ZnS:Cu,Cl phosphor was coated by solid-gel reaction with $SiO_2$ outside layer. The effect of $Cu^{2+}$-doping concentration has been investigated on the luminescence characteristics of ZnS:Cu,Cl blue-green phosphors for inorganic electro luminescent device. Also, SiO2 coated layers' effect on luminescence characteristics. Evaluation of luminescence characteristics dependent on the synthesis conditions is important to get high-performance phosphors properties. EL and PL properties such as luminescence intensity and chromaticity of ZnS:Cu,Cl phosphors synthesized with different concentration of activator, $Cu^{2+}$, were analysed separately

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2007.11a
• /
• pp.112-113
• /
• 2007

ZnS:Cn,Cl phosphor was coated by solid-gel reaction with $SiO_2$ outside layer. The effect of $Cu^{2+}$ -doping concentration has been investigated on the luminescence characteristics of ZnS:Cn,Cl blue-green phosphors for inorganic electro luminescent device. Also, SiO2 coated layers' effect on luminescence characteristics. Evaluation of luminescence characteristics dependent on the synthesis conditions is important to get high-performance phosphors properties. EL and PL properties such as luminescence intensity and chromaticity of ZnS:Cn,Cl phosphors synthesized with different concentration of activator, $Cu^{2+}$, were analysed separately

• Journal of the Korean Vacuum Society
• /
• v.15 no.5
• /
• pp.541-546
• /
• 2006

In this study we have investigated cathodoluminescence (CL) and structural properties of thin film $ZnGa_2O_4:Mn$ oxide phosphor by using field emission scanning electron microscopy (FESEM), atomic force microscopy (AFM), photoluminescence (PL), and cathodoluminescence. PL emission peaked at 506 nm was observed from the $ZnGa_2O_4:Mn$ phosphor target and it was attributed to the $^4T_1-^6A_1$ transition in $Mn^{2+}$ ion. The color coordinates of the emission were x = 0.09 and y = 0.67. The $ZnGa_2O_4:Mn$ films showed the excitation spectrum peaked at 294 nm by $Mn^{2+}$ ion absorption. It was found that the higher intensity of CL emission at 505 nm appears to result from the denser and closely-packed structure in $ZnGa_2O_4:Mn$ phosphor films deposited at lower pressures. The CL intensity did not show any systematic dependence on film surface roughness.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2005.07b
• /
• pp.1323-1326
• /
• 2005

The photoluminescence, electroluminescence and surface properties of ZnS:Cu,Cl phosphor coated by sol-gel process were studies. Na-silicate was used as precursor coating material. pH of solution and the concentration of Na-silicate are the important conditions to obtain the uniform coating on the phosphors. Also, the electroluminescent devices were made with Na-silicate coated phosphor. The spectroscopic characterization is performed by photospectrometer.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.2
• /
• pp.187-191
• /
• 2005

A ZnGa$_2$O$_4$ phosphor target was synthesized through solid-state reactions at a calcine temperature of 700 $^{\circ}C$ and sintering temperature of 1300 $^{\circ}C$ in order to deposit ZnGa$_2$O$_4$ phosphor thin film at various temperature using rf magnetron sputtering system. A ZnGa$_2$O$_4$ phosphor thin film was deposited on Si(100) substrate and annealed by a rapid thermal processor(RTP) at 700 $^{\circ}C$, for 15 sec. The x-ray diffraction patterns of ZnGa$_2$O$_4$ phosphor target and thin film showed the main peak (311) direction. ZnGa$_2$O$_4$ thin film has better crystalization due to as function of increasing substrate and annealing temperature. The cathodoluminescence(CL) spectrums of ZnGa$_2$O$_4$ phosphor thin film showed the main peak 420 nm wavelength and the maximum intensity at the substrate temperature of 500 $^{\circ}C$ and annealing temperature of 700 $^{\circ}C$, for 15 sec.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07b
• /
• pp.980-983
• /
• 2003

The preparation of ZnS:Mn,Cl phosphor has been carried out by combustion method. Manganese nitrate was decomposed with an organic fuel at $500^{\circ}C$ to give fine sized crystallites in presence of alkali metal halides at a lower temperature than the conventional synthesis. The phosphors thus obtained were then heated at 900 to $1200^{\circ}C$ in an inert atmosphere, for 3hours to get better luminescent properties. The phosphors were prepared at different temperatures and at different doping concentrations of manganese to determine the optimal conditions for synthesizing the phosphors with superior optical properties. Scanning electron microscopy (SEM) investigations have been carried out to observe the particle morphology and the grain size. Powder X-ray diffraction(XRD) was also performed to characterize the phosphors.

• Journal of radiological science and technology
• /
• v.20 no.1
• /
• pp.65-69
• /
• 1997

[ $Mg_2SiO_4(La.Ho)$ ] thermoluminescent phosphor was made by putting the $MgCl_2.6H_2O$ and $SiO_2$ and by doping the rare earth element of $LaCl_3.7H_2O$ and $HoCl_3$. The heating rate is $10^{\circ}C/sec$ for the thermoluminescent phosphor. Two peaks are found in the measured $Mg_2SiO_4(La.Ho)$ Tl glow curve at $152^{\circ}C$ and $205^{\circ}C$ when the heating rate is $5^{\circ}C/sec$. The peak value at $205^{\circ}C$ is the most sensitive to X-ray among the glow peaks. The activation energy of the main peak has been estimated by the peak shape method. The estimated activation energies for Ho and La are $0.52{\sim}1.77\;eV$ respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.8
• /
• pp.671-679
• /
• 2007

[ $SrAl_2O_4:Eu^{2+},\;Dy^{3+}$ ] phosphor was synthesized using the impregnation method, and its photoluminescence and long-afterglow properties were investigated, A mixture of $Sr(NO_3)_2,\;Al(NO_3)_2\;9H_2O,\;EuCl_3\;6H_2O,\;DyCl_3\;6H_2O,\;NdCl_3\;6H_2O$ salts were dissolved in distilled water and impregnating into the polymer precursor. After drying, the impregnated mixture was heat treated at $900-1400^{\circ}C$ for 2h in a $N_2-H_2$ reduction atmosphere. The microstructure and crystal structure of the $SrAl_2O_4:Eu^{2+},\;Dy^{3+}$ powders were examined by scanning electron microscopy and X-ray diffraction, respectively. The photoluminescence spectra showed an excitation band along over wide wavelength of 250-450nm, and a broaden emission with a maxima peak at 360nm. In addition, the spectra also showed a good long after glow that decayed over a 1000sec period after 10 min excitation illumination.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.271-274
• /
• 1999

In this paper, we studied the matrix type Powder AC Electroluminescence using ZnS:Cu,Cl Phosphor. Previously, Powder AC EL was used in Backlighting of LCD. Rescently, organic Thin Film EL was rapidly developed because of high Luminescence and low applied voltage. But Powder AC EL has Superior features that include sheet like flexibility thickness, low weight, self-emission, a wide viewing angle and a fast response time. We tried to change of phosphor thickness and binder mixture rate in order to obtain the good condition of powder AC EL and we obtained the very low breakdown voltage that was just 15V. Till now, we measured the current-voltage(V-I), luminance-voltage(V-L), Luminance-current (L-I), color coordinate (CIE), and phosphor Intensity of variable thickness. In experiment result, the devices has the luminance of 840 cd/$m^2$ and improved color coordinate, x=0.1557, y=0.2145, using a 10kHz drive frequency.