• Journal of the Korean Ceramic Society
• /
• v.56 no.1
• /
• pp.49-55
• /
• 2019

$Ti_{0.33}Al_{0.67}N/CrN$ nano-multilayers, which are known to have excellent wear resistance, were prepared using an unbalanced magnetron sputter to have various periods of 2-5 nm. $Ti_{0.33}Al_{0.67}N$ had a hexagonal structure in a single layer, but converted to a cubic structure by forming a multilayer with CrN, which has a cubic structure. Thus, $Ti_{0.33}Al_{0.67}N$ formed a superlattice in the multilayer. The $Ti_{0.33}Al_{0.67}/CrN$ multilayer with a period of 2.5 nm greatly exceeded the hardness of the $Ti_{0.33}Al_{0.67}N$ and the CrN single layer, reaching 39 GPa. According to the low angle X-ray diffraction results, the $Ti_{0.33}Al_{0.67}N/CrN$ multilayer maintained its as-coated structure to a temperature as high as $700^{\circ}C$ and exhibited hardness of 30 GPa. The thickness of the oxide layer of the $Ti_{0.33}Al_{0.67}N/CrN$ multilayered coating was less than one-tenth of those of the single layers. Thus, $Ti_{0.33}Al_{0.67}N/CrN$ multilayered coating had hardness and oxidation resistance far superior to those of its constituent single layers.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.21 no.5
• /
• pp.791-799
• /
• 1997

The wear characteristics and wear mechanisms of plasma sprayed Al/sub 2/ O/sub 3/-40%TiO/sub 2/ and Cr/sub 2/O/sub 3/ deposited on casting aluminum alloy(AC4C) were investigated. Specimens were processed for various coating thicknesses. Ball on disk type wear tester was used for wear test. The scratch test on plasma sprayed coating surface showed that critical load to break the coating layer was greater than 40 N. The critical load increase with the increase of coating thickness of specimens. The friction coefficient of Cr/sub 2/O/sub 3/ coating layer was less than that of Al/sub 2/O/sub 3/-40%TiO/sub 2/ coating layer. The wear resistance of Cr/sub 2/O/sub 3/ coating layer was greater than that of Al/sub 2/O/sub 3/-40%TiO/sub 2/ coating layer. Microscopic observation of worn surfaces was made by SEM. SEM observation showed that the main mechanism of wear for Al/sub 2/O/sub 3/-40%TiO/sub 2/ coating layer was abrasive wear under 50 N. For the case of Al/sub 2/O/sub 3/-40%TiO/sub 2/ coating layer, as the surface cracks perpendicular to sliding direction propagated, the wear debris was generated in wear track. However, the main mechanism of wear for Cr/sub 2/O/sub 3/ coating layer was brittle fracture under 150 N.

• Proceedings of the Korean Magnestics Society Conference
• /
• 1999.04a
• /
• pp.22-23
• /
• 1999

• Journal of Technologic Dentistry
• /
• v.31 no.4
• /
• pp.15-23
• /
• 2009

The aim of this study was to evaluate the bond strength of using a Au bonding agent applied on cp-Ti and nonprecious metal-gold-ceramic system. Metallic frameworks(diameter: 5mm, height: 20mm)(N=56, n=7per group) cast in Ni-Cr alloy, Co-Cr alloy and cp-Ti were obtained using acrylic templates and airborne particle abraded with $110{\mu}m$ aluminum oxide. Au bonding agent was applied on wash opaque firing as intermediate layer. SEM and SEM/EDS line profile were performed on the cutting the cross-section of the metal substrate-porcelain with intermediate Au coating. Groups were tested using shear bond strength(SBS) testing at 0.5mm/min. The mean SBS values for the ceramic-Au layer-metal combination were significantly higher than those ceramic-metal combination. While ceramic-Au layer-cp-Ti combinations failed to increase bond strength instead of using a titanium bonding porcelain. The appication of using Au intermediate layer significantly improve the bond strength combination with metal-ceramic system.

• KSII Transactions on Internet and Information Systems (TIIS)
• /
• v.8 no.11
• /
• pp.3775-3788
• /
• 2014

With the increasing number of the wireless and mobile networks, the way that people use the Internet has changed substantively. Wireless multimedia services, such as wireless video streaming, mobile video game, and mobile voice over IP, will become the main applications of the future wireless Internet. To accommodate the growing volume of wireless data traffic and multimedia services, cognitive radio (CR) and Information-Centric Network (ICN) have been proposed to maximize the utilization of wireless spectrum and improve the network performance. Although CR and ICN have high potential significance for the future wireless Internet, few studies have been conducted on collaborative operations of CR and ICN. Due to the lack of infrastructure support in multi-hop ad hoc CR networks, the problem is more challenging for video streaming services. In this paper, we propose a Cross-layer Video Streaming Mechanism (CLISM) for Cognitive Radio Ad Hoc Information Centric Networks (CRAH-ICNs). The CLISM included two distributed schemes which are designed for the forwarding nodes and receiving nodes in CRAH-ICNs. With the cross-layer approach, the CLISM is able to self-adapt the variation of the link conditions without the central network controller. Experimental results demonstrate that the proposed CLISM efficiently adjust video transmission policy under various network conditions.

• Journal of the Korean institute of surface engineering
• /
• v.34 no.2
• /
• pp.161-168
• /
• 2001

A Thermal Barrier Coating (TBC) can play an important role in protecting parts from harmful environments at high temperatures such as oxidation, corrosion, and wear in order to improve the efficiency of aircraft engines by lowering the surface temperature of the turbine blade. The TBC can increase the life span of the product and improve the operating properties. Therefore, in this study the mechanical and thermal properties of the TBC such as oxidation, fatigue and shock at high temperatures were evaluated. A samples of a bond coat (CoNiCrAlY) produced by the High Velocity Oxygen Fuel (HVOF) and Low Pressure Plasma Spray (LPPS) method were used. The thickness of the HVOF coating layer was approximately $450\mu\textrm{m}$ to 500$\mu\textrm{m}$ and the hardness number of the coating layer was between 350Hv and 400Hv. The thickness of the LPPS coating was about 350$\mu\textrm{m}$ to 400$\mu\textrm{m}$ and the hardness number of the coating was about 370Hv to 420Hv. The X-ray diffraction analysis showed that CoNiCrAlY coating layer of the HVOF and LPPS was composed of the $\beta$and ${\gamma}$phase. After the high temperature oxidation test, the oxide scale with about l0$\mu\textrm{m}$ to 20$\mu\textrm{m}$ thickness appeared at the coating surface on the Al-depleted zone was observed under the oxide scale layer.

• Journal of the Korean Magnetics Society
• /
• v.15 no.5
• /
• pp.257-260
• /
• 2005

We investigated the half-metallicity and magnetism for the zinc-blende CrS(001) surfaces by use of the full-potential linearized augmented plane wave (FLAPW) method. We considered two-types of (001) surfaces terminated by Cr (Cr-Term) and S (S-Term) atoms, respectively. From the calculated layer-by-layer density of states, it is found that both of the systems retain the half-metallicity at the (001) surfaces. The calculated magnetic moment ($4.07\;{\mu}_B$) for the CrS(S) atom in Cr-Term is enhanced considerably compared to the bulk value ($3.61\;{\mu}_B$) while that ($3.15\;{\mu}_B$) of the Cr(S-1) in S-Term is much reduced.

• Journal of Sensor Science and Technology
• /
• v.5 no.5
• /
• pp.69-77
• /
• 1996

In this paper, we fabricated the micro hotplate which consisted of a thin film heater(Pt/Cr bilayers) sandwiched with the thermal oxide and E-beam evaporated oxide. And we studied the electrical and the structural properties of Pt/Cr bilayers due to annealing temperature. When we compared the temperature measured from type k thermocouples with the temperature acquired from I.R. thermo-vision system according to the variations of emissivity, the emissivity of I-beam evaporated oxide was 0.5. The sheet resistance of Pt/Cr bilayers didn't depend on the Cr layer thickness, and it was considered as the existence of CrO between the Pt and the Cr layer. When the annealing temperature was increased from $500^{\circ}C$ to $700^{\circ}C$, the out-diffusions of Cr were increased(which was confirmed by AES depth profile) and the grain size of Pt(220) phase was enlarged also(analyzed by XRD and SEM photographs). From the results of XRD analysis and AES depth profile, the Pt/Cr bilayers annealed at $500^{\circ}C$ were more stable than any other cases in structural properties.

• Transactions of Materials Processing
• /
• v.26 no.3
• /
• pp.137-143
• /
• 2017

In this study, a wear test method was proposed to predict the wear life of the CrN layer coated on the surface of the press tools for manufacturing the auto-parts with ultra high strength steel (UHSS) with a tensile strength of 1.5 GPa. The pin-on-disc type wear test was carried out to confirm the feasibility and the reproducibility of the wear amount according to the test conditions such as the normal force, the sliding velocity, and the sliding speed. The test conditions were obtained from the finite element stamping analysis and the wear simulation. With the wear amount from the wear test, a prediction model of the wear depth in the CrN coating layer was proposed according to the test conditions with the design of experiments such as Taguchi method and the response surface method. The derived prediction model was then compared to the result of the Archard wear model, fully describing that the proposed model can effectively predict the wear life of the press tools for the auto-parts with UHSS.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.05a
• /
• pp.278-281
• /
• 2009

Selective laser sintering(SLS), a kind of rapid prototyping technology, can provide a process to form many types of coatings. Coated layers by selective laser melting are highly influenced by substrate, powder and laser parameters such as laser power, scan rate, fill spacing and layer thickness. Therefore an attempt to fabricate Fe-Ni-Cr coating on AISI H13 tool steel has been performed by selective laser sintering. In this study, Fe-Ni-Cr coating was produced by experimental facilities consisting of a 200W fiber laser which can be focused to 0.08mm and atmospheric chamber which can control atmospheric pressure with Ar. With power increase or energy density decrease, line width was decreased and line surface quality was improved with energy density increase. Surface quality of coating layer was improved with fill spacing optimization or layer thickness decrease.