• Journal of Dental Rehabilitation and Applied Science
• /
• v.25 no.1
• /
• pp.1-12
• /
• 2009

The objective of this study was to test the effects of crown material, cement type, the direction in which stress is applied and distribution of luting cement that might lead to cement microfracture using 2D Finite Element Method. Twenty three finite element models with a chamfer margin configuration were generated for a mandibular first molar. Crown models exhibited four crown materials: type 3 gold alloy, Ni-Cr alloy, ceramic and composite resin, and two luting cements: zinc phosphate and glass ionomer cements with a thicknesses of $70{\mu}m$. Modeled crowns were loaded axially or obliquely at unit load of 1 N. Areas and levels of stress concentrations within the cement were determined. Stress in the cement layer at the margins of crowns were higher than those in the area away from the margin. Stress under oblique loads were much higher than under axial load. The stiffer crown material produced higher stress and similarly, higher stress were found in cements with the greater Young's modulus.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.34 no.4
• /
• pp.579-589
• /
• 2007

The objective of this study was to compare the shear bond strengths of five adhesive systems to the enamel and dentin of primary and permanent teeth. Fifty noncarious primary and fifty permanent teeth were collected and stored in an 0.1% thymol solution at room temperature after extraction. The tested adhesives were: Adper Scotchbond Multi-purpose Plus Adhesive (SM) Adper Single bond 2 (SB), Clearfil SE Bond (SE), Adper Prompt L-Pop (PL), GBond (GB). For the shear bonding test, the labial and lingual surfaces of primary and permanent teeth were used. To obtain a flat surface, the labial and lingual surfaces of the teeth were sanded on $SiO_2$ with number 600 grit and then divided into 20 groups of 10 surfaces each. All samples were theromocycled in water $5^{\circ}C$ and $55^{\circ}C$ for 1000 cycles. The results were as follows: 1. For primary enamel, shear bond strengths of SM and SB were significantly higher than that of SE and also SM, SB, and PL were higher than GB(p<0.05). 2. For primary dentin, there were no significant differences among the shear bond strengths of any other bonding systems except difference between SE and GB. 3. For permanent enamel, SB showed significantly higher mean shear bond strength than those of any other bonding systems(p<0.05). 4. For permanent dentin, SM showed significantly higher mean shear bond strength than that of PL and GB(p<0.05). 5. Between the primary enamel and dentin, there were significant differences in SM, SB, and GB, whereas there was statistically significant difference in PL between the permanent enamel and dentin(p<0.05). 6. Between the primary and permanent teeth on enamel, there were no significant differences among all bonding systems, whereas there were statistically significant differences in SM and SB between the primary and permanent teeth on dentin(p<0.05).

• Journal of Dental Rehabilitation and Applied Science
• /
• v.29 no.1
• /
• pp.37-44
• /
• 2013

Sodium hypochlorite and ethylene diamine tetra acetic acid are substances usually used during endodontic treatment. Several studies found that the bonding was negated with certain irrigants and some of the used irrigants have demineralizing and chealating effects, so it was advocated to omit the etching step in etch and rinse adhesive systems. The purpose of this in vitro study was to evaluate the influence of NaOCl & EDTA on the bonding strength of ethanol wet bonding. Thirty human molars were selected and mesiodistally sectioned into halves, thus providing sixty specimens. The specimens were randomly assigned to 4 groups(n=15) according to the irrigant regimen used : (1) irrigated with distilled water for 10min (control); (2) irrigated with 5.25% NaOCl(10min), flushed with 5.25% NaOCl(1min) (3) irrigated with 5.25% NaOCl, flushed with 17% EDTA (4) irrigated with 5.25% NaOCl, flushed with 17% EDTA. Each group was acid-etched with 37% phosphoric acid(except group 4) and had their dentin surfaces dehydrated with ethanol solutions : 50%, 70%, 80%, 95%, 3x100%, 30s for each application. After dehydration, a primer( 50% all bond 3 resin + 50% ethanol) was used, followed by the adhesive(ALL-BOND 3 RESIN) application. Resin composite build-ups were then prepared using an incremental technique. Specimens were sectioned into beams and submitted to a tensile load using a Micro Tensile Tester(Bisco Inc.). The data were statistically analyzed using one-way ANOVA and Tukey HSD at p<0.5 level. There was no significant difference on G1(control) and G2(irrigated with NaOCl only ). (p>0.05). G3(flushed with EDTA) showed significantly high tensile bonding strength compared to the G2 (p<0.05). G4( treated with EDTA but no acid-etching) was significantly lower value than G3. (p<0.05) Although there was no significant difference, 5.25% NaOCl seemed to have an adverse effect on the bonding strength of ethanol wet bonding. The flushing with EDTA after NaOCl irrigation prevents the decrease of bonding strength. The use of 17% EDTA as a final flush can enhance the bonding strength but EDTA flushing can't substitute for a acid-etching.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.27 no.1
• /
• pp.1-13
• /
• 2011

The aim of this study was to evaluate shear bond strength of pressed reinforced composite resin ($TESCERA^{TM}$ ATL) veneering to zirconia with various surface treatments. Forty sintered zirconia specimens and forty pockmarked zirconia specimens were fabricated. All the materials were categorized as Group 1 (Control : porcelain veneering on zirconia surface), Group 2 ( $TESCERA^{TM}$ ATL dentine veneering after bonding agent application on zirconia surface), Group 3 ($TESCERA^{TM}$ ATL dentine veneering on pockmarked zirconia surface), Group 4 ($TESCERA^{TM}$ ATL dentine veneering after bonding agent application on pockmarked zirconia surface), Group 5 (Thermocycling on Group 1), Group 6 (Thermocycling on Group 2), Group 7 (Thermocycling on Group 3), and Group 8 (Thermocycling on Group 4). SBS(Shear bond strength) of 8 groups was determined with an Instron Universal Testing Machine. Also fractured surface of specimens were observed with a scanning electron microscope. There were no significant differences in the initial SBS between Group 1(control group), Group 3, and Group 4. (p>0.05) Group 2 presented the lowest SBS values. There was a no significant difference between just as 24hour water storage and simulated aging on pockmarked zirconia groups. (p>0.05) A formation of pockmarked irregularities on zirconia surface as mechanically pitted surface was reliable method for establishing a stronger bond between $TESCERA^{TM}$ ATL and zirconia-based material.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.31 no.2
• /
• pp.190-201
• /
• 2004

The aim of this study was to evaluate the resistance to degradation and to compare the wear resistance characteristics of four esthetic restorative materials in an alkaline solution. The brands studied were Charmfil, Charmfil flow(composite resin), Compoglass F and PrimaFlow(compomer). The results were as follows: 1. The mass loss were not significantly different among the materials(p>0.05). 2. The sequence of the degree of degradation layer depth was in descending order by Compoglass F, PrimaFlow, Charmfil, and Charmfil flow. There were significant differences between Compoglass F and the others(p<0.05). 3. The sequence of the Si loss was in descending order by Charmfil flow, Charmfil, PrimaFlow, and Compoglass F. There were significant differences among these materials(p<0.05). 4. When observed with SEM, destruction of bonding between matrix and filler was observed and when observed with CLSM, the depth of degradation layer of specimen surface was observed. 5. The sequence of maximum wear depth was in descending order by Comfoglass, PrimaFlow Charmal, and Charmfil flow. There were significant differences among these materials(p<0.05). 6. The correlation coefficient between Si loss and degradation layer depth (r=0.602, p<0.05) Vicker's hardness number and maximum wear depth (r=0.501, p<0.05) were relatively high. These results indicate that wear and hydrolytic degradation may be considered to be evaluation factors of composite resins and compomers.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.32 no.3
• /
• pp.557-568
• /
• 2005

The aim of this study was to evaluate the resistance to degradation and to compare the wear resistance characteristics of four esthetic restorative materials in an alkaline solution(0.1N NaOH). The brands studied were MetafilCX(Sun medical, Japan) Solitaire 2(Heraeus Kulzer, USA), Composan LCM(Promedica, Germany), DenFil(Vericom, Korea). The results were as follows: 1. The mass loss of each brand was 0.74~7.94% and highest value in Metafil($7.94{\pm}0.39%$). 2. The sequence of the degree of degradation layer depth was in descending order by Metafil, Solitaire 2, DenFil, Composan LCM. There were significant differences between Metafil and the others(p<0.05). 3. The sequence of the Si loss was in descending order by Metafil, Solitaire 2, Composan LCM, DenFil. There were significant differences among the materials(p<0.05). 4. On SEM, destruction of bonding between matrix and filler and on CLSM, the depth of degradation layer of specimen surface was observed. 5. The sequence of maximum wear depth was in descending order by Metafil, Solitaire 2, Composan LCM and DenFil. There were significant differences among the materials(p<0.05). 6. The correlation coefficient between Si loss and degradation layer depth (r=0.491, p<0.05) and Vicker's hardness number and maximum wear depth (r=-0.942, p<0.05) were relatively high. These results indicate that hydrolytic degradation and wear may consider as a evaluation factors of composite resins.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.16 no.1
• /
• pp.51-60
• /
• 2000

The purpose of this study was to compare the microleakage at the interface of cast post and tooth according to the type of cement. Forty anterior teeth with single root were used. The teeth were cut 2 mm coronal from the cementoeamel junction and chamfer finish line was made on 1 mm coronal from the cementoeamel junction. After the routine endodontic treatment, post space was prepared using #5.5 Parapost drill to a depth of 7 mm. After the pick up impression, core building was made to 3 mm of clinical crown with burnout wax, then post and core was cast with nonprecious metal. The teeth were divided into four groups of ten each. In Group I, post and core were cemented with Fleck's(Zinc phosphate cement) In Group II, post and core were cemented with Fuji I(Glass ionomer cement) In Group III, post and core were cemented with Superbond C & B(Composite resin cement) In Group IV, post and core were cemented with Panavia 21(Composite resin cement) All cemented teeth were stored in normal saline at $37^{\circ}C$ for 7 days and thermocycled from $5^{\circ}C$ to $55^{\circ}C$ for 500 cycles with a dwell time of 30 seconds. After thermocycling, teeth were immersed in 1% Basic fuchsin dye for 48 hours. All 40 teeth were then embedded in the epoxy resin and cut buccolingually with a cutting instrument. The degree of penetration of dye at interface was graded on a scale of 0 to 4 using a stereomicroscope at 25 to 40 times magnification. Through the findings of this study, the following conclusion were obtained. 1. All the groups showed the microleakage at the interface of cast post core and tooth. 2. Group I showed the highest microleakage score among the groups with a significant difference(p<0.05). 3. Group II showed higher microleakage score than Group III and Group IV with a significant difference(p<0.05). 4. Group IV showed the lowest microleakage score but there were no significant difference with Group III(p>0.05).

• Restorative Dentistry and Endodontics
• /
• v.29 no.2
• /
• pp.177-184
• /
• 2004

Objectives : This study investigated the hypothesis that increasing light-curing time would leave the oxygen-inhibited layer (OIL) of the adhesive thinner, and in turn, result in lower shear bond strength (SBS) than those obtained by the routine curing procedures. Methods：120 human extracted posterior teeth were randomly divided into three groups for bonding with three adhesives：All Bond 2/sup (R)/, One Step/sup (R)/, and Adper Prompt/sup (R)/. They were subsequently divided into four subgourps with different light-curing time (10, 20, 30 and 60s). The assigned adhesives were applied on superficial occlusal dentin according to the manufacturer's instructions and cured with one of the four curing times. Composite resin cylinder, 2.35㎜ in diameter, were built on the cured adhesive and light-cured for 40s. SBS were measured after 24h from the bonding using a universal testing machine (crosshead speed 1.0 ㎜/min). The relative thickness of the OIL and the degree of conversion (DC) were determined from the adhesive on a slide glass using FT-NIR in an absorbance mode. Data were analysed with One-way ANOVA and Duncan's multiple test (p〈0.05), Results：With increasing cure time, although there were no significant difference in th SBS of One-step and Adper Prompt (p〉0.05), those of All Bond 2 decreased significantly (p〈0.05). The relative thicknesses of the OIL on each adhesive were not affected by the cure time (p〉0.05). Although the DC of All-Bond 2 were statistically not different with increasing cure time (p〉0.05), those of One-Step and Adper Prompt showed an increasing trends with increasing cure time (p〈0.05). Conclusions：Increasing light-curing time did not affect on the relative thickness of the OIL of the adhesives, and in turn, on the SBS to dentin.

• The Journal of Korean Academy of Prosthodontics
• /
• v.53 no.4
• /
• pp.295-300
• /
• 2015

Purpose: The aim of this study was to evaluate the shear bond strength between Ni-Cr alloy and composite resin using universal adhesive systems coMPared to conventional method using metal primers. Materials and methods: For this study, a total of 120 cast commercial Ni-Cr alloy (Vera Bond 2V) disks were embedded in acrylic resin, and their surfaces were smoothed with silicon carbide papers and airborne-particle abrasion. Specimens of each metal were divided into 6 groups based on the combination of metal primers (Metal primer II, Alloy primer, Metal & Zirconia primer, MKZ primer) and universal adhesive systems (Single Bond Universal, All Bond Universal). All specimens were stored in distilled water at $37^{\circ}C$ for 24 hours. Shear bond strength testing was performed with a universal testing machine at a cross head speed of 1 m/min. Data (MPa) were analyzed using one-way ANOVA and the post hoc Tukey's multiple comparison test (${\alpha}$=.05). Results: There were significant differences between Single Bond Universal, All Bond Universal, Metal Primer II and Alloy Primer, MKZ Primer, Metal & Zirconia Primer (P<.001). Conclusion: Universal Adhesive system groups indicated high shear bond strength value bonded to Ni-Cr alloy than that of conventional system groups using primers except Metal Primer II. Within the limitations of this study, improvement of universal adhesive systems which can be applied to all types of restorations is recommended especially non-precious metal alloy. More research is needed to evaluate the effect of silane inclusion or exclusion in universal adhesive systems.

• Restorative Dentistry and Endodontics
• /
• v.36 no.2
• /
• pp.119-124
• /
• 2011

Objectives: The purpose of this experiment was to evaluate four different polishing systems of their polishability and polishing time. Materials and Methods: 4 mm diameter and 2 mm thickness Teflon mold was made. Z-250 (3M ESPE) hybrid composite resin was slightly overfilled and pressed with slide glass and cured with Optilux 501 for 40 sec each side. Then the surface roughness (glass pressed: control group) was measured with profilometer. One surface of the specimen was roughened by #320 grit sand paper and polished with one of the following polishing systems; Sof-Lex (3M ESPE), Jiffy (Ultradent), Enhance (Dentsply/Caulk), or Pogo (Dentsply/Caulk). The surface roughness and the total polishing time were measured. The results were analyzed with one-way ANOVA and Duncan's multiple range test. Results: The surface roughness was lowest in Pogo, and highest in Sof-Lex. Polishing times were shortest with Pogo, and followed by the Sof-Lex, Enhance and Jiffy. Conclusions: One-step polishing system (Pogo) is very effective to get the smooth surface in a short time, therefore it can be recommended for final polishing system of the restoration.