• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.9 no.2
• /
• pp.281-285
• /
• 2008

Die hobbing is one of the dieblock manufacturing methods of cold forging die, which makes the upper side of dieblock indented using master punch, hobb to produce impression not using cutting work. SKD11, alloy tool steel was used as the material of dieblock and stainless sheet metal was used as product material in cold forging work. The life span of the die was 6,000 strokes. In this research, the material of dieblock was changed into SKH51, the high speed tool steel and the product material was S45C, the carbon steel in the cold forging work. The life span of the die was 21,000 strokes, which is 350% of the life span of the die using the former method.

• Proceedings of the KAIS Fall Conference
• /
• 2007.11a
• /
• pp.337-340
• /
• 2007

냉간단조금형(Cold Forging Die)의 다이블록(Dieblock)을 제작하는 방법 중의 하나로, 다이블록 제작용 재료를 면가공 하여 다이블록 상면(上面)을 마스터펀치(Master Punch)인 호브(Hob)로 압입(Indentaion) 시켜 절삭가공((Cutting Work)이 아닌 다이호빙(Die Hobbing) 방법으로 임프레션(Impression)을 성형하여 제작하고 있다. 이 방법에 의하여 다이블록의 재료를 합금공구강(Alloy Tool Steel)인 SKD11을 사용하여 제작하고, 스테인리스판(Stainless Sheet Metal)을 제품 재료로 하여 냉간단조가공(Cold Forging Work)을 하였더니 6,000 스트로크(Stroke)에서 금형수명(Die Life)을 다 하였다. 본 논문에서는 다이블록 재료를 고속도공구강(High Speed Tool Steel)인 SKH51로 교체 제작하고, 탄소강(Carbon Steel)인 S45C를 제품 재료로 하여 냉간단조가공을 수행 하였더니 21,000 스트로크에서 금형수명을 다하고 종료 되어 종래의 방법과 비교 검토 하였을 때 350%의 금형수명 연장 효과를 얻게 되었다.

• Journal of Powder Materials
• /
• v.20 no.4
• /
• pp.291-296
• /
• 2013

SKD11 (ASTM D2) tool steel is a versatile high-carbon, high-chromium, air-hardening tool steel that is characterized by a relatively high attainable hardness and numerous, large, chromium rich alloy carbide in the microstructure. SKD11 tool steel provides an effective combination of wear resistance and toughness, tool performance, price, and a wide variety of product forms. The CNTs was good additives to improve the mechanical properties of metal. In this study, 1, 3 vol% CNTs was dispersed in SKD11 matrix by mechanical alloying. The SKD11+ CNT hybrid nanocomposites were investigated by FE-SEM, particle size distribution, hardness and wear resistance. The CNT was well dispersed in the SKD11 matrix and the mechanical properties of the composite were improved by CNTs addition. It shows good feasibility as cold work die tool.

• Journal of the Korean Society for Heat Treatment
• /
• v.30 no.5
• /
• pp.197-206
• /
• 2017

The microstructure of a high-carbon and high-chromium cast steel (HK700) for cold-work die inserts was analyzed by advanced scanning electron microscopy. A continuous network of primary $M_7C_3$ carbide was developed among austenitic matrix after casting. A small amount of $M_2C$ was added to the carbide network owing to the enrichment of Mo and W during the solidification. After quenching in which the austenitization was performed at $1030^{\circ}C$ and double tempering at $520^{\circ}C$, the network structure of $M_7C_3$ was preserved while most of the matrix was transformed to martensite because of additional carbide precipitation. The $M_2C$ in the as-cast microstructure was also transformed to $M_6C$ due to its instability. The continuous network of coarse carbides owing to the absence of hot-working had little influence on the hardness after quenching and tempering, whereas it resulted in severe brittleness upon flexural loading.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2005.05a
• /
• pp.317-320
• /
• 2005

The micro-alloying forging steels have been developed to save energy consumption during forging and subsequent heat treatment stages. The work hardening ability of micro-alloying forging steels is one of major hardening component while it gives severe die damage if the forging process design is poorly set up on the other hand. In the present study, it was tried to characterize three types of micro-alloying forging steels to understand the differences with the conventional low carbon steels used fur cold forging with a spherodizing heat treatment. After forging of a certain forging part with both micro-alloying forging steels and conventional low carbon steel, several mechanical tests were carried out.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.19 no.3
• /
• pp.877-885
• /
• 1995

Cold forging die for metal scissor is made by electric discharge machine. The impression of female die is made by electric discharge machine, the heat treatment is applied, and the impression is polished. When we forge goods by using this kind of die, the abrasion is severe and the crack occurs after forging about 240 strokes. Because the die should be frequently produced in the case, the cost rises, the work is delayed, and the precesion of goods is not good. Therefore, the electric discharge machine was not used in this study. Main die was produced by making hob, installing the hob to cold hobbing press, indenting the die material, and cold hobbing the impression. The die life was increased to 5,000-6,000 strokes in this case. In the future study, the die life will be increased to 10,000 strokes by changing the following : (1) the pre-treatment of slug, (2) the structure of die block, (3) the heat treatment of die material

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2005.10a
• /
• pp.326-329
• /
• 2005

Since the required strength of forged part is achieved by work hardening with the accumulation of plastic strain during the cold working, severe load can be exerted on die system. So, dies are liable to the early fracture for the non-heat treated steel forging in comparison with the conventional mild steels. Therefore, it is necessary to lower the flow stress of steels as much as possible during forging steps. Bauschinger effect can be utilized to lower flow stress during forging steps by giving the tensile prestrain on the forging billet during wire drawing step. In the present study, the prestrain effect on Bauschinger phenomenon is studied to avoid difficulties with application of non-heat treated cold forging steels in practice.

• Journal of the Korean Society for Precision Engineering
• /
• v.29 no.4
• /
• pp.395-408
• /
• 2012

An experimental investigation with 2.8kW Nd:YAG laser system was carried out to study the effects of different laser process parameters on the microstructure and hardness of STD11. The optical lens with the elliptical profile are designed to obtain a wide surface hardening area with uniform hardness. The Laser beam is allowed to scan on the surface of the work piece varying the power (1600, 1800 and 1900kW) and traverse speed (200, 400, 600, 800 and 1000mm/min) at three different F-numbers of lens. After laser surface treatment three zones, In the microstructure have been observed : melted zone(decarburization), heat affected zone(martensite), and the substrate.

• Journal of the Korean Society for Heat Treatment
• /
• v.31 no.6
• /
• pp.290-299
• /
• 2018

The microstructure of a newly developed alloy tool steel (KV1) for casting cold-work press dies was analyzed using advanced scanning electron microscopy. Its mechanical properties and durability in use as piercing inserts were tested. It contained a continuous network structure which originated from the micro-segregation during solidification and was composed of retained austenite and primary carbides. However, after quenching and tempering, its continuity was destroyed due to the decomposition of austenite. The discontinuous spatial distribution and the smaller amount of primary carbide in the network presented KV1 enhanced ductility compared to the common alloy (HK700). The reduced C and Cr, the addition of V resulted in a small amount of primary carbides which primarily consisted of MC, as well as fine and uniform dispersion of precipitates. Owing to these features, KV1 exhibited delayed initiation of chipping when used for piercing inserts.

• Journal of the Korean Society for Heat Treatment
• /
• v.6 no.2
• /
• pp.59-69
• /
• 1993

Bending fracture strength test and impact strength test were made for VC coated die steels treated by immersing in molten borax bath and for hardened steels which were quenched and tempered, in order to clarify the effect of VC coating at $1000^{\circ}C$. The material used in this investigation was representative cold and hot work die steels STD11, STD61. The results obtained are as follows. 1) The bending fracture strength of VC coated die steel (STD11, STD61) was lessened with increasing the thickness of the VC coated layer. 2) With increasing the immersing time (imcreasing the thickness of the VC coated layer) the maximum hardness was obtained at 480 minutes holding, after that holding time hardness was decreased. 3) The impact strength of the VC coated die steel was not decreased. In the casse of STD11, it was higher than that of the quenched condition especially at low tempering temperature, and vice versa at high tempering temperature. However in the case of STD61 shows the result to the contrary.