• 대한치과보철학회지
• /
• 제38권1호
• /
• pp.38-49
• /
• 2000

The purpose of this study was to evaluate the effects of thermocycling on the shear bond strength of Co-Cr alloy to denture base resin. PMMA denture base resin such as heat-cured $Vertex-RS^{(R)}$, self-cured $Vertex-SC^{(R)}$ and 4-META denture base resin such as heat-cured $Meta-Dent^{(R)}$, self-cured $Meta-Fast^{(R)}$ was bonded to Co-Cr alloy. Samples were divided into 3 groups : no thermocycling group as control, thermocycling between $5^{\circ}C\;and\;55^{\circ}C$ with 15 second dwell time as group 1, thermocycling with 1 minute dwell time as group 2. The shear bond strength was measured and the interface between metal and resin was observed by SEM. The results were as follows. 1. The shear bond strength decreased significantly according to thermocycling and dwell time(P<0.001). 2. The bond strength of Co-Cr alloy and 4-META denture base resin was significantly higher than that of Co-Cr alloy and PMMA denture base resin(P<0.001) 3. In SEM, there was no gap in control group, but there was much and large gap in group 1, 2. The longer dwell times, the lower bond strength. PMMA denture base resin had more gap than 4-META denture base resin in the interface. These results revealed that thermocycling decreased the bond strength between Co-Cr alloy and denture base resin and dwell time of thermocycling changed the effect of thermocycling. The results suggested that oral temperature change affect the bond strength of prosthesis.

• 생체재료학회지
• /
• 제22권4호
• /
• pp.259-270
• /
• 2018

Background: Total hip arthroplasty (THA) is probably one of the most successful surgical interventions performed in medicine. Through the revolution of hip arthroplasty by principles of low friction arthroplasty was introduced by Sir John Charnley in 1960s. Thereafter, new bearing materials, fixation methods, and new designs has been improved. The main concern regarding failure of THA has been the biological response to particulate polyethylene debris generated by conventional metal on polyethylene bearing surfaces leading to osteolysis and aseptic loosening of the prosthesis. To resolve these problems, the materials of the modern THA were developed since then. Methods: A literature search strategy was conducted using various search terms in PUBMED. The highest quality articles that met the inclusion criteria and best answered the topics of focus of this review were selected. Key search terms included 'total hip arthroplasty', 'biomaterials', 'stainless steel', 'cobalt-chromium', 'titanium', 'polyethylene', and 'ceramic'. Results: The initial search retrieved 6921 articles. Thirty-two articles were selected and used in the review. Conclusion: This article introduces biomaterials used in THA and discusses various bearing materials in currentclinical use in THA as well as the newer biomaterials which may even further decrease wear and improve THA survivorship.

• 한국수소및신에너지학회논문집
• /
• 제5권1호
• /
• pp.1-8
• /
• 1994

Lattice structure, hydrogen absorption characteristics, discharge capacity and cycle life of $V_{22}Ti_{16}Zr_{16}Ni_{39}X_7$(X= Cr, Co, Fe, Mn, Al) alloys were investigated. The matrix phases of these alloys were the C14 Laves phase. Chromium-containing alloy had a vanadium-rich phase in addition to the Laves phase. The chromium, maganese, or aluminum-containing alloys had lower hydrogen equilibrium pressure and larger hydrogen absorption content than the cobalt or iron-containing alloys. The discharge capacities of these alloys were 270~330mAh/g. The discharge capacity according to the alloying element X decreased in the order of Mn>Cr>Co, Al)Fe. The charge/discharge cycle lives of the chromium, cobalt or iron-containing alloys were longer than those of maganese or aluminum-containing alloys due to the lower vanadium dissolution rate.

• 대한치과기공학회지
• /
• 제18권1호
• /
• pp.15-25
• /
• 1996

This study is to measure and compare the hardness and tensile strength of each time after we recast seven times continually only with and metal alloy Chromium-Cobalt alloy used in the production of partial denture frame work. The result of the experiment were as follow; 1) The result of the hardness measurement The result of the first casting was $490.48{\pm}38.38$ and that of the second recasting was $455.18{\pm}35.61$ and form the third recasting. the result were $518.38{\pm}37.68$ and over. The change of the hardness difference between each recasting was as follow; The hardness difference between the first casting and the second recasting was $35.25{\pm}31.93$ and that between the second recasting and the third recasting was $63.20{\pm}54.02$. There was a statistically significant difference(P<0.01) in the above hardness, however, there was little difference on the whole. And after the third recasting, the hardness grew high a little bit. That is why low-melting metals such as Cr, Mn, Cu of alloy ingredient was evaporated or there was an effect of changes in metal crystal structure, I suppose. 2) The result of the tensile strength measurement. There was a statistically significant difference(P<0.01) between the first casting and the second, the fourth recasting, however. there was little difference in general.

• 공업화학
• /
• 제17권2호
• /
• pp.150-157
• /
• 2006

최근 들어 크롬대체 도금공정의 필요성이 대두되고 있는 가운데, 크롬도금과 색차가 적고 기계적 특성이 우수하며 환경 친화적인 주석 계 합금도금의 사용이 확대되고 있다. 따라서 본 연구에서는 Sn-Co 합금도금공정을 바탕으로 광택제, 착화제로서 glycine 사용에 대한 연구를 수행하고자 하였다. Sn-Co 합금도금과 glycine 첨가에 따른 물리적 특성 및 표면 광택측정을 위해 Hull-cell 분석 및 도금표면분석을 수행하였다. Hull-cell 분석결과 glycine의 첨가량이 증가함에 따라 광택특성은 우수한 것으로 관찰되었으며, 표면광택성이 가장 우수한 도금조건으로는 $50^{\circ}C$, pH = 8의 조건에서 전전류 공급량 1 A로 1 min간 도금한 경우 음극전류밀도 $1A/dm^2$인 영역을 추천할 수 있었다. 동일조건의 pilot 실험을 $10{\mu}m$ 두께로 Ni하지 도금 후 Sn-Co 합금도금액 기본조성인 0.03 M $SnCl_{2}{\cdot}2H_{2}O$, 0.05 M $CoSO_{4}{\cdot}7H_{2}O$, 0.7 M $K_{4}P_{2}O_{7}$의 혼합 용액에서 수행하 였다. $0.2{\sim}0.6 {\mu}m$의 도금두께를 갖는 Sn-Co 합금도금 표면의 기계적 특성과 도금표면의 성분분석 결과 glycine의 첨가량이 15 g/L일 때 우수한 밀착성, 내식성, 내마모성을 보였다. 따라서 Sn-Co 합금도금공정에 glycine을 첨가한 용액을 크롬도금공정의 최적 도금용액으로 추천할 수 있었다.

• 대한치과보철학회지
• /
• 제43권2호
• /
• pp.218-231
• /
• 2005

Statement of problem. In the partially edentulous patients, removable partial dentures have been working as a important treatment modality. Clasps, a kind of direct retainers, received some amount of stresses during the insertion and removal of partial denture on the abutment tooth. Purpose. The study is to investigate stresses of the different clasps. Material and methods. In order to investigate the degree of stresses, maxillary partial edentulism (Kennedy Class II modification I) was assumed and removable partial dentures were designed on it with three kinds of metallic materials; cobalt-chromium alloy, type IV gold alloy and commercially pure (c.p.) titanium. Aker's clasp was applied on the left second molar. RPA (mesial rest-proximal plate-Aker's) clasp was on the left first premolar and wrought wire clasp was on the right first premolar. Three dimensional, non-linear, dynamic finite element analysis method was run to solve this process. Results. 1. Cobalt-chromium alloy had the highest von Mises stress value and c.p. titanium had the lowest one irrespective of the types of clasps. 2. In the Aker's clasps, stress on the retentive tips was shown shortly after the appearance of stresses of the middle and minor connector areas. These time lag was much shorter in the RPA clasps than in the Aker's clasp. 3. In general. retentive tips of wrought wire clasps had much less amount of stress than other clasps. Conclusion. The amount of stress was the highest in the RPA clasp and the lowest in the wrought wire clasp, in general.

• 대한치과기공학회지
• /
• 제45권4호
• /
• pp.87-94
• /
• 2023

Purpose: This study aimed to observed changes in the shape of dental barrels based on application time. Machinability measures the angle of alloy specimens. Polishing performance measures the surface roughness of alloy specimens. Methods: The dental barrel polishing equipment used in this study was a Snow Barrel (DK Mungyo). Three types of cobalt-chromium alloys for partial dentures were used as specimens (BC CAST R [BP]; Bukwang, Vera PDI [VP]; Aalbadent, and GM 800+ [GP]; Dentaurum). Specimens were prepared in the form of plates (10 mmx10 mmx2 mm). Dental barrel polishing was performed at 450 rpm for 60 minutes with intervals of 5 minutes. The processing angle was measured using a microscope (SZ61; Olympus). Results: For the angle measurement, the VPC specimen was measured at 78.64°, 36.00° for the VP60 specimen, 79.57° for the BP control (BPC) specimen, 28.07° for the BP60 specimen, 75.01° for the GPC specimen, and 39.92° for the GP60 specimen. For the surface roughness measurements, the average surface roughness of the VPC and VP15 specimens were 1.09 ㎛ and 0.26 ㎛, respectively. The average surface roughness of the BPC and BP20 specimens were 1.77 ㎛ and 0.29 ㎛, respectively. The average surface roughness of the GPC and GP15 specimens were 1.08 ㎛ and 0.27 ㎛. Conclusion: The results were excellent after about 20 minutes of dental barrel polishing conditions presented in this study.

• 대한치과보철학회지
• /
• 제38권4호
• /
• pp.510-525
• /
• 2000

The effects of pretreatment of Co-Cr alloy, including two adhesive primers that contain either MDP or MAC-10, and silicoating on the bond The result sobtained as follows; o Strength of 4-META/MMA-TBB resin were investigated using FT-IR, SEM, and EDAX. o In the SEM observation of surface morphologies, the sandblasted specimen exibited a very rough surface, whereas the surfaces of the two groups primed with either MDP or MAC-10 were covered with a layer of primer, and the surface morphology of the silicoated specimen remained almost the same after sandblasting. o Before the thermocycling tests, the group treated with MDP demonstrated the highest mean tensile bond strength and the sandblasted group showed the lowest bond strength. o After 20,000 thermocyling, the mean tensile bond strength of the sandblasted group exhibited a 50% reduction in bond strength, while the others showed a $20\sim30%$ reduction. o Observation of the metal-resin interface revealed that in all groups the resin permeated the rough surface formed by sandblasting thereby producing a mechanical bond between the metal and the resin. It was also found that thermocycling resulted in a gap formation at the metal-resin interface of the specimens, and the sandblasted group exhibited a larger gap width than the other groups. o In fracture mode, all specimens indicated a cohesive fracture within the resin before thermocycling. However, thermocyling produced adhesive failure at the edge of the resin-metal interface in most specimens. The sandblasted group, which exhibited the lowest bond strength after thormocycling, also demonstrated the largest area of adhesive failure.

• 한국재료학회지
• /
• 제10권12호
• /
• pp.831-837
• /
• 2000

고분자전해질형 연료전지에서 촉매의 활성을 증가시키기 위하여 기존에 사용되고 있는 백금과 전이금속인 chromium, nickel과의 합금을 제조하였다. XRD를 이용하여 합금의 구조가 $33^{\circ}$에서 superlattice line을 가지고 있는 것으로 보아 face centered cubic 구조를 가진 ordered alloy로 이루어졌다는 것을 알 수 있었다. 열처리 온도가 증가할수록 합금의 입자 크기는 증가하였으며, 결정 격자 상수는 감소하였다. 전지성능테스트, cyclic voltammogram 등을 통하여 mass activity, specific activity, Tafel slope, 개회로 전압을 측정한 결과, 합금촉매의 활성이 순수한 백금촉매보다 크게 향상되었음을 알 수 있었다.

• 한국방사선학회논문지
• /
• 제17권1호
• /
• pp.25-30
• /
• 2023

의료분야에 3D 프린팅 기술이 활용됨에 따라 금속 재료에 대한 관심이 높아지고 있다. 방사선종양학과에서는 전자선 치료 시 환자의 정상조직에 대한 불필요한 피폭을 차폐하기 위해 차폐블록을 사용하고 있다. 하지만, 납(Lead)과 카드뮴(Cadmium) 같은 중금속 물질의 취급, 숙련도에 따른 재현성과 배치의 불확실성 등에 대한 문제점이 보고되고 있다. 본 연구에서는 금속 3D 프린팅에 사용될 수 있는 재료별 물리적 특성 및 방사선량을 분석하여 전자선 치료 시 활용할 수 있는 맞춤형 차폐블록을 개발하고자 한다. 후보 재료는 알루미늄 합금(d = 2.68 g/cm³), 티타늄 합금(d = 4.42 g/cm³), 코발트 크롬 합금(d = 8.3 g/cm³)을 선별하였다. 10 × 10 cm² 조사면, 6, 9, 12, 16 Me V 에너지로 몬테카를로 시뮬레이션을 이용하여 차폐율 95% 지점의 두께를 도출하였다. 시뮬레이션 결과, 금속 3D 프린팅 재료 중 코발트 크롬 합금(d = 8.35 g/cm³)이 에너지별 차폐두께에서 기존 차폐블록(d = 9.4 g/cm³)과 유사하였다. 향후 금속 3D 프린팅으로 제작한 맞춤형 차폐블록을 이용하여 임상에서의 유용성 검증 평가 및 다양한 방사선 치료계획 조건 등을 통한 실험 검증이 필요할 것으로 사료된다.