• Journal of Welding and Joining
• /
• 제35권2호
• /
• pp.58-62
• /
• 2017

A319 aluminum alloy containing 6.5% Si and 3.5% Cu as major alloying elements has been widely used in machinery parts because of its excellent castability and crack resistance. However it needs more wear resistance to extend its usage to the severe wear environments. It has been known that hyper-eutectic Al-Si alloy having more than 12.6% Si contains pro-eutectic Si particles, which give better wear resistance and lubrication characteristics than hypo-eutectic Al-Si alloy like A319 alloy. In this study, it was tried to clad hyper-eutectic Al-Si alloy on the surface of A319 alloy. In the experiments, Al-36%Si alloy powder was mixed with organic binder to make a fluidic paste. The paste was screen-printed on the A319 alloy surface, melted by pulsed Nd:YAG laser and alloyed with the A319 base alloy. As experimental parameters, the average laser power was changed to 111 W, 202 W and 280 W. With increasing the average laser power, the melting depth was changed to $142{\mu}m$, $205{\mu}m$ and $245{\mu}m$, and the dilution rate to 67.2 %, 72.4 % and 75.7 %, and the Si content in the cladding layer to 16.2 %, 14.6 % and 13.7 %, respectively. The cross-section of the cladding layer showed very fine eutectic microstructure even though it was hyper-eutectic Al-Si alloy. This seems to be due to the rapid solidification of the melted spot by single laser pulse. The average hardness for the three cladding layers was HV175, which was much higher than HV96 of A319 base alloy. From the block-on-roll wear tests, A319 alloy had a wear loss of 5.8 mg, but the three cladding layers had an average wear loss of 3.5 mg, which meant that an increase of 40 % in wear resistance was obtained by laser cladding.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2000년도 제18회 학술발표회 논문개요집
• /
• pp.148-148
• /
• 2000

지금까지 반도체 표면에 대한 연구는 주로 (1000, (111) 표면 등 낮은 밀러 지표를 가진 표면에 대해 이루어져 왔다. 이에 반해 밀러 지표가 높은 Si 면은 불안정하고, 가열하면 다른 표면, 즉 지표가 낮은 면으로 재배열하는 경향이 있는 것으로 알려져 있는데 아직 이들 높은 밀러 지표를 가진 표면에 대한 연구는 미미한 상태이다. 그러나, Si(113)면은 밀러 지표가 높으면서도 안정하기 때문에 Si(113)의 구조를 정확하게 알 수 있다면 밀러 지표가 낮은 Si 표면이 안정한 이유를 이해할 수 있을 것이다. 따라서 본 연구에서는 TOF-CAICISS 장치(Time of Flight - CoAxial Impact Collision Ion Scattering Spectroscopy) 장비와 RHEED(Reflection High Energy Electron Diffrction)를 이용하여 Si(113) 표면의 구조와 Si(113) 표면의 온도에 따른 구조 변화를 관찰하였다. TOF-CAICISS 실험결과를 보면 (3$\times$2)에서 (3$\times$1)으로 상변환하면서 Si(113) 표면에 오각형을 이루는 dimer 원자들과 adatom 원자들간의 높이차가 작아짐을 알 수 있다. RHEED 실험결과와 전산 모사 결과로부터 상온에서 Si(113)(3$\times$2) 구조를 가지다가 45$0^{\circ}C$~50$0^{\circ}C$에서 Si(113) (3$\times$1) 구조로 상변환한다는 것을 알 수 있다. 그러나, 아직 상전이 메카니즘은 명확하게 밝혀지지 않았다. 실험결과를 전산 모사와 비교함으로써 Si(113) 표면에 [33]방향으로 이온빔을 입사시켰을 경우 dabrowski 모델과 Ranke AI 모델이 적합하지 않다는 것을 알 수 있다./TEX>, shower head의 온도는 $65^{\circ}C$로 설정하였다. 증착된 Cu 박막은 SEM, XRD, AFM를 통해 제작된 박막의 특성을 비교.분석하였다. 초기 plasma 처리를 한 경우에는 그림 1에서와 같이 현저히 증가한 초기 구리 입자들이 관측되었으며, 이는 도상 표면에 활성화된 catalytic site의 증가에 기인한다고 보여진다. 이러한 특성은 Cu films의 성장률을 향상시키고, 또한 voids를 줄여 전기적 성질 및 surface morphology를 향상시키는 것으로 나타났다. 결과 필름의 잔류 응력과 biaxial elastic modulus는 필름의 두께가 감소함에 따라 감소하는 경향을 나타냈으며, 같은 두께의 필름인 경우, 식각 깊이에 따른 biaxial elastic modulus 의 변화를 통해 최적의 식각 깊이를 알 수 있었다.도의 값을 나타내었으며 X-선 회절 data로부터 분석한 박막의 변형은 증온도에 따라 7.2%에서 0.04%로 감소하였고 이 이경향은 유전손실은 감소경향과 일치하였다.는 현저하게 향상되었다. 그 원인은 SB power의 인가에 의해 활성화된 precursor 분자들이 큰 에너지를 가지고 기판에 유입되어 치밀한 박막이 형성되었기 때문으로 사료된다.을수 있었다.보았다.다.다양한 기능을 가진 신소재 제조에 있다. 또한 경제적인 측면에서도 고부가 가치의 제품 개발에 따른 새로운 수요 창출과 수익률 향상, 기존의 기능성 안료를 나노(nano)화하여 나노 입자를 제조, 기존의 기능성 안료에 대한 비용 절감 효과등을 유도 할 수 있다. 역시 기술적인 측면에서도 특수소재 개발에 있어 최적의 나노 입자 제어기술 개발 및 나노입자를 기능성 소재로 사용하여 새로운 제품의 제조와 고압 기상 분사기술의 최적화에 의한 기능성 나노 입자 제조 기술을 확립하고 2차 오염 발생원인 유기계 항균제를 무기계 항균제로 대체할 수 있다.

• 한국표면공학회지
• /
• 제47권6호
• /
• pp.303-310
• /
• 2014

In this study, the average in-situ stress in metallic thin film was measured during deposition of the Cu thin films on the Si(111) wafer and then the phenomenon of stress shift by the interruption of deposition was measured using Cu thin films. We have observed the stress shift in accordance with changing amount of atom's movement between the surface and grain boundary through altering the grain size of the Cu thin film with variety of parameters. The grain size is known to be affected on the deposition rate, film thickness and deposition temperature. As a experimental results, the these parameters was not adequate to explain stress shift because these parameters affect directly on the amount of atom's movement between the surface and grain boundary as well as the grain size. Thus, we have observed the stress shift toward tensile side in accordance with the grain size changing through the interlayer deposition. From an experiment with inserting interlayer before deposit Cu, in thin film which has big grain size with high roughness, amount of stress movement is higher along direction of tensile stress after deposition that means, after deposition process, driving force of atoms moving in grain boundary and on the surface of the film is relatively higher than before.

• 자원환경지질
• /
• 제31권2호
• /
• pp.111-125
• /
• 1998

Dispersion, migration and enrichment of environmental toxic elements from the Samkwang Au-Ag mine area were investigated based upon major, minor and rare earth element geochemistry. The Samkwang mine area composed mainly of Precambrian granitic gneiss. The mine had been mined for gold and silver, but closed in 1996. According to the X-ray powder diffraction, mineral composition of stream sediments and soils were partly variable mineralogy, which are composed of quartz, orthoclase, plagioclase, amphibole, muscovite, biotite and chlorite, respectively. Major element variations of the host granitic gneiss, stream sediments and soils of mining and non-mining drainage, indicate that those compositions are decrese $Al_2O_3$, $Fe_2O_3$, MgO, $TiO_2$, $P_2O_5$ and LOI with increasing $SiO_2$ respectively. Average compositional ranges (ppm) of minor and/or environmental toxic elements within those samples are revealed as As=<2-4500, Cd=<1-24, Cu=6-117, Sb=1-29, Pb=17-1377 and Zn=32-938, which are extremely high concentrations of sediments from the mining drainage (As=2006, Cd=l1, Cu=71, Pb=587 and Zn=481 ppm, respectively) than concentrations of the other samples and host granitic gneiss. Major elements (average enrichment index=6.53) in all samples are mostly enriched, excepting $SiO_2$, $Na_2O$ and $K_2O$, normalized by composition of host granitic gneiss. Rare earth element (average enrichment index=2.34) are enriched with the sediments from the mining drainage. Minor and/or environmental toxic elements within all samples on the basis of host rock were strongly enriched of all elements (especially As, Br, Cu, Pb and Zn), excepting Ba, Cr, Rb and Sr. Average enrichment index of trace elements in all samples is 15.55 (sediments of mining drainage=37.33). Potentially toxic elements (As, Cd, Cr, Cu, Ni, Pb, and Zn) of the samples revealed that average enrichment index is 46.10 (sediments of mining drainage=80.20, sediments of nonmining drainage=5.35, sediments of confluent drainage=20.22, subsurface soils of mining drainage=7.97 and subsurface soils of non-mining drainage=4.15). Sediments and soils of highly concentrated toxic elements are contained some pyrite, arsenopyrite, sphalerite, galena and goethite.

• 한국재료학회지
• /
• 제6권7호
• /
• pp.700-708
• /
• 1996

Flip chip bonding에 무전해도금기술을 적용하여 solder bumper형성의 최적 조건을 규명하였다. 시편은 AI 패턴된 4 inch Si 웨이퍼를 사용하고, 활성화 처리시 zincate 용액을 사용하였으며, 무전해 도금은 Ni-P 도금액고 Au immersion 용액을 사용하였다. 활성화 물질의 AI 침식정도 및 Zn 석출 정도를 알아보기 위하여 EDS측정을 하였고, 각 공전에서의 표면형상을 알아보기 위해 SEM 분석을 하였다. 열처리 후 금도금층의 주 결정성장 방향은 XRD를 이용하여 측정하였다. 산처리에서 질산과 황산 중 질산에 의한 산화막제거 정도가 더 우수하게 나타났다. 활성화 처리시 zincate 용액을 희석시킬수록 입자 크기가 미세해 지고, 활성화 물질은 pH 13-13.5, 상온, 농도 15-25%의조건에서 크기가 작은 Zn 활성화 물질이 균일하게 분포하였다. Ni과 Auan전해도금 속도는 온도와 pH가 증가할수록 증가하였다. Ni 무전해 도금 조건은 pH 4.5, 온도 $90^{\circ}C$, 시간 20분이며, Au 무전해 도금조건은 pH7, 온도 $80^{\circ}C$, 시간 10분이었다. 상온에서 $400^{\circ}C$까지 30분동안 열처리 한 후 금도금막의 결정 방향은 pH 7, 온도 $80^{\circ}C$, 시간 10분이었다. 상온에서 $400^{\circ}C$까지 30분 동안 열처리 한 후 금도금막의 결정 방향은 pH 7에서 (111), pH 9에서는 (200)과 (111)이 주 peak로 나타났으며, 열처리에 의한 결정 방향의 변화는 없었다. 전체 공정에서 최종적인 표면 형상에 영향을 주는 단계는 활성화 처리로서 flip chip의 bonding layer형성에 가장 중요한 요소임을 알 수 있었다.보다 자생지(自生地)에서 높은 함량(含量)을 보였다. 5. 무기성분함양(無機成分含量)의 차이(差異)는 K의 경우(境遇) 자생지(自生地)에서 보다 재배지(栽培地)에서 평균적(平均的)으로 10배이상(倍以上) 정도(程度) 높은 함량(含量)의 차이(差異)를 보였으나 Mn, Zn, Na, Cu 등(等)은 일정(一定)한 경향(傾向)을 보이지 않는 것으로 나타났다. 6. 유리(遊離) 아미노산(酸)의 함량(含量)은 자생지(自生地은)보다 재배지(栽培地)에서 전반적(全般的)으로 높은 함량(含量)을 나타내었고, 특(特)히 Arginine은 다른 성분(成分)들과 비교(比較)해 볼 때 가장 높은 조성(組成)의 차이(差異)를 나타내었다. 7. 야생(野生)더덕과 재배(栽培)더덕의 정유성분수율(精油成分收率)은 자생지재배(自生地栽培)에서는 모두 0.004% 였고 재배지(栽培地)에서는 야생(野生)더덕이 0.005%였다. 8. 더덕의 재배장소(栽培場所)에 따른 향기성분(香氣成分)은 총(總) 21종(種)이었으며 自生地(自生地)에서 야생(野生)더덕은 16종(種), 재배(栽培)더덕은 18종(種)이었고, 재배지(栽培地)에서 야생(野生) 더덕은 14종(種), 재배(栽培)더덕은 20(種)이었다. 9. Trans-2-hexanol은 야생(野生)더덕의 자생지(自生地) 재배(栽培)에서 피이크 면적(面積) 당(當) 50.3%, 재배지(栽培地)에서 피이크 면적(面積) 당(當) 43.3%를 보였으며 amylalcohol, furfuryl acetate, 2-methoxy-4-vinyl phenol(MVP)는 재배(栽培)더덕에서만 확인(確認)되었다.는 KI, BMI와 유의적인 양의 상관관계를 보였고 (p<0.01), HCL-C은 비체중, BMI, LBM, TBM와 유의적인 음의 상관관계를 보였으며, (p<0.01), KI, SBP와도 음의 상관관계를 보였다. (p<0.05), LCL-C는 KI와 유의적이인 양의

• 대한화학회지
• /
• 제44권3호
• /
• pp.220-228
• /
• 2000

청송 달기약수(상탕,중탕,하탕)의 수질특성을 파악하기 위해 1999년 5월부터 2000년 2월까지 약 1년 동안 계절별로 총 28개 항목의 함유성분을 분석하여 다음과 같은 결론을 얻었다. 각 탕별 약수의 수질에 큰 차이가 있었다. 하탕약수는 Mg과 Na이 상대적으로 높았?만? 중탕약수는 Ca, K, Si, Fe, Mn, 전기전도도, 총염기도, DO, $Cl^-$, $SO_4^{2-}$등에서 상대적으로 높은 값을 보였다. 건강상 유해성분인 As, Cd, $Cr^{6+}$, Hg는 검출되지 않았으며, Pb는 기준이하로 나타났다. 먹는물 수질기준을 초과한 항목으로는 경도, Fe와 Mn이었다. 그러나 샘물의 경우에는 이 기준을 적용하지 아니한다고 규정하였다. 약수의 계절별 특징으로는 온도를 제외한 기타 항목에서는 뚜렷한 차이가 없었다. 음용수에서 섭취할 수 있는 미네랄 양을 알아보고자 미국 국립과학아카데미의 하루 요구허용량과 섭취 음용수의 양을 1.O L로 하고 購종善嗤?기준으로 계산한 결과, Ca 35.05%, Mg 36.43%, Na 5.88∼10.63%, K 0.19∼0.57%, Mn 21.86∼43.72%, Zn 0.65%, Cr,Cu, P 등은 0.01% 이하이고, Fe는 95.1%이었다. 따라서 달기약수는 철분이 풍부한 약수임을 알 수 있었다.달기약수는 K index가 111.7∼254.6,O index가 2.3∼4.5로서 Hashimoto가 주장한 K index 5.2,O index 2.O을 상회하므로 건강에 좋고 맛있는 물의 조건을 만족하고 있다.

• 한국결정학회:학술대회논문집
• /
• 한국결정학회 2003년도 춘계학술연구발표회
• /
• pp.26-26
• /
• 2003

산업 폐기물로서 전량 매립되고 있는 styrene monomer (SM) 공정에서 발생되는 산화철 폐촉매를 사용하여 NiZn-페라이트를 합성하였고, 그 자기적 특성을 조사하였다. 평균입경 0.5㎛로 미분쇄된 산화철 폐촉매에 NiO 및 ZnO를 혼합하여 900℃에서 하소한후 1230℃에서 5시간 동안 소결하여 스핀넬형 페라이트 소결체를 얻었다. Ni/sub x/Zn/ub 1-x/Fe₂O₄(x=0.36, 0.50, 0.66) 및 (Ni/sub 0.5/Zn/sub 0.5/)/sub 1-y/Fe/sub 2+y/O₄(y=-0.02, 0, 0.02) 조성에 대하여 초투자율을 측정하였다. S-parameter를 측정하여 반사 감쇄량을 계산하였다. Ni/sub 0.5/Zn/sub 0.5/fe₂O₄ 조성의 경우 밀도 5.38 g/㎤ kHz에서의 초투자율이 59인 특성을 얻었다. 산화철 폐촉매를 이용하여 X-band 주파수 영역에서 높은 전자파 흡수능을 갖는 전파흡수체를 제조할 수 있음을 확인하였다. Ni/sub 0.5/Zn/sub 0.5/Fe₂O₄ 조성에 대하여 1100℃에서 하소한 분말을 사용하여 실리콘 고무에 복합시킨 후 전파흡수능을 측정하였다. 폐촉매에는 산화철 이외에 CeO₂가 주된 첨가물로 함유되어 있어서 페라이트의 합성 후에도 2차상으로서 존재하였다. 출발 원료인 산화철 폐촉매에 존재하는 K₂O 및 CeO₂를 제거하기 위하여 산처리와 분산제를 이용한 CeO₂ 분리과정을 행하였다. 정제된 산화철 폐촉매에 NiO 및 ZnO를 혼합하여 900℃에서 하소하여 스핀넬형 페라이트를 합성하고 1325℃에서 5시간 소결하였다. 위와 마찬가지로 Ni/sub x/Zn/sub 1-x/Fe₂O₄(x=0.36, 0.50, 0.66)과 (Ni/sub 0.5/Zn/sub 0.5/)/sub 1-y/Fe/sub 2+y/O₄(y=-0.02, 0, 0.02) 조성에 대하여 자기적 특성을 조사하였다.화된 중성자빔으로 측정하였다 BPC-Si를 구부려 슬랩의 곡률반경을 변화시키면서 단색기-시료-검출기가 평행파 반평행배치일 때 Cu(111), (200), (220), (311), (331), (420)면의 회절선을 측정하여 각 조건에서 분해능과 강도를 평가하였다.료의 가시적 변화를 통해 illumination angle 1.25mrad(Dose rate : 334 × 10³ e/sup -//sec·n㎡)일 경우 약 3초 이내에 비정질화가 시작됨을 알 수 있었고 이는 약 1 × 10/sup 6/ e/sup -//sec·n㎡ 의 전자선량에 해당되며 이를 기준으로 각각의 illumination angle에 대한 임계전자선량을 평가할 수 있었다. 실질적으로 Cibbsite와 같은 무기수화물의 직접가열실험 시 전자빔 조사에 의해 야기되는 상전이 영향을 배제하고 실험을 수행하려면 illumination angle 0.2mrad (Dose rate : 8000 e/sup -//sec·n㎡)이하로 관찰하고 기록되어야 함을 본 자료로부터 알 수 있었다.운동횟수에 의한 영향으로써 운동시간을 1일 6시간으로 설정하여, 운동횟수를 결정하기 위하여 오전, 오후에 각 3시간씩 운동시키는 방법과 오전부터 6시간동안 운동시키는 두 방법을 이용하여 품질을 비교하였다. 각 조건에 따라 운동시킨 참돔의 수분함량을 나타낸 것으로, 2회(오전 3시간, 오후 3시간)에 나누어서 운동시키기 위한 육의 수분함량은 73.37±2.02%를 나타냈으며, 1회(6시간 운동)운동시키기 위한 육은 71.74±1.66%을 나타내었다. 각각의 운동조건에서 양식된 참돔은 사육초기에는 큰 변화가 없었으나, 사육 5일 이후에는 수분함량이 증가하여 15일에는 76.40±0.14, 75.62±0.98%의 수분함량을 2회와 1회 운동시킨 참돔의 육에서 각각 나타났다. 운동횟수에 따른 지질함량은 2회 운동시킨 참돔은 5.83±2.08, 1회 운