• 한국재료학회지
• /
• 제26권3호
• /
• pp.130-135
• /
• 2016

To alloy high melting point elements such as boron, ruthenium, and iridium with copper, heat treatment was performed using metal oxides of $B_2O_3$, $RuO_2$, and $IrO_2$ at the temperature of $1200^{\circ}C$ in vacuum for 30 minutes. The microstructure analysis of the alloyed sample was confirmed using an optical microscope and FE-SEM. Hardness and trace element analyses were performed using Vickers hardness and WD-XRF, respectively. Diffusion profile analysis was performed using D-SIMS. From the microstructure analysis results, crystal grains were found to have formed with sizes of 2.97 mm. For the copper alloys formed using metal oxides of $B_2O_3$, $RuO_2$, and $IrO_2$ the sizes of the crystal grains were 1.24, 1.77, and 2.23 mm, respectively, while these sizes were smaller than pure copper. From the Vickers hardness results, the hardness of the Ir-copper alloy was found to have increased by a maximum of 2.2 times compared to pure copper. From the trace element analysis, the copper alloy was fabricated with the expected composition. From the diffusion profile analysis results, it can be seen that 0.059 wt%, 0.030 wt%, and 0.114 wt% of B, Ru, and Ir, respectively, were alloyed in the copper, and it led to change the hardness. Therefore, we verified that alloying of high melting point elements is possible at the low temperature of $1200^{\circ}C$.

• Asian Pacific Journal of Cancer Prevention
• /
• 제17권10호
• /
• pp.4609-4614
• /
• 2016

Purpose: To evaluate the therapeutic effects of copper reduction on angiogenesis-related factors in patients with glioblastoma multiforme treated by gamma knife radiosurgery. Materials and Methods: In the present block randomized, placebo-controlled trial, fifty eligible patients with a diagnosis of glioblastoma multiforme who were candidates for gamma knife radiosurgery were randomly assigned into two groups to receive daily either 1gr penicillamine and a low copper diet or placebo for three months. The intervention started on the same day as gamma knife radiosurgery. Serum interleukin-6 (IL-6), tumor necrosis $factor-{\alpha}$ ($TNF-{\alpha}$), vascular endothelial growth factor (VEGF) and copper levels were measured at baseline and after the intervention. The serum copper level was used as the final index of compliance with the diet. In order to control probable side effects of intervention, laboratory tests were conducted at the beginning, middle and end of the study. Results: The patients had a mean age and Karnofsky Performance Scale of 43.7 years and 75 respectively. Mean serum copper levels were significantly reduced in intervention group. Mean survival time was 18.5 months in intervention group vs. 14.9 in placebo group. VEGF and IL-6 levels in the intervention group were also significantly reduced compared to the placebo group and $TNF-{\alpha}$ increased less. Conclusions: It seems that reducing the level of copper in the diet and dosing with penicillamine leads to decline of angiogenesis-related factors such as VEGF, IL-6 and $TNF-{\alpha}$. Approaches targeting angiogenesis may improve survival and can be used as a future therapeutic strategy.

• 보존과학회지
• /
• 제34권4호
• /
• pp.259-271
• /
• 2018

Outdoor copper alloy is exposed to the atmospheric environment, accelerating corrosion progress compared with indoor copper alloy. In order to prevent corrosion, the outdoor copper alloy is coated with wax to block external corrosion factors. However, corrosion of the inside of the coating film is highly likely to continue without the internal corrosion prevention treatment. B.T.A, which is used as a copper alloy water-soluble corrosion inhibitor, has a high possibility of being harmful to the human body and is mainly used to treat excavated artifacts. This study had selected the water-soluble corrosion inhibitor, which was easier to use than the existing wax and B.T.A being used in corrosion inhibition treatment for outdoor copper alloy. A comparative study was conducted on B.T.A, which is a water-soluble corrosion inhibitor used on excavated artifacts, and $VCI^{(R)}$, $Rus^{(R)}$, and L-cys, an amino acid corrosion inhibitor, used for tin bronze test pieces. The experimental method was conducted for a certain period of time with the salt, acid, and air pollution affecting the corrosion of outdoor copper alloy. Based on experiment results, it was concluded that the best water - soluble copper alloy corrosion inhibitor in the atmospheric environment is $VCI^{(R)}$. and it could be considered to be applied in replacement of B.T.A due to its low harmfulness. In addition, $VCI^{(R)}$ is judged to serve as a corrosion inhibitor for outdoor copper alloy because it showed the best result even in the outdoor exposure test which is a real atmospheric environment.

• 한국기계가공학회지
• /
• 제12권4호
• /
• pp.61-68
• /
• 2013

As an advance study for the development of a heat sink for special purpose high power illumination, an investigation was made to find feasibility for the application of copper plated EP to a heat sink of small LED light of less than 10W installed in commercial product. In this study, the plated heat sink with EP copper was fabricated for the conventional LED light. It was used actually for finding heat radiation property and effectiveness of the heat sink accompanied with measurement of luminous intensity. The heat is radiated by transfer and dissipation only through the copper plated surface due to extremely low heat conductivity of EP in case of EP heat sink; however the total area of the plate plays the function of heat transfer as well as heat radiation in case of the aluminum heat sink. It seems that the volume difference of heat radiating material is so big that the temperature $P_1$ is 9.0~12.3% higher in 3W and 42.7~54.0% higher in case of 6W volume difference of heat radiating material is so big that the temperature $P_1$ is 9.0~12.3% higher in 3W and 42.7~54.0% higher in case of 6W even though heat transfer rate of copper is approximately 1.9 times higher than that of aluminum. It was thought that this is useful to utilize for heat sink for low power LED light with the low heating rate. Also, the illumination could be greatly influenced by the surrounding temperature of the place where it is installed. Therefore, it seems that the illumination installation environment must be taken into consideration when selecting illumination. Further study was expected on order to aims at development of an exterior surface itself made into heat radiation plate by application of this technology in future.

• 한국재료학회지
• /
• 제15권4호
• /
• pp.240-245
• /
• 2005

An oxygen free copper was severely deformed by accumulative roll-bonding (ARB) process for improvement of its mechanical properties. Two copper sheets 1 m thick, 30 mm wide and 300 m long are first degreased and wire-brushed for sound bonding. The sheets are then stacked to each other, and roll-bonded by about $50\%$ reduction rolling without lubrication at ambient temperature. The bonded sheet is then cut to the two pieces of same dimensions and the same procedure was repeated to the sheets up to eight cycles $(\varepsilon-6.4)$. TEM observation revealed that ultrafine grains were developed after the third cycle, and their size was slightly increased at higher cycles. Tensile strength of the copper increased with the strain at low strain levels, but it hardly increased from 3 cycles $(\varepsilon>2.4)$ due to occurrence of dynamic recovery, even if the imposed strain increased.

• 한국세라믹학회지
• /
• 제54권1호
• /
• pp.61-65
• /
• 2017

Examined in this study were the effects of copper oxide (II) addition and sintering conditions on the chromatic characteristics of copper glaze. Oxidatively sintered samples exhibited the negative increase of $CIEa^*$ and the positive increase of $CIEb^*$ with the increase of CuO concentration, leading to Green and Green-Yellow coloration. On the other hand, $CIEa^*$ and $CIEb^*$ of reductively sintered samples were positively increased in direct proportion. The green color of oxidatively sintered samples was originated from the $Cu^{2+}$ ions formed by the dissolution of CuO. The reductively sintered samples resulted in dull tone red color with low chroma. Such behavior seems to be influenced by the interplay of metal Cu aggregation, metal Cu globule, and $Cu_2O$ formed in the glaze layer through the redox interaction of CuO during the sintering process.

• Carbon letters
• /
• 제18권
• /
• pp.49-55
• /
• 2016

Refuse-derived fuel (RDF) produced using municipal solid waste was pyrolyzed to produce RDF char. For the first time, the RDF char was used to remove aqueous copper, a representative heavy metal water pollutant. Activation of the RDF char using steam and KOH treatments was performed to change the specific surface area, pore volume, and the metal cation quantity of the char. N₂ sorption, Inductively Coupled Plasma-Atomic Emission Spectrometer (ICP-AES), and Fourier transform infrared spectroscopy were used to characterize the char. The optimum pH for copper removal was shown to be 5.5, and the steam-treated char displayed the best copper removal capability. Ion exchange between copper ions and alkali/alkaline metal cations was the most important mechanism of copper removal by RDF char, followed by adsorption on functional groups existing on the char surface. The copper adsorption behavior was represented well by a pseudo-second-order kinetics model and the Langmuir isotherm. The maximum copper removal capacity was determined to be 38.17 mg/g, which is larger than those of other low-cost char adsorbents reported previously.

• 전기화학회지
• /
• 제7권4호
• /
• pp.173-178
• /
• 2004

플라즈마 화학 기상 증착법으로 구리 막$(foil,\;35{\mu}m)$표면 위에 $SiH_4$와 Ar혼합가스를 공급하여 실리콘 박막을 증착 한 후 리튬 이온전지의 음극으로 활용하였다. 증착 온도에 따라 비정질 실리콘 박막과 copper silicide박막 형태의 다른 두 종류의 실리콘 박막 구조가 형성되는 것이 관찰되었다. $200^{\circ}C$ 이하의 온도에서는 비정질 실리콘 박막이 증착되었고, $400^{\circ}C$ 이상의 온도에서는 실리콘 라디칼과 확산된 구리 이온의 반응에 의한 그래뉼러 형태의 copper silicide박막이 형성되었다. 비정질 실리콘 박막은 copper silicide박막 보다 높은 용량을 나타냈으나 충·방전 반응에 의한 급격한 용량 손실을 나타냈다. 이것은 비정질 실리콘 박막의 부피 팽창에 의한 것으로 추정된다. 그러나 copper silicide 박막을 음극으로 사용했을 때는 copper silicide를 형성한 실리콘과 구리의 화학결합이 막 구조의 부피변화를 감소 시켜줄 뿐 아니라 낮은 전기 저항을 갖기 때문에 싸이클 특성이 향상되었다.

• 한국재료학회지
• /
• 제23권7호
• /
• pp.392-398
• /
• 2013

A two-pass differential speed rolling(DSR) was applied to a deoxidized low-phosphorous copper alloy sheet in order to form a homogeneous microstructure. Copper alloy with a thickness of 3 mm was rolled to 75 % reduction by two-pass rolling at $150^{\circ}C$ without lubrication at a differential speed ratio of 2.0:1. In order to introduce uniform shear strain into the copper alloy sheet, the second rolling was performed after turning the sample by $180^{\circ}$ on the transverse direction axis. Conventional rolling(CR), in which the rotating speeds of the upper roll and lower roll are identical to each other, was also performed by two-pass rolling under a total rolling reduction of 75 %, for comparison. The shear strain introduced by the conventional rolling showed positive values at positions of the upper roll side and negative values at positions of the lower roll side. However, samples processed by the DSR showed zero or positive values at all positions. {100}//ND texture was primarily developed near the surface and center of thickness for the CR, while {110}//ND texture was primarily developed for the DSR. The difference in misorientation distribution of grain boundary between the upper roll side surface and center regions was very small in the CR, while it was large in the DSR. The grain size was smallest in the upper roll side region for both the CR and the DSR. The hardness showed homogeneous distribution in the thickness direction in both CR and DSR. The average hardness was larger in CR than in DSR.

• Corrosion Science and Technology
• /
• 제7권2호
• /
• pp.99-111
• /
• 2008

Copper was exposed unsheltered and sheltered in four humid tropical sites, representing urban, urban-industrial, urban-marine and rural environments. The corrosion rates and the sequence of corrosion product formation are presented and discussed in relation with climatic and atmospheric pollution parameters. Chemical compositions of corrosion products were found to depend on environments and duration of exposure. In all environments, cuprite was the predominating corrosion product that formed first and continuously increased during the exposure. Among the sulphur-containing corrosion products, posnjakite and brochantite were more frequently found and the first formed earlier. Nantokite was the most common chlorine-containing products for most cases, except the high-chloride environment, where atacamite was detected instead. The corrosion rate of copper was well indicated by the colour of patina. The red-purple colour corresponded to the high corrosion rate and the greenish grey colour corresponded to the low corrosion rate. Corrosion rate of sheltered copper in urban-marine environment increased with the exposure time.