• Restorative Dentistry and Endodontics
• /
• 제26권1호
• /
• pp.16-22
• /
• 2001

The purpose of this study was to evaluate the marginal microleakage of condensable composite resin restorations according to flowable resin lining of internal cavity wall. The eighty extracted human molar teeth without caries and/or restorations are used The experimental teeth were randomly assigned into four groups of ten teeth each. Eighty caries-free extracted human molars were used in this study. The conventional class II cavities (box-shaped on mesial and distal surface, faciolingual width : 3mm, gingival wall depth : 1.5mm) were prepared 1mm below cementoenamel junction with a # 701 carbide bur. The teeth were divided into four groups, and then each group were subdivided into A & B group according to flowable resin & compomer lining ; Group 1-A : Tetric Ceram filling, Group 1-B : Tetric Flow lining and Tetric Ceram filling, Group 2-A Ariston pHc filling, Group 2-B : Tetric Flow lining and Ariston pHc filing, Group 3-A SureFil filling, Group 3-B : Dyract Flow lining and SureFil filling, Group 4-A : Pyramid filling, Group 4-B : Aeliteflo lining and Pyramid filling. To simulate as closely as possible the clinical situation during retoration placement, a "restoration template" was fabricated, and the condensable resin was filled using a three-sited light-curing incremental technique. All the materials used were applied according to the manufacturers' instructions. The specimens were stored in the 100% humidity for 7 days prior to thermocycling (100 thermal cycles of 5~55$^{\circ}C$ water with a 30-second dwell time) The specimens were immersed in 2% metyleneblue dye for 24 hours, and then embedded in transparent acrylic resin and sectioned mesiodistally with diamond wheel saw. The degree of marginal leakage was scored under stereomicroscope ($\times$20) and the data were analyzed by Kruskal-Wallis test and Wilcoxon signed ranks test. The results were as follows : 1. In the gingival margins of all the group, microleakage of subgroup B was less than subgroup A. 2. In the group 1, 2, 4, there was significant differences between subgroup A and B (p<0.05), but in the group 3, there was not significant different between group 3-A (SureFil) and group 3-B (Dyract flow/SureFil) (p>0.05). 3. In the subgroup A and B, there was significant different between all group except group 4 of subgroup A. From the results above, it was suggested that the cavity lining of flowable resin and flowable compomer in condensable resin restoration decrease microleakage at gingival margin, and does improve their ability to seal the gingival margin of class II preparation.

• 대한소아치과학회지
• /
• 제31권1호
• /
• pp.66-78
• /
• 2004

초기의 접착 시스템은 여러 단계의 술식을 필요로 하였으며 술자의 기술과 재료의 성질에 크게 좌우되었으나 최근 산부식, priming, adhesive를 한번에 적용할 수 있는 all-in-one adhesive system이 등장하였다. 치과에서의 vibration의 이용은 치석의 제거 및 접착제의 점도를 낮추는데 이용되어왔으며 vibration은 접착제의 흐름성을 향상시켜 film thickness를 낮추어 수복물 주위의 미세누출을 줄이는데 도움을 준다. 이에 저자들은 all-in-one adhesive system에서 vibration이 법랑질과 상아질의 접착강도와 레진침투에 미치는 효과를 알아보고자 하였다. 법랑질 시편은 발거 후 실온에서 0.1% thymol 용액에서 보관된 30개의 건전한 사람의 대구치를 무작위로 10개씩 세군으로 나누고 근원심 방향으로 두 부분으로 분리하여 각각은 같은 접착제를 사용하고 초음파진동여부를 다르게 하였고, 아크릴레진을 이용하여 직경 1-inch의 PVC관에 매몰한 후 협설면이 아크릴봉과 동일한 높이가 되도록 220-, 600-grit 연마지로 순차적으로 연마하였고 군당 10개씩 여섯 군으로 분류하였다. 1군과 2군은 Prompt L-Pop(3M-ESPE, Seefeld, Germany), 3군과 4군은 One-Up Bond F(Tokuyama Corp., Tokyo, Japan), 5군과 6군은 AQ bond(Sun Medical Co., Kyoto, Japan)를 제조사의 지시에 따라 도포하였다. 2군, 4군, 6군은 초음파 치석제거기를 이용하여 치면에 대고 15초간 진동을 가한 후 광중합하였다. 상아질 시편은 치관부 법랑질을 제거한 후 상아질면을 아크릴 봉과 동일한 높이가 되도록 하고 법랑질 시편과 동일하게 처리하였다. 이후 직경 2mm, 높이 3mm의 Teflon mold(Ultradent, U.S.A.)를 이용하여 복합레진을 충전한 후 40초씩 두 번에 나누어 광중합한 후 24시간동안 실온에서 증류수에 보관하였다. 열순환 시행한 후, 만능측정기(Instron 4465)로 전단결합강도를 측정하였으며 Resin tag의 양상을 비교하기 위해 각 군의 시편의 치질을 완전히 용해시킨 후 표면을 주사전자현미경사진으로 관찰하여 다음과 같은 결과를 얻었다. 1 법랑질에서 초음파 진동을 가한 군(2, 4, 6군)은 가하지 않은 군(1, 3, 5군)에 비해 평균 전단결합강도가 높게 나타났다. 그 차이는 Ad bond 군을 제외하고 통계적으로 유의하였다(p<0.05). 2. 상아질에서 초음파 진동을 가한 군(2, 4, 6군)은 가하지 않은 군(1, 3, 5군)에 비해 평균 전단결합강도가 높게 나타났다. 그러나 그 차이는 One-Up Bond F군을 제외하고는 통계적으로 유의한 차이가 없었다. 3. 전자 현미경 관찰에서 초음파 진동을 가한 군에서 더 많은 법랑질의 소실과 상아질에서 resin tag의 길이가 길었고 lateral branch의 수도 많이 관찰되었다.