• 대한치과보철학회지
• /
• 제45권2호
• /
• pp.169-181
• /
• 2007

Statement of problem: Titanium is well known as a proper metal for the dental restorations, because it has an excellent biocompatibility, resistance to corrosion, and mechanical property. However, adhesion between titanium and dental porcelains is related to the diffusion of oxygen to the reaction layers formed on cast-titanium surfaces during porcelain firing and those oxidized layers make the adhesion difficult to be formed. Many studies using mechanical, chemical and physical methods to enhance the titanium-ceramic adhesion have been actively performed. Purpose: This study meant to comparatively analyse the adhesion characteristics depending on different titanium surface coatings after coating the casts and wrought titanium surfaces with Au and TiN. Material and method: In this study, the titanium specimens (CP-Ti, Grade 2, Kobe still Co. Japan) were categorized into cast and wrought titanium. The wrought titanium was cast by using the MgO-based investment(Selevest CB, Selec). The cast and wrought titanium were treated with Au coating($ParaOne^{(R)}$., Gold Ion Sputter, Model PS-1200) and TiN coating(ATEC system, Korea) and the ultra low fusing dental porcelain was fused and fired onto the samples. Biaxial flection test was done on the fired samples and the porcelain was separated. The adhesion characteristics of porcelain and titanium after firing and the specimen surfaces before and after the porcelain fracture test were observed with SEM. The atomic percent of Si on all sample surfaces was comparatively analysed by EDS. In addition, the constituents of specimen surface layers after the porcelain fracture and the formed compound were evaluated by X-ray diffraction diagnosis. Result: The results of this study were obtained as follows : 1. The surface characteristics of cast and wrought titanium after surface treatment(Au, TiN, $Al_2O_3$ sandblasting) were similar and each cast and wrought titanium showed similar bonding characteristics. 2. Before and after the biaxial flection test, the highest atomic weight change of Si component was found in $Al_2O_3$ sandblasted wrought titanium(28.6at.% $\rightarrow$ 8.3at.%). On the other hand, the least change was seen in Au-Pd-In alloy(24.5at.% $\rightarrow$ 9.1at.%). 3. Much amount of Si components was uniformly distributed in Au and TiN coated titanium, but less amount of Si's was unevenly dispersed on Al2O3 sandblasting surfaces. 4. In X-ray diffraction diagnosis after porcelain debonding, we could see $Au_2Ti$ compound and TiN coating layers on Au and TiN coated surfaces and $TiO_2$, typical oxide of titanium, on all titanium surfaces. 5. Debonding of porcelain on cast and wrought titanium surface after the biaxial flection is considered as a result of adhesion deterioration between coating layers and titanium surfaces. We found that there are both adhesive failure and cohesive failure at the same time. Conclusion: These results showed that the titanium-ceramic adhesion could be improved by coating cast and wrought titanium surfaces with Au and TiN when making porcelain fused to metal crowns. In order to use porcelain fused to titanium clinically, it is considered that coating technique to enhance the bonding strength between coating kKlayers and titanium surfaces should be developed first.

• 한국의학물리학회지:의학물리
• /
• 제20권2호
• /
• pp.80-87
• /
• 2009

비혈관 스텐트(식도용, 담도용, 대장용, 십이지장용, 기관지용) 재질로 가장 널리 사용되고 있는 Nitinol wire 형상기억합금의 기계적 특성 향상을 위해 초음파 나노표면 개질(UNSM) 기술을 적용하여 Nitinol wire의 상변화와 초탄성 특성 및 표면 잔류응력 등의 변화를 연구하였으며, 탄력에너지와 부식내구성을 통한 스텐트의 수명 연장방법을 연구하고자 하였다. 본 연구에 사용된 Nitinol wire는 ${\phi}1.778$ mm로 UNSM 처리 전후의 표면거칠기 값은 Ra=0.092${\mu}m$와 Ra=0.093${\mu}m$로 비슷 하였지만, 초기시편에서는 미세결함과 인발가공 흔적이 확연히 관찰되었으나, UNSM 후에는 인발가공 흔적과 미세 표면 결함은 사라진 것이 발견되었다. 또한 잔류응력 측정 결과, 초기 시험편에는 +3.65 MPa였으나 UNSM 처리 후에는 -4.09 MPa로 확인되었으며, XRD를 통한 결정구조 분석 결과 $42.28^{\circ}$에서 초기보다 약한 (110) 오스테나이트 피크가 관찰되었으며, 대신 (020), ($1{\overline{1}}1$), 그리고 (021) 피크가 명확히 Martensite (B19' Monoclinic lattices) 구조로 확인되었고, (300)의 R상 (Rhombohedral lattices)에 대한 추가 피크가 미비하게 관찰되었다. 탄성변형에 따른 에너지 흡수력과 하중 제거에 따른 에너지의 회복력인 탄력계수(modulus of resilience) $U_r$은 단위체적당 변형률 에너지로 4.31 $MJ/m^3$에서 5.85 $MJ/m^3$로 증가하였다. 이와 같이 표면결함 제거와 인장응력을 압축응력으로 재편성하는 것만으로도 피로내구성을 크게 향상시킬 수 있다고 사료되며, 생체적합성과 더불어 내부식성, 내마모성 및 내구수명 향상을 실용화할 수 있는 표면개질 장치가 개발된다면, 현재 한국인 사망원인 1위인 순환계 질환(심근경색, 뇌졸중 등)에 사용되는 혈관계통의 스텐트 개발에도 응용개발연구가 가능할 것으로 예상된다.

• 한국자기학회지
• /
• 제27권2호
• /
• pp.41-48
• /
• 2017

$CrPt_3$ 합금은 큰 Kerr 효과를 보여 주는 강한 자기결정 이방성을 가지고 있고 흥미롭게도 훈트 제3법칙을 따르지 않는 것으로 알려져 있다. 본 연구에서는 $CrPt_3$ 합금 박막의 두께의 따른 자성과 자기결정 이방성의 변화를 제일원리계산 방법을 이용하여 연구하였다. 기준 자료로 활용하기 위해 덩치 $CrPt_3$의 다양한 자성 상태, 즉 강자성(FM), A-, C-, G-type 반강자성(A-, C-, G-AF)에 대한 계산을 우선 수행하였는데 덩치 $CrPt_3$은 FM 상태가 안정하였고 이는 실험과 일치하였다. A-, C-, G-AF 상태가 FM 상태일 때 보다 총에너지가 각각 0.517, 0.591, 0.183 eV 만큼 높았고 Cr의 자기모멘트는 FM, A-, C-, G-AF 일 때 각각 2.782, 2.805, 2.794, $2.869_{{\mu}_B}$으로 확인되었다. $CrPt_3$(001) 박막의 표면은 CrPt 표면과 Pt 표면으로 두 종류의 원소 구성을 가질 수 있다. 각각의 표면에 대해 3층에서 9층까지 두께를 변화시켜 가면서 계산을 수행하였다. CrPt 표면의 3층 박막은 덩치와는 다르게 C-AF 상태가 FM 상태에 비해 8 meV 안정하였고 그 보다 두꺼운 5층, 7층, 9층 박막은 덩치처럼 FM 상태가 안정하였다. Pt 표면의 3층 박막은 C-AF 상태가 FM 상태에 비해 37 meV, 5층 박막은 G-AF이 FM 상태에 비해 54 meV 만큼 안정하였고 그 보다 두꺼운 7, 9층 박막은 덩치와 같이 FM 상태가 더 안정하였다.