• 한국신재생에너지학회:학술대회논문집
• /
• 2006.06a
• /
• pp.51-54
• /
• 2006

Cathode material, $(Ba_{0.5}Sr_{0.5})_{0.99}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$, for low temperature SOFC was prepared by the glycine-nitrate synthesis process (GNP). The characteristics of the synthesized powders were studied with controlling pH of a precursor. The synthesis BSCF powders with pH were agglomeration state and calcinations temperature has not influence on particles. Highly acidicprecursor solution increased a single phase forming the temperature. Also, synthesis BSCF powder was show result for thermal analysis and alteration of difference crystal with pH. It is considered that Ba and Sr cannot complex by carboxylic acid group of glycine, because under highly acidic condition the caboxylic group mainly combined with $H^+$ insead of alkali and alkaline earth cations. In case of using precursor solution with pH $2{\sim}3$, a single perovskite phase was obtained at $1000^{\circ}C$. Polarization resistance of $(Ba_{0.5}Sr_{0.5})_{0.99}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ was measured by AC impedance spectroscopy from the two electrode symmetric cell. Area specific resistance of the $(Ba_{0.5}Sr_{0.5})_{0.99}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ air electrode at $500^{\circ}C\;and\;600^{\circ}C$ were $0.96{\Omega}?cm^2$ and $0.16{\Omega}?cm^2$, respectively.

• Current Applied Physics
• /
• v.18 no.12
• /
• pp.1577-1582
• /
• 2018

While controlling the cation contents in perovskite rare-earth nickelate thin films, a metal-to-insulator phase transition is reported. Systematic control of cation stoichiometry has been achieved by manipulating the irradiation of excimer laser in pulsed laser deposition. Two rare-earth nickelate bilayer thin-film heterostructures with the controlled cation stoichiometry (i.e. stoichiometric and Ni-excessive) have been fabricated. It is found that the Ni-excessive nickelate film is structurally less dense than the stoichiometric film, albeit both of them are epitaxial and coherent with respect to the underlying substrate. More interestingly, as a temperature decreases, a metal-to-insulator transition is only observed in the Ni-excessive nickelate films, which can be associated with the enhanced disproportionation of the Ni charge valence. Based on our theoretical results, possible origins (e.g. anti-site defects) of the low-temperature insulating state are discussed with the need of future work for deeper understanding. Our work can be utilized to realize unusual physical phenomena (e.g. metal-to-insulator phase transitions) in complex oxide films by manipulating the chemical stoichiometry in pulsed laser deposition.

• Journal of the Korean institute of surface engineering
• /
• v.56 no.6
• /
• pp.380-385
• /
• 2023

In this study, an MPB PMNT system containing 0.05 to 0.10 wt.% BaTiO₃ was synthesized using a traditional chemical method and its pyroelectricity was investigated. Pyroelectricity, dielectricity, and ferroelectricity of the synthesized BaTiO₃-PMNT system were analyzed by heat treatment at 1240~1280 ℃ for 4 hours to evaluate its applicability as a pyroelectric sensor. Unlike the simple ABO₃ ferroelectric, the BaTiO₃-doped PMNT system exhibited phase transition characteristics over a wide temperature range typical of complex perovskite structures. Although no dramatic change could be confirmed depending on the amount of BaTiO₃ added, stable pyroelectricity was maintained near room temperature and over a wide temperature range. When the amount of BaTiO₃ added increased from 0.05BaTiO₃-PMNT to 0.10BaTiO₃-PMNT, the electric field slightly increased from 5.00×10³ kV/m to 6.75×10³ kV/m, and the maximum value of remanent polarization slightly increased from 0.223 C/m² to 0.234 C/m². The pyroelectric coefficients of 0.05BaTiO₃-PMNT and 0.10BaTiO₃- PMNT at room temperature were measured to be ~0.0084 C/m²K and ~0.0043 C/m²K, respectively. The relaxor ferroelectric properties of the BaTiO₃-PMNT system were confirmed by analyzing the plot of K_max/K versus (T-T_max)^γ. The BaTiO₃-doped MPB PMNT system showed a distinct pyroelectric performance index at room temperature, and the values were F_v ~ 0.0362 m²/C, F_d ~ 0.575×10^-4 Pa^-1/2.

• Korean Chemical Engineering Research
• /
• v.50 no.1
• /
• pp.1-5
• /
• 2012

$Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ hollow fiber with o.d. 1.02 mm and i.d. 0.437 mm were fabricated by a phase-inversion spinning technique.The starting $Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ precursor was synthesized by the polymerized complex method and then calcined at $900^{\circ}C$. As-prepared powder was dispersed in a polymer solution, and extruded as form of hollow fiber through a spinneret. Finallydense $Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ hollow fiber membrane was obtained by sintering for 2 h at $1,080^{\circ}C$ for the application of oxygen separation. In addition, despite a very thin membrane with 0.58 mm, the BSCF hollow fiber membrane possessed a proper mechanical strength of 602.5 MPa.

• Journal of the Korean Ceramic Society
• /
• v.37 no.3
• /
• pp.256-262
• /
• 2000

The dielectric properties of complex perovskite ($Pb_{1-x}Ca_{x}$)($Fe_{0.5}Ta_{0.5}$)$O_{3}$ with >($0.5{\le}x{\ge}0.65$ were investigated at microwave frequencies. Dilectric constant decreased with increasing Ca content, and was directly proportional to the cube of average ionic ra야 of A-site. For the specimen of x=0.6 sintered at $1250^{\circ}C$ for 3 h in air, dielectric constant (k) of 63, QF of 11000 GHz, and the temperature coefficient of resonant frequency(TCF) of -14ppm/$^{\circ}C$ were obtained. As Ca content increased, TCF of the specimen negatively increased due to the reduction of the tolerance factor(t). Changes in intrinsic loss with varying Ca content was investigated by the infrared reflectivity spectra ranging 50 to 4000 $cm^{-1}$, which were calculated by the Kramers-Kronig analysis and classical oscillator model. The relative tendency of microwave dielectric properties of the ($Pb_{1-x}Ca_{x}$)($Fe_{0.5}Ta_{0.5}$)$O_{3}$ specimens calculated from the reflectivity data were in good agreement with the results by the post resonant method.