• Journal of the Korean institute of surface engineering
• /
• v.53 no.4
• /
• pp.160-168
• /
• 2020

A polymer-based carbon nanomaterial composite was fabricated and characterized for the application of a thermal conductive adhesive. Low-dimensional carbon nanomaterials with excellent thermal conductivity such as carbon nanotube (CNT) and graphene were selected as a filler in the composite. Thermal, electrical and adhesive properties of the composite were investigated with respect to the morphology and content of the low-dimensional carbon nanomaterials. As a result, the composite-based adhesive fabricated by the loading of surface-treated MWCNTs of 0.4 wt% showed uniform dispersion, moderate adhesion and effective heat dissipation properties. Finally, it was confirmed through the thermal image analysis of LED module that the temperature reduction of 10℃ was achieved using the fabricated composite adhesive with MWCNT-6A. Expecially, heat dissipation performance of the optimized composite adhesive was evident at the hot spot in the module compared to other samples mixed with graphene or different MWCNT loading ratios.

• Elastomers and Composites
• /
• v.52 no.1
• /
• pp.22-26
• /
• 2017

The thermal conductivity and the adhesive properties were measured, after synthesis of thermal conductive composite which was obtained as a result of mixing alumina or graphite with acrylic adhesive synthesized by UV polymerization. The adhesive properties of the composite were evaluated measuring the peel strength at 180 degrees, the retention, and the initial tack;the thermal conductivity was estimated using laser flash analysis. As the filler contents increased, a decrease in peel strength and initial tack and an increase in retention and thermal conductivity were observed. When compared to alumina, the adhesion of graphite showed a dramatic decrease, whereas the thermal conductivity was further enhanced. It was found out that the small size of graphite increased the mechanical interlocking between the polymer and the filler, and it was easier for graphite to come into contact with other graphite in the matrix.

• ETRI Journal
• /
• v.32 no.3
• /
• pp.414-421
• /
• 2010

The interconnection mechanisms of a smart anisotropic conductive adhesive (ACA) during processing have been characterized. For an understanding of chemorheological mechanisms between the fluxing polymer and solder powder, a thermal analysis as well as solder wetting and coalescence experiments were conducted. The compatibility between the viscosity of the fluxing polymer and melting temperature of solder was characterized to optimize the processing cycle. A fluxing agent was also used to remove the oxide layer performed on the surface of the solder. Based on these chemorheological phenomena of the fluxing polymer and solder, an optimum polymer system and its processing cycle were designed for high performance and reliability in an electrical interconnection system. In the present research, a bonding mechanism of the smart ACA with a polymer spacer ball to control the gap between both substrates is newly proposed and investigated. The solder powder was used as a conductive material instead of polymer-based spherical conductive particles in a conventional anisotropic conductive film.

• Journal of the Semiconductor & Display Technology
• /
• v.10 no.4
• /
• pp.37-42
• /
• 2011

In this paper, novel carbon nanotube (CNT)-filled Solderable electrically conductive adhesive (ECA) and joining process have been developed. To investigate the bonding characteristics of CNT-filled Solderable ECA, three types of Solderable ECAs with different CNT weight percent (0, 0.1, 1wt%) were formulated. For a joining process, the quad flat package (QFP) chip was used. The QFP chip had a size of $14{\times}14{\times}2.7$ mm and a 1 mm lead pitch. The test board had a Cu daisy-chained pattern with 18 ${\mu}m$ thick. After the bonding process, the bonding characteristics such as morphology of conduction path, electrical resistance and pull strength were measured for each formulated ECAs. As a result, the electrical and mechanical bonding characteristics for a QFP joints using CNT-filled ECA were improved about 10% compared to those of QFP joints using ECA without CNT.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2010.11a
• /
• pp.545-546
• /
• 2010

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2011.06a
• /
• pp.749-750
• /
• 2011

• Journal of Information Display
• /
• v.4 no.1
• /
• pp.17-23
• /
• 2003

A thermoset type anisotropic conductive adhesive film (ACAF) comprising epoxy resin and natural butyl rubber (NBR) as the binder, micro-encapsulated imidazole as the curing agent, and Ni/Au coated polymer bead as a conductive particle has been studied. These films have been prepared to respond to requirements such as improved contact resistance, current status less of than 60 ${\mu}m$ and reliability. These films can also be used for connection between the ITO glass for LCD panel and the flexible circuit board. The curing conditions for the connection were 40, 20 and 15 seconds at 150, 170 and 190 $^{\circ}C$, respectively. The initial contact resistance and adhesion strength were 0.5 ${\Omega}/square$ and 0.4 kg/cm under the condition of 30 kgf/$^{cm}^2}$, respectively. After completing one thousand thermal shock cycling tests between -15 $^{\circ}C$ and 100 $^{\circ}C$, the contact resistance was maintained below 0.7 ${\Omega}/square$. Durability against high temperature (80$^{\circ}C$) and high humidity (85 % RH) was also tested to confirm long-term stability (1000 hrs) of the conduction.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2004.11a
• /
• pp.66-66
• /
• 2004

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2004.11a
• /
• pp.67-67
• /
• 2004

• Journal of Welding and Joining
• /
• v.33 no.5
• /
• pp.41-46
• /
• 2015

The snap cure NCP(non-conducive paste) adhesive material is essentially required for the high productivity flip chip bonding process. In this study, the accessibility of DEA(dielectric analysis) method for the evaluation of snap cure behavior was investigated with comparison to the isothermal DSC(differential scanning calorimetry) method. NCP adhesive was mainly formulated with epoxy resin and imidazole curing agent. Even though there were some noise in the dielectric loss factor curve measured by DEA, the cure start and completion points could be specified clearly through the data processing of cumulation and deviation method. Degree of cure by DEA method which was measured from the variation of the dielectric loss factor of adhesive material was corresponded to about 80% of the degree of cure by DSC method which was measured from the heat of curing reaction. Because the adhesive joint cured to the degree of 80% in the view point of chemical reaction reveals the sufficient mechanical strength, DEA method is expected to be used effectively in the estimation of the high speed curing behavior of snap cure type NCP adhesive material for flip chip bonding.