• Structural Engineering and Mechanics
• /
• 제53권5호
• /
• pp.867-880
• /
• 2015

Mechanical fastening is still one of the main methods used for joining components. Different techniques have been applied to reduce the effect of stress concentration of notches like fastener holes. In this work we evaluate the feasibility of combining laser shock peening (LSP) and cold expansion to improve fatigue crack initiation and propagation of open hole specimens made of 6061-T6 aluminum alloy. LSP is a new and competitive technique for strengthening metals, and like cold expansion, induces a compressive residual stress field that improves fatigue, wear and corrosion resistance. For LSP treatment, a Q-switched Nd:YAG laser with infrared radiation was used. Residual stress distribution as a function of depth was determined by the contour method. Compact tension specimens with a hole at the notch tip were subjected to LSP process and cold expansion and then tested under cyclic loading with R=0.1 generating fatigue cracks on the hole surface. Fatigue crack initiation and growth is analyzed and associated with the residual stress distribution generated by both treatments. It is observed that both methods are complementary; cold expansion increases fatigue crack initiation life, while LSP reduces fatigue crack growth rate.

• 대한기계학회논문집
• /
• 제13권3호
• /
• pp.451-460
• /
• 1989

본 논문에서는 기계용 부품소재로 많이 사용되는 SM45C에 대하여 이온질화 처리시 N$_{2}$:H$_{2}$ 가스조성비 변화에 따른 효과가 반복인장-압축하중을 받는 부식피로파괴의 거동에 미치는 영향을 중점적으로 연구하였다.

• 대한조선학회논문집
• /
• 제37권2호
• /
• pp.118-126
• /
• 2000

용접이음재에서는 용착금속, 열영항부 및 모재가 열사이클 및 조직의 변화에 의하여 각종 기계적 성질의 차이가 있으며, 특히 부식환경에서는 이들의 영향이 현저하게 나타나는 경우가 많다. 또 용접이음재의 피로강도는 이음형식, 용접금속 및 열영향부의 특성, 사용환경과 응력의 종류에 따라 변화한다. 따라서 본 연구에서는 현재 선박 및 해양구조물의 건조에 많이 채용되고 있는 TMCP 강재의 $CO_2$ 가스 용접이음재의 열영향부에 대한 대기중 및 부식환경중에서의 회전굽힘피로시험을 실시하여 피로균열의 발생 및 성장거동을 조사 검토하였다. 또한 대기중의 피로강도와 부식환경중의 피로강도를 비교함으로써 부식효과 및 응력집중효과 등을 고려한 용접이음재의 부식환경중에서의 피로강도 평가법 및 피로강도 설계곡선을 검토하였다.