• Journal of Magnetics
• /
• v.6 no.2
• /
• pp.70-72
• /
• 2001

We have investigated the activation magnetic moment, which characterizes the basic magnetic moment acting as a single magnetic particle during magnetization reversal. The activation magnetic moment was measured from each local area on continuous ferromagnetic thin films, by analyzing the magnetic field dependence of magnetization reversal of the corresponding local area, based on a thermally activated relaxation process. It was found that the activation magnetic moment was nonuniform on a submicrometer scale; the fluctuation increased with increasing the number of layers in Co/Pd multilayers. The distribution could be well described by exp($\delta m^{3/2}$), where $\delta$m is the deviation of the activation magnetic moment from the mean value.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.28A no.10
• /
• pp.840-846
• /
• 1991

In case of the rapid thermal process by halogen lamps, an optical pyrometer is generally used to measure the temperature. It is, however, necessary to measure the temperature by the thermocouple when the process temperature is lower than 700$^{\circ}C$ and the correction of the temperature is required. Contact by the PdAg paste is commonly used out but in this case it is impossible to see the effect of surface states of the substrate, which is critical in the rapid thermal process. In this study, real temperature ramping speed of silicon substrates coveredwith various thin films such as SiO$_2$2, Si$_{3}N_{4}$, dopants, and conductive layers (Ti or Co) was investigated by a mechanical contact of the thermocouple. And the results were compared with the case in which the contact was made by the PdAg paste. Effect of process ambient was also studied. It was found that depending on the surface state, overshoot more than 100$^{\circ}C$ could occur. It was also found that in case of the substrate covered with conductive layers, mechanical contact might render the correct temperature.

• Journal of the Korean Magnetics Society
• /
• v.25 no.1
• /
• pp.1-3
• /
• 2015

We demonstrate here an optical measurement technique to quantify the spin-orbit torques. The magnetization dynamics induced by the spin-orbit torques with a sinusoidal current injection is measured by use of polar magneto-optical Kerr effect. The measured signal is then analyzed based on the Landau-Lifhshitz-Gilbert equation with consideration of the spin-orbit torques. The present measurement technique is applied to Pd/Co/Pt films and then, the longitudinal and transverse components of the spin-orbit torques are successfully quantified. The present optical technique provides an alternative way to quantify the spin-orbit torques.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2001.07a
• /
• pp.92-92
• /
• 2001

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.10
• /
• pp.601-607
• /
• 2016

Piezoelectric thick films of soft $Pb(Zr,Ti)O_3$ (PZT) based commercial material (S55) were fabricated using a conventional tape casting method. Ag-Pd electrodes were printed on the piezoelectric film at room temperature and all 5 layered films with a dimension of $12mm{\times}16mm$ were successfully laminated for a multi-layered piezoelectric ceramic actuator. The laminated specimens were co-fired at $1,100^{\circ}C$ for 1 h. A flat layered and dense microstructure was obtained for the $112{\mu}m$ thick piezoelectric actuator after sintering process. Thereafter, a prototype piezoelectric speaker was fabricated using the multi-layered piezoelectric ceramic actuator which can operate as a bimorph. Its SPL (sound pressure level) characteristic was also evaluated for speaker application. Frequency response revealed that the output SPL with a root mean square voltage of 10 V increased gradually to the highest peak of 87.5 dB for 1.5 kHz and exhibited a relatively stable behavior over the measured frequency range (${\leq}20kHz$) at a distance of 10 cm, implying that the fabricated piezoelectric speaker is potential for speaker applications.

• Journal of the Korean Magnetics Society
• /
• v.2 no.3
• /
• pp.263-267
• /
• 1992

We have developed new techniques to measure the magnetization and coercivity of a uniaxial magnetic material using a torque magnetometer. The magnetization could be measured from the slope of the linear region in a plot of the torque ${\tau}/H$ versus the applied field H, when the direction of the applied field was normal to the uniaxial orientation. While, the coercivity could be obtained by taking the value of applied field where the torque was zero, when the direction of the applied field was $(180+{\delta})$ degrees from the uniaxial orientation. The techniques were applied to determine the magnetizations and coercivities of several Co /Pd multilayer thin films and the results were confirmed to be similar within a 2 % difference to those obtained by a vibrating sample magnetometer.

• Journal of the Korea Institute of Military Science and Technology
• /
• v.7 no.2 s.17
• /
• pp.81-87
• /
• 2004

Semiconductor thick film gas sensors based on tin oxide are fabricated and their gas response characteristics are examined for four simulant gases of chemical warfare agent (CWA)s. The sensing materials are prepared in three different sets. 1) The Pt or Pd $(1,\;2,\;3\;wt.\%)$ as catalyst is impregnated in the base material of $SnO_2$ by impregnation method.2) $Al_2O_3\;(0,\;4,\;12,\;20\;wt.\%),\;In_2O_3\;(1,\;2,\;3\;wt.\%),\;WO_3\;(1,\;2,\;3\;wt.\%),\;TiO_2\;(3,\;5,\;10\;wt.\%)$ or $SiO_2\;(3,\;5,\;10\;wt.\%)$ is added to $SnO_2$ by physical ball milling process. 3) ZnO $(1,\;2,\;3,\;4,\;5\;wt.\%)$ or $ZrO_2\;(1,\;3,\;5\;wt.\%)$ is added to $SnO_2$ by co-precipitation method. Surface morphology, particle size, and specific surface area of fabricated sensing films are performed by the SEM, XRD and BET respectively. Response characteristics are examined for simulant gases with temperature in the range 200 to $400^{\circ}C$, with different gas concentrations. These sensors have high sensitivities more than $50\%$ at 500ppb concentration for test gases and also have shown good repetition tests. Four sensing materials are selected with good sensitivity and stability and are fabricated as a sensor array A sensor array Identities among the four simulant gases through the principal component analysis (PCA). High sensitivity is acquired by using the semiconductor thick film gas sensors and four CWA gases are classified by using a sensor array through PCA.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.9
• /
• pp.581-588
• /
• 2016

Piezoelectric thick films of a soft $Pb(Zr,Ti)O_3$ (PZT) based commercial material were produced by a conventional tape casting method. Thereafter, the interdigitated (IDT) Ag-Pd electrode pattern was printed on the $25{\mu}m$ thick piezoelectric film at room temperature. Co-firing of the 10-layer laminated piezoelectric thick films was conducted at $1,100^{\circ}C$ and $1,150^{\circ}C$ for 1 h, respectively. Piezoelectric cantilever energy harvesters were successfully fabricated using the IDT electrode pattern embedded piezoelectric laminates for 3-3 operation mode. Their energy harvesting characteristics were investigated with an excitation of 120 Hz and 1 g under various resistive loads (ranging from $10k{\Omega}$ to $200k{\Omega}$). A parabolic increase of voltage and a linear decrease of current were shown with an increase of resistive load for all the energy harvesters. In particular, a high output power of 3.64 mW at $100k{\Omega}$ was obtained from the energy harvester (sintered at $1,150^{\circ}C$).