• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.4
• /
• pp.308-317
• /
• 2007

We fabricated thermally-evaporated 10 nm-Ni/(poly)Si and 10 nm-$Ni_{0.5}Co_{0.5}$/(Poly)Si structures to investigate the microstructure of nickel silicides at the elevated temperatures required lot annealing. Silicides underwent rapid annealing at the temperatures of $600{\sim}1100^{\circ}C$ for 40 seconds. Silicides suitable for the salicide process formed on top of both the single crystal silicon actives and the polycrystalline silicon gates. A four-point tester was used to investigate the sheet resistances. A transmission electron microscope and an Auger depth profilescope were employed for the determination of vortical microstructure and thickness. Nickel silicides with cobalt on single crystal silicon actives and polycrystalline silicon gates showed low resistance up to $1100^{\circ}C$ and $900^{\circ}C$, respectively, while the conventional nickle monosilicide showed low resistance below $700^{\circ}C$. Through TEM analysis, we confirmed that a uniform, $10{\sim}15 nm$-thick silicide layer formed on the single-crystal silicon substrate for the Co-alloyed case while a non-uniform, agglomerated layer was observed for the conventional nickel silicide. On the polycrystalline silicon substrate, we confirmed that the conventional nickel silicide showed a unique silicon-silicide mixing at the high silicidation temperature of $1000^{\circ}C$. Auger depth profile analysis also supports the presence of this mixed microstructure. Our result implies that our newly proposed NiCo-alloy composite silicide process may widen the thermal process window for the salicide process and be suitable for nano-thick silicides.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.29A no.2
• /
• pp.68-76
• /
• 1992

Concurrent Junction process (simultaneous formation of a silicide and a junction on the implanted substrate) by Rapid Thermal Annealig has been investigated. Electrical and material properties of CoSi$_2$ films were analyzed with Alpha Step, 4-point probe, X-ray diffraction(XRD) and Scanning Electron Microscope(SEM). And CoSi$_2$ junctions were examined with Spreading Resistance probe in order to see the redistribution of electrically activated dopants and determined the junction depth. Two step annealing process, which was 80$0^{\circ}C$ for 30sec and 100$0^{\circ}C$ for 30sec in NS12T ambient was employed to form CoSi$_2$ and shallow junctions. Resistivity of CoSi$_2$ was turned out to be 11-15${\mu}$cm and shallow junctions less than 0.1$\mu$m were successfully formed by the process. It was found that the dopant concentration at CoSi$_2$/Si interface increased as decreasing the thickness of Co films in case of $p^{+}/n$ and $n^{+}/p$ junctions while the junction depth decreased as increasing CoSiS12T thickness in case of $p^{+}/n$ junction.

• Journal of the Korean Ceramic Society
• /
• v.35 no.5
• /
• pp.505-511
• /
• 1998

The silicide formation mechanisms of Co/Hf and Co/Nb bilayer on (100) Si have been investigated. We ob-served that crystallographic orientationso f the 500$^{\circ}C$ formed cobalt silcides were different each other with the varying intermediate layers. Epitaxial and non-epitaxial CoSi2 formed simultaneously in Co/Hf/(100Si. While only non-epitaxial CoSi2 formed in Co/Nb/(100) Si. The reason why the crystallographic orientation of CpSi2 is different for those two systems seemed to be relate to the formation and decomposition of stable reaction barriers at high temperature. The stable reaction barrier formed at high temperature could control the uniform diffusion of Co atoms which enables epitaxial growth of CoSi2.

• Korean Journal of Materials Research
• /
• v.14 no.12
• /
• pp.846-850
• /
• 2004

NiCo silicide films have been fabricated from $300{\AA}-thick\;Ni_{1-x}Co_{x}(x=0.1\sim0.9)$ on Si-substrates by varying RTA(rapid thermal annealing) temperatures from $700^{\circ}C\;to\;1100^{\circ}C$ for 40 sec. Sheet resistance, cross-sectional microstructure, and chemical composition evolution were measured by a four point probe, a transmission electron microscope(TEM), and an Auger depth profilemeter, respectively. For silicides of the all composition and temperatures except for $80\%$ of the Ni composition, we observed small sheet resistance of sub- $7\;{\Omega}/sq.,$ which was stable even at $1100^{\circ}C$. We report that our newly proposed NiCo silicides may obtain sub 50 nm-thick films by tunning the nickel composition and silicidation temperature. New NiCo silicides from NiCo-alloys may be more appropriate for sub-0.1${\mu}m$ CMOS process, compared to conventional single phase or stacked composit silicides.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.18 no.4
• /
• pp.1-7
• /
• 2017

Cobalt silicide was used as a counter electrode in order to confirm its reliability in dye-sensitized solar cell (DSSC) devices. 100 nm-Co/300 nm-Si/quartz was formed by an evaporator and cobalt silicide was formed by vacuum heat treatment at $700^{\circ}C$ for 60 min to form approximately 350 nm-CoSi. This process was followed by etching in $80^{\circ}C$-30% $H_2SO_4$ to remove the cobalt residue on the cobalt silicide surface. Also, for the comparison against Pt, we prepared a 100 nm-Pt/glass counter electrode. Cobalt silicide was used for the counter electrode in order to confirm its reliability in DSSC devices and maintained for 0, 168, 336, 504, 672, and 840 hours at $80^{\circ}C$. The photovoltaic properties of the DSSCs employing cobalt silicide were confirmed by using a simulator and potentiostat. Cyclic-voltammetry, field emission scanning electron microscopy, focused ion beam scanning electron microscopy, and energy dispersive spectrometry analyses were used to confirm the catalytic activity, microstructure, and composition, respectively. The energy conversion efficiency (ECE) as a function of time and ECE of the DSSC with Pt and CoSi counter electrodes were maintained for 504 hours. However, after 672 hours, the ECEs decreased to a half of their initial values. The results of the catalytic activity analysis showed that the catalytic activities of the Pt and CoSi counter electrodes decreased to 64% and 57% of their initial values, respectively(after 840 hours). The microstructure analysis showed that the CoSi layer improved the durability in the electrolyte, but because the stress concentrates on the contact surface between the lower quartz substrate and the CoSi layer, cracks are formed locally and flaking occurs. Thus, deterioration occurs due to the residual stress built up during the silicidation of the CoSi counter electrode, so it is necessary to take measures against these residual stresses, in order to ensure the reliability of the electrode.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.8 no.2
• /
• pp.195-200
• /
• 2007

We fabricated thermally-evaporated 10 nm-Ni/70 w-Poly-Si/200 $nm-SiO_2/Si$ and $10nm-Ni_{0.5}Co_{0.5}/70$ nm-Poly-Si/200 $nm-SiO_2/Si$ structures to investigate the microstructure of nickel monosilicide at the elevated temperatures required fur annealing. Silicides underwent rapid anneal at the temperatures of $600{\sim}1100^{\circ}C$ for 40 seconds. Silicides suitable for the salicide process formed on top of the polycrystalline silicon substrate mimicking the gates. A four-point tester was used to investigate the sheet resistances. A transmission electron microscope and an Auger depth profile scope were employed for the determination of cross sectional microstructure and thickness. 20nm thick nickel cobalt composite silicides on polycrystalline silicon showed low resistance up to $900^{\circ}C$, while the conventional nickle silicide showed low resistance below $900^{\circ}C$. Through TEM analysis, we confirmed that the 70nm-thick nickel cobalt composite silicide showed a unique silicon-silicide mixing at the high silicidation temperature of $1000^{\circ}C$. We identified $Ni_3Si_2,\;CoSi_2$ phase at $700^{\circ}C$ using an X-ray diffractometer. Auger depth profile analysis also supports the presence of this mixed microstructure. Our result implies that our newly proposed NiCo composite silicide from NiCo alloy films process may widen the thermal process window for the salicide process and be suitable for nano-thick silicides.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.6 no.3
• /
• pp.273-277
• /
• 2005

We prepared $0.25\~l.5um$ poly silicon gate array test group with $SiO_2$ spacers in order to employ NiCo composite salicide process from 15nm Ni/15nm Co/poly structure. We investigate the residual metal shape evolution by varying the rapid thermal silicide anneal temperature from $700^{\circ}C\;to\;1100^{\circ}C$. We observed the residual metals agglomerated into maze type and line type on $SiO_2$ field and silicide gate, respectively as temperature increased. We propose that lower silicide temperature would be favorable in newly proposed NiCo salicide in order to lessen the agglomeration causing the leakage and scum formation.

• Journal of the Microelectronics and Packaging Society
• /
• v.12 no.2 s.35
• /
• pp.149-154
• /
• 2005

We fabricated Ni/Co(or Co/Ni) composite silicide layers on the non-patterned wafers from Ni(20 nm)/Co(20 nm)/poly-Si(70 nm) structure by rapid thermal annealing of $700{\~}1100^{\circ}C$ for 40 seconds. The sheet resistance, cross-sectional microstructure, and surface roughness were investigated by a four point probe, a field emission scanning electron microscope, and a scanning probe microscope, respectively. The sheet resistance increased abruptly while thickness decreased as silicidation temperature increased. We propose that the poly silicon inversion due to fast metal diffusion lead to decrease silicide thickness. Our results imply that we should consider the serious inversion and fast transformation in designing and process f3r the nano-height fully cobalt nickel composite silicide gates.