• Journal of the Korean Society for Railway
• /
• 제7권1호
• /
• pp.14-19
• /
• 2004

The effect of surface damage on fatigue properties of catenary wires were investigated to estimate their service lift. As surface defects of the wires caused by surface corrosion increase, surface roughness gets worse, and as roughness increases, it is easy for moisture coming from rain and dew to be condensed around uneven parts of the surface. The condensed moisture causes a locally severe corrosion which leads to damage of the wires. Corrosion of catenaty wires can make their actual lifetime shorter than that originally designed. The amount of decrease was more prominent as environmental conditions became more corrosive. They are also vibrated with some amplitude everytime pantographs touch contact line. The frequent cyclic load on the wire may result in a fatigue fracture. Surface damage by corrosion can make formation of crack initiation at fatigue. In the present study, the fatigue life of the used wire was measured 35 to 50% compared with that of new one in average.

• Journal of Welding and Joining
• /
• 제11권2호
• /
• pp.42-52
• /
• 1993

The corrosion fatigue fracture behaviour of dual phase steel was investigated in 3% NaCl solution at 302MPa and 137MPa. Fatigue test was conducted by cantilever type of self-made rotary bending fatigue testing machine. The fatigue strength increased with increasing the hardness of 2nd phase. Corrosion pit originated at the boundary of the 2nd phase. The size and number of corrosion pits were influenced by the 2nd phase hardness, and pits remained constant in size just after they were transited into cracks. The life of crack initiation was effected by stress level. The shape of relation of .DELTA. K and da/dN has smaller scattering in it in 3% NaCl solution than that in air. The higher the 2nd phase hardness is, the greater the corrosion fatigue life becomes. Corrosion fatigue fracture behaviour was primarily effected by mechanical factor in case of high stress(302MPa), but by electro-chemical reaction in a lower stress(137MPa). As stress level got lower and hardness of the 2nd phase got higher, the roughness of fracture surface increased.

• Proceedings of the KSR Conference
• /
• 한국철도학회 2003년도 추계학술대회 논문집(III)
• /
• pp.558-567
• /
• 2003

The catenary wires are damaged by periodic running of train as well as repeated stress. The wires are also degraded by atmosphere corrosion at fields. Corrosion of wires increased surface roughness and deteriorated mechanical properties by providing fatigue crack initiation sited resulting in a bad effect on service life of the wires. Fatigue test of catenary wires performed to estimate service lifetime. Also, simulation to analyze stress on catenary wires was conducted through modelling the finite elements for dynamic behaviors of wires. Fatigue life of catenary wires was estimated with fatigue and simulation tests.

• Transactions of the Korean Society of Mechanical Engineers
• /
• 제16권8호
• /
• pp.1503-1512
• /
• 1992

The strength evaluation and life prediction on the corrosion part of structure is one of the most important subjects, as a viewpoint of reducing economic loss by regular inspection, maintenance, repair and replace. For this purpose, it has been difficult to obtain the available data on growth of pit depth or growth rate of each pit which depends on time. In this paper, the life prediction and strength evaluation method was suggested for the structure with irregular stress concentration part by surface corrosion. The statistical distribution pattern of corrosion depth and the degree of fatigue strength decline were confirmed according to corrosion period by artificial corrosion of SS41 steel. The life prediction and the fatigue strength evaluation of materials with consideration of the corrosion period on the extreme value statistic analysis by the data of maximum depth of corrosion and on random variable was studied.

• Proceedings of the KSME Conference
• /
• 대한기계학회 2005년도 창립60주년 기념 추계 학술대회
• /
• pp.140.2-140.2
• /
• 2005

• Proceedings of the KSME Conference
• /
• 대한기계학회 2005년도 창립60주년 기념 추계 학술대회
• /
• pp.141.1-141.1
• /
• 2005

• Journal of Welding and Joining
• /
• 제14권2호
• /
• pp.36-45
• /
• 1996

Fatigue strength of the spot welded lap joint is considerably influenced by corrosive environments. Particularly, the chloride and the sulfide are most injurious to strength of the spot welded lap joint. Therefore, there is a need to evaluate its effect to corrosion fatigue strength for safe life design of spot welded structures. In order to evaluate their corrosion fatigue strength, corrosion fatigue tests on the spot welded lap joints of the uncoated and the coated high strength steel sheets were conducted in air and in 10% NaCl solution. Corrosion fatigue strength of the uncoated specimens were entirely lower than the coated one in NaCl solution, but those of the coated specimens in NaCl solution were lower than in air. And stress distribution in single spon welded lap joint subjected to tension-shear load was investigated by the finite element method. Using these results, we tried to evaluate corrosion fatgue strength of the various spot welded lap joints with maximum stress $\sigma_{max}$ at edge on loading side of the spot welded lap joint. We could find that corrosion fatigue strength could be quantitatively and systematically rearranged by $\sigma_{max}$.

• Journal of the Korean Society for Railway
• /
• 제5권1호
• /
• pp.32-39
• /
• 2002

As most railways are gradually electrified with modernized electric cars, the demand for catenary wires and their facilities are also increased. Catenary Wires are exposed to the marine area with air-borne salt or severely polluted industrial area with much corrosive emission gases depending on the locations. Corrosion of catenaty wires can make their actual lifetime shorter than that originally designed. Thus, the messenger and ACSR wires, kinds of catenary wire system, were investigated with respect to corrosion, which include new and used ones collected at the field. Tensile strengths and elongations appeared to decrease when the wires were exposed to corrosive environments. The amount of decrease was more prominent as environmental conditions became more corrosive. They are also vibrated with some amplitude everytime pentographs touch contact line. The frequent cyclic load on the wire may result in a fatigue damage. Surface damage by corrosion can make fatigue crack initiate with ease. In the present study, the fatigue life of the used wire was measured 50 to 60% compared with that of new one in average.

• Transactions of the Korean Society of Automotive Engineers
• /
• 제16권5호
• /
• pp.1-7
• /
• 2008

A study of new materials that are light-weight, high in strength has become vital to the machinery of auto industries. But then, there are a lot of problems with developing such materials that require expensive tools, and a great deal of time and effort. Therefore, the improvement of fatigue strength and fatigue life are mainly focused on by adopting residual stress. And Influence of corrosive condition for corrosion fatigue crack was investigated, after immersing in 3.5%NaCl, $10%HNO_3$+3.5%HF, $6%FeCl_3$. The immersion period was performed for 365days. The compressive residual stress was imposed on the surface according to each shot velocity based on shot peening, which is the method of improving fatigue life and strength. Fatigue life shows more improvement in the shot peened material than in the un peened material in corrosion conditions. The threshold stress intensity factor range was decreased in corrosion environments over ambient. Compressive residual stress of surface on the Shot-peen processed operate resistance force of fatigue crack propagation. The fatigue crack growth rate of the Shot-peened material was lower than that of the un peened material. Also m, fatigue crack growth exponent and number of cycle of the shot peened material was higher than that of the un peened material. That is concluded from effect of da/dN.

• Journal of the Korean Society for Railway
• /
• 제6권1호
• /
• pp.21-28
• /
• 2003

Environment-dependent fatigue life of Cu-Cd alloy wires used as messenger wires was investigated. Tensile test results showed the decrease of tensile strength and elongation of messenger wires by 3.7% and 16.8%, respectively, in used specimens when compared to new ones. Messenger wires used at industrial region for 26 yeras showed 35∼50% decrease in fatigue life, which is partly due to the in stress concentrations by formation of corrosion products at the surface. Single wires showed better fatigue properties than stranded wires, especially at low cycle regions with higher stresses. Stranded wires showed shorter fatigue lives than single wires because of friction between wires by surface contact. Service life of messenger wires was dependent upon the environments which they were exposed to. SO$_2$ and humidity deteriorated the fatigue properties by environmental degradation.