• Journal of Magnetics
• /
• 제22권2호
• /
• pp.188-195
• /
• 2017

The ferromagnetic resonance and other magnetic properties dependence on $Ni^{2+}/Fe^{3+}$ ratio and crystallite size were investigated for nano nickel ferrite ($NiFe_2O_4$). The crystallite size was controlled by controlling the nickel content in the starting material solution. The XRD and TEM were utilized to measure the crystallite size through Scherrer formula and particle size respectively. The most frequent particle sizes were lower than crystallite size, which ranged from 16.5 to 44.65 nm. The general behavior of M-H loop shapes and parameters showed superparamagnetic one. The saturation magnetization had a maximum value at $Ni^{2+}/Fe^{3+}$ molar ratio equal to 0.186. The FMR signals showed, generally, broad linewidths, where the maximum width and minimum resonance field were for the sample of the lowest crystalline size. Furthermore, FMR resonance field shows linear dependence on crystalline size. The fitting relation was estimated to express this linear dependency on the base of behavior coincidence between particle size and the inverse of saturation magnetization. The given interpretations to understand the intercept and the slope meanings of the fitted relation were based on Larmor equation, and inhomogeneous in the anisotropy constant.

• Bulletin of the Korean Chemical Society
• /
• 제33권6호
• /
• pp.1962-1966
• /
• 2012

Boehmite sols have been prepared by crystallization of amorphous aluminum hydroxide gel obtained by hydrolysis and peptization of aluminum using acetic acid. The size of the boehmite crystallites could be controlled by Al molar concentration in amorphous gel by means of controlling grain growth at nucleation stage. The size of boehmite increases as a function of Al molar concentration. With increasing boehmite crystallite size, the $d_{(020)}$ spacing and the specific surface area decreases, whereas the pore volume increases along with pore size. Especially, the pore size of the boehmite sol particles is comparable to the crystallite size along the b axis, suggesting that the fibril thickness along the b axis among the crystallite dimensions of the boehmite contributes to the pore size. Therefore, the physical properties of boehmite sols can be determined by the crystallite size controlled as a function of initial Al concentration.

• 한국분말재료학회지
• /
• 제10권5호
• /
• pp.318-324
• /
• 2003

The nano-scale crystallite sizes of uranium oxide powders in simulated spent fuel were measured by the neutron diffraction line broadening method in order to analyze the sintering behavior of the dry process fuel. The mixed $UO_2$ and fission product powders were dry-milled in an attritor for 30, 60, and 120 min. The diffraction patterns of the powders were obtained by using the high resolution powder diffractometer in the HANARO research reactor. Diffraction line broadening due to crystallite size was measured using various techniques such as the Stokes' deconvolution, profile fitting methods using Cauchy function, Gaussian function, and Voigt function, and the Warren-Averbach method. The non-uniform strain, stacking fault and twin probability were measured using the information from the diffraction pattern. The realistic crystallite size could be obtained after separation of the contribution from the non-uniform strain, stacking fault and twin.

• 한국산업융합학회 논문집
• /
• 제4권4호
• /
• pp.413-418
• /
• 2001

The change of crystalline structure and mechanical properties of drawn PP filaments which was treated by tensioned and non-tensioned annealing was investigated. Measurements were carried out with XRD for crystallite size, density gradient tube for crystallinity. and UTM for mechanical properties. Tensioend and non-tensioned annealing were carried out $80^{\circ}C$, $100^{\circ}C$, $120^{\circ}C$: for 10min., 30min., 60min, in oil bath. It was found that the crystallinity and crystallite size of (110) plane of samples were increased with increasing of annealed temperature and time. Also crystallinity and crystallite size of samples which was tensioned annealing were larger than those of non-tensioned annealed samples. Initial modulus and tensile strength of tensioned annealed samples were higher than non-tensioned annealed samples, But elongation of tensioned annealed samples was lower than non-tensioned annealed samples.

• 한국재료학회지
• /
• 제3권4호
• /
• pp.319-326
• /
• 1993

Hydroxide법으로 ${\alpha}$-주산산(stannic acid)을 만든후, 하고온도를 $500^{\circ}C$~$1100^{\circ}C$로 조정하여 일차입자(Crystallite)크기가 8-54nm인 $SnO_2$ 분말을 제작하였다. 분말의 입자(drystalite)클기에 따른 분말특성와 $H_2$, CO가스(0.5v/o)에 대한 감응성 미치공기중에서의 저상변화특성에 미치는 영향을 조사하였다. 입자크기가 감소함에 따라, 분말의 FTIR 흡습특성은 증가하였으나, 격자상수는 일정하였다. 후막소자에서, $H_2$가스에 대해 최대감도를 나타내는 온도와 공기중에서 최소저항을 나타내는 온도는 입자크기가 미세해짐에 따라 점차 낮아졌다. 최소저항점과 최대감도점의 온도저하를 산소흡착종의 활성화에너지의 감소라고 유추하였고, 이러한 에너지의 감소가 미세입자에 의한 감도향상요인 중의 한가지라고 제의하였다.

• 한국산업융합학회 논문집
• /
• 제3권4호
• /
• pp.345-351
• /
• 2000

The change of crystalline structure of drawn PP filaments were investigated. Samples were treated by isothermally annealed after elevated heating from $20^{\circ}C$. Measurements were carried out with XRD for crystallite size and density gradient tube for crystallinity. Isothermally heat treatment were carried out at the temperature of $100^{\circ}C$, $120^{\circ}C$ and $140^{\circ}C$ for 10min., 30min. and 60min. in dry oven. The isothermal heat treatment after elevated heating from $20^{\circ}C$ were carried out at the temperature of $100^{\circ}C$, $120^{\circ}C$ and $140^{\circ}C$ for 10min., 30min. and 60min. with heating rate of $1^{\circ}C$/min., $5^{\circ}C$/min. and $10^{\circ}C$/min. From the results of this study, it found the following facts. It was found that the crystallinity and crystallite size of (110) plane of sample were increased with increasing of annealed temperature and time. Also crystallinity and crystallite size of samples which were isothermally annealed after elevated heating from $20^{\circ}C$ were higher than those of isohtermally annealed samples.

• Fibers and Polymers
• /
• 제6권3호
• /
• pp.206-218
• /
• 2005

Structural studies of series of 'as spun' and drawn PEEK fibers have been carried out using X-ray diffraction and optical microscopy techniques. The analysis of results suggest that fibers produced at a constant draw ratio with increasing draw temperatures show enhanced orientation and crystalline behaviour. The resolved equatorial and meridional traces provide additional structural parameters in terms of crystallinity, crystallite size, and crystallite thickness. It is concluded that drawing at a temperature below $T_g(i.e.,\;144^{\circ}C)$ results in poorly oriented non-crystalline materials, whereas drawing above $T_g$ results in highly oriented semi crystalline materials. Additional drawing proved to increase the overall orientation with slight improvements in lateral order of the chain molecules. Quantitative analysis revealed that the crystallite size increases with increasing drawing temperature. The results also revealed the increased crystallite size upon additional drawing. Crystalline orientation parameter, $_c$, suggests almost perfect orientation. In all cases, the amorphous orientation is found to be lower than the overall orientation parameter obtained from the optical birefringence. As a result of additional drawing, crystalline orientation was found to increase slightly but the increase in the orientation of non-crystalline material was found to be substantial. An average crystalline density was determined from the orthorhombic unit cell dimensions. It was found to vary as a result of processing conditions. It was also found that the value of the maximum birefringence shows heavy dependence on the chain conformation.

• 열처리공학회지
• /
• 제7권1호
• /
• pp.11-16
• /
• 1994

Anatase $TiO_2$ particles prepared by experiment were used to study the change of crystal structure by calcination temperature. The results were as follows. Crystallite size of anatase $TiO_2$ particles increased with calcination temperature. The rate of increasing the crystallite size of anatase $TiO_2$ particles was decreased below $700^{\circ}C$ and was markedly increased above $700^{\circ}C$. Unit cell volume of $TiO_2$ was expanded at low temperature and was contracted at high temperature. This result means that the growth of crystallite size was occured in the direction.

• 한국세라믹학회지
• /
• 제37권4호
• /
• pp.376-380
• /
• 2000

Carbon nanofibers with an average diameter of 100nm were reacted with SiO vapor generated from a mixture of Si and SiO2 to produce silicon carbide nanofibers at temperature ranging 1200∼1500$^{\circ}C$ under vacuum. The nanofiber reacted at 1200$^{\circ}C$ for two hours consisted of silicon carbide with an average crystallite size of 10-20nm, amorphous silica and a significant amount of unreacted carbon. The surface area of silicon carbide nanofiber, obtained after removal of amorphous silica and unreacted carbon from converted carbon nanofibers at 1200$^{\circ}C$, was as high as 150㎡/g. With increasing reaction temperature to 1500$^{\circ}C$, the surface area was decreased to 14㎡/g. Growth of SiC crystallite size with increasing conversion temperature of carbon nanofiber was confirmed from Scherrer formula using the (111) diffraction line and TEM images of converted carbon nanofibers.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.424-425
• /
• 2006

The effects of reaction temperature and precursor concentration on the microstructure and magnetic properties of ${\gamma}-Fe_2O_3$ nanoparticles synthesized as final products of iron acetylacetonate in chemical vapor condensation (CVC) were investigated. Pure ${\gamma}-Fe_2O_3$ phase was obtained at temperature above $900^{\circ}C$ and crystallite size of ${\gamma}-Fe_2O_3$ nanoparticles decreased with lowering precursor concentration. Also, the coercivity decreases with decreasing crystallite size of nanopowder. The lowest coercivity was 7.8 Oe, which was obtained from the ${\gamma}-Fe_2O_3$ nanopowder sample synthesized at precursor concentration of 0.3M. Then, the crystallite size of ${\gamma}-Fe_2O_3$ nanoparticles was 8.8 nm.