• International Journal of Korean Welding Society
• /
• 제1권1호
• /
• pp.58-62
• /
• 2001

The surface of AC8A Ah alloy was modified by adding the Cu powder using a Plasma Transferred Arc (PTA) welding process. Under the optimum fabricating conditions, the modified surface of AC8A Ah alloy was observed to possess the sound microstructure with a minimum porosity. Hardness and wear resistance properties of the as-fabricated alloy were compared with those of the 76 heat-treated one. In case of the as-fabricated alloy, the hardness of the modified layer was twice that of the matrix region. Although significant increase in the hardness of the matrix region was observed after T6 heat treatment, the hardness of the modified layer was not observed to change. The wear resistance of the modified layer was significantly increased compared to that of the matrix region. The microstructure of a weld zone and the matrix region were investigated using the optical microscope, scanning electron microscope (SEM), electron probe microanalysis (EPMA), and transmission electron microscope (TEM). The primary and eutectic silicon in the weld zone were finer and more curved than in the matrix region, while some precipitates has had been found therein. According to the TEM observation, the predominant precipitate present in the weld zone was the $\theta$'phase, which is precipitated during cooling by rapid solidification in PTA welding process. Improvement of hardness and wear properties in the weld zone in the as-fabricated condition can be explained based on the presence of $\theta$’precipitates and fine primary and eutectic silicon distribution.

• 한국산학기술학회논문지
• /
• 제15권10호
• /
• pp.6282-6288
• /
• 2014

본 논문은 용접 산업현장에서 많이 사용 되는 $CO_2$ 용접에서는 차량내부 및 탱크내부 용접에서 제어 패널을 볼 수 없는 곳, 작업장이 먼 곳 등에서 용접사가 용접을 하면서 용접조건에 맞는 전류와 전압을 조절할 수가 없고, 전류와 전압을 조절하기 위해 용접을 중단하고 잦은 이동으로 용접 구조물의 순간적인 냉각에 의해 용접결함이 발생된다. 본 연구에서는 기존의 $CO_2$ 용접기 3종류를 각각 사용하여 원격제어 토치의 용접에 대해 SS400 용접구조용 압연강재를 사용하여 원격제어 토치와 기존 $CO_2$ 용접 토치를 V형 맞대기 수직자세로 용접실험을 실시하고 용접 부의 표면비드 상태의 형상을 육안검사 관찰하고 또한 이를 침투탐상검사 및 굽힘 시험을 통해 용접부의 외관품질에 대하여 중점적으로 수행하여 용접결함 감소 및 기존 상용용접기에 교체사용에 대한 성능 및 호환성여부에 미치는 영향에 대해 평가하였다.

• 한국기계가공학회지
• /
• 제20권7호
• /
• pp.33-40
• /
• 2021

Current industrial flow is directed toward reducing the usage of raw materials by reusing parts, which is referred to as a circular economy (CE). Repair is one of the most value-added approaches in CE, which can be efficiently accomplished via additive manufacturing. The repair technology of metallic parts via the directed energy deposition process, which includes the selective removal and redeposition of damaged regions of metallic parts. Residual stress characteristics depend on the shape of the part and the shape of the redeposition region. The objective of this study is to investigate the effects of the radius and corner position of the substrate on the residual stresses for repair by using finite element analysis (FEA). The residual stress distribution of the 45° angle groove at the edge of the circular shape models on the outer and inner radii was analytically investigated. The analysis was accomplished using SYSWELD software by applying a moving heat source with defined material properties and cooling conditions integrated into the FEA model. The results showed a similar pattern of concentrated stress distribution for all models except the 40-mm and 60-mm radii, for which the maximum stress locations were different. The maximum residual stresses are high but lower than the yield strength, suggesting the absence of cracks and fractures due to residual stresses.

• 대한토목학회논문집
• /
• 제7권1호
• /
• pp.93-101
• /
• 1987

용접부(鎔接部)에서 잔류응력(殘留應力)은 용접열(鎔接熱)에 의한 국부(局部) 가열(加熱)과 불규칙적(不規則的)이고 비교적(比較的) 급속(急速)한 냉각(冷却)으로 유발(誘發)되는 열응력(熱應力)과 구조물(構造物)의 강성(剛性) 및 재료(材料) 등에 의하여 발생(發生)되며, 잔류응력(殘留應力)의 존재(存在)는 취성파괴강도(脆性破壞强度), 피로강도(疲勞强度), 좌굴강도(挫屈强度), 진동특성(振動特性), 부식저항(腐蝕抵抗) 등에 영향(影響)을 미치는 궁극적(窮極的) 요인(要因)으로 간주(看做)됨으로 본(本) 연구(硏究)는 구조물(構造物)의 강도(强度)를 저하(低下)시키고 기능(機能)에 악영향(惡影響)을 끼치는 잔류응력(殘留應力)의 기구학적(機構學的) 특성(特性)을 파악(把握)하기 위하여 SWS 58 강판(鋼板)을 X홈 용접(鎔接)하여 이것을 4단계(段階) 즉 $350^{\circ}C$, $500^{\circ}C$, $650^{\circ}C$, $800^{\circ}C$로 열처리(熱處理)하여 hole drilling method를 사용(使用)하여 잔류응력(殘留應力)을 측정(測定)한 결과(結果), 다음과 같은 결론(結論)을 얻었다. 잔류응력(殘留應力)을 제거(除去)시키는 가장 효과적(效果的)인 온도(溫度)는 $650^{\circ}C$ 정도(程度)이었고, 구멍의 직경(直經)이 구멍의 깊이와 일치할 때 구멍바로 근처(近處)의 소성변형(塑性變形)은 완전(完全)히 해방(解放)되었으며, 경도시험(硬度試驗)을 통(通)해 열처리(熱處理) 후(後) 열영향부(熱影響部)의 높은 경도(硬度)가 모두 삭감(削減)되는 것을 알 수 있었으며 또한 잔류응력(殘留應力)에 끼치는 용접입열(鎔接入熱)의 영향(影響)은 입열량(入熱量)의 표준(標準)보다 1/4 이상(以上), 이하(以下)인 경우 잔류응력(殘留應力)은 용접입열(鎔接入熱)에 큰 영향(影響)이 없음을 알았다.

• 한국산학기술학회논문지
• /
• 제16권2호
• /
• pp.1339-1347
• /
• 2015

본 연구는 현장의 GMAW 용접기에 더블 와이어 릴을 겸비한 원격제어토치의 시스템에 관한 것이다. 산업현장 용접에서는 용접기 본체로부터 와이어 송급장치까지의 거리가 약 30m 떨어져 있고 송급장치로부터 토치까지의 거리는 약 3~5m 정도이다. 이에 따라 차량 및 탱크 내부의 용접에서 제어 패널을 볼 수 없는 곳이나 작업장이 먼 곳 등에서 용접사가 용접을 하면서 용접조건에 맞는 전류와 전압을 조절할 수가 없고 또한 용접와이어가 완전히 소모되면 용접을 중단하고 와이어 릴을 갈아 끼워야하는 번거로운 문제점이 있다. 이 때문에 전류와 전압 조절 및 와이어를 교체하기 위해 용접을 중단하고 잦은 이동으로 용접구조물의 순간적인 냉각에 의해 용접결함이 발생된다. 본 연구에서는 이러한 제반 문제를 감소하기 위해 기존의 GMAW 용접기의 제반기능을 토대로 간소화 및 합리화하여 더블 와이어 릴을 겸비한 원격제어토치를 자체 제작하였다. 실험은 SM50A 용접구조용 압연강재 6mm를 사용하여 와이어 더블 릴을 겸비한 원격제어 토치와 기존 $CO_2$ /MAG 용접토치를 V형 맞대기 수직자세로 용접을 실행하였다. 용접 완료 후 용접부의 표면비드 상태의 형상을 육안검사 관찰하고 또한 이를 방사선투과검사를 통해 용접부의 내부 용접품질에 대하여 용접현상을 분석하였다. 이 연구를 통해 용접결함 감소, 원가절감 및 기존 상용용접기에 교체사용에 대한 성능 및 호환성여부에 미치는 영향에 대해 평가하였다.