• Journal of the Korean Ceramic Society
• /
• v.43 no.7 s.290
• /
• pp.439-444
• /
• 2006

Artificial graphite generally manufactured by carbonization sintering of shape-body of kneaded mixture using granular cokes as filler and pitch as binder, going through pitch impregnation process if necessary and finally applying graphitization heat treatment. Graphite materials are used for core internal structural components of the High-Temperature Gas-cooled Reactors (HTGR) because of their excellent heat resistibility and resistance of crack progress. The HTGR has a core consisting of an array of stacked graphite fuel blocks are machined from IG-110, a high-strength, fine-grained isotropic graphite. In this study, crack stabilization and micro-structures were measured by bend strength and fracture toughness of isotropic graphite grade IG-110. It is important to the reactor designer as they may govern the life of the graphite components and hence the life of the reactor. It was resulted crack propagation, bend strength, compressive strength and micro-structures of IG-110 graphite by scanning electron microscope and universal test machine.

• Transactions on Electrical and Electronic Materials
• /
• v.15 no.2
• /
• pp.81-86
• /
• 2014

The process parameter in optimized KOH alkali activation of soft carbon series coke material in high purity was set with DOE experiments design. The activated carbon was produced by performing the activation process based on the set process parameters. The specific surface area was measured and pore size was analyzed by $N_2$ absorption method for the produced activated carbon. The surface functional group was analyzed by Boehm method and metal impurities were analyzed by XRF method. The specific surface area was increased over 2,000 $m^2/g$ as the mixing ratio of activation agent increased. The micro pores in $5{\sim}15{\AA}$ and surface functional group under 0.4 meq/g were obtained. The contents of the metal impurity in activated carbon which is the factor for reducing the electrochemical characteristics was reduced less than 100 ppm through the cleansing process optimization. The electrochemical characteristics of activated carbon in 38.5 F/g and 26.6 F/cc were checked through the impedance measuring with cyclic voltammetry scan rate in 50~300 mV/s and frequency in 10 mHz ~100 kHz. The activated carbon was made in the optimized activation process conditions of activation time in 40 minutes, mixing ratio of activation agent in 4.5 : 1.0 and heat treatment temperature over $650^{\circ}C$.

• 한국신재생에너지학회:학술대회논문집
• /
• 2011.05a
• /
• pp.111.2-111.2
• /
• 2011

야금학적 방법을 통한 태양전지용 실리콘 제조를 위하여 아크로(Arc furnace)에서 제조된 용융 상태의 금속급 실리콘을 슬래그와 직접 반응시켜 불순물을 제거하는 공정에 관한 연구를 수행하였다. 이를 위해 아크로와 고주파 유도용해로(High-frequency induction furnace)를 이용하여 금속급 실리콘을 제조와 정련 특성 실험을 수행하였다. 본 연구에서 금속급 실리콘을 제조하기 위한 장비로 150kW급-DC 아크로와 300kW급-AC 아크로를 사용하였다. 원재료로 규석, 코크스(Cokes), 숯, 그리고 우드칩(Wood chip)을 실험 비율에 맞춰 아크로 내부에 장입하고, 이를 용융환원 방법을 통해 반응을 시켰다. 이때 생산된 금속급 실리콘의 순도는 약 99.2~99.8% 이었으며, 원재료의 순도, 장입 비율 및 아크로 운전 특성에 따라 편차가 있다. 아크로에서 생산된 금속급 실리콘의 경우 인(phosphorus), 붕소(boron)를 다량 함유하고 있고, 이를 제거하기 위하여 50kW급 고주파 유도용해로 장비를 사용하여 슬래그 정련 실험을 수행하였다. 슬래그 정련시 사용한 성분은 SiO2, CaO 그리고 CaF2 이며, 금속급 실리콘과 슬래그의 질량비 및 반응 시간에 따른 실리콘 불순물 특성을 평가하였다. 실험결과 인과 붕소는 각각 1 ppm 이하, 5 ppm 이하 였으며, 칼슘을 제외한 대부분의 금속 불순물의 경우 0.1~0.2% 임을 확인하였다.

• Applied Chemistry for Engineering
• /
• v.9 no.7
• /
• pp.1065-1069
• /
• 1998

This study was investigated to improve peformance of carbon negative electrode for lithium ion secondary battery. The carbon electrode was prepared by mixing with graphitic carbon material, natural graphite, and nongraphitic carbon material, petroleum cokes, which was heat-treated at $700^{\circ}C$ for l hour. Its electrochemical and charge-discharge characteristics were tested according to mixing ratio of different two types of carbon material. The carbon electrode prepared with various mixing ratio showed both charateristcs of two different types of carbon materials and the best characteristics as carbon electrode was demonstrated at mixing ratio of 1:1.

• Carbon letters
• /
• v.3 no.1
• /
• pp.13-16
• /
• 2002

The modification of coal-tar pitch has been carried out by heat treatment of pitch at different temperatures in the range ($300^{\circ}-400^{\circ}C$) for different times (2-5 hrs) in air and nitrogen. The pitch heat treated in air at lower temperature ($300^{\circ}C$) exhibit increase in softening point by $20^{\circ}C$ as compared to only $2^{\circ}C$ when treated in nitrogen. The changes are faster in air than in pure nitrogen. Pitch as such as well as after heat treatment were further treated with metal complexes by solution route. Silver intake has been found to increase from 0.5 to 0.8 % in nitrogen treated pitch while the uptake is found to decrease for pitches treated in air at $350^{\circ}C$ for 5 hrs. Experiments have also been made to incorporate silver into PAN and PAN-ox fibers through solution route. The metal intake has been found to be more in PAN-ox fibers than in PAN as such. Metal loaded carbon composites have been made by using metal loaded fibers as well as cokes. These composites as such exhibit higher surface oxygen complexes but decrease after activation.

• Carbon letters
• /
• v.10 no.4
• /
• pp.293-299
• /
• 2009

Potassium hydroxide activated carbons were prepared from Egyptian petroleum cokes with different KOH/coke ratios and at different activation temperatures and times. The textural properties were determined by adsorption of nitrogen at $-196^{\circ}C$. The adsorption of iodine and methylene blue was also investigated at $30^{\circ}C$. The surface area and the non-micropore volume increased whereas the micropore volume decreased with the increase of the ratio KOH/coke. Also the surface area and porosity increased with the rise of activation temperature from 500 to $800^{\circ}C$. Textural parameter considerably increased with the increase of activation time from 1 to 3 h. Further increasing of activation time from 3 to 4 h was associated with a less pronounced increase in textural parameters. The adsorption of iodine shows the same trend of surface area and porosity change exhibited by nitrogen adsorption, with KOH/coke ratio and temperature of activation. Adsorption of methylene blue follows pseudo-first-order kinetics and its equilibrium adsorption follows Langmuir and D-R models.

• Journal of computational fluids engineering
• /
• v.21 no.1
• /
• pp.110-116
• /
• 2016

The present study numerically investigated the deformation of the interface of two-phase fluids flow in a blast furnace. To simulate three-dimensional(3D) incompressible viscous two-phase flow in the furnace filled with the air and molten iron, the volume of fluid(VOF) method based on the finite volume method has been utilized. In addition, the porous medium with the porosity has been considered as the bed of the particles such as cokes and char etc. For the comparison, the single phase flow and the two-phase flow without the porosity have been simulated. The two-phase flow without porosity condition revealed the smooth parabolic profile of the free surface near the outlet. However, the free surface under the porosity condition formed the viscous finger when the free surface was close to the outlet. This viscous finger accelerated the velocity of the free surface falling and the outflow velocity of the fluids near the outlet.

• Resources Recycling
• /
• v.17 no.5
• /
• pp.19-27
• /
• 2008

In this study, the porosity and electrical resistivity of the formed coke produced by sintering the mixture of domestic anthracite and phenolic resin were mainly investigated, when the effect of the amount of binder, the hydration temperature and time, the hardening temperature and time, sintering temperature and time, the particle size of anthracite, the grade of anthracite, and the mixing ratio of phenolic resin on the physical properties of the coke were studied. As a result, It was found that the electrical resistivity and porosity of the formed coke are varied in the range of $0.3\sim1.2\Omega{\cdot}cm$ of $10\sim30%$, respectively, in accordance with the variation of factors.

• Proceedings of the Korea Society for Energy Engineering kosee Conference
• /
• 1998.10a
• /
• pp.180-192
• /
• 1998

One of the conventional gas burners has nowadays been used for ladle preheating. As a ladle is one of the open-type furnaces, however, it causes to consume much fuel because of high temperature of exhaust gas from the ladle and the exhaust gas passing through ladle cover makes it worsen a working environment nearby. Therefore, the objective of this study is to develop the recuperative burner system applying for an existing teeming ladle , which is integrated with burner, recuperator and eductor as one of the new type combustion equipments and has many advantages of simple installation, compactness and easy control, especially a great deal of energy saving through the waste heat recovery from exhaust gas. The contents of the study is to design, manufacture of recuperative burner system and to perform its tests experimentally after applying to the teeming ladle in the capacity of 100 ton. Its heat release rate is 1,700,000 kcal/h with COG(Cokes Oven Gas) as fuel gas. The test items are the temperature distribution inside the ladle and the preheated air temperature change depending upon the exhaust gas. Nox, exhaust gas analysis and noise.

• 한국신재생에너지학회:학술대회논문집
• /
• 2011.11a
• /
• pp.54.2-54.2
• /
• 2011

야금학적 정련 공정 중 슬래그 처리, 일방향 응고, 플라즈마-전자기유도용해 공정을 적용한 태양전지용 실리콘 제조 기술에 관한 연구를 수행하였다. 원소재인 금속급 실리콘을 제조하기 위해원재료로 규석, 코크스(Cokes), 숯, 그리고 우드칩(Wood chip)을 사용하였으며, 150kW급 DC 아크로(Arc furnace)를 이용하여 순도 99.8% 금속급 실리콘을 제조하였다. 제조된 용융 상태의 금속급 실리콘은 슬래그와 반응시켜 불순물을 제거하였다. SiO2-CaO-CaF2 계의 슬래그를 이용하였으며, 금속급 실리콘과 슬래그의 질량비 및 반응 시간에 따른 실리콘 불순물 특성을 평가하였다. 이후 고액 계면이 제어 가능한 일방향 응고 장치를 이용하여 금속불순물을 제거하였다. 고액상태의 온도 조건 및 응고 시간에 따른 불순물 농도 변화를 평가하였으며, 순도 6N급의 실리콘을 제조하였다. 마지막 공정으로 스팀 플라즈마 토치와 냉도가니가 적용된 전자기 유도 용해장치를 이용하여 붕소와 인을 제거하였다. 플라즈마 토치 가스로는 아르곤, 스팀, 수소를 이용하였다. 붕소와 인의 제거율은 각각 94%와 96%를 달성하였으며, 최종 순도 6N급의 실리콘을 제조하였다.