• Membrane Journal
• /
• v.22 no.4
• /
• pp.272-279
• /
• 2012

The neutral polymer, poly (vinyl alcohol) (PVA), was coated onto polyamide (PA) thin film composite reverse osmosis (RO) membranes. And then these membranes were investigated for the model foulants, bovine serum albumin (BSA), humic acid (HA), and sodium alginate (SA) whether there are aome improvement. As the operating pressure increased with 2, 4, 8 atm for BSA, HA and SA 100 ppm in feed solution, the fouling phenomena was worse for both none and PSSA coated membranes. The fouling occurred in the sequence of BSA > HA > SA due to the interactions between PVA snd functional groups of foulants, and on the other hand the fouling reduction was observed in the order of HA > BSA > SA. The observation of scanning electron microscopy photographs showed the same trend. As a result, there should be the improvement of fouling phenomena for the PVA coated RO membranes and the case of HA was shown distinct.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.189-189
• /
• 2012

Lead sulfide (PbS) nanocrystal quantum dots (NQDs) are promising materials for various optoelectronic devices, especially solar cells, because of their tunability of the optical band-gap controlled by adjusting the diameter of NQDs. PbS is a IV-VI semiconductor enabling infrared-absorption and it can be synthesized using solution process methods. A wide choice of the diameter of PbS NQDs is also a benefit to achieve the quantum confinement regime due to its large Bohr exciton radius (20 nm). To exploit these desirable properties, many research groups have intensively studied to apply for the photovoltaic devices. There are several essential requirements to fabricate the efficient NQDs-based solar cell. First of all, highly confined PbS QDs should be synthesized resulting in a narrow peak with a small full width-half maximum value at the first exciton transition observed in UV-Vis absorbance and photoluminescence spectra. In other words, the size-uniformity of NQDs ought to secure under 5%. Second, PbS NQDs should be assembled carefully in order to enhance the electronic coupling between adjacent NQDs by controlling the inter-QDs distance. Finally, appropriate structure for the photovoltaic device is the key issue to extract the photo-generated carriers from light-absorbing layer in solar cell. In this step, workfunction and Fermi energy difference could be precisely considered for Schottky and hetero junction device, respectively. In this presentation, we introduce the strategy to obtain high performance solar cell fabricated using PbS NQDs below the size of the Bohr radius. The PbS NQDs with various diameters were synthesized using methods established by Hines with a few modifications. PbS NQDs solids were assembled using layer-by-layer spin-coating method. Subsequent ligand-exchange was carried out using 1,2-ethanedithiol (EDT) to reduce inter-NQDs distance. Finally, Schottky junction solar cells were fabricated on ITO-coated glass and 150 nm-thick Al was deposited on the top of PbS NQDs solids as a top electrode using thermal evaporation technique. To evaluate the solar cell performance, current-voltage (I-V) measurement were performed under AM 1.5G solar spectrum at 1 sun intensity. As a result, we could achieve the power conversion efficiency of 3.33% at Schottky junction solar cell. This result indicates that high performance solar cell is successfully fabricated by optimizing the all steps as mentioned above in this work.

• Journal of the Korean Ceramic Society
• /
• v.39 no.3
• /
• pp.315-320
• /
• 2002

Treatment effects of dilute hydrofluoric acid (6 wt% HF) on the surface properties of $Al(OH)_3$ were investigated at the molar ratio of F/Al(fluoride/aluminum)=0.15. Temperature and pH variations in the reaction system were recorded to analyze reaction mechanism between $Al(OH)_3$ and aqueous Hf. The reaction of HF to the surface of $Al(OH)_3$ accompanied with a quantity of heat evolution, resulting in increasing temperature of a reactionsystem. And also the reaction was proceeded as transitional state which metastable ${\alpha}-form\;AlF_3{\cdot}3H_2O$ was transferred to insoluble ${\beta}$-form. The resulting ${\beta}-form\;AlF_3{\cdot}3H_2O$ formed by a surface treatment was identified by FT-IR and X-ray diffractormetry. The formation of ${\beta}$-form aluminum fluoride hydrates with diameter less than $1{\mu}m$ on the surface of $Al(OH)_3$ could be visulaized by SEM imgae, making up a coating layer as precipitate-like. The surface whiteness of $Al(OH)_3$ treated with aqueous HF was furthermore increased approximately 6.6% due to the formation of surface hydrates.

• Polymer(Korea)
• /
• v.34 no.6
• /
• pp.565-573
• /
• 2010

Copoly(2-(dimethylamino)ethyl methacrylate)(DAEMA)/butyl acrylate (BA) and copoly(methyl methacrylate)(MMA)/BA/2-(cinnamoyloxy)ethyl methacryate (CEMA), which were cross-linked with dibromoalkane and UV irradiation, respectively, were prepared for the precursors of interpenetrating polymer network (IPN) humidity-sensitive films. 3-(Triethoxysilyl)propyl cinnamate (TESPC) was used as a surface-pretreating agent for the attachment of IPN-polyelectrolyte to the electrode surface by UV irradiation. Humidity sensitive polymeric thin films with an IPN structure were prepared by crosslinking reactions of copoly(DAEMA/BA) with 1,4-dibromobutane (DBB) and copoly(MMA/BA/CEMA) by UV-irradiation. The anchoring of an IPN-polyelectrolyte into the substrate was carried out via the photochemical $[2{\pi}+2{\pi}]$ cycloaddition. The resulting humidity sensors showed a high sensitivity in the range of 20~95%RH and a small hysteresis (<1.5%RH). The response time for adsorption and desorption process at 33~94%RH was 48 and 65 s, respectively, indicating a fast response. The effects of the concentration of copolymers, molar ratio of crosslinking agents and time of the precursor solution for dip-coating on their humidity sensitive properties including water durability were investigated.

• Applied Chemistry for Engineering
• /
• v.16 no.3
• /
• pp.385-390
• /
• 2005

In this study, nano sized colloidal Ag was made by using a seed sol method. Colloidal Ag solution was spouted on the surface of the inorganic pigment using the hybridizer system and spray nozzle. Then, the surface of the inorganic pigment was modified by $TiO_2$ to obtain the antibacterial ability. In the manufacturing process of nano sized colloidal Ag, it was confirmed that the size of particles increased by addition of $AgNO_3$ and increased the reaction time. The antibacterial measurement of the inorganic pigment showed that the growth of fungus decreased as the reaction time was increased. After the antibacterial ability appeared, in 5~7 h of the antibacterial inoculation experiment, it was measured that the antibacterial activity was excellent at a fixed time frame. The photodecomposition of benzene using $TiO_2$ as the photocatalyst showed 60~70% efficiency in about 80 min. reaction time. It was shown that more than 90% of this efficiency was achieved in the reaction time of about 30 min.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.1
• /
• pp.7-15
• /
• 2004

The ferroelectric SBT thin films as a material of capacitors for non-volatile FRAMs have some problems that its remanent polarization value is relatively low and the crystallization temperature is quite high abovc 80$0^{\circ}C$. Therefore, in this paper, SBTN solution with S $r_{0.9}$B $i_{2.1}$T $a_{1.8}$N $b_{0.2}$$O_{9}$ composition was synthesized by sol-gel method. Sr(O $C_2$ $H_{5}$)$_2$, Bi(TMHD)$_3$, Ta(O $C_2$ $H_{5}$)$_{5}$and Nb(O $C_2$ $H_{5}$)$_{5}$ were used as precursors, which were dissolved in 2-methoxyethanol. SBTN thin films with 200 nm thickness were deposited on Pt/Ti $O_2$/ $SiO_2$/Si substrates by spin-coating. UV-irradiation in a power of 200 W for 10 min and rapid thermal annealing in a 5-Torr-oxygen ambient at 76$0^{\circ}C$ for 60 sec were used to promote crystallization. The films were well crystallized and fine-grained after annealing at $650^{\circ}C$ in oxygen ambient. The electrical characteristics of 2Pr=11.94 $\mu$C/$\textrm{cm}^2$, Ps＋/Pr＋=0.54 at the applied voltage of 5 V were obtained for a 200-nm-thick SBTN films. This results show that 2Pr values of the UV irradiated and rapid thermal annealed SBTN thin films at the applied voltage of 5 V were about 57% higher than those of no additional processed SBTN thin films. thin films.lms.s.s.

• Membrane Journal
• /
• v.15 no.2
• /
• pp.147-156
• /
• 2005

It is well-known that polyethersulfone (PES) has high $CO_2$ selectivity over $N_2\;(or\;CH_4)$ and excellent pressure resistance of $CO_2$ plasticization among muy commercialized engineering plastics[1-4]. Asymmetric PES hollow fiber membranes for flue gas separation were developed by dry-wet spinning technique. The dope solution consists of PES, NMP and acetone. Water and water/NMP mixtures are used in outer and inner coagulants, respectively. Gas permeation rate (i.e., permeance) and $CO_2/N_2$ selectivity were measured with pure gas, respectively and the micro-structure of hollow fiber membranes was characterized by scanning electron microscopy. The effects of polymer concentration, ratio of NMP to acetone, length of air gap, evaporation condition and silicone coating were investigated on the $CO_2/N_2$ separation properties of the hollow fibers. Optimized PES hollow fiber membranes exhibited high permeance of $25\~50$ GPU and $CO_2/N_2$ selectivity of $30\~40$ at room temperature and have the apparent skin layer thickness of about $0.1\;{\mu}m$. The developed PES hollow fiber membranes, would be a good candidate suitable for the flue gas separation process.

• Membrane Journal
• /
• v.6 no.2
• /
• pp.101-108
• /
• 1996

The oxidation/degradation efficiency of formic acid through the photoelectrochemical reaction has been investigated as a basic research in order to develope the process for degrading toxic organic compounds dissolved in water. A $TiO_{2}$ photoelectro-membrane reactor for purification of water, in which filtration as well as photoelectrocatalytic oxidation of organic compounds could be carried out simultaneously, was developed. Porous $SnO_{2}$ tubes prepared by slip casting and commercial porous stainless steel tubes, being electrically conductive, were used as not only supports but also working electrodes. The UV light with the wavelength of 365 nm was applied as a light source for photocatalytic reactions. The photoelectrocatatytic composite membranes were prepared by coating the support surface with the $TiO_{2}$ sol of pH 1.45. The oxidation efficiency of formic acid increased with the reaction time and the applied voltage, but was almost independent of the solution flux. The results showed that more than 90% of formic acid could he dograded at 27V using the $TiO_{2}$/stainless steel composite membrane, while about 77% in case of the $TiO_{2}/SnO_{2}$ Composite membrane. It was also concluded that the oxidation efficiencies of formic acid could be significantly improved by about 6~7 times by the photoelectrochemical reaction in comparison with those by the photocatalytic reaction only.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.19 no.6
• /
• pp.277-281
• /
• 2009

Superhydrophobic $SiO_2$ thin films were successfully fabricated on a glass substrate by sol-gel method. To fabricate $SiO_2$ thin film with a high roughness, $SiO_2$ nano particles were added into tetraethoxysilane (TEOS) solution. The prepared $SiO_2$ thin film without an addition of $SiO_2$ nano particles showed a very flat surface with ca. 1.27 nm of root mean square (RMS) roughness. Otherwise, the $SiO_2$ thin films fabricated by using coating solutions added $SiO_2$ nano particles of 1.0, 2.0 and 3.0 wt% showed a RMS roughness of ca. 44.10 nm, ca. 69.58 nm, ca. 80.66 nm, respectively. To modify the surfaces of $SiO_2$ thin films to hydrophobic surface, a hydrophobic treatment was carried out using a fluoroalkyltrimethoxysilane (FAS). The $SiO_2$ thin films with a high rough surface were changed from hydrophilic to hydrophobic surface after the FAS treatment. Especially, the prepared $SiO_2$ thin film with a RMS roughness of 80.66 nm showed a water contact angle of $163^{\circ}$.

• Journal of the Korean Ceramic Society
• /
• v.42 no.7 s.278
• /
• pp.475-482
• /
• 2005

Zn$_{l-x}$Co$_{x}$O (x = 0.05 - 0.20) films were grown on Coming 7059 glass by sol-gel process. A homogeneous and stable Zn$_{l-x}$Co$_{x}$O sol was prepared by dissolving zinc acetate dihydrate (Zn(CH$_{3}$COO)$_{2}$$\cdot$2H$_{2}$O), cobalt acetate tetrahydrate ((CH$_{3}$)$_{2}$$\cdot$CHOH) and aluminium chloride hexahydrate (AlCl$_{3}$ $\cdot$ 6H$_{2}$O) as solute in solution of isopropanol ((CH$_{3}$)$_{2}$$\cdot$CHOH) and monoethanolamine (MEA:H$_{2}$NCH$_{2}$CH$_{2}$OH). The films grown by spin coating method were postheated in air at 650°C for 1 h and annealed in the condition of vacuum (5 $\times$ 10$^{-6}$ Torr) at 300$^{\circ}C$ for 30 min and investigated the nature of c-axis preferred orientation and physical properties with different Co concentrations. Znl_xCOxO thin films with different Co concentrations were well oriented along the c-axis, but especially a highly c-axis oriented Zn$_{l-x}$Co$_{x}$O thin film was grown at 10 at$\%$ Co concentration. The transmittance spectra showed that Zn$_{l-x}$Co$_{x}$O thin films occur typical d-d transitions and sp-d exchange interaction became activated with increasing Co concentration. The electrical resistivity of the films at 10 at$\%$ Co had the lowest value due to the highest c-axis orientation. X-ray photoelectron spectroscopy and alternating gradient magnetometer analyses indicated that no Co metal cluster was formed, and the ferromagnetic properties appeared, respectively. The characteristics of the electrical resistivity and room temperature ferromagnetism of Zn$_{l-x}$Co$_{x}$O thin films suggested the possibility for the application to dilute magnetic semiconductors.