• Journal of the Korean Recycled Construction Resources Institute
• /
• v.2 no.3
• /
• pp.217-224
• /
• 2014

This study carried out to evaluate the hydration heat analysis and fundamental characteristics such as air content, slump and compressive strength for field application of low heat concrete with premixed cement. The results of experiment show that low heat concrete with premixed cement have sufficient performances on the workability and compressive strength. In addition, hydration heat analysis shows that low heat concrete with premixed cement make sure of target thermal cracking index. Therefore, it is desirable to apply the low heat concrete with premixed cement on pier foundation-column.

• Journal of the Korean Institute of Gas
• /
• v.5 no.4 s.16
• /
• pp.79-84
• /
• 2001

In this study, the effect of polyol structure(OH-value, functionality) on the reactivity, mechanical property and cell morphology of polyurethane foam and the possibility of replacing HFC-36smfc was examined by evaluating how each blowing agent(CFC-11, HCFC-l4lb, HFC-36smfc) affects the reactivity, mechanical property and cell morphology. Results of the experiment showed that as the functionality and OH-value of polyol increased, there was an increase in the temperature profile, reaction rate, density and compressive strength. However. as the functionality and OH-value increased. the ceil size became smaller The use of different kinds of blowing agents did not appear to have and significant influence on the temperature profile, reaction rate, density and compressive strength. The foam using HFC-365mfc produced more uniform cells compared to the foam using HCFC-l4lb.

• KCI Concrete Journal
• /
• v.13 no.1
• /
• pp.3-9
• /
• 2001

This research concerns the effect of kaolin as material of cement admixture. which has the advantage of low price and high adaptability. Kaolin, a kind of soil, is well known as a raw material of pottery. which is widely scat-tered on the earth (especially in Korea). This research shows the method and process for activating kaolin to have the properties of a cement admixture through experiment. In the experiments, kaolin is baked in high temperature and then cooled suddenly to be activated. The temperature zone and time span, on which kaolin is activated are examined. The research looks over the effect of the activated kaolin based on several criteria regarding to chemical and physical characteristic of general admixtures. The results of this research are as follows; kaolin start activation at the temperature above 50$0^{\circ}C$ and make ends of activation at the temperature below 95$0^{\circ}C$ and there was little effect by the change of duration. It is concluded that compressive strength can be increased by putting activated kaolin in the concrete and the activated kaolin is good for water resistance and anti-chemical , and that it is effective for protecting the leakage of hazardous article like Cl- and for protecting damage by an organic salt like acid. The activated kaolin of proper temperature and time is effective in compressive strength, salt resistance and acid resistance. The adaptability of activated kaolin as a cement admixture was shown through this research.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.2 no.1
• /
• pp.10-18
• /
• 2014

This study carried out to evaluate the hydration heat analysis and fundamental characteristics such as air content, slump, compressive strength and dry shrinkage according to concrete with premixed cement, ternary concrete and OPC concrete for using concrete with premixed cement. The results of experiment are founded that concrete with premixed cement have sufficient performances such as workability, compressive strength and dry shrinkage. Also, the results of hydration heat analysis are founded that concrete with premixed cement have more performance than ternary concrete and OPC concrete at a point of view for the quality control such as thermal crack reducing and economic benefit. Therefore, it is desirable that concrete with premixed cement should be used to rise durability performance and convenience of maintenance.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.601-604
• /
• 2008

When the concrete is placed, the water, needed for hydration of the cement, is under 30% of W/C including bound and gel water. However, as minimum water content cause bad workability, the W/C have to be higher. Therefore, fresh concrete produce 10${\sim}$20% extra water. As those water remain entrapped air in the concrete, life of the structure is reduced because of the degradation caused by entrapped air. For that reason, if extra water is eliminated, it will be great to improve the durability of the structures. Therefore, this study was performed to verity the fundamental properties through the experiment on the dewatering system using the euro form for eliminating extra water. When the dewatering form was applicated, the compressive strength was increased by 16% than those of normal form. However, the increasing rate of compressive strength got lower as the height is higher. In terms of ultrasonic pulse speed and surface roughness, the dewatering form showed better results than the normal one.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.11 no.1
• /
• pp.25-31
• /
• 2023

In this study, the basic properties of CO₂ immobilized desulfurized gypsum (CFBG) and the possibility of being used as a stimulus for slag cement were reviewed, and performance evaluation was conducted through a concrete mixing test. The main components of CFBG were CaO and SO₃, and CaO and SO₃ increased as the drying temperature increased. The moisture content of undried CFBG was 15.7 %, the drying temperature was 1.7 % and the drying temperature was 0.03 % at 105 ℃. Mortar using CFBG tended to have a lower flow value as the drying temperature increased, and the compressive strength was equivalent to that of the FGB use mixture. As a result of the concrete experiment using CFBG SC, both slump and air volume satisfied the target range after 60 minutes, and the compressive strength tended to increase overall compared to the ternary binder mixture.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.11 no.4
• /
• pp.341-348
• /
• 2023

In this study, in order to minimize the increase in the amount of various industrial by-products due to the rapid growth of the industry and the intensification of the depletion of natural aggregate resources, the material test using recycled aggregate and steelmaking slag and the proper mixing ratio of recycled concrete were to be derived. In this study, first, the conformity of the quality standards of the materials used in the field was confirmed, and the workability and molding results were shown when used alone or mixed. Therefore, the feasibility of application as aggregate for concrete was evaluated through a total of 4-type mixtures of cement types, admixtures, coarse aggregates, and fine aggregates. As a result of the experiment, it was confirmed that the slump of unhardened concrete, the amount of air, chloride and compressive strength of hardened concrete according to the replacement rate were different from the measured values of general concrete quality characteristics. According to this, it was confirmed that the quality characteristics of the standard design criteria were satisfied.

• Journal of Korean Society of Steel Construction
• /
• v.24 no.5
• /
• pp.521-534
• /
• 2012

In this research, we carry this study into effect on the basis of utilizing character of composite beam and developing applicable section to some of high strength steel. We evaluated flexural capacity of composite beam that is a unit member through experiments. The existing nominal strength formula of Composite Beam which is a previous method was reviewed and the experiment had been progressive by using each composite members as main variables though the result. Capacity evaluation of U-shape Hybrid Forming Beam(HyFo Beam) which is a new shape show as follow from the result. First, it is resonable to resist demand moment by couple moments which are occurred in concrete compressive-strength and steel tensile-strength. Second, the capacity was stably increased in proportion to the depth of beams and the thickness of steel plates. The last, HyFo Beam was showed as ductile behavior.

• Magazine of the Korea Concrete Institute
• /
• v.11 no.1
• /
• pp.221-230
• /
• 1999

A study was conducted to investigate the flexural behavior of reinforced high-strength concrete beams using Belite cement. In this study, fourteen reinforced Belite and control beams were tested. The major experimental variables are compressive strength(350kgf/$cm^2$ and 600kgf/$cm^2$)of concrete and reinforcement ratios(0.0086~0.0345). They were tested by three point loading method. Comparing with flexural behavior of normal reinforced concrete beams, the investigation were to : (1) determine experimentally the load-displacement relationships and the strain distribution on the section of test beams : (2) determine experimentally the moment-curvature and the load-neutral axis relationship of Belite ; (3) investigate the flexural ductility of Belite ; (4) estimate the ratio of the capacities of nominal moment strength as a function of ACI to as a experiment. From the test results, the flexural behavior of reinforced high-strength concrete beams using Belite cement are similar to flexural behavior of normal reinforced concrete beams.

• Journal of the Korea Institute of Building Construction
• /
• v.4 no.1
• /
• pp.127-132
• /
• 2004

CFT(Concrete Filled Steel Tube) is a structure of circular or squared of steel column filled with concrete. The steel tube holds the concrete inside and that makes this structure to perform superior features on stiffness, proof stress, transformation, fire resistance and construction itself. In this study, by over the 800kgf/$\textrm{cm}^2$ of high strength concrete for CFT column, research has been done on the basic property of matter such as fluidity, resistance on segregation, compressive strength, setting icons of the concrete filled in the steel tube under conditions of standard weather. Physical properties of concrete for CFT that Concrete with silica fume, fly ash of air entraining and high-range water reducing agent, that used to CFT column research purpose to find the most ideal composition, which is achieved by the investigation in the concrete's property of matter like ability of Slump, Slump Flow, Air content, Bleeding, and Settlement. For this study, experiments which are bused on obtained the result through physical test are practiced, with all of the experiment, specimens only for control are produced in each method of curing and analyzed to relations with core strength in mock-up test. In mock-up test, the research is studied compactability of concrete filled in tube and degree of hydration hysteresis, as a basic reference for applying to field of CFT column which is used over 800kgf/$\textrm{cm}^2$ high strength concrete.