• Journal of Welding and Joining
• /
• v.19 no.5
• /
• pp.512-519
• /
• 2001

Sink roll has been used in molten Zn-0.2%Al alloy bath of continuous galvanizing line in sinking and stabilizing process of the steel strip in molten metal bath. In this process, although the scraper scraps off the sink roll surface, the dross compounds is builded up on the sink roll surface and the life time of the sink roll is shorten by the dross compounds. The present study was investigated the application of the spray coating layer on sink roll body for improving durability In molten Zn-0.2%Al alloy. Through the durability tests in molten Zn-0.2%Al alloy with various ceramic and cermet coating layer, the optimum bond and top coating material was obtained. As the results, the system of STS430F base metal, WC-l7Co bond and $ZrO_2-SiO_2$ top coating was clarified to be the best quality of durability in molten Zn-0.2%Al alloy.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.139-139
• /
• 2010

Rhenium-Iridium(Re-Ir) thin films were deposited onto the tungsten carbide(WC) molding core by sputtering system. The Re-Ir thin films on tungsten carbide molding core were analyzed by scanning electron microscope(SEM) and surface roughness. The Re-Ir coating technique has been intensive efforts in the field of coating process because the coating technique and process have been their feature, like hardness, high elasticity, adrasion resistance and mechanical stability and also have been applied widely the industrial and biomedical areas. In this report, tungsten carbide(WC) molding core was manufactures using high performance precision machining and the efforts of Re-Ir coating on the surface roughness.

• Korean Journal of Air-Conditioning and Refrigeration Engineering
• /
• v.17 no.2
• /
• pp.183-190
• /
• 2005

In the process of ice-slurry making, ice adhesion on cooling wall or in narrow flow Path disturbs continuous ice formation. In this study, the effect on the ice adhesion to cooling surface by some freezing experiments was investigated, quantitatively. Three types of solutions were frozen in various coating vessels with stirring. In the experiment, the ice adhesion between cooling wall and Ice-slurry was evaluated by measuring stirring power. From the result, the stirring power of slurry mixture in PTFE-coating vessel was smaller than those in PE-coating, PFA-coating and bare SUS vessel. Especially, in EG H PG 1.S/ HD 1.5 mass$\%$ solution, the stirring power in the PE-coating vessel was smaller than that in the PFA-coating or SUS vessel.

• Journal of the Korean Ceramic Society
• /
• v.37 no.3
• /
• pp.288-293
• /
• 2000

Effects of contact damage and residual stress for two kinds of dental restorative layered ceramics, porcelain/alumina and porcelain/zirconia bilayers, were observed with Hertzian and Vickers indentation methods. Indentation stress-strain behavior of each material, strength degradation of the coating material, and crack propagation behavior in the coating layer after Vickers indentation were examined by an optical microscope. As a result, porcelain as coating materials showed the classical brittleness. It was inferred that damage and strength in two bilayer system were dependent on thermal expansion mismatch between the coating material and the substrate, which affected the strength degradation. Residual stress resulting from thermal expansion mismtch was formed in the coating layer, and specially in the case of porcelain/zirconia, residual stress was eliminated as coating thickness decreased.

• Journal of the Korean institute of surface engineering
• /
• v.32 no.3
• /
• pp.472-483
• /
• 1999

Hard coatings playa continuously increasing role in the field of tribology as well as for decorative applications. In both areas they are often also exposed to corrosive media. While especially hard nitride coatings show a high corrosion resistance for themselves, hard $coating_strate systems may suffer from a severe corrosion attack due to the defects in the coating structure (pores, pinholes) resulting from the PVD-typical film morphology. While a huge number of investigations cover the tribological properties, only limited studies deal with the corrosion behavjour of coating substrate systems and attempts are made to improve their corrosion resistance. The present paper shortly describes the corrosion mechanisms and repots characteristic examples of the system behaviour. Special emphasis is laid on recent investigations to improve the corrosion resistance by alloying, interlayers or multilayered coating structures.es.

• Journal of the Korean Society for Precision Engineering
• /
• v.30 no.6
• /
• pp.638-643
• /
• 2013

Laser beam machining (LBM) is fast, contactless and able to machine various materials. So it is used to cut metal, drill holes, weld or pattern the imprinted surface. However, after LBM, there still leave burrs and recast layers around the machined area. In order to remove these unwanted parts, LBM process often uses electrochemical etching (ECE). But, the total thickness of workpiece is reduced because the etching process removes not only burrs and recast layers, but also the entire surface. In this paper, surface coating was performed using enamel after LBM on metal. The recast layer can be selectively removed without decreasing total thickness. Comparing with LBM process only, the surface quality of enamel coating process was better than that. And edge shape was also maintained after ECE.

• Transactions on Electrical and Electronic Materials
• /
• v.17 no.3
• /
• pp.178-181
• /
• 2016

In this study a coating experiment was performed to fabricate blue light cut films, which represent a 390~430 nm cut off rate of more than 40% and a transmittance rate of more than 90%, using a roll-to-roll nano micro coating system. The study also analyzed the characteristics of the blue light cut films. Thus, the hardness, which is more than 3H, is ensured through fabricating films using a Sol-Gel process that will determine the proper hardness level. Also, the experiment shows excellent results by cutting blue light through a mixing blue light powder.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.33 no.2
• /
• pp.162-168
• /
• 2009

In this study, disk type of thermal barrier coating system for gas turbine blade was isothermally aged in the furnace changing exposure time and temperature. The aging conditions that delamination occurs were determined by the extensive microscopic analyses and bond tests for each aging condition. The delamination map was drawn from the time-temperature matrix form which summarize the delamination conditions. Finally, a method to draw the delamination life diagram of a thermal barrier coating system by using the delamination map was suggested.

• Journal of Power System Engineering
• /
• v.17 no.6
• /
• pp.108-114
• /
• 2013

This paper describes process optimization for thermal-sprayed Co-based self-flux alloy coating by Taguchi method. Co-based self-flux alloy coatings were fabricated according to $L_9(3^4)$ orthogonal array using flame spray process. Hardness test and wear test were performed, the results were analyzed by analysis of variance(ANOVA) considering a multi response signal to noise ratio(MRSN). From the results of ANOVA, the optimal combination of the flame spray parameters on Co-based self-flux alloy coating could be predicted. The calculated hardness and wear rate of the coatings by ANOVA were found to be close to that of confirmation experimental result.

• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.216-221
• /
• 2008

In this study, disk type of thermal barrier coating system for gas turbine blade was isothermally aged in the furnace changing exposure time and temperature. The aging conditions that determination occurs were determined by the extensive microscopic analyses and bond tests for each aging condition. The delamination map was drawn from the time-temperature matrix form which summarize the delamination conditions. Finally, a method to draw the delamination life diagram of a thermal barrier coating system by using the delamination map was suggested