• Progress in Superconductivity and Cryogenics
• /
• v.9 no.3
• /
• pp.9-12
• /
• 2007

In this study. we searched for the mechanical and electrical properties of laminated coated conductors with stabilizer tape. Stabilizer tape plays a role for mechanical and electrical stability and environmental protection. Cu material stabilizer was laminated to Ag capping layer on SmBCO conductor layer. This architecture allows the wire to meet operational requirements including the stressless at cryogenic temperature and winding tension as well as mechanical bending requirements including thermal and electrical stability under fault current conditions. First, we have experimentally studied mechanical bonding properties of the laminated Cu stabilizers on SmBCO coated conductors. We have laminated SmBCO coated conductors by continuous dipping soldering process, Second, we have investigated electrical properties of the SmBCO coated conductors with stabilizer lamination. We evaluated bonding properties, peeling strength and critical current for laminated SmBCO coated conductors with Cu stabilizers.

• Progress in Superconductivity and Cryogenics
• /
• v.14 no.1
• /
• pp.4-7
• /
• 2012

Coated conductors have been developed to increase piece length and critical current for electric power applications. Otherwise, Many efforts were carried out to reduce AC loss of coated conductor for AC applications. Twisting and cabling processes are effective to reduce AC loss but, these processes can not be applied for tape shaped coated conductor. It is inevitable to have thin rectangular shape because coated conductor is fabricated by thin film deposition process on metal substrate. In this study, round shape superconducting wire was first fabricated using coated conductors. First of all, Ag coated conductor was used. coated conductor was slitted to several wires with narrow width below 1mm. 12ea slitted wires were parallel stacked on top of another until making up the square cross-section. The bundle of coated conductors was heat treated to stick on each other by diffusion bonding and then copper plated to make round shape wire. Critical current of round wire was measured 185A at 77K, self field.

• 한국초전도학회:학술대회논문집
• /
• v.12
• /
• pp.12-12
• /
• 2002

• Transactions on Electrical and Electronic Materials
• /
• v.10 no.2
• /
• pp.62-65
• /
• 2009

YBCO-coated conductors, called "second-generation wires," show a remarkably greater increase in the amount or speed of their resistance than BSCCO wires when a quench occurs. This is probably because of the specific resistance at their stabilizer layer, which also affects their voltage grade. YBCO coated conductors with copper as a stabilizer layer have a voltage grade of 1.5-2 V/cm, and those with stainless steel as a stabilizer layer have a voltage grade of about 0.5-0.6 V/cm. The voltage grade of YBCO coated conductors is important in selecting and applying superconducting wires to power instruments later. In this study, two kinds of YBCO-coated conductors with different stabilizer layers and one kind of BSCCO wire were prepared. Among them, based on the YBCO coated conductors that had a stainless steel stabilizer layer with a low voltage grade, five kinds of experimental samples for joining were prepared with the remaining two kinds of wires. Using the prepared samples, the current application properties and the resistance increase in the flux-flow and the quench states of the single wire and the joined wires were compared.

• Progress in Superconductivity and Cryogenics
• /
• v.8 no.3
• /
• pp.32-36
• /
• 2006

Simplification of the buffer architecture in the fabrication of coated conductors is required because the deposition of multi-layers leads to a longer production time and a higher cost of coated conductors. In this study, a single layered buffer deposition of $CeO_2$ for low cost coated conductors has been tried using thermal evaporation technique. l00nm-thick $CeO_2$ layers deposited by thermal evaporation were found to act as a diffusion layer. $0.4{\mu}m$-thick SmBCO superconducting layers were deposited by thermal co-evaporation on the $CeO_2$ buffered Ni-W substrate. Critical current of $55.4 A/cm^2$ was obtained for the SmBCO coated conductors.

• Progress in Superconductivity and Cryogenics
• /
• v.10 no.1
• /
• pp.10-14
• /
• 2008

Differently from BSCCO tapes which are fabricated by powder-in-tube method, the coated conductors are made by the evaporation of YBCO on metal substrate. Due to this structural merit, although the coated conductors are generally used for large current transportation, they are expected to be favorable to the purpose of the fault current limitation as well. In this study, using YBCO coated conductor having copper stabilizer formed by plating technique(produced by Superpower Co.), we investigated the over-current characteristics of the coated conductor. The coated conductors had 85 A $I_c$ and 90 K $T_c$. The resistance of the conductor was 0.93 $m{\Omega}/cm$ at 300 K and 0.17 $m{\Omega}/cm$ at the temperature right above $T_c$. To the coated conductors, we applied the voltages of the range from 150 $V_{rms}$ to 230 $V_{rms}$ and measured the V-I curves using four probe method. From the results, we could analyze the electric behavior of the coated conductor in flux flow state. As the current exceed $I_c$, the currents were distributed into the superconductor and metal stabilizer. The amounts of the currents shared through both current paths were calculated under the assumption that the ,Joule heating was perfectly eliminated by $LN_2$ surrounding the conductor. Finally, the condition for the stable current flowing state which does not affect the conductor was established from the analysis on the over-current characteristics.

• Transactions on Electrical and Electronic Materials
• /
• v.10 no.2
• /
• pp.66-69
• /
• 2009

To manufacture YBCO-coated conductors as superconducting fault current limiters, it is important to conduct researches on their durability. To test their durability, it is necessary to investigate their properties before and after the quench in more severe conditions than in general operating conditions. In this study, their voltage-current and resistance properties were measured before and after a fault current was repetitively applied to them. For the applied voltage, the voltage grades of the YBCO coated conductors were considered. The current amplitude was controlled using protective resistance on an experimental track, and the time and number of applications were fixed to produce the quench occurrence at the fault angles of $0^{\circ}$, $45^{\circ}$, and $90^{\circ}$. The operating conditions of the YBCO coated conductors as the main components of superconducting fault current limiters were determined using their voltage properties. The voltage properties of the YBCO coated conductors that were analyzed in this research will be used as important data for their practical application to superconducting fault current limiters.

• Progress in Superconductivity and Cryogenics
• /
• v.15 no.4
• /
• pp.1-5
• /
• 2013

This paper reviews recent progress in research and development (R&D) of reactive co-evaporation for high performance REBCO coated conductors in Korea. Two types of reactive co-evaporation methods were developed for the deposition of SmBCO and GdBCO superconducting layers respectively on the IBAD (Ion Beam Assisted Deposition)-MgO template in the Korean coated conductor project. Batch type reactive co-evaporation equipment and its processing were developed for SmBCO coated conductors at Korea Electrotechnology Research Institute (KERI) in conjunction with the Korea Advanced Institute of Science and Technology (KAIST), and a very high critical current exceeding 1,000 A/cm at 77 K in the self field was achieved through the optimization of deposition parameters. Reel-to-reel type reactive co-evaporation processing with a high conversion rate was also developed, while long length GdBCO coated conductors have been routinely produced by SuNAM Co. The minimum critical current of 422 A/cm-w at 77 K in self field was confirmed for 1 km-long GdBCO tape.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.240-241
• /
• 2007

In general, high temperature superconducting coated conductors have intermediary buffers layer consisting of seed, diffusion barrier and cap layers. Simplification of the oxide materials buffer architecture in the fabrication of high temperature superconducting coated conductors is required because the deposition of multi-layers buffer architecture leads to a longer manufacturing time and a higher cost process of coated conductors. Thus, single buffer layer deposition seems to be important for practical coated conductor manufacturing process. In this study, a single gradient layered buffer deposition process of YZO for low cost coated conductors has been tried using DC reactive sputtering technique. About several thick YZO gradient single buffer layers deposited by DC co-sputtering process were found to act as a diffusion layer.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.262-263
• /
• 2005

For mechanical and electrical stability and environment protection, Cu and stainless steel stabilizer is laminated to Ag layer to produce a composite neutral-axis(N-A) architecture in which the YBCO layer is centered between the oxide buffered metallic substrate and stabilizer strip lamination. this architecture allows the wire to meet operational requirements including stresses at cryogenic temperature, winding tensions, mechanical bending requirements thermal and electrical stability under fault conditions. we have experimentally studied mechanical properties of laminated stainless steel stabilizer on YBCO coated conductors. we have laminated YBCO coated conductors by continuous dipping soldering process. we have investigated lamination interface between solder and stabilizer, YBCO coated conductor. we evaluated bonding properties tensile / shear bonding strength, peeling strength laminated YBCO coated conductors.