• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.317-321
• /
• 2008

Piping in the Nuclear Power plants (NPP) are mostly consisted of carbon steel pipe. The wall thinning defect is mainly occurred by the affect of the flow accelerated corrosion (FAC) of fluid which flows in carbon steel pipes. This type of defect becomes the cause of damage or destruction of piping. Therefore, it is very important to measure defect which is existed not only on the welding partbut also on the whole field of pipe. Over the years, Infrared thermography (IRT) has been used as a non destructive testing methods of the various kinds of materials. This technique has many merits and applied to the industrial field but has limitation to the materials. Therefore, this method was combined with lock-in technique. So IRT detection resolution has been progressively improved using lock-in technique. In this paper, the quantitative analysis results of the location and the size of wall thinning defect that is artificially processed inside the carbon steel pipe by using IRT are obtained.

• Corrosion Science and Technology
• /
• v.4 no.4
• /
• pp.164-170
• /
• 2005

Pipelines have the highest capacity and are the safest and the least environmentally disruptive means for transmitting gas or oil. Recently, failures due to corrosion defects have become a major concern in maintaining pipeline integrity. A number of solutions have been developed for the assessment of remaining strength of corroded pipelines. In this paper, a Fitness-For-Purpose(FFP) type limit load solution for corroded city gas pipelines is proposed. For this purpose, a series of burst tests with various types of machined defects were performed. Finite element simulations were carried out to derive an appropriate failure criterion. Based on such solution along with existing solutions, an integrity evaluation program for corroded city gas pipeline, COPAP-CITY, has been developed.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.2
• /
• pp.172-177
• /
• 2016

In this paper, various electrochemical experiments were conducted in seawater solution to evaluate corrosion damage behavior of arc thermal sprayed Inconel 625 coating on SS400 steel in marine environment. As a result, corrosion damages of thermal sprayed Inconel 625 coating preferentially occurred at the defect area, and they were observed as a form of pitting corrosion in the galvanostatic experiments. In Tafel analysis, corrosion current density of Inconel 625 coating was relatively high due to influence of interconnected pores and Cr oxides in the thermal spray coating layer. On the other hand, the result of the potential measurement, thermal sprayed Inconel 625 coating should need the post-treatment which can compensate the defects like pores and cracks because Inconel 625 coating presented a higher potential of about 290 mV than that of the SS400 steel.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.06a
• /
• pp.929-933
• /
• 2003

Internal defects of thin pressure vessel used in the power plants or the chemical plants may be created and grow due to corrosion or creep fatigue to reduce the strength and cause critical failure during operation. Therefore it is very important to detect this defect at the early stage. For this purpose, non-destructive, non-contact and highly sensitive method should be considered for on-line application. In this paper, a laser shearographic interferometer is applied to inspect circular defects and notch defects existed inside of thin pressure vessel under the presence of pressure up to 3 times of atmospheric pressure. The influences of the defect shape and size as well as the internal pressure to the characteristic pattern in the shearography fringe are investigated, and the quantitative evaluation of the defect size is tried. Also the experimental results are compared with the destructive test results to show the applicability of this method to the quantitative evaluation of internal defects in the thin pressure vessel.

• Journal of the Korean Institute of Intelligent Systems
• /
• v.26 no.5
• /
• pp.343-350
• /
• 2016

Remaining lifetime prediction of the underground gas pipeline plays a key role in maintenance planning and public safety. One of main causes in the pipeline failure is metal corrosion. This paper deals with estimating the pipeline reliability in the presence of corrosion defects. Because a pipeline has uncertainty and variability in its operation, probabilistic approximation approaches such as first order second moment (FOSM), first order reliability method (FORM), second order reliability method (SORM), and Monte Carlo simulation (MCS) are widely employed for pipeline reliability predictions. This paper presents a fuzzy inference based reliability method (FIRM). Compared with existing methods, a distinction of our method is to incorporate a fuzzy inference into quantifying degrees of variability in corrosion defects. As metal corrosion depends on the service environment, this feature makes it easier to obtain practical predictions. Numerical experiments are conducted by using a field dataset. The result indicates that the proposed method works well and, in particular, it provides more advisory estimations of the remaining lifetime of the gas pipeline.

• Journal of the Korean Society for Heat Treatment
• /
• v.31 no.1
• /
• pp.12-17
• /
• 2018

We investigated the corrosion behavior of commercially pure cold working processed (CP)-Ti with coarse-grained (CG) microstructure heat-treated at $400^{\circ}C$ and $600^{\circ}C$, respectively. It is observed that corrosion resistance of as-received CP-Ti heat-treated at $400^{\circ}C$, at which recrystallization proceeds, is largely improved. Interestingly, the mechanical property of CP-Ti sample at $400^{\circ}C$ was scarcely deteriorated. It is attributed to the decrease of the defects such as strain variance and dislocation density. On the other hand, the annealing treatment at $600^{\circ}C$ of CP-Ti plate causes to grain growth with the noticeable reduction of mechanical property. Hence, it is considered that defect density such as strain and dislocation density is important microstructural parameter for the improvement of corrosion resistance. The introduction of proper annealing treatment can help to improve corrosion resistance without scarifying mechanical property of CP-Ti.

• Structural Engineering and Mechanics
• /
• v.84 no.3
• /
• pp.337-344
• /
• 2022

Due to corrosion defects on the surface of the oil pipe, the sealing performance of the annular blowout preventer (BOP) decreases, and the leakage of toxic and harmful gases such as H₂S and SO₂ will threaten the safety of operators on the well. Therefore, this paper establishes the FE model for evaluating the sealing performance of BOP-oil pipe corrosion defects, which is based on the rubber large deformation theory and rubber core sealing mechanism, and designs the experiment of BOP sealing performance to verify the accuracy of the FE model. The sealing performance of BOP sealing oil pipe with corrosion defects is studied. The research results show that the sealing performance of BOP is more sensitive to the axial size of corrosion defects. With the increase of oil pipe outer diameter, the critical size of defects increases continuously. The sensitivity of radial and depth dimensions is low, When for 88.9 mm outer diameter oil pipe, the axial critical size of corrosion defect is 20 mm, the radial critical size is 16 mm and the critical depth is 2 mm. Fit the formula between the outer diameter of oil pipe and the piston increment. According to the formula, the operator can calculate the piston stroke increment required by the BOP to complete the sealing when the oil pipe is corroded.

• Journal of the Korean Society for Precision Engineering
• /
• v.26 no.11
• /
• pp.55-61
• /
• 2009

The wall thinning defect of nuclear power pipe is mainly occurred by the affect of the flow accelerated corrosion (FAC) of fluid. This type of defect becomes the cause of damage or destruction of in carbon steel pipes. Therefore, it is very important to measure defect which is existed not only on the welding part but also on the whole field of pipe. This study use dual-beam Shearography, which can measure the out-of-plane deformation and the in-plane deformation by using another illuminated laser beam and simple image processing technique. And this study proposes Infrared thermography, which is a two-dimensional non-contact nondestructive evaluation that can detect internal defects from the thermal distribution by the inspection of infrared light radiated from the object surface. In this paper, defect of nuclear power pipe were, measured using dual-beam shearography and infrared thermography, quantitatively evaluated by the analysis of phase map and thermal image pattern.

• Corrosion Science and Technology
• /
• v.3 no.1
• /
• pp.20-25
• /
• 2004

In order to clarify the durability of protective coatings for maritime steel structures, various anti-corrosive organic coated steel samples were exposed for twelve years in semitropical marine environment at Miyakojima Island, Okinawa, JAPAN. Samples were various organic coated steel pipes, 4.0 m in length and 150 mm in diameter. While the bare steel pipe entirely corroded in 4.5 mm thickness in four and half years, these organic coated steel pipes exhibited protective appearances after twelve-year-exposure except for the defect in the coatings. Polyethylene (PE) lining pipe exhibited a good protective performance. Urethane painted pipe was also good but some barnacles stuck to its surface. A combination of petrolatum tape and FRP cover showed sufficient corrosion resistance for steel surface. The correlation in results between exposure and laboratory acceleration test was examined. It was found that salt spray test (SST) results corresponded to rusted area of scratched portion and that adhesion change of coating layer corresponded to the rotating immersion test result. Among the on-site measured data, volume resistivity is utilized for the index of corrosion protection performance of organic coating.

• Corrosion Science and Technology
• /
• v.19 no.1
• /
• pp.8-15
• /
• 2020

In this paper, the efficiency and the inhibition mechanisms of cobalt salts (cobalt nitrate and cobalt-exchange silica Co/Si) for the corrosion protection of AA2024 were investigated in a neutral aqueous solution by using the electrochemical impedance spectroscopy (EIS) and polarization curves. The experimental measurements suggest that cobalt cation plays a role as a cathodic inhibitor. The efficiency of cobalt cation was important at the concentration range from 0.001 to 0.01 M. The formation of precipitates of oxides/hydroxides of cobalt on the surface at low inhibitor concentration was confirmed by the Scanning Electron Microscopy/Energy Dispersive X-Ray Spectroscopy (SEM/EDS) analysis. EIS measurements were also conducted for the AA2024 surface covered by water-based epoxy coating comprising Co/Si salt. The results obtained from exposure in the electrolyte demonstrated the improvement of the barrier and inhibition properties of the coating exposed in the electrolyte solution for a lengthy time. The SEM/EDS analysis in artificial scribes of the coating after salt spray testing revealed the release of cobalt cations in the coating defect to induce the barrier layer on the exposed AA2024 substrate.