• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2002년도 추계학술발표대회 논문집
• /
• pp.131-134
• /
• 2002

Braided carbon fiber reinforced Al matrix composites were developed and characterized. Braided carbon fiber preforms with braiding angles of $30^{\circ}$, $45^{\circ}$ and $60^{\circ}$ were manufactured by using a braiding machine. The manufactured braided carbon fibers were used as reinforcement to fabricate Al matrix composites by employing a pressure infiltration casting method. In the processing of pressure infiltration casting, important processing parameters such as melting temperature, preheating temperature of preform and applied pressure were optimized. Prediction of elastic constants on composites was performed by using the volume averaging method, which utilizes the coordinate transformation and the averaging of stiffeness and compliance constants based upon the volume of each reinforcement and matrix material. The elastic moduli of composites were evaluated by using Resonant Ultrasound Spectroscopy(RUS) method and compared with the elastic moduli obtained from static tensile test method.

• Transactions on Electrical and Electronic Materials
• /
• 제11권2호
• /
• pp.89-91
• /
• 2010

Partial discharge (PD) resistances were investigated for three types of samples: original epoxy resins, epoxy micro composites with and without the silane processing, and mixture composites with micro and nano particles. The PD was applied to these materials using rod, gap, and plane electrodes. The partial discharge resistance found in the micro composites was better than that found in the original epoxy resin. Moreover, the mixture composites of $SiO_2$ nano and micro particles had much larger resistances than the original epoxy resin or microcomposites. It can be regarded that this excellent property was due to the fact that the nano particles have a dense structure between the micro particles.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2005년도 봄학술 발표회 논문집(I)
• /
• pp.371-374
• /
• 2005

The research reported in this paper provides the test results of eleven reinforced concrete beams strengthened with FRP composites. Three parameters were considered in this investigation: the amount of FRP composites, the types of bonding schemes(continuous sheets or strips), and the material types of FRP composites (Carbon or Glass). The experimental results indicated that because the rupture strain of FRP composites was relatively higher that the yield strain of steel bars, the RC beams strengthened with FRP composites failed due to concrete crushing before the FRP composites arrived at its rupture strain. The compatibility-aided truss model showed reasonable agreement between the predicted and experimental shear stress-strain curves of the beams throughout the entire loading history.

• 한국주조공학회지
• /
• 제17권2호
• /
• pp.170-179
• /
• 1997

A noble technique has been developed for fabricating in situ formed $TiC_p/Al$ composites. In this process, fairly stable TiC particles were in situ synthesized in liquid aluminum by the interfacial reaction between an Al-Ti melt and SiC, which is a comparatively unstable carbide from the view-point of thermodynamics. It is possible in the present process to generate TiC particles of nearly 1 ${\mu}m$ in diameter, even utilizing SiC of 14 ${\mu}m$ as raw material. However, the dispersion behavior of TiC particles in the matrix depends on the size of the raw material SiC. Decomposing finer SiC makes the dispersion of TiC particles more uniform and the mechanical properties of composites are improved accordingly. The structure of in situ composites and their mechanical properties are affected by the fabrication temperature and the stirring time. It has been found that the most suitable condition for fabrication should be applied depending on the size of the raw material, even if the same kinds of carbide are used. Furthermore, although Al-Ti-Si system intermetallic compounds are detected in a $TiC_p/Al-Si$ composite which is fabricated by conventional melt-stirrng method, these compounds can not be observed in a $TiC_p/Al-Si$ composite made by this in situ production method. Hence the mechanical properties of the in situ $TiC_p/Al-Si$ composite are superior to those of the conventional $TiC_p/Al-Si$ composites.

• Imaging Science in Dentistry
• /
• 제43권3호
• /
• pp.145-151
• /
• 2013

Purpose: This study was performed to evaluate and compare the radiopacity of dentin, enamel, and 8 restorative composites on conventional radiograph and digital images with different resolutions. Materials and Methods: Specimens were fabricated from 8 materials and human molars were longitudinally sectioned 1.0 mm thick to include both enamel and dentin. The specimens and tooth sections were imaged by conventional radiograph using #4 sized intraoral film and digital images were taken in high speed and high resolution modes using a phosphor storage plate. Densitometric evaluation of the enamel, dentin, restorative materials, a lead sheet, and an aluminum step wedge was performed on the radiographic images. For the evaluation, the Al equivalent (mm) for each material was calculated. The data were analyzed using one-way ANOVA and Tukey's test (p<0.05), considering the material factor and then the radiographic method factor, individually. Results: The high speed mode allowed the highest radiopacity, while the high resolution mode generated the lowest values. Furthermore, the high resolution mode was the most efficient method for radiographic differentiation between restorative composites and dentin. The conventional radiograph was the most effective in enabling differentiation between enamel and composites. The high speed mode was the least effective in enabling radiographic differentiation between the dental tissues and restorative composites. Conclusion: The high speed mode of digital imaging was not effective for differentiation between enamel and composites. This made it less effective than the high resolution mode and conventional radiographs. All of the composites evaluated showed radiopacity values that fit the ISO 4049 recommendations.

• Advanced Composite Materials
• /
• 제17권3호
• /
• pp.247-258
• /
• 2008

This paper is concerned with the long-term performance of geo-textile (GT) composites in terms of creep deformation and frictional properties. Composites of PVA GT and HDPE GM were made to investigate the advanced properties of long-term performance related to waste landfill applications. The same experiments were also performed for typical polypropylene and polyester GT and compared to PVA GT/HDPE GM composites. We also develop high performance GT composites with GM by using PVA GT, which is capable of improving the frictional properties and thus enhances long-term performance of GT composites. Experimental study reveals that the friction coefficient of GT composites is relatively large compared with those of polyester and polypropylene non-woven GT as long as the friction media has similar size to the particles of domestic standard earth. In addition, the geo-composites bonded with geo-grid by a chemical process were investigated experimentally in terms of strain evaluation and creep response values. Geo-grid plays an important role as a reinforcing material. Three kinds of geo-grid were prepared as strong yarn polyester and they were woven type, non-woven type, and wrap knitted type. The sample geo-grids were then coated with PVC. The rib tensile strength tests were conducted to evaluate geo-grid products in terms of tensile strength with regard to single rib. The test was performed according to GRI-GGI. It was concluded again from the experiments that the tensile and creep strains of the geo-grid showed such stable values that the geo-grid prepared in this study could protect geo-textile partially in practical structures.

• Composites Research
• /
• 제36권1호
• /
• pp.32-36
• /
• 2023

최근 탄소 중립 등 지속 가능한 발전을 위한 지구환경 문제가 대두되면서 기존 풍력터빈의 소재인 유리섬유 복합재의 폐기 시 처리 방안이 문제가 되고 있다. 이를 해결하기 위해 본 연구에서는 기존의 유리섬유 복합재를 대체할 수 있는 친환경 복합재인 아마섬유 기반 복합재를 활용하여 30kW 풍력터빈 블레이드를 제조하고 적합성을 평가하였다. 먼저 친환경 천연 아마섬유 복합재의 풍력터빈 블레이드 소재로 활용 가능성을 검증하기 위해 기계적 강도 시험을 수행하였으며, 그 결과 선행 아마섬유 복합재 물성 연구 대비 좀 더 우수한 강도가 측정된 것을 확인하였다. 또한 제작된 30kW 급 아마섬유 복합재 블레이드를 활용하여 아마섬유 복합재 블레이드의 정적강도를 측정하는 정적강도 성능평가 시험을 통하여 적합성을 확인하였다.

• Restorative Dentistry and Endodontics
• /
• 제24권2호
• /
• pp.299-309
• /
• 1999

The composite resin, due to its esthetic qualities, is considered the material of choice for restoration of anterior teeth. With respect to shade control, the direct-placement resin composites offer some distinct advantages over indirect restorative procedures. Visible-light-cured (VLC) composites allow dentists to match existing tooth shades or to create new shades and to evaluate them immediately at the time of restoration placement. Optimal intraoral color control can be achieved if optical changes occurring during application are minimized. An ideal VLC composite, then, would be one which is optically stable throughout the polymerization process. The shade guides of the resin composites are generally made of plastic, rather than the actual composite material, and do not accurately depict the true shade, translucency, or opacity of the resin composite after polymerization. So the numerous problems associated with these shade guides lead to varied and sometimes unpredictable results. The aim of this study was to assess the color changes of current resin composite restorative materials which occur as a result of the polymerization process and to compare the color differences between the shade guides provided with the products and the actual resin composites before- and after-polymerization. The results obtained from this investigation should provide the clinician with information which may aid in improved color match of esthetic restoration. Five light activated, resin-based materials (${\AE}$litefil, Amelogen Universal, Spectrum TPH VeridonFil-Photo, and Z100) and shade guides were used in this study. Three specimens of each material and shade combination were made. Each material was condensed inside a 1.5mm thick metal mold with 10mm diameter and pressed between glass plates. Each material was measured immediately before polymerization, and polymerized with Curing Light XL 3000 (3M Dental products, USA) visible light-activation unit for 60 seconds at each side. The specimens were then polished sequentially on wet sandpaper. Shade guides were ground with polishing stones and rubber points (Shofu) to a thickness of approximately 1.5mm. Color characteristics were performed with a spectrophotometer (CM-3500d, Minolta Co., LTD). A computer-controlled spectrophotometer was used to determine CIELAB coordinates ($L^*$, $a^*$ and $b^*$) of each specimen and shade guide. The CIELAB measurements made it possible to evaluate the amount of the color difference values (${\Delta}E{^*}ab$) of resin composites before the polymerization process and shade guides using the post-polishing color of the composite as a control, CIE standard D65 was used as the light source. The results were as follows. 1. Each of the resin composites evaluated showed significant color changes during light-curing process. All the resin composites evaluated except all the tested shades of 2100 showed unacceptable level of color changes (${\Delta}E{^*}ab$ greater than 3.3) between pre-polymerization and post-polishing state. 2. Color differences between most of the resin composites tested and their corresponding shade guides were acceptable but those between C2 shade of ${\AE}$litefil and IE shade of Amelogen Universal and their respective shade guides exceeded what is acceptable. 3. Comparison of the mean ${\Delta}E{^*}ab$ values of materials revealed that Z100 showed the least overall color change between pre-polymerization and post-polishing state followed by ${\AE}$litefil, VeridonFil-Photo, Spectrum TPH, and Amelogen Universal in the order of increasing change and Amelogen Universal. Spectrum TPH, 2100, VeridonFil-Photo and ${\AE}$litefil for the color differences between actual resin and shade guide. 4. In the clinical environment, the shade guide is the better choice than the shade of the actual resin before polymerization when matching colors. But, it is recommended that custom shade guides be made from resin material itself for better color matching.

• 한국재료학회지
• /
• 제10권10호
• /
• pp.677-683
• /
• 2000

3Y-TZP/12Ce-TZP 의 3층 5층 복합체를 슬립주입법으로 제조하고, 그 기계적 성질을 검토하였다. 지름-원반압축시험법으로 구한 다층복합체의 파괴강도는 327~534MPa이었다. Vickers압입하중의 증가(~300N)와 더불어 압입강도는 전반적으로 감소하였으나, 다층물질은 단상물질에 비하여 우수한 손상저항을 나타내었다. 49N의 하중으로 압입후 다층물질의 4점 꺽임강도는 620~674MPa 인데 반하여 단상 물질의 경우는 129~339MPa을 나타내었다. 압자압입에 의한 다층물질의 인서은 $7.7~13.1\;MPa{\cdot}m^{1/2}$ 정도를 나타내었다.

• Composites Research
• /
• 제32권1호
• /
• pp.29-36
• /
• 2019

본 논문의 목적은 소재대체법과 치수최적화 기법을 이용한 2층 고속열차 알루미늄 압출재 차체의 경량 설계를 제시하는 것이다. 소재대체법을 수행하기 위해 위상최적화 기법을 이용하여 차체 구조물의 샌드위치 복합재 적용 부위를 결정하였다. 해석결과, 루프와 2층 언더프레임에 샌드위치 복합재가 적용 가능함을 보여주었다. 치수최적화는 알루미늄 압출재와 카본/에폭시 복합재의 두께를 결정하는데 사용되었다. 치수최적화를 수행하기 위해, 설계변수, 제약조건, 목적함수를 정식화 하였으며 이러한 조건에 의해 유효설계를 도출하였다. 경량 설계의 결과로 2층 고속열차 하이브리드 차체의 무게를 2.18 ton(17.70%)까지 줄일 수 있음을 보여주었다.