• 한국기계가공학회지
• /
• 제3권3호
• /
• pp.79-85
• /
• 2004

The lightness of components required in automobile and machinery industry is requiring high strength of components. In particular, fatigue failure phenomena, which happen in metal, bring on danger in human life and property. Therefore, antifatigue failure technology takes an important part of current industries. Currently, the shot peening is used for removing the defects from the surface of steel and improving the fatigue strength on surface. Therefore, in this paper the effect of compressive residual stress of spring steel(JISG SUP-9)by shot peening on fatigue crack growth characteristics in stress ratio(R=0 1, R=0 3, R=0 6)was investigated considering fracture mechanics. By using the methods mentioned above, I arrived at the following conclusions: (1) The fatigue crack growth rate(da/dN) of the shot peening material was lower than the unpeening material And in stage I, ${\Delta}K_{th}$, the threshold stress intensity factor, of the shot peening material is high in critical parts unlike the unpeening material. (2) Fatigue life shows more Improvement in the shot peening material than in the unpeening material. And compressive residual stress of surface on the shot peening processed operate the resistance of fatigue crack propagation.

• Journal of Advanced Marine Engineering and Technology
• /
• 제29권4호
• /
• pp.426-435
• /
• 2005

The lightness of components required in automobile and machinery industries is requiring high strength of components. Therefore this requirement is accomplished as the process of shot-peening method that the compressive residual stress is made on the metal surface as one of various improvement methods. Special research is, therefore, needed about compressive residual stress on the metal surface in the process of shot-peening method. Therefore, in this paper the effect of compressive residual stress of spring steel(JISG SUP-9) by shot-peening on fatigue crack growth characteristics in environmental condition(temperature) and mechanical condition(shot velocity, stress ratio) was investigated with considering fracture mechanics. By using the methods mentioned above, the following conclusions have been drawn. (1) The fatigue crack growth rate(da/dN) of the shot-peened material was lower than that of the un-peened one. In high temperature range. fatigue crack growth rate decreased with increasing temperature range, while fatigue crack growth rate increased by decreasing temperature in low temperature. (2) Fatigue life shows more improvement in the shot-peened material than in the un-peened material. And compressive residual stress of surface on the shot-peen processed operate resistance force of fatigue crack propagation.

• 한국구조물진단유지관리공학회 논문집
• /
• 제12권4호
• /
• pp.71-78
• /
• 2008

철도교량의 경우, 열차하중에 의한 영향으로 교량 단부에서 상향력이 발생하였으며, 이 상향력은 체결장치에 압축력과 인장력을 유발시켰다. 현재까지 이에 대한 안전성을 검토하기 위해 체결장치를 1방향의 스프링 요소로 모사하여 구조해석을 수행해 왔다. 이러한 경우에 스프링 요소의 강성은 압축력을 재하한 실험적 연구에 의하여 산정되었다. 따라서, 상향력은 체결장치에 압축력뿐만 아니라 인장력도 유발시키기 때문에 합리적이고 정확한 구조해석을 수행하기 위해서는 인장력을 재하한 실험적 연구로부터 산정된 병진방향 강성 그리고 회전방향 강성을 함께 고려해야 한다. 본 연구에서는 6가지 실험체에 대하여 탄성과 비탄성 실험을 수행하여 레일 연직방향 병진강성과 레일 강축에 대한 회전강성을 검토하였고, 체결장치의 구조적인 거동을 분석하였다.

• 한국강구조학회 논문집
• /
• 제29권3호
• /
• pp.229-236
• /
• 2017

이 연구에서는 고무스프링의 동적 압축실험을 수행하여 고무스프링의 거동 및 특성을 규명하고 압축 강성도를 계산하여 실제 설계값에 대해 알아보고자 하였다. 고무스프링의 동적 압축실험을 수행하기 위하여, L80-D55, L90-D58, L100-D60의 고무스프링의 형상계수를 구하여 총 9개의 고무스프링을 주문 제작 하여 실험에 사용하였다. 실험은 고무스프링의 길이에 따라 기압축을 제어하여 수행하였으며, 기압축은 변형률의 5%, 10%, 15%, 20%, 25% 순서로 증가시켰다. 실험결과를 통해 힘-변형률 곡선을 얻을 수 있었고, 변형률의 증가함에 따라 강도감소 현상과 강도증가 현상이 발생함을 확인하였다. 또한 고무스프링의 크기와 지름에 따라 강성저하 및 강성증가 현상이 확연하게 나타남을 확인하였고, 힘-변형률 곡선에서 할선기울기를 이용하여 유효 압축강성도를 추정하였다. 유효압축강성도를 이용하여 실제 설계에 사용할 수 있는 설계값을 제시하였다.

• 한국기계가공학회지
• /
• 제2권1호
• /
• pp.22-31
• /
• 2003

The compressive residual stress, which is induced by shot peening process, seems to be an Important factor in increasing the fatigue strength. And then it was showed that residual stress was disappearenced at the high temperature. The fatigue charateristic investigation of a SUP9 spring steel processed shot peening is performed by considering the high temperature service conditions in the range of room temperature through $180^{\circ}C$ in the range of stress ratio of 0.3 by means of opening mode displacement. The fatigue resistance characteristics and fracture strength at high temperature is considerable lower than that of room temperature in the early stage and stable of fatigue crack growth region.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2000년도 추계학술대회 논문집
• /
• pp.421-424
• /
• 2000

Valve springs with high fatigue strength corresponding to the incresement of working stresses, are required for the higher generating power and the better fuel economy of automobile engines. For this purpose, high strength oil tempered wires are being used. By a method of the high strength for the valve spring, modification of manufacturing processes is being applied. In this case, the cause and effect for the improvement of the fatigue strength has not yet been explained obviously. Therefore, in this report, comparison of fatigue life between valve springs of conventional processes with oil tempered wires and new manufacturing processes was made. As a result of the fatigue test, the fatigue life of the latter was attained maximum 7 times than that of the former. It was cleared that the improvement of the fatigue life was caused by difference of compressive residual stresses at depth of 0.2mm below the inner side surface of both valve springs.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2004년도 춘계학술대회
• /
• pp.314-319
• /
• 2004

High temperature fracture toughness characteristics of shot peened spring steel(SUP-9), which is used for automobile suspension system and railroad, was investigated in this paper. Fracture tougness test for room temperature, $100^{\circ}C$ , and $200^{\circ}C$ were evaluated by material test system(MTS). The experimental results show that the fracture toughness was improved by peened and unpeened. The fracture toughness for high temperature were also improved by peened and unpeened.

• 한국해양공학회:학술대회논문집
• /
• 한국해양공학회 2002년도 추계학술대회 논문집
• /
• pp.347-353
• /
• 2002

The compressive residual stress, which is induced by shot peening process, seems to be an important factor of increasing the fatigue strength. And then it was showed that residual stress was disappearenced at the high temperature. The fatigue characteristic study of a SUP9 spring steel processed shot peening is performed by considering the high temperature service conditions in the range of room temperature through $180^{\circ}C$ in the range of stress ratio of 0.3 by means of opening mode displacement. The fatigue resistance characteristics and fracture strength at high temperature is considerable lower than that of room temperature in the early stage and stable of fatigue crack growth region.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2004년도 추계학술대회
• /
• pp.325-330
• /
• 2004

Recently, the request for the high strength of material is more and more increased in the area of industrial environment and machinery. To accomplish the high strength of materials, carbonizing treatment, nitrifying treatment, shot-peening method are representatively applied, however, shot-peening method is generally used among the surface processes. Shot peening is a cold working process used to impact Compressive residual stressed in the exposed surface layers. Benefits due to shot peening are increase in resistance to fatigue, stress corrosion cracking, fretting, galling, erosion and closing of pores. In this study, the influence of shot peening on the corrosion was investigated on spring steel immersed in 3.5% NaCl. The immersion test as performed on the two kinds of specimens. Corrsion potential, polarization curve, residual stress and etc, were investigated from experiment results. From test result the effect of shot peening on the corrosion was evaluated. The important results of the experimental study on the effects of shot peened on the environment corrosion of spring steels are as follows; In case of corrosion potential, shot peened specimen shows more activated negative direction as compared with parent mental. Surface of specimen, which is treated with the shot peened is placed as more activated state against inner base metal. It can cause t도 anti-corrosion effect on the base metal.

• 한국자동차공학회논문집
• /
• 제13권1호
• /
• pp.159-165
• /
• 2005

Shot peening can be defined as the process of work hardening of the surface of components by means of propelled stream of spherical shot. Benefits due to shot peening are increase in resistance to fatigue, stress corrosion cracking, fretting, galling, erosion and closing of pores. In this study, the influence of shot peening on the corrosion was investigated on spring steel immersed in $3.5\%\;NaCl$. The immersion test was performed on the two kinds of specimens. Corrosion potential, polarization curve, residual stress and etc. were investigated from experimental results. From test results, the effect of shot peening on the corrosion was evaluated. The important results of the experimental study on the effects of shot peened spring steels on the environment corrosion are as follows; In case of corrosion potential, shot peened specimen shows more activated negative direction as compared with parent metal. Surface of specimen, which is treated with the shot peened, is placed as more activated state against inner base metal. It can cause the anti-corrosion effect on the base metal.