• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2021년도 봄 학술논문 발표대회
• /
• pp.307-308
• /
• 2021

Corrosion of reinforced steel inside concrete is an important cause of performance degradation of reinforced concrete structures and has a profound influence on the durability of structures. In this study, three groups of different reinforced concrete structures exposed to the natural environment were subjected to chloride ion accelerated corrosion tests for up to 180 days. The corrosion velocity and ambient temperature of the samples were measured and recorded every day. Based on Faraday's law, the corrosion speed of steel bars could be measured, and the ambient temperature and humidity around the structure in corresponding time were compared. Through the measurement of up to 180 days, the influence of external ambient temperature and humidity on the corrosion speed of steel bars inside the concrete structure was found out. The results show that there is a good direct proportional relationship between temperature and corrosion speed. When the ambient temperature increases by 15℃, the corrosion rate increases by about one time.

• Tribology and Lubricants
• /
• 제18권4호
• /
• pp.299-304
• /
• 2002

This paper reports the studies on the wear-corrosion behavior of ductile cast iron in the acidic environment. In atmosphere and variety of pH solution, specific wear rate and wear-corrosion characteristics of GCD 60 with various sliding speed and distance were investigated. And electrochemical polarization test of GCD 60 was examined in the environment of various pH values. The main results are as following : As the contact pressure increases, the critical velocity of specific wear rate becomes transient at low sliding speed. As pH value becomes low, wear-corrosion loss increases in the aqueous solution. As the corrosion environment is acidified, corrosion potential of GCD 60 becomes noble and corrosion current density increases.

• Journal of Advanced Marine Engineering and Technology
• /
• 제38권8호
• /
• pp.974-980
• /
• 2014

Aluminum acts as sacrificial anode and corrosion protection with Al2O3 formation. If the same current on material for Al ships with steel ships supplies, the more hydrogen would be occurred, that result is bring about over-protection. For this reason, the damage by hydrogen embrittlement leads to the serious accident. In this study, we evaluate electrochemical behavior with rotation speed of 5083-H116 Al alloy material for Al ship in seawater. To examine the electrochemical characteristics with rotation speed and its effects on performance, experiments were conducted at four rotation speed. Results of experiments, the corrosion current density and damage were increased by applying the rotation speed compared to static state.

• 한국철도학회논문집
• /
• 제11권1호
• /
• pp.107-113
• /
• 2008

최근 생애주기비용 분석이 사회기반 시설물 경제성 평가 분야의 필수적 방법으로 대두됨에 따라 체계적이고 합리적인 방법으로 각 시설물의 생애주기비용을 산정하기 위한 노력이 진행되고 있다. 합리적인 생애주기비용 분석을 위해서는 초기비용 뿐만 아니라 유지관리 비용의 예측이 필요하나 국내에서는 고속철도 구간에 강교량을 가설한지 얼마 되지 않았기 때문에 이에 대한 유지관리 특성 등을 파악하고 있지 못한 실정이다. 이에 본 연구에서는 고속철도 소수주형교의 계측데이터와 Rahgozar 등이 제안한 부식열화를 고려한 피로강도감소계수 및 Miner 손상누적법칙을 이용하여 강교량의 주된 열화의 요인이 되는 부식과 피로의 손상을 고려한 체계신뢰성해석을 실시하였다. 이 체계신뢰성 해석결과를 바탕으로 고속철도 소수주형교의 설계단계 생애주기비용 분석 모델을 제안하였다.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2009년 추계학술발표대회
• /
• pp.82-82
• /
• 2009

강관은 물, 유류, 천연 가스 등을 운송하는 배관용 및 건물의 골조, 유압 및 공압 실린더, 가이드 레일 등 의 기계적 부품으로도 널리 사용되기도 한다. 이렇게 사용되는 강관의 70% 이상은 고주파 전기저항용접(High Frequency Electrical Resistance Welding,이하 ERW)으로 제조되고 있다. 아파트 등 실제 현장에서 ERW 강관에 흐르는 유체는 비드가 제거된 내면 부위에서 와류 (vortex)를 일으켜 기계적 침식(erosion)을 수반할 가능성이 있으며, 수격현상으로 인해 부식 부위에서 반복피로 하중을 받아 부식의 전파속도가 증가되어 최종적 으로 파손되는 경우도 예상할 수 있다. 이에 본 연구에서는 입열량을 달리하여 제조된 ERW 강관을 대상으로 강관 내부에서의 유속에 따라 홈부식 감수성에 미치는 영향을 확인하고자 하였다. 이를 위해 실제 사용 환경을 모사할 수 있는 장치를 제작하고 경계 조건을 선정하여 실험을 실시하였다. ERW 강관의 내부에서 유속이 빨라질 경우 부식속도는 증가를 하였고, 입열을 많이 받은 강관의 경우 부식속도가 감소하는 경향을 가졌다. 이러한 결과를 바탕으로 하여 ERW 강관에서 발생하고 있는 결함발생에 의한 피해를 극소화시킴으로서 안전하고 효율적인 관리에 기여하고자 한다.

• Corrosion Science and Technology
• /
• 제12권4호
• /
• pp.179-184
• /
• 2013

Pipe wall thinning caused by erosion and corrosion can adversely affect the operation of aged nuclear power plants. Some injured workers owing to pipe rupture has been reported and power reduction caused by unexpected pipe damage has been occurred consistently. Therefore, it is important to develop erosion-corrosion damage prediction model and investigate its mechanisms. Especially, liquid droplet impingement erosion(LDIE) is regarded as the main issue of pipe wall thinning management. To investigate LDIE mechanism with corrosion environment, we developed erosion-corrosion damage simulation apparatus and its capability has been verified through the preliminary damage experiment of 6061-Al alloy. The apparatus design has been based on ASTM standard test method, G73-10, that use high-speed rotator and enable to simulate water hammering and droplet impingement. The preliminary test results showed mass loss of 3.2% in conditions of peripheral speed of 110m/s, droplet size of 1mm-diameter, and accumulated time of 3 hours. In this study, the apparatus design revealed feasibility of LDIE damage simulation and provided possibility of accelerated erosion-corrosion damage test by controlling water chemistry.

• Journal of Mechanical Science and Technology
• /
• 제14권2호
• /
• pp.152-158
• /
• 2000

The contents of this paper include the evaluation of corrosion characteristics and the behaviour of stress corrosion cracking (SCC) for the weldment and post weld heat treatment (PWHT) specimen and parent of HT -60 steel using a slow strain rate test (SSRT) in synthetic seawater. Corrosion characteristics were obtained from the polarization curves by potentiostat, and SCC phenomena were evaluated through the parameters such as reduction of area and time to failure by comparing the experimental results in corrosive environment with those obtained in air. Corrosion rate of the weldment was the fastest, followed by parent and PWHT specimen. SCC phenomena between the weldment of HT-60 steel and synthetic seawater were shown. Besides, SCC was dependent upon the pulling speed greatly. Maximum severity of SCC was obtained at a speed of $10^{-6}mm/min$, whereas SCC could not be seen almost at $10^{-4}mm/min$. The resistance to SCC for PWHT specimen was improved considerably compared that of the weldment at $10^{-6}mm/min$. In case of SCC failure, it was verified from SEM examination that brittle mode and lots of pits could be seen at the fractured region near the surface of the specimen.

• 대한화학회지
• /
• 제55권4호
• /
• pp.575-580
• /
• 2011

Borate 완충용액에서 전극의 회전속도와 용액에 녹아 있는 $O_2$가 Zn-RDE의 부식에 미치는 영향을 조사하였다. 아연의 부식은 RDE의 회전속도와 산소의 양에 크게 영향을 받았으며, 부식 반응구조로 가역적 1-전자 전이에 이어서 일어나는 불균등화 반응(disproportion reaction)을 제안하였다.

• 한국철도학회:학술대회논문집
• /
• 한국철도학회 2007년도 추계학술대회 논문집
• /
• pp.1132-1140
• /
• 2007

As it recently appears that Life Cycle Cost Analysis may be considered as new methodology for economic valuation of infrastructure many researches have been made to assess LCC(Life Cycle Cost) of each facility based on a reasonable methods. In general, LCC is composed of construction cost and expected maintenance repair cost. And especially, maintenance repair cost must be estimated to enhance the reliability through systematic and reasonable methods. However in Korea, because high speed railway steel bridges are recently constructed no direct statistical data are available for the account of the maintenance cost and then their maintenance characteristics are not linear yet. Therefore, the approach proposed in the paper utilizes a theoretical determination and degradation of the corrosion and fatigue of the bridges based on Rahgozar et al.(2006)'s model on fatigue notch factor considering into the corrosion to incorporate the corrosion effect into the fatigue strength reduction model. And then, the corresponding probability of failure is calculated in terms of the reliability index using S-N curve to formulate the fatigue limit state. Therefore, this paper proposes the minimum Life Cycle Cost through optimum maintenance plan analysis of high-speed railway steel bridges under construction. Finally, this paper reviews the proposed model in oder to confirm the applicability and feasibility by appling it to high speed railway steel bridges under construction

• 한국표면공학회지
• /
• 제30권1호
• /
• pp.33-43
• /
• 1997

The effects of process parameters substrate such as substrate current and substrate temperature on the corrosion resistance of ion plated TiN film were investigated. TiN fims were deposited on speed steel on which Ti or Ni hed been previously evaporated. Dense TiN films could be obtained under higher substrate current(1A) and substrate temperature($500^{\circ}C$), whereas TiN films deposited with lower substances current(0.5A) and substrate temperature($300^{\circ}C$) showed porous structure. The corrosion resistances of high speed steel was considerably increased when dense TiN films had been formed on it. The effect of Ti and Ni interlayer on the increase of the corrosion resistance was also significant with dense TiN films, while there was little effect of interlayer on the corrosion resistance when TiN films were porous. the effect of interlayer on the corrosion resistance was more outstanding with Ti then with Ni, because Ti reacts more easily with oxygen to form an oxide layer, and it also shows higher resistance against chlorine containing corrosion media.