• Korean Journal of Metals and Materials
• /
• v.50 no.1
• /
• pp.1-7
• /
• 2012

The fracture resistance and tensile properties of $Y_2O_3$ oxide dispersion strengthened steel containing 9 wt% Cr(9Cr-ODS) were measured at various temperatures up to $700^{\circ}C$. The fracture characteristics were compared with those of commercial E911 ferritic/martensitic steel. The strength of 9Cr-ODS was at least 30% higher than that of E911 steel at the test temperatures below $500^{\circ}C$. The strength difference between the two materials was almost diminished at $700^{\circ}C$. 9Cr-ODS showed cleavage fracture behavior at room temperature and unstable crack growth behaviors at $300^{\circ}C$ and $500^{\circ}C$. The J-R fracture resistance of 9Cr-ODS was much lower than that of E911 steel at all temperatures. It was deduced that the coarse $Cr_2O_3$ particles that were formed during the alloying process provided the crack initiation sites of cleavage fracture in 9Cr-ODS.

• Journal of Powder Materials
• /
• v.27 no.1
• /
• pp.37-43
• /
• 2020

The Fe-22wt.%Cr-6wt.%Al foams were fabricated via the powder alloying process in this study. The structural characteristics, microstructure, and mechanical properties of Fe-Cr-Al foams with different average pore sizes were investigated. Result of the structural analysis shows that the average pore sizes were measured as 474 ㎛ (450 foam) and 1220 ㎛ (1200 foam). Regardless of the pore size, Fe-Cr-Al foams had a Weaire-Phelan bubble structure, and α-ferrite was the major constituent phase. Tensile and compressive tests were conducted with an initial strain rate of 10^-3/s. Tensile yield strengths were 3.4 MPa (450 foam) and 1.4 MPa (1200 foam). Note that the total elongation of 1200 foam was higher than that of 450 foam. Furthermore, their compressive yield strengths were 2.5 MPa (450 foam) and 1.1 MPa (1200 foam), respectively. Different compressive deformation behaviors according to the pore sizes of the Fe-Cr-Al foams were characterized: strain hardening for the 450 foam and constant flow stress after a slight stress drop for the 1200 foam. The effect of structural characteristics on the mechanical properties was also discussed.

• Journal of Technologic Dentistry
• /
• v.37 no.1
• /
• pp.23-29
• /
• 2015

Purpose: The selective laser melting (SLM) process for dentistry, which is one of the additive manufacturing technologies (AM) allows for rapid production of a three-dimensional model with complex shape by directly melting metal powder. This process generates detailed items of a three-dimensional model shape through consolidation of a thin powder layer by utilizing both selective melting and laser beam simultaneously. In regard to SLM process, Fe-base powder, Ti-6AI-4V powder, AI-base powder, etc. have been researched. It is believed that the aforementioned technologies will be widely utilized in manufacturing metal parts using metal powder of raw material. This study chose Ni-Cr-Mo metal powder in order to manufacture metal powder materials that would be used in the selective laser melting for dentistry. Methods: This study manufactured metal powder using mechanical alloying technique (MA) among those metal powder manufacturing techniques. Moreover, this study aimed to utilize the metal powder manufactured after observing the characteristics of powder as preliminary data of Ni-Cr-Mo metal powder. This study could obtain the following conclusions within the experimental limitations. Results: As a result of mechanically alloying Ni-Cr-Mo powder over time, its mean particle size was $66.93{\mu}m$ $54.4{\mu}m$ and $45.39{\mu}m$ at 10h, 20h and 30h, respectively. The gtain form of metal powder by mechanical alloying technique was a sponge-like shape of irregular plate; however, the gtain form manufactured by high-pressure water aromization process had the following three types: globular type, chain type and oval type. Conclusion: This study found $37.65{\mu}m$ as the mean particle size of Ni-Cr-Mo metal powder, which was manufactured using water atomization technique under the following conditions: water atomization flux of 300 liter/min, hydraulic pressure of $400kgf/cm^2$ and injection angle of $45^{\circ}$. This study confirmed that the grain form of powder (solid particle form) would vary depending on the manufacturing process.

• Transactions of Materials Processing
• /
• v.8 no.3
• /
• pp.327-327
• /
• 1999

The oxidation behavior of 60%Cu-40%Zn brass haying small amounts of Zr, Cr, Mg, Al, and Si was studied between 873 and 1043 K in air. The alloying element of Mg was harmful, while other alloying elements were beneficial to oxidation resistance. Particularly, the simultaneous addition of Al and Si decreased the oxidation rate drastically. During oxidation, Zr formed ZrO₂, Cr formed CuCr₂O₄, Mg formed MgO, Al formed A1₂CuO₄, and Si formed amorphous SiO₂. These oxides were incorporated in the oxide scale composed predominantly of ZnO. The oxide scales formed on all the tested alloyswere prone to cracking, wrinkling, and spallation.

• Journal of Korea Foundry Society
• /
• v.22 no.6
• /
• pp.293-298
• /
• 2002

The effects of alloying elements added on the microstructure and high temperature oxidation behavior of the electro-slag remelted Fe-22Cr-5Al alloy were investigated. The amount of casting defect was makedly reduced by the electro-slag remelting. The electro-slag remelted ingot had a directionally solidified structure and cleaner surface than that of air-melted one. The high temperature oxidation reststance was greatly improved by the addition of Be and Zr.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 1998.10b
• /
• pp.31-31
• /
• 1998

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 1994.10b
• /
• pp.14-14
• /
• 1994

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 1999.10a
• /
• pp.14-14
• /
• 1999

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 1994.04c
• /
• pp.27-27
• /
• 1994

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1998.11a
• /
• pp.111-111
• /
• 1998