• International Journal of Precision Engineering and Manufacturing
• /
• v.4 no.1
• /
• pp.30-36
• /
• 2003

Brittle materials such as glasses and ceramics, which are very weak under impact loading, show fragile failure mode due to their low fracture toughness and crack sensitivity. When brittle materials are subjected to impact by small spheres, high contact pressure occurs at the impacted surface causing local damage on the specimen. This damage is a dangerous factor in causing the final fracture of structures. In this research, the crack propagation process of soda-lime glass by the impact of small spheres is explained and the effects of several constraint conditions for impact damage were studied by using soda-lime glass; that is, the effects for the materials and sizes of impact ball, thickness of specimen and residual strength were evaluated. Especially, this research has focused on the damage behavior of ring cracks, cone cracks and several other kinds of cracks.

• Journal of the Korean Society for Precision Engineering
• /
• v.18 no.11
• /
• pp.93-100
• /
• 2001

Brittle materials are very weak for impact because of typical characteristics which happen to be easily fractured with low fracture toughness and crack sensitivity. When brittle materials are subjected to impact due to small spheres, high contact pressure is occurred to impact surface and then local damage on specimen is developed, since there are little plastic deformations due to contact pressure compared to metals. This local damage is a dangerous factor which gives rise to final fracture of structures. In this research, the crack propagation process of soda lime glass by impact of small sphere is explained and the effects of the constraint conditions of impact spheres and materials for the material damage were studied by using soda-lime glass. that is the effects for the materials and sizes of impact ball, thickness of specimen and residual strength. Especially, this research has focused on the damage behavior of ring crack, cone crack and several kinds of cracks.

• Proceedings of the Korean Geotechical Society Conference
• /
• 2010.03a
• /
• pp.907-910
• /
• 2010

This study has developed a numerical analysis technique newly which can evaluate the damage propagation characteristics of civil infrastructures. To do this, numerical techniques are incorporated for the concrete members up to the compressive damage due to the bending compressive forces after the tensile crack based on the deformation mechanism. Especially, for the compressive damage stage after the tensile crack, the crack propagation process will be analyzed numerically using the concept of an equivalent plastic hinged length. Using this concept, we investigate the reasonability of the developed module by comparing commercial program for the tunnel structure. It can be established from this study that section forces, such as axial forces and the moment cracks takes place, can be related to the width of the crack making it possible to analyze the crack extension.

• Journal of the Earthquake Engineering Society of Korea
• /
• v.19 no.2
• /
• pp.75-83
• /
• 2015

The purpose of this study is to improve the previous damage evaluation model for RC members which is proposed by Igarashi[1] in 2010.The previous model was not confirmed by enough data of damage such as, residual crack length, width and area for exfoliation of concrete, etc. In addition, validation of the model is still insufficient. Therefore, experiment of a real-scale RC structure and experiment of RC columns using the high-strength concrete were conducted to gather the data of damage in RC members. The investigation has been conducted gathering the data not only additional experiments data but also existing data for modification of damage evaluation model. It has been investigated on changing damage in RC due to axial force ratio, shear reinforcement and shear span ratio. As a result, several problems were founded in the previous model, such as, hinge length($l_p$), spacing of flexural crack($S_{av,f}$), total width of flexural cracks regulated by maximum width of flexural crack($n_f$) and total width of shear cracks regulated by maximum width of shear crack($n_s$). New model is proposed and evaluated the damage properly.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.26 no.1
• /
• pp.153-159
• /
• 2002

Brittle materials such as ceramics and glasses show fragile fracture due to the low toughness and the crack sensitivity. When brittle materials are subjected to impact loading by small spheres, high contact pressure occurs to the surface of the specimen. Local damage is subsequently generated in the specimen. This local damage is a dangerous factor which gives rise to the final fracture of structures. In this research, impact damage of soda-lime glass plates by small spheres was evaluated by considering the effects of impact directions of indenter, pressure condition of specimen and residual strength after impact loading.

• Journal of the Korean Society for Precision Engineering
• /
• v.16 no.7
• /
• pp.168-177
• /
• 1999

Fatigue damage is the phenomena which is accumulated gradually with loading cycle in material. It is represented by fatigue crack growth rate da/dN and fatigue life ratio $N/N_{f}$. Fracture mechanical parameters estimating large crack growth behavior can calculate quantitative amount of fatigue crack growth resistance in engineering material. But fatigue damage has influence on various load, material and environment. Therefore, In this study, we propose that artificial intelligent fatigue damage model can predicts fatigue crack growth rate da/dN and fatigue life ratio $N/N_{f}$ simultaneously using fracture mechanical and nondestructive parameters.

• Journal of the Korean Society for Precision Engineering
• /
• v.14 no.6
• /
• pp.135-141
• /
• 1997

Low velocity impact test and compressive residual strength test after impact were performed by using Hercules AS4/3501-6[45/0/-45/90]$_{2s}$ laminated plate to investigate the low velocity impact damage behavior and the post-impact strength degradation on orthotropic composite laminate plate. Due to the lateral impact losd, the load path showed "" shape according to the laminate central deflection. Damage in a laminate occurs by inclined matrix crack at the damage initiation load stage and vertical matrix crack, occurs on the outer surface. Evaluating the compressive residual strength after the low velocty impact test, it could be found that there is a transient range where the compressive residual strength drop suddenly in the initial damage which is in the matrix crack range and the initial delamination area. is in the matrix crack range and the initial delamination area.

• The Journal of Engineering Geology
• /
• v.20 no.1
• /
• pp.89-100
• /
• 2010

Although various methods for determination of damage threshold in rock have been suggested, clear damage thresholds were determined by some methods, but different thresholds were measured by other methods. We determined the damage thresholds in Hangdeung granite using all the methods suggested, and investigated the best methods, applicability and errors of each method. The crack initiation threshold and the crack damage threshold which are important in investigation of characteristics of crack development and failure were verified by field strength ratio method and long-term constant load test. The crack closure stress and the crack initiation stress were 57.5 MPa and 77.6 MPa, and the most exact values were yielded by crack volumetric strain. The secondary crack initiation stress was 90.6 MPa and AE event count and AE event count rate were the effective methods. The volumetric stiffness, AE event count and AE event count rate were the most effective methods for determination of crack coalescence threshold and crack coalescence stress was 110.3 MPa. The crack damage stress was 127.5 MPa and was measured correctly by volumetric stiffness and AE event count rate. The ratio between crack initiation stress and uniaxial compressive strength was 0.47 which was very similar with the FSR value of 0.46. The ratio between crack damage stress and uniaxial compressive strength was almost the same as the ratio between long-term strength and uniaxial compressive strength, indicating that the crack initiation stress and the crack damage stress measured were correct.

• Structural Engineering and Mechanics
• /
• v.36 no.4
• /
• pp.481-497
• /
• 2010

The shaking table tests were conducted on two small-scale models (Model 1 and Model 2) to examine the earthquake-induced damage of a concrete gravity dam, which has been planned for the construction with the recommendation of the peak ground acceleration of the maximum credible earthquake of 0.42 g. This study deals with the numerical simulation of shaking table tests for two smallscale dam models. The plastic damage constitutive model is used to simulate the crack/damage behavior of the bentonite-concrete mixture material. The numerical results of the maximum failure acceleration and the crack/damage propagation are compared with experimental results. Numerical results of Model 1 showed similar crack/damage propagation pattern with experimental results, while for Model 2 the similar pattern was obtained by considering the modulus of elasticity of the first and second natural frequencies. The crack/damage initiated at the changing point in the downstream side and then propagated toward the upstream side. Crack/damage accumulation occurred in the neck area at acceleration amplitudes of around 0.55 g~0.60 g and 0.65 g~0.675 g for Model 1 and Model 2, respectively.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.05a
• /
• pp.155-158
• /
• 2005

Damage and fracture of concrete is characterized as the degradation of strength and stiffness. There can be modeled as the so-called homogenized crack model which can overcome the mesh sensitivity. But the plasticity and damage modeling for damage behavior before the fracture of concrete should be combined with the crack model. In this study, a damage function and an unified hardening-softening function are applied to the homogenized crack model to develope a 3-dimensional FEM program for nonlinear damage and fracture analysis of concrete. The comparison of numerical results and experimental data show that the combined modeling in this study can simulate the damage and fracture of concrete without the mesh-sensitivity. It is also shown that the behavior of the so-called Engineering Cementitious Composite(ECC) characterized by strain-hardening and multiple cracks can be well simulated using the modeling.