• Steel and Composite Structures
• /
• v.50 no.3
• /
• pp.363-374
• /
• 2024

The fatigue life of steel wire is affected not only by fatigue load, but also by corrosion environment in service period. Specially, the corrosion pit will lead to stress concentration on the surface of steel wire inducing the formation of fatigue cracks, and the fatigue cracks will accelerate the corrosion process. Therefore, the corrosion fatigue of steel wire is a coupling effect. In this study, the corrosion-fatigue coupling life curve is derived with considering corrosion-fatigue pitting stage, corrosion-fatigue short crack stage and corrosion-fatigue long crack stage. In addition, the stress concentration factors of different corrosion pits are calculated by COMSOL software. Furthermore, the effect of corrosion environment factors, that is, corrosion rate, corrosion pit morphology, frequency and action factor of fatigue load, on fatigue life of steel wire is analyzed. And then, the corrosion-fatigue coupling life curve is compared with the fatigue life curve and fatigue life curve with pre-corrosion. The result showed that the anti-fatigue performance of the steel wire with considering corrosion-fatigue coupling is 68.08% and 41.79% lower than fatigue life curve and fatigue life curve with pre-corrosion. Therefore, the corrosion-fatigue coupling effect should be considered in the design of steel wire.

• Computers and Concrete
• /
• v.21 no.4
• /
• pp.419-429
• /
• 2018

Climate changes, such as increasing of $CO_2$ concentration and global warming, will impact on the carbonation service life of concrete structures. Moreover, slag blended concrete has a lower carbonation resistance than control concrete. This study presents a probabilistic numerical procedure for evaluating the impact of climate change on carbonation service life of slag blended concrete. This numerical procedure considers both corrosion initiation period and corrosion propagation period. First, in corrosion initiation period, by using an integrated hydration-carbonation model, the amount of carbonatable substances, porosity, and carbonation depth are calculated. The probability of corrosion initiation is determined through Monte Carlo method. Second, in corrosion propagation period, a probabilistic model is proposed to calculate the critical corrosion degree at surface cracking, the probability of surface cracking, and service life. Third, based on the service life in corrosion initiation period and corrosion propagation period, the whole service life is calculated. The analysis shows that for concrete structures with 50 years service life, after considering climate changes, the service life reduces about 7%.

• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• v.35 no.1
• /
• pp.46-51
• /
• 2007

In this study, test results for fatigue crack propagation of Al-2024-T3511 are presented considering corrosion effects, and fatigue lifes are compared for the cases of corrosion and non-corrosion. Higher corrosion environments show lower fatigue life and faster crack growth. To predict the corrosion fatigue life, a corrosion factor concept is newly introduced and applied in Paris' law. The predicted results show good agreement with experimental data and this corrosion fatigue model can be successfully used for the prediction of fatigue life of aluminum structure with corrosion effects.

• Journal of Ocean Engineering and Technology
• /
• v.1 no.2
• /
• pp.123-129
• /
• 1987

Corrosion fatigue fracture of dual phase steel(SS41) and raw material steel(SS41) were investigated in 3.5% NaCl aqueous solution at PH 4,6,9 and 11. The fatigue limit of dual phase steel is increased approximately 1.8 times larger than that of raw material in air. The corrosion fatigue life of dual phase steel is about 5-10 times larger than that of raw material in 3.5% NaCl aqueous solution. The reduction of fatigue life is larger for the acidsalt solution than for the alkali salt solution. The reduction of stress level on the reduction ratio of corrosion fatigue life is large as pH 6-11. The reduction ratio of corrosion fatigue life of dual phase steel and raw material is nearly coincided at pH 2. While at pH4-2 the reduction ratio of corrosion fatigue life only depends on the corrosion effect. It has been found that the corrosion resistance effect of dual phase steel is smaller than that of raw material in corrosion fatigue crack propagation rate. As pH below 6 is changed, it can be clearly observed from raw material that the brittle intergranular fracture is characterized, and from the above result, the influence of corrosion of dual phase steel is small.

• Corrosion Science and Technology
• /
• v.12 no.5
• /
• pp.209-214
• /
• 2013

In the industry, accelerated corrosion test is used for the life time prediction. When anti-corrosion test proceeds in real environments, it is difficult that we predict and evaluate the corrosion life time because of the long test time such as 10 years or more time. Accelerated corrosion test and Salt spray test are able to test corrosion life time of products in the laboratory instead of outdoor corrosion test. Experimental procedure is selected for the corrosion standard specimen, exposure of the specimens, measurements of the mass loss and evaluating the mass loss data. As a result, the acceleration factor of the accelerated corrosion test to the outdoor corrosion test is 414.8. Therefore we can predict the corrosion life time of carbon steel during a short time period.

• Proceedings of the KSME Conference
• /
• 2003.04a
• /
• pp.220-225
• /
• 2003

In order to develop a method of corrosion fatigue design and estimate reliability of TMCP steel using as the material of heavy industries and plants, its corrosion susceptibilities and corrosion fatigue life considering corrosion degradation were investigated. From the results, the corrosion characteristic of TMCP steel is very susceptible in 3.5wt.% NaCl solution. Its susceptibility was linearly increased with the solution temperature increase. The potential difference due to the crack growth behavior in $25^{\circ}C$, 3.5wt.% NaCl solution is very susceptible. And it was found that stress amplitude has a linear relationship with the critical potential. Therefore, it is expected that the corrosion fatigue life of TMCP steel can be nondestructively predicted using the DCPD method.

• Journal of the Society of Naval Architects of Korea
• /
• v.44 no.4
• /
• pp.417-424
• /
• 2007

With regard to corrosion fatigue crack initiation life (Nc), it has been treated ambiguously for the member which doesn't have stress concentration area. In this research, in order to clarify the corrosion fatigue crack initiation life (Nc), corrosion fatigue tests were carried out. Reasonable and universal corrosion fatigue crack initiation life (Nc) was defined and corrosion fatigue crack initiation/propagation model was suggested also. As the fatigue crack which emanates from the pit is usually small, accordingly it is treated as a small crack. In addition, the observation of the corrosion fatigue fracture surfaces using SEM was conducted. And the fracture mechanics analysis using an intrinsic crack model was conducted for the treatment of the small crack. Finally, the followings were obtained. When there is no clear stress concentration point which seems to fall into a corrosion fatigue crack initiation life, the significance of the definition and suggestion of the moment of the reasonable and universal corrosion fatigue crack initiation life (Nc), at which the fatigue crack propagation rate becomes faster than the corrosion pit growth rate so that the fatigue crack initiates from the pit and propagates in earnest, has been clarified.

• Corrosion Science and Technology
• /
• v.4 no.3
• /
• pp.100-107
• /
• 2005

Reinforcing steel bars in reinforced concrete structures are protected from corrosion by passive film on the steel surface inside concrete with high alkalinity. However, when the passive film breaks down due to chloride ion ingressed into the RC structures, a corrosion initiates at the surface of steel bars. Then, internal pressure by volume expansion of corrosion products in reinforcing bars induces cracking and spalling of cover concrete, which reduces not only durability performance but also structural performance in RC structures. In this paper, a service life prediction of RC structures is carried out by using a micro-mechanics based corrosion model. The corrosion model is composed of a chloride penetration model to evaluate the initiation of corrosion and an electric corrosion cell model and an oxygen diffusion model to evaluate the rate and the accumulated amounts of corrosion. Then, a corrosion cracking model is combined to the models to evaluate critical amount of corrosion product for initiation cracking in cover concrete. By implementing the models into a finite element analysis program, a time and space dependent corrosion analysis and a service life prediction of RC structures due to chloride attack are simulated and the results of the analysis are compared with test results. The effect of crack width on the corrosion and the service life of the RC structures are analyzed and discussed.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2023.05a
• /
• pp.33-34
• /
• 2023

Corrosion of reinforcement steel is a major cause of deterioration in reinforced concrete (RC) structures. In order to protect these structures from corrosion, corrosion inhibitors are added to the concrete mix. In recent years, zwitterionic compounds have shown promising results as corrosion inhibitors in concrete due to their ability to form a protective layer on the surface of the reinforcement steel. The experimental study involves preparing concrete samples with different concentrations of adding the hybrid corrosion inhibitor at a high concentration of chloride ions. This study aims to determine the chloride threshold value and service life of hybrid corrosion inhibitors in reinforced concrete based on zwitterions. The samples are subjected to accelerated corrosion tests in a chloride environment to determine the threshold value and service life of the corrosion inhibitor. The effect of hybrid inhibitor on mechanical properties is guaranteed in allowable range. The chloride threshold concentration and service life of hybrid inhibitor containing samples perform greater than those of plain RC.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.11 no.6
• /
• pp.867-876
• /
• 1987

Corrosion fatigue fracture with change in the grain size of M.E.F. dual phase steel is investigated in 3.5% NaCI aqueous solution at pH 2, 4, 6, 9, and 11. Generally speaking, decrease in corrosion fatigue life is strongly dependent on decrease in pH and slightly on the grain size. For the B material with the big grain size, the fatigue life is small due to its large reduction ratio of corrosion fatigue life. The influence of grain size on the reduction ratio of corrosion fatigue life is large at pH 11-6. Whi9le at pH 4-2 the reduction ratio of corrosion fatigue life only depends on the corrosion effect. The larger grain size and the lass pH result in the greater influence on corrosion fatigue crack propagation rate. As pH decreases, the plateau portion in the crack propagation rate curves of the B material are distinct. Crack propagation rate curves become slow down at high .DELTA.K range because crack closure effect by minute corrosion products inside crack causes the oxidation corrosion action less effective for a certain period of time. In A material with small grain size, fatigue life is increased in proportion with increase of martensite intergranular which brings forth restraining the crack propagation decreases crack propagation rate. Corrosion pit which is created in the surface of specimen is found at pH 6,4 and 2 which is noticeable and the unevenness of the surface of the specimen becomes severe as pH decreases. The unevenness of corrosion fatigue fracture surface is severe as the effect of pH increases i.e. as pH decreases. In proportion with increase in the grain size and decrease in pH, the aspect of brittle fracture becomes evident.