• Journal of the Korean Recycled Construction Resources Institute
• /
• v.3 no.1
• /
• pp.72-79
• /
• 2007

This study investigates the engineering properties of concrete incorporating lime stone crushed fine aggregate(Ls), which has been abandoned about 20% of total production due to the low purity. Test results showed that increase of Ls had favorable fluidity and slightly decreased air content. Bleeding capacity of all specimens was not appeared as those were high strength mixture proportion, but the specimens using more Ls accelerated initial and final setting. For the mechanical properties, specimens incorporating higher ratio of Ls, overall, resulted in increase of compressive strength, and exhibited very small inclined tendency in a dynamic elasticity modulus test In addition, for the durability properties, specimens incorporating higher Ls dramatically decreased a drying shrinkage and showed similar tendency in a frost & thaw test, as well as showing no more change in an accelerated neutralization test from the beginning. In conclusion, as it was confirmed in the experimental test, the high strength concrete applying Ls did not showed any problems in the aspects of engineering properties and mostly exhibited even more excellent quality than the specimens using natural fine aggregate.

• International Journal of Concrete Structures and Materials
• /
• v.4 no.2
• /
• pp.97-104
• /
• 2010

The crushed limestone sand is an abundant material in Tunisia, which induces many environmental problems. Indeed, available stocks of siliceous sand drastically decrease because of its massive use in hydraulic concrete. Some recent research works, carried out in Tunisia, concluded that crushed limestone sand may be used in concrete manufacture instead of siliceous sand traditionally used. In this context, an experimental study was achieved in order to quantify the influence of a partial or total substitution of siliceous sand by crushed limestone sand on hydraulic concrete performances. Preliminary chemical and physical tests on crushed sand indicated that it presented the minimum requirement for its use as aggregate in hydraulic concrete. 79 concretes were then prepared with siliceous sand, crushed limestone sand and a mix of the two sands. Their slump value and compressive strengths were measured on plain concretes. Complementary structural tests on reinforced concrete beam were also performed. The results proved that crushed limestone sand concretes showed workability and mechanical performances closed to those of siliceous sand concretes.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.46 no.2
• /
• pp.59-66
• /
• 2004

This study was performed to evaluate the freezing and thawing properties of the high strength concrete using recycled coarse aggregate. The recycled coarse aggregate replaced natural crushed aggregate by 0%, 25%, 50%, 75% and 100%. The compressive strength of the concrete using recycled coarse aggregate showed more than 300 kgf/$cm^2$ at the curing age 28 days. The mass loss ratio by freezing and thawing was less than 1% at all mix type. The relative dynamic modulus of elasticity was decreased with increasing the freezing and thawing cycles. Also, the durability factor by the freezing and thawing was decreased with increasing the content of recycled coarse aggregate. But, the recycled concrete except 100% recycled coarse aggregate showed 60 or more durability factor in the freezing and thawing 300 cycles. Accordingly, these recycled coarse aggregate can be used for high strength concrete.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.05b
• /
• pp.101-104
• /
• 2005

It analyzed the supply status of fine aggregate and find the point of issue related alternative fine aggregate through researches and interviews. The conclusions of the study are as follows. 1. Ready mixed concrete manufacture used crushed fine aggregate (15.5$\%$) and recycled fine aggregate (1.5$\%$) for alternatives aggregate than 1.3$\%$ in 1991. It is not allowed to use a recycled fine aggregate in ready mixed concrete, but they used it. 2. All alternative aggregate are satisfied the Korean Standard, But they showed low properties of mortar compared to when it replaced with natural fine aggregate. So, it is needed to make another special Korean Standard to use alternative aggregate in normal concrete by mixing method to recover the workability and compressive strength.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.11a
• /
• pp.197-200
• /
• 2004

The increase of the use of recycled aggregate is necessary for the decrease of building waste, but it is not possible to use concrete because of the various range of quality. Therefore, the quality grade and application method of recycled aggregate should be prescribed before the site application so in that this study we investigated the effect of the quality of recycled aggregate on the compressive strength, resistance freezing and thawing. As results of this study, the compressive strength of recycled aggregate concrete used recycled aggregate, as if it had high quality recycled aggregate is similar or higher to that of crushed stone. Also, this high quality recycled aggregate affect the increase of resistance freezing and thawing.

• Journal of the Korea Institute of Building Construction
• /
• v.17 no.1
• /
• pp.55-61
• /
• 2017

This paper is to investigate experimentally the effect of substitution of recycled coarse aggregate(RCA) under 13mm on the engineering properties of the concrete using gap graded coarse aggregates. Concretes with 0.4 of water to cement ratio(W/C) were fabricated to achieve 30MPa of design strength with coarse aggregate over 13mm in size with the maximum size of 25mm. RCA was substituted for coarse aggregate over 13mm from 10% to 50% and crushed coarse aggregate under 13mm was also substituted for coarse aggregate over 13mm from 20% to 40%, respectively. Test results indicated that the replacement of RCA up to 20% resulted in an increase of fluidity and strength. It also caused a decrease in the drying shrinkage due to dense packing effect by achieving continuous grading of mixed aggregates. For practical application of RCA, when properly substituted, the use of RCA enabled the concrete to reduce water contents and sand to aggregate ratio in mixing design stage of the concrete. And, it can also enhance the compressive strength of the concrete.

• Journal of the Korea Institute of Building Construction
• /
• v.19 no.5
• /
• pp.391-399
• /
• 2019

This study reviewed the possibility of recycling into exhausted aggregate resources in Korea as a means of utilizing coal gasification slag(CGS) from integrated gasification combined cycle(IGCC) while being commissioned in order to introduce the new system to Korea. In other words, in order to solve the problem of insufficient aggregate resources, CGS generated by IGCC as a residual aggregate for concrete secondary products, which is an empty mortar, was considered to replace CGS in the range of 0 to 100 % for mixed residual aggregate mixed with crushed sand A(CSa) of good quality and sea sand(SS) of deep particles, which are the most commonly used in the domestic construction industry. According to the study, replacing CGS with CSa or crushed sand B(CSb)+SS by 25 % to 50 % resulted in good results in the aspect of the granularity of the aggregate and the workability and compressive strength of cement mortar, which were found to be usable.

• Journal of the Korea Concrete Institute
• /
• v.26 no.3
• /
• pp.361-367
• /
• 2014

This paper investigates the punching shear strength of lightweight aggregate concrete (LWAC) slabs through a series of experimental study. Five full scale slabs were constructed using normal concrete and four different types of LWAC. Each lightweight aggregate (LWA) used in this study had different sources (clay, shale, or slate) and shapes (crushed or spherical shape). Based on the test results, the effect of the lightweight aggregates (LWA) on the punching shear behavior was investigated. From the test results, it was found that the punching shear failure surface of LWAC slab with spherical shape coarse aggregate was less inclined than that with crushed shape coarse aggregate, which resulted in an increase of the area of the shear failure surface. As a result, it leads to the increased punching shear strength of the slab. On the other hand, the failure surfaces of LWAC slab with crushed shape coarse aggregate and normal coarse aggregate were inclined similarly. Finally, the test results of this study were compared with the punching shear strength obtained from current design models, such as ACI and CEB-FIP, to examine the validation of current design model to predict the punching shear strength of the LWAC slab.

• Journal of the Korea Institute of Building Construction
• /
• v.20 no.4
• /
• pp.331-338
• /
• 2020

The aim of the research is to evaluate the possibility of using coal gasification slag (CGS) as a combined aggregate for concrete mixture. To achieve this goal, the fundamental properties and the durability of concrete were analyzed depending on various combining ratio of CGS into both fine aggregate with favorable gradation and relatively coarse particles. According to the results of the experiment, slump and slump flow were increased with content of CGS regardless of crushed fine aggregate with good and poor gradations while the air content was decreased. For the compressive strength of the concrete, in the case of using the crushed aggregate with good gradation, increasing CGS content decreased compressive strength of the concrete, while when the concrete used crushed aggregate with poor gradation, the compressive strength was the maximum at 50% of CGS content. As a durability assessment, drying shrinkage was decreased and carbonation resistance was improved by increasing CGS content. On the other hand, for freeze-thawing resistance, CGS influenced adverse effect on freeze-thawing resistance. Therefore, it is known that an additional air entrainer is needed to increase the freeze-thawing resistance when CGS was used as a combined aggregate for concrete.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.3 no.1
• /
• pp.15-21
• /
• 2015

Recently, attempts of replacing some of natural aggregate with mix of low quality aggregate are carried out for stable supply of aggregate. However, low quality aggregate such as recycled aggregate produced during the disposal process of construction wastes and by-product aggregate produced by industrial activities has problem of failing to comply to KS Standards. Therefore, we have compared fundamental properties of concrete by using granite crushed aggregate, recycled aggregate, blast furnace and electric arc furnace slag aggregate for effective utilization of lacking aggregate resources. As the result, slump in case of mixed use of aggregate was increased 0~10% compared to single use. Therefore, it is judged to be economically advantageous as it can expect effects in unit quantity or reduction of SP agent. Compressive strength in case of mixed use of aggregate was increased 0~10% compared to single use as it filled internal crevice of concrete with continuous particle size distribution. Accordingly, if we utilize by satisfying standard particle scope through mix of aggregate with different cause of formation in proper ratio, it was possible to confirm utility of mixed aggregate with demonstration of effects of increases of fluidity and compressive strength of concrete.