• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2004년도 춘계 학술발표대회 개요집
• /
• pp.252-254
• /
• 2004

Fatigue life a box weldment was predicted with the stress concentration and residual stress using the equation reported. In order to change the stress concentration and residual stress of the box weldment, Post treatments such as smooth grinding of weld bead, weld toe grinding and hammer peening were applied. The fatigue life of the weldment after post treatment clearly increased, which is attributed to the reduction of stress concentration and/or introduction of compressive residual stress at the weld toe. The predicted fatigue life was a relatively good agreement with the experiment for a long fatigue life, while it was underestimated for a short fatigue life.

• 한국해양공학회지
• /
• 제15권3호
• /
• pp.93-99
• /
• 2001

Recently the steel parts used at automobils are required to be used under high stress more than ever before in need of the weight down. To achieve this requirement of a high strength steel, it must be necessary to decrease inclusion content and surface defect as like decarburization, surface roughness etc.. In this study, the surface conditions are measured to know the influence on fatigue properties by two cases of shot peening of two-stage shot peening and single-stage shot peening. And for this study, two kinds of spring steel (SAE 9254, DIN50CrV4) are used. This study shows the outstanding improvement of fatigue properties at the case of two-stage shot peening in the rotary bending fatigue test and this is assumed to be from (1) on low stress condition, th 1st stage shot peening is not affected by nonmetallic inclusion under metal.(2) it is possible that the 2nd stage shot peening increases the fatigue life and the high stress but that is affected by nonmetallic inclusion under metal. (3) so far beeasily DIN50CrV4 have made high stress. But, results also show fatigue failures originated at inclusion near surface, and this inclusion type is turned out to be a alumina of high hardness.

• International Journal of Safety
• /
• 제1권1호
• /
• pp.24-27
• /
• 2002

Recently the steel parts used in automobiles are required to be used under high stress more than ever before due to the need of keeping the weight down. To achieve this requirement of the high strength steel, it must be necessary to decrease inclusion contents and surface defects as like decarburization, surface roughness etc. In this study, the surface conditions are measured to know the influence on fatigue properties by two cases of two-stage shot peening and single-stage shot peening. And for this study, three kinds of spring steel (JISG408l-SUP7, SAE 9254 and DIN 50CrV4) are shaped. This study shows the outstanding improvement of fatigue properties at the case of two-stage shot peening in the rotating bending fatigue test and it results from (1) decreasing the surface roughness (2) unchanging the surface hardness (3) increasing the compressive residual stress. Moreover, results also show fatigue failures originated at the inclusion near the surface, and this inclusion type is turned out to be an alumina of high hardness.

• 한국농공학회논문집
• /
• 제46권6호
• /
• pp.29-36
• /
• 2004

In this study, The fatigue properties of the GFRP composite panels of which core was made of the polymer mortar and both facings were reinforced by the high-tensile GFRP were surveyed. Composite-panel specimens consisted of polymer mortar core and GFRP compressive and tensile sides with various thickness were produced for an experimental study. Flexural fatigue tests were conducted to examine the correlation between the fatigue load and the fatigue life for various thickness of core and facings, and its results are presented. The correlation obtained in this study between the fatigue load and the fatigue life for various thickness arc in good agreement with the modified Miner's law.

• 한국해양공학회지
• /
• 제18권5호
• /
• pp.43-49
• /
• 2004

The lightness of components required in the automobile and machine industry necessitates the use of high strength components. In particular, the fatigue failure phenomena, which occurs when using metal, increases the danger to human life and property. Therefore, antifatigue failure technology is an integral part of current industries. Currently, the shot peening is used for removing the defect from the surface of steel, while improving the fatigue strength on surface. Therefore, in this paper, the effect of compressive residual stress of spring steel(JISG SUP-9) by shot-peening on fatigue crack growth characteristics in a stress ratio(R=0.1, R=0.3, R=0.6) was investigated, giving consideration to fracture mechanics. By using the methods mentioned above, following conclusions are drawn: (1) The fatigue crack growth rate(da/dN) of the shot-peening material was lower than that of the un-peening material and in stage I, ΔKth, the threshold stress intensity factor of the shot-peen processed material is high in critical parts, unlike the un-peening material. Also m, fatigue crack growth exponent and number of cycle of the shot-peening material, was higher than that of the un-peening material, as concluded from effect of da/dN. (2) Fatigue life shows more improvement in the shot-peening material than in the un-peening material, and the compressive residual stress of surface on the shot-peen processed operate resistance of fatigue crack propagation.

• 한국강구조학회 논문집
• /
• 제21권1호
• /
• pp.55-62
• /
• 2009

강교 제작에는 강재 표면의 이물질 제거와 피복방식재료의 부착성 증대를 위하여 블라스트 표면처리가 실시되고 있다. 블라스트 표면처리는 쇼트나 그릿 등의 연마재를 압축공기로 분사하여 강재 표면에 충격을 가하는 표면처리법으로, 블라스트 처리에 의해 표면형상이 개선되고 압축잔류응력이 도입되어 용접이음의 피로수명이 향상될 것으로 예상된다. 본 연구에서는 하중비전달형 십자필렛 용접이음의 피로실험을 실시하여, 블라스트 표면처리가 용접이음의 피로거동에 미치는 영향을 실험적으로 검토하였다. 피로실험에는 용접 후 무처리 시험편(용접 그대로), 용접 후 블라스트 표면처리 한 시험편과 블라스트 처리 후 열처리에 의해 잔류응력을 제거한 시험편의 합계 3종류의 용접시험편을 대상으로 하였다. 그 결과 블라스트 표면처리에 의해 용접지단부의 곡률반경은 약 29% 증가하였으며, 용접지단부의 인장잔류응력이 제거되고 압축잔류응력이 도입되었다. 그리고 블라스트 처리에 의해 피로수명과 피로한계가 증가하였다. 피로수명은 응력범위가 낮을수록 더 크게 증가하였고, 피로한계는 약 1.5배 증가하였다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1993년도 봄 학술발표회 논문집
• /
• pp.169-175
• /
• 1993

Possibility of fatigue failure in punching shear of reinforced concrete decks of highway bridges is analytically investigated by applying Matsui et al.'s experimental finding to models of 2-meter span decks designed in compliance with previous and current codes. Decks made of concrete of compressive strength of 240㎏/㎠ showed longer fatigue life than decks made of 210㎏/㎠ concrete at the same Md/U rations ; higher Md/U ratio resulted in linger fatigue life but its effect is insignificant in decks having effective depths of 14 and 15cm. Decks designed to higher load factors as specified by current codes showed longer fatigue life than decks designed to lower load factors specified by previous codes ; yet fatigue failure appeared to occur in both decks within their normal life span, thus indicating need for redefining the minimum deck thickness.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2005년도 창립60주년 기념 추계 학술대회
• /
• pp.140.2-140.2
• /
• 2005

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2005년도 창립60주년 기념 추계 학술대회
• /
• pp.141.1-141.1
• /
• 2005

• 한국공작기계학회논문집
• /
• 제11권2호
• /
• pp.43-49
• /
• 2002

SB41 material is welded automatically and is investigated some effects of the welding residual stress in the growth and propagation of fatigue crack, so as to study the fatigue behaviour in the welding residual stress field. The summarized results are as follows; 1) In case of the load amplitude is constant, as the stress ratio is changing to 0.1, 0.33 and 0.5 the propagation life is constant but the growth life decreases. And than, when maximum load or minimum load is constant as the stress ratio increases the growth life and propagation life. 2) It was shown that fatigue crack propagation ratio da/dN was almost constant regardless of the stress ratio change at constant load amplitude and that the larger stress ratio, the slower was the fatigue crack propagation ratio. 3) The opening ratio U is influenced by $K_max$ but it isn't only the function of $K_max$ because data range is very large. 4) The fatigue life of the specimens on tensile compressive residual stress field was decreased and increased respectably more than that of the base metal.