• Journal of the Korean Ceramic Society
• /
• v.44 no.4 s.299
• /
• pp.214-218
• /
• 2007

The decrease of polarization resistance in cathode is the key point for operating at intermediate temperature SOFC (solid oxide fuel cell). In this study, the influence of Co substitution in B-site at complex perovskite on the electronic conductivity of PSCM ($Pr_{0.3}Sr_{0.7}Co_xMn_{(1-x)}$) was investigated. The PSCM series exhibits excellent MIEC (mixed ionic electronic conductor) properties. The ASR (area specific resistance) of PSCM3773 was $0.174{\Omega}{\cdot}cm^2\;at\;700^{\circ}C$. The activation energy of PSCM3773 was also lower than other compositions of PSCM. The TEC(thermal expansion coefficient) was decreased by addition of Mn. The ASR values were increased gradually during the thermal cycling test of PSCM37773 due to the delamination between electrolyte and cathode materials. The delamination was caused by the difference of TEC.

• Metals and materials international
• /
• v.24 no.6
• /
• pp.1285-1292
• /
• 2018

Microstructural properties of as-grown and annealed CoCrFeMnNi high entropy alloy (HEA) oxynitride thin films were investigated. The CoCrFeMnNi HEA oxynitride thin film was grown by magnetron sputtering method using an air gas, and annealed under the argon plus air flow for 5 h at $800^{\circ}C$. The as-grown film was homogeneous and uniform composed of nanometer-sized crystalline regions mixed with amorphous-like phase. The crystalline phase in the as-grown film was face centered cubic structure with the lattice constant of 0.4242 nm. Significant microstructural changes were observed after the annealing process. First, it was fully recrystallized and grain growth happened. Second, Ni-rich region was observed in nanometer-scale range. Third, phase change happened and it was determined to be $Fe_3O_4$ spinel structure with the lattice constant of 0.8326 nm. Hardness and Young's modulus of the as-grown film were 4.1 and 150.5 GPa, while those were 9.4 and 156.4 GPa for the annealed film, respectively.

• Applied Chemistry for Engineering
• /
• v.10 no.3
• /
• pp.407-414
• /
• 1999

We have studied the reduction of NO by CO over perovskite-type oxides prepared by malic and method. The catalysts were modified to enhance the activity by substitution of metal into A or B site of perovskite oxides. In the $LaCoO_3$ type catalyst, the partial substitution of Sr into A site enhanced the catalytic activity on the conversion of NO at less than $350^{\circ}C$. In the $La_{0.6}Sr_{0.4}Co_{1-x}Fe_xO_3$ catalyst, the partial substitution of Fe or Mn into B site enhanced the conversion of NO, but excess amount of Fe decreased the conversion of NO. In addition, $La_{0.6}Sr_{0.4}Co_{0.8}Fe_{0.2}O_3$ mixed with $SnO_2$ or $MnO_2$ showed the synergy effect on the reduction of NO. The introduction of water into reactants feed decreased the catalytic activity but the deactivation was shown to be reversible. The introduction of $SO_2$ into reactants feed also decreased the catalytic activity.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.25 no.5
• /
• pp.225-229
• /
• 2015

This study was performed to investigate crystal structure of cubic spinel-type monophase oxide composed of the Mn-Co-Ni ternary system. Starting material was prepared by mixing Mn, Co, Ni oxides then evaporation to dryness. The XRD patterns were analyzed by in-situ XRD as increasing temperature from room temperature to $1400^{\circ}C$ in air atmosphere. The cubic spinel phase was existed in a temperature range from $900^{\circ}C$. However, separation of NiO phase was detected from $1300^{\circ}C$, which was the origin of deterioration in the crytallinity. The surface morphology of the manufactured NTC thermistors were analyzed by FE-SEM for comparison of good and bad samples.

• Journal of the Korean Magnetics Society
• /
• v.25 no.5
• /
• pp.144-148
• /
• 2015

We grew spinel structured $CoMn_2O_4$ thin films and have studied post-growth annealing effects on their physical properties. After post-growth annealing at $700^{\circ}C$ that is lower than the growth temperature ($720^{\circ}C$), crystal structure became cleared accompanying a change of surface structure. In the temperature dependences of magnetization, phase transitions were observed at ~100 K for both before and after post-growth treated samples which were not observed for the bulk. For both samples, ferromagnetic behaviors were observed above 100 K while it turned to ferrimagnetism at low temperature below 100 K. In particular, the ferrimagnetic behavior became strong after the post-growth treatment. These results indicate that the post-growth annealing process plays an important role in determining the physical properties of spinel $CoMn_2O_4$ thin film.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.801-804
• /
• 2002

Electrochemical capacitors are becoming attractive energy storage systems particularly for applications involving high power requirements such as hybrid systems consisting of batteries and electrochemical capacitors for electric vehicle propulsion. Both of amorphous cobalt oxide and manganese dioxide were prepared by sol-gel process reported in our previous work. Nanostructured supramolecular oligomer of 1,5-diaminoanthraquinone(DAAQ) coated metal oxides were successfully prepared by electrochemical oxidation from an acidic non-aqueous medium. We established process parameters of the technique for the formation of nano-structured materials. Furthermore, improved the capacitive properties of the nano structured metal oxide electrodes using controlled solution chemistry. $CoO_2$ and $MnO_2$-based composite electrode showed relatively good electrochemical behaviors in acidic electrolyte system with respect to specific capacity and scan rate dependency.

• Resources Recycling
• /
• v.11 no.5
• /
• pp.21-23
• /
• 2002

A new process based on the co-precipitation method was developed fer removing harmful impurities during Mn-Zn ferrite production such as $SiO_2$ and P from waste pickle liquor. By this process a final result of less than 100 ppm of $SiO_2$ and less than 10 ppm of P content in the ferric oxide is easily attained. Though Ca cannot be removed by this process, water rinsing of the ferric oxide is effective fer reducing Ca content to less than 100 pm. For further purification, the origins of each impurity must be investigated and then taken away.

• Journal of Electrochemical Science and Technology
• /
• v.12 no.4
• /
• pp.377-386
• /
• 2021

The Li-rich oxides are promising cathode materials due to their high energy density. However, characteristics such as low rate capability, unstable cyclic performance, and rapid capacity fading during cycling prevent their commercialization. These characteristics are mainly attributed to the phase instability of the host structure and undesirable side reactions at the cathode/electrolyte interface. To suppress the phase transition during cycling and interfacial side reactions with the reactive electrolyte, K (potassium) doping and Nb oxide coating were simultaneously introduced to a Li-rich oxide (Li_1.2Ni_0.13Co_0.13Mn_0.54O₂). The capacity and rate capability of the Li-rich oxide were significantly enhanced by K doping. Considering the X-ray diffraction (XRD) analysis, the interslab thickness of LiO₂ increased and cation mixing decreased due to K doping, which facilitated Li migration during cycling and resulted in enhanced capacity and rate capability. The K-doped Li-rich oxide also exhibited considerably improved cyclic performance, probably because the large K⁺ ions disturb the migration of the transition metals causing the phase transition and act as a pillar stabilizing the host structure during cycling. The Nb oxide coating also considerably enhanced the capacity and rate capability of the samples, indicating that the undesirable interfacial layer formed from the side reaction was a major resistance factor that reduced the capacity of the cathode. This result confirms that the introduction of K doping and Nb oxide coating is an effective approach to enhance the electrochemical performance of Li-rich oxides.

• Journal of the Korean Magnetics Society
• /
• v.14 no.6
• /
• pp.236-239
• /
• 2004

We studied the specular spin valve (SSV) having the spin filter layer (SFL) in contact with the ultrathin free layer composed of Ta3/NiFe2/IrMn7/CoFel/(NOLl)/CoFe2/Cu1.8/CoFe( $t_{F}$)/Cu( $t_{SF}$ )/(NOL2)/Ta3.5 (in nm) by the magnetron sputtering system. For this antiferromagnetic I $r_{22}$M $n_{78}$-pinned spin filter specular spin valve (SFSSV) films, an optimal magnetoresistance (MR) ratio of 11.9% was obtained when both the free layer thickness ( $t_{F}$) and the SFL thickness ( $t_{SF}$ ) were 1.5 nm, and the MR ratio higher than 11% was maintained even when the $t_{F}$ was reduced to 1.0 nm. It was due to increase of specular electron by the nano-oxide layer (NOL) and of current shunting through the SFL. Moreover, the interlayer coupling field ( $H_{int}$) between free layer and pinned layer could be explained by considering the RKKY and magnetostatic coupling. The coercivity of the free layer ( $H_{cf}$ ) was significantly reduced as compared to the traditional spin valve (TSV), and was remained as low as 4 Oe when the $t_{F}$ varied from 1 nm to 4 urn. It was found that the SFL made it possible to reduce the free layer thickness and enhance the MR ratio without degrading the soft magnetic property of the free layer.

• Journal of Environmental Science International
• /
• v.15 no.4
• /
• pp.333-340
• /
• 2006

A (5 wt.%)Mn-(1 wt.%)$V_{2}O_{5}/TiO_{2}$ catalyst were prepared by co-precipitation method and used for low-temperature selective catalytic reduction (SCR) of $NO_x$ with ammonia in the presence of oxygen. The properties of the catalysts were studied by X-ray diffraction (XRD), temperature programmed reduction (TPR) and scanning electron microscope-energy dispersive X-ray spectroscopy (SEM-EDS). The experimental results showed that (5 wt.%)Mn-(1 wt.%)$V_{2}O_{5}/TiO_{2}$ catalyst yielded 81% NO conversion at temperature as low as $150^{\circ}C$ and a space velocity of $2,400\;h^{-1}$. Crystalline phase of $Mn_{2}O_3$ was present at ${\ge}\;15%$ Mn on $V_{2}O_{5}/TiO_{2}$. XRD confirmed the presence of manganese oxide ($Mn_{2}O_{3}$) at $2{\theta}=32.978^{\circ}(222)$. The XRD patterns presented of (5 wt.%)Mn-(1 wt.%)$V_{2}O_{5}/TiO_{2}$ did not show intense or sharp peaks for manganese oxides and vanadia oxides. The TPR profiles of (5 wt.%)Mn-(1 wt.%)$V_{2}O_{5}/TiO_{2}$ catalyst showed main reduction peat of a maximum at $595^{\circ}C$.