• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2004년도 추계학술대회
• /
• pp.319-324
• /
• 2004

In this study, the high strength and superior toughness spring steels as the suspension material, used for automobile and railroad industries were utilized to carry out the following investigations. Corrosion times were controlled in 7, 14, 30 and 60days to examine the relation between corrosion pit and compressive residual stress in the static corrosion environment after shot peened. And then corrosion current and corrosion potential were measured for every 24 hours to investigate the corrosion mechanism. Shot peened material shows the low or rate of corrosion current as compared with unpeened material. In case of peened material which has the highest residual stress, it has a low corrosion current density.

• Corrosion Science and Technology
• /
• 제5권3호
• /
• pp.90-93
• /
• 2006

Prevention of crevice corrosion was studied for STS 304 stainless steel using a Mg-alloy galvanic anode in solutions with various specific resistivity. The crevice corrosion and corrosion protection characteristics of the steel was investigated by the electrochemical polarization and galvanic corrosion tests. Experimental results show that the crevice corrosion of STS 304 stainless steel does not occur in solutions of high specific resistivity, but it occurs in solutions of low specific resistivity like in solutions with resistivities of 30, 60 and $115{\Omega}{\cdot}m$. With decreasing specific resistivity of the solution, the electrode potential of STS 304 stainless steel in the crevice is lowered. The potential of STS 304 stainless steel in the crevice after coupling is cathodically polarized more by decreasing specific resistivity indicating that the crevice corrosion of STS 304 stainless steel is prevented by the Mg-alloy galvanic anode.

• 한국산학기술학회논문지
• /
• 제14권9호
• /
• pp.4117-4123
• /
• 2013

본 연구에서는 해수용 열교환기의 코팅에 따른 해수 부식특성을 조사하기 위해 실험이 수행되었다. 코팅은 테플론, 전착, 세라믹+실리콘 3종을 선정하였고, 코팅되지 않은 알루미늄 부식과 비교하였다. 해수부식을 가속시키기 위하여 $70^{\circ}C$ 고온의 농도 3.5% 인공해수를 제작하여 9주 동안 침지부식을 시켰다. 침지기간에 따른 코팅의 부식특성 변화를 관찰하기 위하여 임피던스 분광법과 SEM을 이용하였다. Bode 선도에서 얻어진 분극저항으로부터 코팅재질의 내부식성을 확인하였다. 이중코팅은 4주 이후에도 코팅의 내부식성을 유지하였다. 또한 침지기간에 따라서 금속모재와 점착된 코팅면 사이에 블리스터가 발생할 수 있음을 확인하였다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1998년도 가을 학술발표회 논문집(I)
• /
• pp.197-202
• /
• 1998

The corrosion of steel reinforcements in concrete is of much concern in recent years. The mechanism of corrosion, however, is not clear yet. This study is focused on the corrosion of steel induced by internal chlorides in concrete at early ages. To examine the critical concentration of steel, half-cell potential, chemical composition of expressed pore solutions of mortars and rate of corrosion area were observed with respect to additions of chlorides, types of binders, water-binders ratio.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2001년도 추계학술대회논문집A
• /
• pp.216-221
• /
• 2001

The surface treatment technique to increase corrosion resistance is very important in mechanical components of structures. Therefore, this paper investigates the effects of shot peening on the corrosion resistance of SCM 420steel. The results show that the surface compressive residual stress largely increases, which cause the increase of corrosion resistance.

• 한국방사성폐기물학회:학술대회논문집
• /
• 한국방사성폐기물학회 2018년도 추계학술논문요약집
• /
• pp.179-180
• /
• 2018

Al - MMC, used as a neutron absorber, shows pitting corrosion and/or galvanic corrosion in 3.5wt.% NaCl solution. If pitting corrosion penetrates the core, neutron absorption performance could be affected. Galvanic corrosion was observed between Al 5052 and Al 1070, and pitting corrosion was observed around $B_4C$.

• 환경위생공학
• /
• 제17권4호
• /
• pp.53-60
• /
• 2002

This experiment was performed to investigate the characteristics of corrosion mechanism of water steel pipes using SEM(Scanning Electron Microscope) from March 1. 2002 to November 30. The characteristics shown in these results can be summarized as the following: 1. When I investigated to the characteristics of iron pipes and zinc pipes using a SEM, I could be found that there was a distintion in interface between an iron pipe and the scale, and that a zinc pipe wears a dark color. 2. I find much rate of $Fe_2O_3$ and a little rate of FeS as corrosion products, but I hardly find $FeCO_3$without carbon. 3 It was found that the oxide corrosion rate was 0.2~0.3mm/year. And then A-1 was 0.323mm/year that was very high.

• 대한안전경영과학회지
• /
• 제5권1호
• /
• pp.129-141
• /
• 2003

In this thesis, using the 400 series ferrite stainless steel such as 434LD$_2$ which are furter excellent then the existing ferric products in mechanical characteristics, and experiment has been conducted on corrosion resistance of sensor ring. The results are following. 1. The products before sintering are much more corrodible in the condition of spray test of salt water and ammonia than humidity and nitrogen condition. 2. 434LD$_2$ ferrite stainless steel has shown a good corrosion resistance without an addition surface treatment. thus the decreasing production process has been obtained. 3. As hardness value of $H_{RB}$ 80 and tensile test, 434LD$_2$ ferrite stainless steel with show a good endurance when it is combined to constant velocity joint (c/v joint), and has a good hardness properties endurable to sand and pebble impact.

• Corrosion Science and Technology
• /
• 제14권2호
• /
• pp.85-92
• /
• 2015

An on-line corrosion rate measurement system was developed using a personal computer, a data acquisition board and program, and a 2-electrode corrosion probe. Reliability of the developed system was confirmed with through comparison test. With this system, the effect of sodium nitrite ($NaNO_2$) as a corrosion inhibitor were studied on iron and aluminum brass that were immersed in sodium chloride (NaCl) solution. Corrosion rate was measured based on the linear polarization resistance method. The corrosion rates of aluminum brass and iron in 1% NaCl solutions were measured to be 0.290 mm per year (mmpy) and 0.2134 mmpy, respectively. With the addition of 200 ppm of $NO{_2}^-$, the corrosion rates decreased to 0.0470 mmpy and 0.0254 mmpy. The addition of $NO{_2}^-$ caused a decrease in corrosion rates of both aluminum brass and iron, yet the $NO{_2}^-$ acted as a more effective corrosion inhibitor for iron. than aluminum brass.

• Tribology and Lubricants
• /
• 제18권4호
• /
• pp.299-304
• /
• 2002

This paper reports the studies on the wear-corrosion behavior of ductile cast iron in the acidic environment. In atmosphere and variety of pH solution, specific wear rate and wear-corrosion characteristics of GCD 60 with various sliding speed and distance were investigated. And electrochemical polarization test of GCD 60 was examined in the environment of various pH values. The main results are as following : As the contact pressure increases, the critical velocity of specific wear rate becomes transient at low sliding speed. As pH value becomes low, wear-corrosion loss increases in the aqueous solution. As the corrosion environment is acidified, corrosion potential of GCD 60 becomes noble and corrosion current density increases.