• Analytical Science and Technology
• /
• v.5 no.1
• /
• pp.97-101
• /
• 1992

Potentiodynamic corrosion tests were conducted to know the corrosion characteristics of the NiTi intermetallic compound composed of pure Ni and Ti in artificial saline. Tafel extrapolation and linear polarization technique show similar results. Corrosion current Icorr and corrosion rate was increased in the order of NiTi

• Corrosion Science and Technology
• /
• v.7 no.4
• /
• pp.212-218
• /
• 2008

Inorganic ion exchange compounds (IECs) including hydrotalcites and bentonite clays are a well known classes of layered mixed metal hydroxides or silicates that demonstrate ion exchange properties. These compounds have a range of applications from water purification to catalyst supports. The use of synthetic versions of these compounds as environmentally friendly additives to paints for storage and release of inhibitors is a new and emerging application. In this paper, the general concept of storage and release of inhibiting ions from IEC-based particulate pigments added to organic coatings is presented. The unique aspects of the IEC structure and the ion exchange phenomenon that form the basis of the storage and release characteristic are illustrated in two examples comprising an anion exchanging hydrotalcite compound and a cation exchanging bentonite compound. Examples of the levels of corrosion protection imparted by use of these types of pigments in organic coatings applied to aluminum alloy substrates is shown. How corrosion inhibition translates to corrosion protection during accelerated exposure testing by organic coatings containing these compounds is also presented.

• Journal of the Korean institute of surface engineering
• /
• v.37 no.2
• /
• pp.128-136
• /
• 2004

Effects of alloying elements on the surface characteristics of Fe-38Al intermetallic compounds were investigated using potentiostat. The specimens were casted by the vacuum arc melting. The subsequent homogenization and the stabilization led to the homogeneous DO$_3$ structure of the specimen. After the corrosion tests, the surface of the tested specimen was observed by the optical microscopy and scanning electron microscopy(SEM). For Fe-38 at.% Al intermetallic compound, the addition of Cr and Mo proved to be beneficial in decreasing the grain boundary attack by decreasing the active current density. Addition of Band Nb resulted in a higher active current density and also a higher passive current density. These results indicated the role of Cr and Mo in improving the pitting corrosion resistance of Fe-38 at.%Al intermetallic compound. Band Nb addition to Fe-38 at.%Al accelerated the granular corrosion. Fe-38 at.%Al containing Cr and Mo showed remarkably improved pitting corrosion resistance in comparison with Band Nb addition to Fe-38 at. %Al.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2022.11a
• /
• pp.73-74
• /
• 2022

The corrosion inhibitive effect of a new hydrazone-based heterocyclic compound for steel in simulated concrete pore solution with 3.5 wt.% sodium chloride was investigated by experimental and computational techniques. Electrochemical studies, up to 30 days of immersion, and surface analysis (X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM), and scanning electron microscope (SEM)) were performed to assess the corrosion protection abilities of investigated compound for steel rebar. Results showed that adding the organic compound to the chloride contaminated concrete pore solution decreased the corrosion rate of the steel rebar thanks to the effective adsorption of inhibitor molecules. After 30 days of immersion of steel rebar in inhibited chloride contaminated synthetic concrete pore solution, the inhibition efficiency exceeded 80% at low concentration of 1 mmol/L. Computational studies by Density Functional based Tight Binding (DFTB) method revealed the formation of covalent bonds between the hydrazone molecule and the iron surface.

• Journal of the Korean institute of surface engineering
• /
• v.34 no.4
• /
• pp.281-288
• /
• 2001

Phosphating treatments have been performed to improve paint adhesion and corrosion resistance of zinc and zinc alloy coated steels for a long time. In this work, the effects of the addition of chelate compound were studied to improve the stability of surface conditioning solution and properties of zinc phosphate films. The coalescence of colloidal Ti-compound and extraneous charged particles (alkaliearth metal cation such as $Mg^{2+}$ , $Ca^{2+}$ ) were suppressed by using a surface conditioning solution with chelate compound. Therefore, after surface conditioning solution containing chelate compound was left standing for one week at room temperature, the formation of a white sediment was decreased comparing to surface conditioning solution without chelate compound. The crystal size of phosphate film was fine and the whiteness value of phosphated zinc coated steel sheets was also high without the decrease of corrosion resistance and anti-patina. It was very effective to use chelate compound improving the stability of surface conditioning solution.

• Corrosion Science and Technology
• /
• v.7 no.3
• /
• pp.158-161
• /
• 2008

It is well known that iron is one of the most common impurity elements found in aluminum and its alloys. Iron in the aluminum forms an intermetallic compounds such as $FeAl_3$. The $FeAl_3$ particles on the aluminum surface are one of the most detrimental phases to the corrosion process and anodizing procedure for aluminum and its alloys. Trial and error surface treatment will be carried out to find the preferential and effective removal of $FeAl_3$ particles on the surfaces without dissolution of aluminum matrix around the particles. One of the preferable surface treatments for the aim of getting $FeAl_3$ free surface was an electrochemical treatment such as cathodic current density of $-2kAm^{-2}$ in a 20-30 mass% $HNO_3$ solution for the period of 300s. The corrosion characteristics of aluminum surface with $FeAl_3$ free particles are examined in a $0.1kmol/m^3$ NaCl solution. It is found that aluminum with free $FeAl_3$ particles shows higher corrosion resistance than aluminum with $FeAl_3$ particles.

• Journal of the Korean Society for Heat Treatment
• /
• v.29 no.4
• /
• pp.168-175
• /
• 2016

Influence of trace amount of Ca addition on the corrosion resistance was comparatively investigated in solutionized Mg-4%Zn and Mg-4%Zn-0.1%Ca alloys. In as-cast state, the alloys were characterized by primary ${\alpha}-(Mg)$ dendrite with MgZn intermetallic compound particles. After solution-treatment, both alloys consisted of single ${\alpha}-(Mg)$ phase by dissolution of the compound particles into the matrix. It was found from the immersion and electrochemical corrosion tests that the Mg-4%Zn alloy had better corrosion resistance than the Mg-4%Zn-0.1%Ca alloy. Morphological and compositional analyses on the surface corrosion products indicate that the incorporation of Ca oxide with low PBR value into the surface corrosion products would be responsible for the decreased corrosion resistance of the Ca-containing alloy.

• Journal of the Korea Institute of Military Science and Technology
• /
• v.14 no.6
• /
• pp.1018-1025
• /
• 2011

The improved properties of corrosion for 90Cu10NiFe alloy in natural seawater were explained by sodium diethyl dithio carbamate(NaDDC), namely organic compound, which is reagent for heavy metal extractions of waste water. The efficiency of NaDDC as corrosion inhibitor for 90Cu10NiFe alloy has been investigated in seawater after immersion in various concentrations of NaDDC solutions for 12~36hrs at pH 8.2 by weight loss test and electrochemical techniques including potentiodynamic polarization and SEM-EDS measurements. The results showed that the corrosion resistance of 90Cu10NiFe alloy improves with the increasing concentration of NaDDC but it did not improves with increasing time any more, so the highest inhibition efficiency was 93% at 100mg/L, 36hrs. The results obtained from weight losses and corrosion rates in polarization curve measurements were in good agreement. Therefore, it showed that NaDDC is a good inhibitor for copper corrosion of 90Cu10NiFe alloy.

• Journal of the Korean Society for Heat Treatment
• /
• v.12 no.1
• /
• pp.9-20
• /
• 1999

The effect of post oxidation, water-quenched after holding in air for 5~420 seconds or cooling or furnace cooling, on corrosion resistance and phase formation characteristics of the surface layer of SM20C and SM45C carbon steels after gas nirtrocarbursing in the $NH_3-5%CO_2-N_2$ gas atmosphere at $580^{\circ}C$ for 3hours is studied. The compound layers of two steels consist of ${\varepsilon}-Fe_{2-3}N$, ${\gamma}^{\prime}-Fe_4N$ and $Fe_3O_4$, phases, however, the quantity of ${\gamma}^{\prime}-Fe_4N$ phase increases for the furnace cooled specimen compared to that of air cooling specimen. With increasing $NH_3$ content in the gas mixture and also increasing the keeping time in the air after gas nitrocarburising, the ${\varepsilon}-Fe_{2-3}N$ phase of compound layer increases, while the decreased current density recognizing the improvement of corrosion resistance are shown. the passive current density of SM45C steel is lower than that of SM20C steel at the same nitrocarburising conditions.

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2018.11a
• /
• pp.179-180
• /
• 2018

Al - MMC, used as a neutron absorber, shows pitting corrosion and/or galvanic corrosion in 3.5wt.% NaCl solution. If pitting corrosion penetrates the core, neutron absorption performance could be affected. Galvanic corrosion was observed between Al 5052 and Al 1070, and pitting corrosion was observed around $B_4C$.