• Proceedings of the KWS Conference
• /
• 2004.05a
• /
• pp.168-170
• /
• 2004

터빈로터는 발전설비 중에서 가장 핵심 부분이며 동시에 심한 고온 응력을 받는 부분이다. 터빈로터 재료로는 Ni-Cr-Mo-V강과 CrMoV 강등이 사용된다. CrMoV 강은 발전 설비로 장시간 사용 중 열적피로나 크립손상, 고온 부식 등의 문제가 단독 혹은 복합적으로 발생하여 재료에 손상을 입히게 되고 결국에는 설비의 수명을 단축 시키곤 한다. (중략)

• Journal of the Korean Society for Precision Engineering
• /
• v.26 no.6
• /
• pp.90-96
• /
• 2009

Ultrasonic method using SH(shear horizontal) wave has been developed to determine the surface damage in fatigued material. Fatigue damages based on propagation energy were analyzed by multi-regression analysis in interrupted fatigue test specimen including CrMoV and 12Cr alloy steel. From the test results, as the fatigue damage increased the propagation time of the launched waves increased and amplitude of wavelet decreased. Also, analysis for the waveform modulation showed a reliable estimation, with confidence limit of 97% for 12Cr steel and 95% for CrMoV steel, respectively. Therefore, It is thought that SH ultrasonic wave technique can be applied to determine fatigue damage of in-service component nondestructively.

• Proceedings of the KSME Conference
• /
• 2001.11a
• /
• pp.266-271
• /
• 2001

Spherical indentation technique was developed to evaluate the flow properties of metallic materials in carbon steel, stainless steel and alloys, etc. Through the spherical indentation test, differently degraded 1Cr-1Mo-0.25V steel's mechanical properties were observed and compared with conventional standard test data. The flow properties of 1Cr-1Mo-0.25V steels were estimated by analyzing the indentation load-depth curve. To characterize the flow property, we used material yield slope and constraint factor index rather than strain-hardening exponent because the variation of strain-hardening exponent was very little and the data showed irregularly. And the constraint factor's effect was small when the material yield slope was taken into account.

• Journal of Advanced Navigation Technology
• /
• v.28 no.4
• /
• pp.532-537
• /
• 2024

In this study, wear characteristics and microstructure changes due to changes in alloy composition of Ni-Cr-Mo-V and Ni-Cr-Mo low-alloy steels used in brake discs for transportation system such as aircraft and high-speed trains. As a result of the hardness test, the hardness of C-Mo-V steel was the highest at 39.4±0.9HRc, and the hardness of Ni-Cr-Mo steel was the lowest at 32.4±0.6HRc. The friction coefficient tended to decrease as the vertical load increased. At a vertical load of 1 N, the friction coefficient of Ni-Cr-Mo steel was the highest at 0.842, and at a vertical load of 5 N, Mn-Cr-V steel was the highest at 0.696. Ni-Cr-Mo showed the largest wear scar width, depth, and wear amount, with a width of 711 ㎛, a depth of 8.24 ㎛, and a wear amount of 11 mg under a vertical load of 1 N, and a width of 1,017 ㎛, a depth of 19.17 ㎛, and a wear amount of 17 mg under a vertical load of 5 N. As a result of wear mechanism analysis, ploughing, delamination, and adhesion in all specimens, with plastic deformation being more prominently observed in Ni-Cr-Mo.

• Journal of Welding and Joining
• /
• v.26 no.3
• /
• pp.37-44
• /
• 2008

Charpy V-Notch test is commonly used to evaluate fracture toughness. However, since the region to be evaluated is limited to bulk material due to the specimen size required, individual evaluation of micro-structures on weldment is very difficult. In this study, ASP(Advanced Small Punch) test was carried out to evaluate material degradation and fracture toughness on the B.M, W.M and each micro-structures of HAZ for X20CrMoV121 and 2.25Cr1Mo steels with artificial aging time. In addition, to evaluate fracture toughness and material degradation of B.M and W.M of X20CrMoV121 steels with aging times, CVN (Charpy V-notch) test was performed. And then the correlation between ASP and CVN test on X20CrMoV121 steels was obtained. Furthermore, through this correlation, material degradation property of each micro-region of the HAZ in weldment, which was impossible to be evaluated by the CVN test, can be estimated and determined.

• Proceedings of the Korean Nuclear Society Conference
• /
• 2002.10a
• /
• pp.282.1-282
• /
• 2002

• Proceedings of the KSME Conference
• /
• 2000.11a
• /
• pp.322-327
• /
• 2000

This paper investigates the time-dependent crack growth in X20CrMoV 12 1 steel weld joints. Crack growth test are carried out $545^{\circ}C$ on side-grooved 1/2T CT specimens under static loads. A simulated material is produced for the intercritical HAZ, where fracture normally occurs. Constitutive properties are obtained for the simulated HAZ material as well as for the base metal and weld metal. Finite element analyses of crack growth are performed on the models with and without a HAZ layer, using the experimental crack length-time history. The inclusion of HAZ layer increase the load line velocities significantly. The crack growth rates are correlated reasonably well with $C^*$. The smallest crack size for the validity of $C^*$ is found much smaller than the ASTM crack initiation size for 1T CT specimen of creep ductile materials.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.20 no.5
• /
• pp.445-450
• /
• 2000

The integrity of the turbine rotors can be assessed by measuring reversible permeability and Vickers hardness of the aged rotors at service temperature. The measurement system of reversible permeability, which measured by applied alternating perturbing magnetic field, was constructed in order to evaluate material degradation, nondestructively. The test specimen was 1Cr-1Mo-0.25V steel used widely for turbine rotor material, and the specimens were prepared by the isothermal heat treatment at $630\;^{\circ}C$. The reversible permeability of the test materials were measured at room temperature. The peak interval of reversible permeability and Vickers hardness decreased with the increase of degradation. The degradation of test material may be determined nondestructively by the lineality of Vickers hardness and the peak interval of reversible permeability.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.12
• /
• pp.2109-2115
• /
• 2001

Miniaturized specimen technology is useful to characterize the mechanical behavior when it is difficult to sample the material enough for the test. In this study, two kinds of miniaturized Charpy impact specimens(i.e., miniaturized specimen with side groove and without side groove) of aged 1Cr- lMo-0.25V steel were prepared and tested. The relationship between the extent of degradation in terms of ductile brittle transition temperature(DBTT) and the fracture stress of 1Cr-1Mo-0.25V steel was established. The fracture stress obtained from miniaturized specimen without side groove turned out to be linearly related with the DBTT of standard specimen. Therefore the fracture toughness of aged turbine rotor steel might be evaluated by the fracture stress. In addition, the correlation between DBTT of standard specimen and that of miniaturized specimen was investigated. As the results of normalizing DBTT by maximum elastic tensile stress, the normalized DBTT of miniaturized specimen without side groove allows one to estimate that of standard specimen.

• Proceedings of the KSME Conference
• /
• 2001.06a
• /
• pp.231-236
• /
• 2001

A newly developed Advanced Indentation System (AIS), which is a portable and nondestructive system for evaluating tensile properties, was used to measure mechanical behavior of materials used under high temperature and pressure conditions. This test measures indentation load-depth curve during indentation and analyzes the mechanical properties related to deformation and fracture. Aging effects of Cr-Mo and Cr-Mo-V steel at high temperature were simulated. Tensile properties including yield strength and tensile strength at various temperature are obtained from the test. For all test materials and conditions, the AIS-derived results were in good agreement with those from conventional standard test method. Examples of the test results ate given and potential applications of the AIS to assess the integrity of aging structures are briefly discussed.