In spray pyrolysis, the effects of the preparation temperature, flow rate of the carrier gas and concentration of the spray solution on characteristics such as the morphology, size, and emission intensity of $Ca_8Mg(SiO_4)_4Cl_2:Eu^{2+}$ phosphor powders under long-wavelength ultraviolet light were investigated. The phosphor powders obtained post-treatment had a range of micron sizes with regular morphologies. However, the composition, crystal structure and photoluminescence intensity of the phosphor powders were affected by the preparation conditions of the precursor powders. The $Ca_8Mg(SiO_4)_4Cl_2:Eu^{2+}$ phosphor powders prepared at temperatures that were lower and higher than $700^{\circ}C$ had low photoluminescence intensities due to deficiencies related to the of Cl component. The phosphor powders with the deficient Cl component had impurity peaks of $Ca_2SiO_4$. The optimum flow rates of the carrier gas in the preparation of the $Ca_8Mg(SiO_4)_4Cl_2:Eu^{2+}$ phosphor powders with high photoluminescence intensities and regular morphologies were between 40 and 60 l/minute. Phosphor powders prepared from a spray solution above 0.5 M had regular morphologies and high photoluminescence intensities.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.04b
• /
• pp.49-52
• /
• 2002

Degradation characteristics of cathodoluminescence (CL) of ZnS:Ag,Cl phosphor were investigated with measurements of CL and photoluminescence (PL). Phosphoric acid treatment was performed to phosphor particles in order to improve CL degradation of phosphor screen that occurred during panel sealing process, and we will discuss mechanisms of degradation and improvement of luminescence mainly with help of AES (auger electron spectroscopy) analysis.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2002.08a
• /
• pp.803-806
• /
• 2002

Flame spray pyrolysis was applied to improve the photoluminescence characteristics of blue-emitting $Sr_5(PO_4)_3Cl:Eu^{2+}$ phosphor particles with high brightness for the application to LED phosphor. $Sr_5(PO_4)_3Cl:Eu^{2+}$ prepared from conventional spray pyrolysis had poor PL intensity than that of commercial products under long-wavelength ultraviolet(UV). $Sr_5(PO_4)_3Cl:Eu^{2+}$ phosphor particles prepared by flame spray pyrolysis had PL intensity as same as that of commercial products under long-wavelength UV. Hollow morphology and porous structure of the particles prepared by the flame spray pyrolysis disappeared after posttreatment. Even though the $Sr_5(PO_4)_3Cl:Eu^{2+}$ phosphor particles prepared by the flame spray pyrolysis had irregular shape, the particles had dense structure and clear surface property.

• Journal of the Korean Ceramic Society
• /
• v.37 no.1
• /
• pp.1-5
• /
• 2000

Cathodoluminescence(CL) properties of ZnO:Zn green phosphor were investigated. ZnO:Zn phosphor was synthesized by varying reducing agents and firing temperatures. ZnS, charcoal and 5% H2 gas mixed with 95% N2 gas(5H2-95N2) were used as the reducing agent and atmosphere. The highest CL intensity of ZnO:Zn phosphor was observed under the condition of 5H2-95N2 atmosphere and firing temperature of 90$0^{\circ}C$ for 1h. Charocal and ZnO as reducing agents in the syntehsis of ZnO:Zn phosphor exhibited about 60% and 40%, respectively, of the CL intensity obtained with 5H2-95N2 atmosphere.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2007.08b
• /
• pp.1537-1538
• /
• 2007

ZnS:Cu,Cl phosphor was synthesized by solid-liquid state reaction with two firing steps. Each stage of the process was carefully monitored so that the final product was comparable to commercially-available phosphor. The effect of $Cu^{2+}-doping$ concentration has been investigated on the luminescence characteristics of ZnS:Cu,Cl blue-green phosphors for inorganic electroluminescent device.

• Journal of the Korean Ceramic Society
• /
• v.39 no.3
• /
• pp.240-244
• /
• 2002

The GdOBr:Ce phosphor were prepared by solid state reaction using starting chemicals of $Gd_2O_3,\;CeO_2\;and\;NH_4Br$. Under 370nm UV excitation, GdOBr:Ce phosphors showed blue emission band with a spectral range of 410∼430nm. The maximum photoluminescence(PL) emission intensity was observed at 2mol% Ce content. In order to look for feasibility of application for low voltage filed emission display, cathodoluminescence(CL) of GdOBr:Ce phosphors were measured. CL emission spectra was found to be in the range of 410∼430nm, which is the same as PL spectra. The phosphors with 1mol% Ce concentration showed the maximum CL emission intensity. For the comparison of degradation property of the prepared phosphors with commercial ones, the electron beam was applied for 10min. From the result, GdOBr:Ce could be used as a blue phosphor for FED.

• Korean Journal of Materials Research
• /
• v.12 no.7
• /
• pp.555-559
• /
• 2002

Blue-emitting $Sr_{10}$($PO$)$_{6}$ $Cl_2$:$Eu^{2+}$ and $_{(Sr,Mg) }$ 10/($PO_4$)$_{6}$ $Cl_2$:$Eu^{2+}$ phosphor particles for application of long-wavelength UV LED were prepared by ultrasonic spray pyrolysis. The luminescence characteristics under long- wave-length ultraviolet of the $Sr_{10}$ ($PO_4$)$_{6}$ $Cl_2$:$Eu^{2+}$ and (Sr,Mg)$_{10}$ ($PO_4$)$_{6}$ $Cl_2$:$^Eu{2+}$ phosphor particles prepared by the spray pyrolysis were compared with that of the commercial product. The PL intensity of the $Sr_{10}$ ($PO_4$)$_{6}$ $Cl_2$:$Eu^{2+}$ particles prepared by the spray pyrolysis was lower than that of the commercial $Sr_{10}$ ($PO_4$)$_{6}$ $Cl_2$:$Eu^{2+}$ particles because prepared $Sr_{10}$ ($PO_4$)$_{6}$ $Cl_2$:$Eu^{2+}$ phosphor particles had porous structure and hollow morphology. However, the PL intensity of the (Sr,Mg)$_{10}$($PO_4$)$_{6}$ $Cl_2$:$Eu^{2+}$ phosphor particles prepared by the spray pyrolysis was 8% higher than that of the commercial one. The high brightness of $(Sr,Mg)_{10}$ ($PO_4$)$_{6}$ $Cl_2$:Eu$^{2+}$ phosphor particles prepared by spray pyrolysis is due to the dense structure and high crystallinity of particles. The TEX>$(Sr,Mg)<_{10}$ ($PO_4$)$_{6}$ /$Cl_2$:$Eu^{ 2+}$ phosphor particles had main emission peak t 448 nm under long- wavelength ultraviolet.

• Korean Chemical Engineering Research
• /
• v.48 no.1
• /
• pp.75-79
• /
• 2010

The precursor powders with thin wall structure were prepared by spray pyrolysis from the spray solution with ethylenediaminetetraacetic acid, citric acid and $NH_4Cl$ flux. The $BaMgAl_{10}O_{17}:Eu$ phosphor powders formed from the spray solution without organic additives and flux material had sizes of $1{\sim}5{\mu}m$ and hollow structure with high thickness at post-treatment temperature of $1,200^{\circ}C$. However, $BaMgAl_{10}O_{17}:Eu$ phosphor powders formed from the spray solution with ethylenediaminetetraacetic acid, citric acid and $NH_4Cl$ flux had fine size and plate-like shape. The mean crystallite sizes of the phosphor powders with fine sizes were 23, 35, and 33 nm when the content of $NH_4Cl$ flux were 0, 6, 35 wt% of phosphor. The photoluminescence intensity of the phosphor powders formed from the spray solution with the optimum amount of $NH_4Cl$ flux as 35 wt% was 215% of that of the phosphor powders formed from the spray solution without flux material.

• Journal of the Microelectronics and Packaging Society
• /
• v.23 no.4
• /
• pp.63-67
• /
• 2016

Divalent europium-activated $Ca_2PO_4Cl$ phosphor powders were prepared by a chemical synthetic method followed by heat treatment in reduced atmosphere, and the crystal structures, morphologies and photoluminescence properties of the powders were investigated by x-ray powder diffraction, scanning electron microscope and spectrometer. The effect of Ca/P mole ratio at the starting materials on the final products was evaluated. The optimized synthesis condition obtained in this study was Ca/P mole ratio of 2.0. The present phosphor materials had higher photoluminescence intensity and better color purity than the commercial blue phosphor powders, $(Ca,Ba,Sr)_{10}(PO_4)_6Cl_2:Eu^{2+}$. The result of excitation spectrum measurement indicated that the excitation efficiency of the synthesized powders was higher for the long-wavelength UV region than that of the commercial phosphor. It was thus concluded that the samples prepared in this study can be successfully applied for the light-emitting devices such as LED excited with long-wavelength UV light sources.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.424-425
• /
• 2006

Zinc sulfide is a well-known host material of phosphor emitting different radiations dependent on different doping impurities of metallic ion. It emits green, blue, orange-yellow or white colors by doping with activators such as copper, silver, manganese and so on. In this study, manganese, copper and chlorine doped ZnS phosphor (ZnS:Mn,Cu,Cl) was synthesized by solid-state reaction method. The optical properties were investigated according to different concentrations of sulfur and activators used during the synthesis process.