stacked structure of substrate. To increase the adhesion between the cooper laminate and PSR(photo solder resist) which is the weakest part, experiments were performed by changing parameters of printing pre-treatment and post-treatment process. As a result of experiments, the factor effects on the adhesion between the cooper laminate and PSR is caused by all of the pre-treatment and post-treatment condition. A considerable change was observed depending on the amount of UV irradiation after thermal cure which is typical of printing post-treatment condition rather than pre-treatment condition.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.3
• /
• pp.252-259
• /
• 2016

In order to form an aluminum-doped zinc oxide (AZO) transparent electrode film on a polyethylene terephthalate (PET) substrate used for a flexible display substrate, the AZO transparent electrode was produced at low temperature without substrate heating. Even though the produced electrode showed characteristic optical transmittance of 90 % (at 550 nm) and sheet resistance within $100{\Omega}/sq$, cracks occurred 10 minutes after loading applied 2 mm radius of curvature, and the sheet resistance increased linearly. An insertion layer of ZrCu was formed between the AZO film and the PET substrate to suppress the generation of cracks on the AZO film. It was verified that the crack was not generated 30 minutes after the loading of 2 mm radius of curvature, and no increase in sheet resistance was recorded. There was also not cracks in the dynamic bending test of 4 mm radius, but surface resistance was slightly increased. As a result, the ZrCu insertion film improved the interfacial adhesion between the substrate and AZO film layer without increasing sheet resistance and decreasing transmittance.

• Journal of the Optical Society of Korea
• /
• v.19 no.3
• /
• pp.217-221
• /
• 2015

Developing a metallization that has low cost and high efficiency is essential in solar-cell industries, to replace expensive silver-based metallization. Ni/Cu two-step metallization is one way to reduce the cost of solar cells, because the price of copper is about 100 times less than that of silver. Alkaline electroless plating was used for depositing nickel seed layers on the front electrode area. Prior to the nickel deposition process, 2% HF solution was used to remove native oxide, which disturbs uniform nickel plating. In the subsequent step, a nickel sintering process was carried out in $N_2$ gas atmosphere; however, copper was plated by light-induced plating (LIP). Plated nickel has different properties under different bath conditions because nickel electroless plating is a completely chemical process. In this paper, plating bath conditions such as pH and temperature were varied, and the metal layer's structure was analyzed to investigate the adhesion of Ni/Cu metallization. Average adhesion values in the range of 0.2-0.49 N/mm were achieved for samples with no nickel sintering process.

• Applied Science and Convergence Technology
• /
• v.24 no.5
• /
• pp.162-166
• /
• 2015

Linear ion beams have been introduced for the ion beam treatments of flexible substrates in roll-to-roll web coating systems. Anode layer linear ion sources (300 mm width) were used to make the linear ion beams. Oxygen ion beams having an ion energy from 200 eV to 800 eV used for the adhesion improvement of Cu thin films on PET substrates. The Cu thin films deposited by a conventional magnetron sputtering on the oxygen ion beam treated PET substrates showed Class 5 adhesion defined by ASTM D3359-97 (tape test). Argon ion beams with 1~3 keV used for the ion beam sputtering deposition process, which aims to control the initial layer before the magnetron sputtering deposition. When the discharge power of the linear ion source is 1.2 kW, static deposition rate of Cu and Ni were 7.4 and $3.5{\AA}/sec$, respectively.

• Tribology and Lubricants
• /
• v.24 no.2
• /
• pp.63-71
• /
• 2008

Friction and adhesion tests were conducted to investigate tribological characteristics of materials for MEMS/NEMS using atomic force microscope (AFM). AFM Si tips were chemically modified with a self-assembled monolayer (SAM) derived from trichlorosilane like octadecyltrichlorosilane (OTS) and (1H, 1H, 2H, 2H-perfluorooctyl) trichlorosilane (FOTS), and various materials, such as Si, Al, Au, Cu, Ti and PMMA films, were prepared for the tests. SAMs were coated on Si wafer by dipping method prior to AFM tip to determine a proper dipping time. The proper dipping time was determined from the measurements of contact angle, surface energy and thickness of the SAMs. AFM tips were then coated with SAMs by using the same coating condition. Friction and adhesion forces between the AFM Si tip modified with SAM and MEMS/NEMS materials were measured. These forces were compared to those when AFM tip was uncoated. According to the results, after coating OTS and FOTS, the friction and adhesion forces on all materials used in the tests decreased; however, the effect of SAM on the reduction of friction and adhesion forces could be changed according to counterpart materials. OTS was the most effective to reduce the friction and adhesion forces when counterpart material was Cu film. In case of FOTS, friction and adhesion forces decreased the most effectively on Au films.

• Journal of the Korean Institute of Telematics and Electronics
• /
• v.27 no.10
• /
• pp.96-100
• /
• 1990

The cordierite ($2MgO,2Al_{2}O_{3},5SiO_{2}$) is of great interest for packaging substrates of multilayer IC. The Cu layer was fabricated on the cordierite substrate by the screen printing method and the adhesion properties of the interfaces at the different cosintering conditions were studied. When cosinted in the $Ar+H_{2}O$atmosphere good adhesion was obtained and the heating was found out to be an important factor for the adhesion.

• Journal of the Korean institute of surface engineering
• /
• v.38 no.2
• /
• pp.49-54
• /
• 2005

Flexible copper clad laminates (FCCL) fabricated by sputtering has advantages in fine pitch etching and dimensional accuracy than previous casting or laminating type FCCL, But its lower adhesion is inevitable technical challenge to solve for commercializing it. Chromium (Cr) which strongly reacts with O moiety was used as tie-coating layer in order to improve low adhesion between copper (Cu) and polyimide (PI). Sputtering raw polyimide (SRPI) and casting raw polyimide (CRPI) were used as substrates at this research. PI was pretreated by plasma before sputtering, and each sample was varied with RF power and Cr thickness on sputtering. Peel strength of the FCCL on SRPI was higher than that on CRPI. Adhesion had maximum value when 10 nm of Cr was deposited on SRPI by RF power of 50 W. It seems to be by the formation of Cu-Cr-O solid solution at the metal-PI interface.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2008.11a
• /
• pp.27.2-27.2
• /
• 2008

• Journal of the Microelectronics and Packaging Society
• /
• v.25 no.2
• /
• pp.41-48
• /
• 2018

The quantitative interfacial adhesion energy measurement method of copper redistribution layer and WPR dielectric interface were investigated using $90^{\circ}$ peel test, 4-point bending test, double cantilever beam (DCB) measurement for FOWLP Applications. Measured interfacial adhesion energy values of all three methods were higher than $5J/m^2$, which is considered as a minimum criterion for reliable Cu/low-k integration with CMP processes without delamination. Measured energy values increase with increasing phase angle, that is, in order of DCB, 4-point bending test, and $90^{\circ}$ peel test due to increasing roughness-related shielding and plastic energy dissipation effects, which match well interfacial fracture mechanics theory. Considering adhesion specimen preparation process, phase angle, measurement accuracy and bonding energy levels, both DCB and 4-point bending test methods are recommended for quantitative adhesion energy measurement of RDL interface depending on the real application situations.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.681-682
• /
• 2013

전기는 우리 주변의 에너지 형태 중에서 가장 편리하고 광범위하게 사용되고 있다. 이러한 전기는 전자제품, 전기자동차, 에너지 저장 플랜트 등 매우 많은 분야에서 저장되고 사용되고 있다. 특히 에너지 저장 용량의 확대는 휴대폰, 노트북 PC 등 휴대용 IT 기기의 성장에 결정적인 역할을 하였다. 가볍고 작으면서도 고용량의 전기 에너지 저장 장치가 없었다면, 통신이나 인터넷 그리고 오락 등 다양한 기능을 작은 휴대용 기기에 구현할 수 없었을 것이다. 그러나 시간이 흐를수록 기기의 요구 성능이 높아지고 소비자의 니즈가 더욱더 다양해지고 고도화될수록 단일 부품으로 가장 큰 부피를 차지하는 에너지 저장 장치의 용량과 디자인은 점점 중요해지고 있다. 이러한 에너지 저장 장치에서 가장 친숙한 형태는 2차 전지 계열이다. 납 축전지를 비롯하여, 니켈수소, 니켈카드뮴, electrochemical capacitor와 Li ion 계열 등이 대표적이다. 특히 Li ion 배터리는 모바일, 자동차 및 에너지 저장 그리드 등과 같은 다양한 분야에 가장 많이 적용되고있다. Li ion 배터리에 대하여 현재의 핵심적인 연구분야는 전극 재료(cathode, anode)와 electrolyte에 대한 것이다. Anode 전극 재료 중에서 가장 많이 사용되는 재료는 카본을 기반으로 하는 재료로 안정성에 대한 장점이 있지만 에너지 밀도가 낮다는 단점이 있다. 에너지 저장 용량 증가에 대한 필요성이 증가하기 때문에 현재 많이 사용되고 있는 에너지 밀도가 낮은 카본 재료를 대체하기 위해서 이론 용량이 높다고 알려진 실리콘과 같은 메탈이나 주석 산화물과 같은 천이 금속 산화물에 대하여 많은 연구가 진행되고 있다. 특히 현재까지 알려진 많은 재료 중에서 가장 큰 capacity (~4,000 mAh/g)를 가지고 있다고 알려진 실리콘이 카본의 대체 재료로 많은 연구가 진행되고 있다. 그러나, Li 과 반응을 하며 약 300~400%에 달하는 부피팽창이 발생하고, 이러한 부피 팽창 때문에 충 방전이 진행됨에 따라 current collector로부터 박리되는 현상을 보여 빠른 용량 감소를 보여주고 있다. 본 연구에서는 adhesion layer를 current collector와 실리콘 전극 재료 사이에 삽입하여 충 방전 시 부피팽창에 의한 미세구조의 변화와 electrochemical 특성에 대한 영향을 알아보았다. 실험에 사용한 anode 전극은 상용 Cu foil current collector에 RF/DC magnetron 스퍼터링을 통해 다양한 종류(Ti, Ta 등)의 adhesion layer과 200 nm 두께의 Si 박막을 증착하였다. 또한 Bio-logic Potentiostat/ Galvanostat VMP3 와 WanAtech automatic battery cycler 장비를 사용하여 0.2 C-rate로 half-cell 타입의 코인 셀로 조립한 전극에 대한 충 방전 실험을 진행하였다. Adhesion layer의 사용으로 인해 실리콘 박막과 Cu current collector 사이의 박리 현상을 줄여줄 수 있었고, 충 방전 시 Cu 원자의 실리콘 박막으로의 확산을 통한 brittle한 Cu-Si alloy 형성을 막아 줄 수 있어 큰 특성 향상을 확인할 수 있었다. 또한, 리튬과 실리콘의 반응을 통한 형태와 미세구조 변화를 SEM, TEM 등의 다양한 장비를 사용하여 확인하였고, 이를 통해 adhesion layer의 사용이 전극의 특성향상에 큰 영향을 끼쳤다는 것을 확인할 수 있었다.