• Restorative Dentistry and Endodontics
• /
• 제49권2호
• /
• pp.18.1-18.13
• /
• 2024

Objectives: This study was conducted to evaluate the mechanical properties of relined and non-relined fiberglass posts when cemented to root canal dentin using a conventional dual-cure resin cement or a self-adhesive resin cement. Materials and Methods: Two types of resin cements were utilized: conventional and self-adhesive. Additionally, 2 cementation protocols were employed, involving relined and non-relined fiberglass posts. In total, 72 bovine incisors were cemented and subjected to push-out bond strength testing (n = 10) followed by failure mode analysis. The cross-sectional microhardness (n = 5) was assessed along the root canal, and interface analyses (n = 3) were conducted using scanning electron microscopy (SEM). Data from the push-out bond strength and cross-sectional microhardness tests were analyzed via 3-way analysis of variance and the Bonferroni post-hoc test (α= 0.05). Results: For non-relined fiberglass posts, conventional resin cement exhibited higher pushout bond strength than self-adhesive cement. Relined fiberglass posts yielded comparable results between the resin cements. Type II failure was the most common failure mode for both resin cements, regardless of cementation protocol. The use of relined fiberglass posts improved the cross-sectional microhardness values for both cements. SEM images revealed voids and bubbles in the incisors with non-relined fiberglass posts. Conclusions: Mechanical properties were impacted by the cementation protocol. Relined fiberglass posts presented the highest push-out bond strength and cross-sectional microhardness values, regardless of the resin cement used (conventional dual-cure or self-adhesive). Conversely, for non-relined fiberglass posts, the conventional dual-cure resin cement yielded superior results to the self-adhesive resin cement.

• 대한치과의사협회지
• /
• 제53권3호
• /
• pp.178-186
• /
• 2015

Dental polymer-based luting materials are classified into esthetic resin cement, adhesive resin cement and self-adhesive resin cement. Due to the different component of each type of resin cement, the preconditioning method of tooth surface and the steps are different from each type of resin cement. The pre-treatment of adherend (ceramic, resin and metal) surface also varies with the type of resin cement and the manufacturer. In this study, the characteristics of each type of resin cement, mechanical properties, indication and advantages were investigated. Through these, clinical tips on using resin cements were suggested.

• The Journal of Advanced Prosthodontics
• /
• 제12권5호
• /
• pp.251-258
• /
• 2020

PURPOSE. The bond strengths between resin denture teeth with various compositions and denture base resins including conventional and CAD/CAM purposed materials were evaluated to find influence of each material. MATERIALS AND METHODS. Cylindrical rods (6.0 mm diameter × 8.0 mm length) prepared from pre-polymerized CAD/CAM denture base resin blocks (PMMA Block-pink; Huge Dental Material, Vipi Block-Pink; Vipi Industria) were bonded to the basal surface of resin teeth from three different companies (VITA MFT^®; VITA Zahnfabrik, Endura Posterio^®; SHOFU Dental, Duracross Physio^®; Nissin Dental Products Inc.) using resin cement (Super-Bond C&B; SUN MEDICAL). As a control group, rods from a conventional heat-polymerizing denture base resin (Vertex™ Rapid Simplified; Vertex-Dental B.V. Co.) were attached to the resin teeth using the conventional flasking and curing method. Furthermore, the effect of air abrasion was studied with the highly cross-linked resin teeth (VITA MFT^®) groups. The shear bond strengths were measured, and then the fractured surfaces were examined to analyze the mode of failure. RESULTS. The shear bond strengths of the conventional heat-polymerizing PMMA denture resin group and the CAD/CAM denture base resin groups were similar. Air abrasion to VITA MFT^® did not improve shear bond strengths. Interfacial failure was the dominant cause of failure for all specimens. CONCLUSION. Shear bond strengths of CAD/CAM denture base materials and resin denture teeth using resin cement are comparable to those of conventional methods.

• Restorative Dentistry and Endodontics
• /
• 제18권1호
• /
• pp.103-113
• /
• 1993

The purpose of this study was to evaluate the tensile bond strength of composite resin inlays according to the their internal surface treatment and types of luting cement and compared them with the conventional direct resin filling thchnique. Class II cavities were prepared in 50 extracted human molar teeth, and then equally divided into five groups. Group 1 : Cavities of control group were directly filled with P-50. Group 2 : Cavities of resin inlay group were luted with resin cement. Group 3 : Cavities of resin inlay group were luted with luting G-I cement. Group 4 : Cavities of resin inlay group were luted with resin cement after sandblasting. Group 5 : Cavities of resin inlay group were luted with luting G-I cement after sandblasting. All specimens were polished with same method and stored in normal saline for 24 hours before testing. An Universal Testing machine(Model No. AGS-100A, Shimadzu, Japan) was used to apply tensile loads in the vertical direction, and the force required for separation was recorded with a cross-head speed of 5mm/min and 100kg in full scale. The results were as follows : 1. The mean tensile bond strength was lowest in group luted with luting G-I cement, with measurements of $14.45{\pm}0.78(kg/cm^2)$ and highest in group luted with resin cement after sandblasting, with measurements of $49.6{\pm}2.74(kg/cm^2)$. 2. The tensile bond strength was greater in resin inlay groups luted with resin cement than in control group and resin inlay groups luted with luting G-I cement(P<0.05). 3. The tensile bond strength was lower in resin inlay groups luted with luting G-I cement than in control group(P<0.05). 4. The tensile bond strength was greater in resin inlay groups luted with resin cement or luting G-I cement after sandblasting than without that(P<0.05).

• Restorative Dentistry and Endodontics
• /
• 제39권4호
• /
• pp.303-309
• /
• 2014

Objectives: Hydrogen peroxide ($H_2O_2$) surface treatment of fiber posts has been reported to increase bond strength of fiber posts to resin cements. However, residual oxygen radicals might jeopardize the bonding procedure. This study examined the effect of three antioxidant agents on the bond strength of fiber posts to conventional and self-adhesive resin cements. Materials and Methods: Post spaces were prepared in forty human maxillary second premolars. Posts were divided into five groups of 8 each: G1 (control), no pre-treatment; G2, 10% $H_2O_2$ pre-treatment; G3, G4 and G5. After $H_2O_2$ application, Hesperidin (HES), Sodium Ascorbate (SA) or Rosmarinic acid (RA) was applied on each group respectively. In each group four posts were cemented with Duo-Link conventional resin cement and the others with self-adhesive BisCem cement. Push-out test was performed and data were analyzed using 2-way ANOVA and tukey's post-hoc test (${\alpha}=0.05$). Results: There was a statistically significant interaction between the cement type and post surface treatment on push-out bond strength of fiber posts (p < 0.001, F = 16). Also it was shown that different posts' surface treatments significantly affect the push-out bond strength of fiber posts (p = 0.001). $H_2O_2$ treated posts (G2) and control posts (G1) cemented with Duo-link showed the highest ($15.96{\pm}5.07MPa$) and lowest bond strengths ($6.79{\pm}3.94$) respectively. Conclusions: It was concluded that $H_2O_2$ surface treatment might enhance the bond strength of fiber posts cemented with conventional resin cements. The effect of antioxidants as post's surface treatment agents depends on the characteristics of resin cements used for bonding procedure.

• Restorative Dentistry and Endodontics
• /
• 제34권3호
• /
• pp.184-191
• /
• 2009

본 연구의 목적은 치면 처리와 수복물 내면의 처리가 필요 없는 자가 접착 레진 시멘트의 물성 및 lithium disilicate ceramic과 상아질에 대한 전단결합강도를 측정하고 기존의 레진 시멘트와 비교하여 임상적 유용성을 알아보고자 하는 것이다. 실험군인 자가 접착 레진 시멘트로는 Rely-X Unicem, Embrace Wetbond, Maxcem, BisCem을, 대조군으로는 기존의 레진 시멘트인 Rely-X ARC, 수복용 복합레진인 Z-350을 사용하였다. 각 레진 시멘트의 물성 평가를 위하여 테플론 주형을 이용하여 시편을 제작하고 만능 시험기를 이용하여 압축강도, 간접인장강도, 굴곡강도를 측정하였다. IPS Empress 2 및 상아질 시편에 제조사의 지시대로 Rely-X ARE군과 Z-350군에만 전처리를 시행 후 각 시멘트를 접착하고 전단결합강도를 측정하였다. 실험 결과는 다음과 같았다. 1. 자가 접착 레진 시멘트인 Biscem이 가장 낮은 물리적 성질을 나타내었다 (P<0.05). 2. 자가 접착 레진 시멘트의 상아질 및 도재에 대한 전단결합강도는 기존의 레진 시멘트에 비해 유의성 있게 낮은 값을 나타내었다. (P<0.05). 이상의 결과로 볼 때 자가 접착 레진 시멘트는 기존의 레진 시멘트에 비해 물리적 성질 및 상아질과 lithium disilicate ceramic에 대한 전단결합강도가 떨어지는 것으로 사료된다.

• 한국건축시공학회지
• /
• 제4권3호
• /
• pp.93-100
• /
• 2004

In recent years, it has widely been studied on the light-weight composites for the purpose of the large space and thermal insulation of building structures. The purpose of this study is to evaluate the properties of light-weight composites made by binders as cement, resin and polymer cement slurry. The concrete composites are prepared with various conditions such as polymer-cement ratio, void-filling ratio, type of resin, filler content and light-weight aggregate content, tested for thermal conductivity. From the test results, the thermal conductivity of concrete composites with the binder of cement tends to decrease with increasing polymer-cement ratio, and to increase with increasing void-filling ratio. The thermal conductivity of concrete composites with the binder of resin are markedly affected by the light-weight aggregate content, type of resin and filler content. The composites made by polymer-modified concrete and polymer cement slurry have a good thermal insulation property. From the this study, we can recommend the proper mix proportions for thermal insulation Panel or concrete. Expecially. the thermal conductivity of concrete composites made by polyurethane resin is almost the same as that of the conventional expanded polystyrene resin.

• 대한치과보철학회지
• /
• 제46권5호
• /
• pp.535-543
• /
• 2008

최근의 레진 접착시스템은 단계를 줄이고 적용과정을 간편화시키는데 주력하고 있으며, 치면에 bonding 및 conditioning 과정 없이 바로 적용 가능한, one-step의 새로운 자가 접착 레진시멘트 (self-adhesive resin luting cement)들이 소개되어 임상에 사용되고 있다. 이에 본 연구의 목적은 자가 접착 레진시멘트와 기존의 레진시멘트의 상아질에 대한 전단 결합 강도를 비교해보고, 자가 접착 레진시멘트 적용시 치면의 식각 처리 여부가 전단 결합 강도에 미치는 영향에 관하여 알아보고자 하는 것이다. 본 연구를 위해 최근 6개월 내 발치된 비교적 건전한 성인의 대구치 45개를 아크릴릭 레진으로 매몰한 다음, 800 grit SiC연마지로 연마를 시행하여 상아질을 노출시켰다. 15개의 치아를 한 군으로 하여, 세 가지 실험군으로 분류하였다. Group 1) 치면에 아무런 전처리 없이 RelyX Unicem 접착. Group 2) 치면에 인산 산부식 처리 후, RelyX Unicem 접착, Group 3) 치면에 Syntac primet + Syntac adhesive + Heliobond 처리 후 Variolink II 접착. 전처리가 완료된 치아 시편 위에 플라스틱 튜브 (직경 3 mm, 높이 3 mm)를 고정한 다음, 제조사의 지시에 따라 각 레진 시멘트를 혼합하여 링 안을 채우고, 광중합을 시행하였다. 접착이 완료된 시편은 $37^{\circ}C$ 항온수조 (증류수)에서 24시간 동안 보관 후, 만능 시험기를 이용하여 1mm/min의 cross head speed로 결합강도를 측정하였으며, 확대경 하에서 파절 양상을 분류 관찰하고, 주사전자현미경을 이용하여 미세구조를 관찰하였다. 측정결과는 SPSS WIN 12.0 프로그램을 사용하여 분석하였으며 다음과 같은 결과를 얻었다. 1. RelyX Unicem의 상아질에 대한 전단결합강도는 Variolink II와 유의한 차이를 보이지 않았다. 2. 상아질에 대한 인산 산부식 처리는 RelyX Unicem과의 전단결합강도를 낮게 하였다. 3. RelyX Unicem과 Variolink II에서는 혼합 파절의 비율이 컸으며, 전단결합강도가 낮았던 인산 산부식 처리 후 RelyX Unicem을 접착한 경우에서는 전체 시편에서 접착성 파절이 관찰되었다. 결론으로 말하면, 자가 접착 레진시멘트와 기존의 레진시멘트의 상아질에 대한 전단결합강도는 유의한 차이를 보이지 않으며, 인산 산부식 처리는 상아질에 대한 자가 접착 레진시멘트의 전단결합강도를 감소시킨다.

• Restorative Dentistry and Endodontics
• /
• 제42권2호
• /
• pp.125-133
• /
• 2017

Objectives: This study compared the effect of hexamethyldisiloxane (HMDSO) and ammonia ($NH_3$) plasmas on the bond strength of resin cement to fiber posts with conventional treatments. Materials and Methods: Sixty-five fiber posts were divided into 5 groups: Control (no surface treatment); $H_2O_2$ (24% hydrogen peroxide for 1 min); Blasting (blasting with aluminum oxide for 30 sec); $NH_3$ ($NH_3$ plasma treatment for 3 min); HMDSO (HMDSO plasma treatment for 15 min). After the treatments, the Ambar adhesive (FGM Dental Products) was applied to the post surface (n = 10). The fiber post was inserted into a silicon matrix that was filled with the conventional resin cement Allcem Core (FGM). Afterwards, the post/cement specimens were cut into discs and subjected to a push-out bond strength (POBS) test. Additionally, 3 posts in each group were evaluated using scanning electron microscopy. The POBS data were analyzed by one-way analysis of variance and the Tukey's honest significant difference post hoc test (${\alpha}=0.05$). Results: The Blasting and $NH_3$ groups showed the highest POBS values. The HMDSO group showed intermediate POBS values, whereas the Control and $H_2O_2$ groups showed the lowest POBS values. Conclusion: Blasting and $NH_3$ plasma treatments were associated with stronger bonding of the conventional resin cement Allcem to fiber posts, in a procedure in which the Ambar adhesive was used.

• The Journal of Advanced Prosthodontics
• /
• 제7권3호
• /
• pp.249-256
• /
• 2015

PURPOSE. The aim of this study was to evaluate the effects of atmospheric plasma (APL) versus conventional surface treatments on the adhesion of self-adhesive resin cement to Ti-6Al-4V alloy. MATERIALS AND METHODS. Sixty plates of machined titanium (Ti) discs were divided into five groups (n=12): 1) Untreated (CNT); 2) Sandblasted (SAB); 3) Tribochemically treated (ROC); 4) Tungsten CarbideBur (TCB); 5) APL treated (APL). SEM analysis and surface roughness (Ra) measurements were performed. Self-adhesive resin cement was bonded to the Ti surfaces and shear bond strength (SBS) tests, Ra and failure mode examinations were carried out. Data were analyzed by one-way analysis of variance and chi-squared test. RESULTS. The lowest SBS value was obtained with CNT and was significantly different from all other groups except for APL. The ROC showed the highest SBS and Ra values of all the groups. CONCLUSION. It was concluded that the effect of APL on SBS and Ra was not sufficient and it may not be a potential for promoting adhesion to titanium.