• 한국염색가공학회지
• /
• 제33권3호
• /
• pp.131-140
• /
• 2021

Collagen and chitosan are used in medical and cosmetic materials as natural polymers. In order to utilize the advantages of the materials, collagen/chitosan conjugated wet-spun fibers were prepared. The analysis of surface, optical, thermal and mechanical properties was carried out on the various composition of collagen and chitosan. As a result of images analysis, it was verified that the collagen/chitosan conjugated fibers were stably spun. In addition, the optical and thermal properties of fibers were observed to be changed by hydrogen bond. As a result, an optimized composition could be found at an appropriate content. Moreover, the optimized fibers have mechanical properties similar to chitosan fibers, while improving the structural and thermal stability by its hydrogen bond. In addition, the wet-spun collagen/chitosan conjugated fibers can be applied to medical and various fields through mechanical properties according to content control.

• 한국의류산업학회지
• /
• 제12권4호
• /
• pp.500-507
• /
• 2010

In this study, physical properties were studied by using latent stretching yarn in order to develop the texturing yarn technique for super bulky yarn, which is better in bulkiness and handle than natural wool and also adds property of synthetic fiber to natural wool. In order to obtain textured conditions by analysing basic properties for manufacturing DTY yarn with super bulky property, DTY 50d/12 after spinning latent yarn spined POY 80d/12 was obtained under the two conditions of (i) false twist(T/M) level 3 in DTY texturing and (ii) draw ratio level 4 in draw texturing. For DTY texturing yarn, Elongation rate increased as the heat treatment time and temperatures increased. In addition, shrinkage became higher as false twist was higher, so that elongation rate became lower. When annealing became longer in time and higher in temperature, initial modulus increased. In addition, as the count of false twist increased, the initial modulus showed higher values. For draw texturing yarn, under the conditions of heat temperature 180 and heating time 30 minutes, shrinkage rate in draw ratio 1.55 and 1.6 draw ratio was 7%, and that in 1.65 and 1.7 draw ratio was 8.5%. High draw ratio samples' tenacity was much influenced by heating time and temperature, but low draw ratio samples' tenacity was influenced not by treated time, but by treated temperature.

• 한국염색가공학회지
• /
• 제24권4호
• /
• pp.288-295
• /
• 2012

Although some degree of mechanical properties of suede fabrics mainly related to non-woven suede fabric has some researched, the thin suede fabric has rarely been researched. In this study, polyester(DTY 50/72) was used for warp, and after producing latent yarn and sea-island yarn for weft, two yarns were compounded to produce sea-island DTY yarn. By using the two produced yarns for warp and weft, we produced thin suede fabric with stretch function. For weft 2ply, weft density 85, 90, 100(picks/in) were applied to weave fabric, and for weft 1ply, weft density 125, 135, 140(picks/in) were applied to produce weft face 5-end satin weave. The mechanical properties of the produced fabric were researched. The result are as followed. The weight loss ratio of the suede fabric produced for this experiment reached 15% on the conditions of temperature $90^{\circ}C$ and 20 minutes, so that island parts were completely separated. The strength of weft 1ply applied suede fabric was about 7.5kg and that of 2ply suede fabric and about 3.5kg. But the strain of two samples ranged from about 40 to 43%. Although Hari was high when weft was denser. The values of Koshi and Kisimi were low. And shear stiffness was high when sea-island DTY yarn was used. The WC value was higher in the case of 2ply than in that of 1ply sea-island DTY yarn for weft, so that we may conclude that Fukurami was more affected in the 2ply case.

• 감성과학
• /
• 제18권1호
• /
• pp.49-58
• /
• 2015

본 연구는 감성의류용 탄화지르코늄 함유 축열 니트의 원적외선 특성을 연구하였다. 탄화지르코늄 함유 축열 PET 원사가 이성분 방사법에 의해 방사되었다. 이 원사의 core부에는 고점도 PET와 탄화지르코늄을 혼합한 용액을, sheath부에는 저점도 PET 용액을 사용하여 콘쥬게이트 방사를 실시하였다. 이들 방사된 원사의 원소분석과 원적외선 특성 분석이 EDS와 FT-IR 계측기기에 의해 분석되었으며 두 가지 조직의 니트 소재를 편직하여 이들의 열적특성을 분석하였다. EDS 분석에서 Zr 피크를 확인하였으며 원사내에 Zr 원소가 19.29% 함유되어 있음을 확인하였다. 또한 원적외선 분석에서 $5{\sim}20{\mu}m$ 파장 영역에서 원적외선 방사에너지가 $3.65{\times}10^2W/m^2$, 방사율이 0.906 임을 확인하였다. KES-F7 측정기 분석에서 ZrC 함유 편성물의 Qmax 값이 일반 PET 편성물의 값보다 낮은 값을 보였고 보온율 값은 ZrC 함유 편성물이 일반 PET보다 더 높은 값을 보이므로서 ZrC의 축열성을 확인하였다. 열전도도는 Zr의 높은 열전도도 때문에 일반 PET 편물보다 더 높은 값을 보였다. ZrC의 함유가 편물의 촉감에 미치는 영향을 없었으며 편성 조직이 더 큰 영향을 주는 것을 확인하였다.