• International Journal of Concrete Structures and Materials
• /
• v.6 no.3
• /
• pp.145-153
• /
• 2012

The aim of this study is to explore the possibility of re-cycling a waste material that is now produced in large quantities, while achieving an improvement of the mechanical properties and durability of the mortar. This study examines the mechanical properties and the durability parameters of mortars incorporating plastics bag wastes (PBW) as fine aggregate by substitution of a variable percentage of sand (10, 20, 30 and 40 %). The influence of the PBW on the, compressive and flexural strength, drying shrinkage, fire resistance, sulfuric acid attack and chloride diffusion coefficient of the different mortars, has been investigated and analyzed in comparison to the control mortar. The results showed that the use of PBW enabled to reduce by 18-23 % the compressive strength of mortars containing 10 and 20 % of waste respectively, which remains always close to the reference mortar (made without waste). The replacement of sand by PBW in mortar slows down the penetration of chloride ions, improves the behavior of mortars in acidic medium and improves the sensitivity to cracking. The results of this investigation consolidate the idea of the use of PBW in the field of construction.

• Proceedings of the KSR Conference
• /
• 2007.05a
• /
• pp.1431-1438
• /
• 2007

This paper presents a refined design model for current railroad design code on concrete structures exposed to marine environment. A time-varying diffusion coefficient(D) as well as surface chloride$(C_S)$ and chloride threshold level$(C_{lim})$ are studied. Averaging value of the D with time over exposed duration were used to refined durability design model to consider time dependent characteristic of D. The values for $C_S$ and $C_{lim}$ for the seashore in Korea revised for realistic durability design. The proposed model was verified by the so-called performance-based durability design, which is widely used in recent durability design code. Results show that the current standard specification underestimates durability performances of concrete structures exposed to marine environment, so that the cover depth design using current durability evaluation in the standard specifications is very much conservative. Thus, it is found that proposed durability design models for the railroad design code for railway concrete structures can be used effectively for service life design of concrete structures in marine environment.

• Journal of the Korea Concrete Institute
• /
• v.28 no.5
• /
• pp.601-609
• /
• 2016

Recently, extreme climate change has been occurring globally not only in the simple form of temperature increases but also in a wide range of extreme climatic events, such as abnormal drought conditions and frequent typhoons. In addition, climate change is delaying the construction period of concrete structures, increasing related economic losses. Forcing construction projects for completion without considering climate change is leading to concrete quality deterioration, poor quality constructions, and consequent casualties and property damage. Therefore, to address these problems and provide a countermeasure to climate change, the present study selected wind speed, and sunlight exposure time as the most important curing conditions among the climate factors affecting concrete structures and examined their effects on the curing and durability of concrete structures. In addition, for the analysis of the experimental results, this study proposed a process of performance based evaluation (PBE) of concrete strength and durability using a method of Satisfaction Curve (SC) generation.

• Bulletin of the Korean Chemical Society
• /
• v.25 no.5
• /
• pp.715-720
• /
• 2004

Amineterminated, ethylenediamine core polyamidoamine starburst dendrimers of generation 2 (G2), generation 4 (G4) and generation 6 (G6) have been successfully surface-modified via an amide coupling reaction with 4-ethyl, 4'-(3-propionic) bipyridinium cation and the electrochemical behavior of the resulting dendrimers were investigated in aqueous potassium chloride electrolyte solutions. The 1-[3-(dimethylamino)propyl]-3-ethylcarbodiimide hydrochloride/N-hydroxysuccinimide-mediated reaction resulted in 25-39% end-group functionalization. The water-soluble 4-ethyl, 4'-(3-propylamide) bipyridinium dibromide dendrimers (G2-V2+, G4-V2+ and G6-V2+) were characterized by $^1H$ NMR and UV-Vis spectroscopic methods. The cyclic voltammetric and chronoamperometric experiments were performed to determine the diffusion coefficient and the number of electrons transferred in the process of the first reduction of the viologen-functionalized dendrimers. Adsorption of viologen-functionalized dendrimers at electrode surface was evidenced in the voltammograms. Experimentally determined diffusion coefficients were in good agreement with the values expected from the Stokes-Einstein relation, while the number of electrons transferred concurred with the extent of functionalization determined by $^1H$ NMR and UV-Vis spectra.

• Journal of the Korea Concrete Institute
• /
• v.28 no.2
• /
• pp.157-165
• /
• 2016

It is possible to achieve high strength ranging from 40 MPa to 70 MPa in alkali-activated slag concrete (AASC), and AASC is also known to have a finer pore structure due to its high latent hydraulicity and fineness of slag cement, which makes it difficult for chloride ions to penetrate. Electrophoresis is mostly used to calculate the effective diffusion coefficient of chloride ions, and then to evaluate resistance to salt damage. Few studies have been conducted on the fixation capacity of chloride ions in AASC. For this reason, in this study the chloride fixation within the hardened paste was evaluated according to the type and the amount of alkaline activators. As a result, it was revealed that among the test specimens, the chloride fixation was greatest in the paste containing $Na_2SiO_3$. In addition, it was found that as more activator was added, a higher level of chloride fixation was observed. Through this analysis, it can be concluded that the type and the amount of alkaline activators have a high correlation with the amount of C-S-H produced.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.585-588
• /
• 2008

To predict the service life of reinforced concrete structures exposed to chloride environment, quantitative measures of material properties such as the critical chloride content for corrosion in concrete and the diffusion coefficient of chloride ions of concrete and the surface chloride content of the concrete are essential. However, it should be noted that they are influenced by several factors such as concrete mix proportions, cement type, and environmental conditions, etc. Thus, the purpose of this research is to estimate more actually the critical chloride content for corrosion of the reinforcing steel in concrete by field exposure experiment. For this purpose, the prism concrete test specimens were made for water-cement(W/C) ratios of 31%, 42%, 50%, and 70%, and then the field exposure experiment for them were conducted at Youngduk of the east coast for about 3 years. During the test, corrosion monitoring by half cell potential method was carried out to detect the time to initiation of corrosion for test specimens and its chloride content was evaluated by breaking the concrete test specimens when corrosion of the reinforcing steel in concrete was perceived. It was observed from the test results that the critical chloride content for corrosion of reinforcing steel in concrete would be dependent on W/C ratio and almost irrespective of concrete cover.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.471-474
• /
• 2005

Reliability-based durability model was developed to consider the uncertainty of analysis variables in durability model for harbor concrete structures. The durability analysis program based on Finite Element Method (FEM) was modified adopting the reliability concept to estimate the probability of durability failure. Water-cement ratio in the durability analysis is the most important factor influencing chloride diffusion coefficient, evaporable water, etc. The probability distribution of water-cement ratio was calculated converting standard deviations of compressive strength in Concrete Standard Code to those of water-cement ratio. Based on the Monte Carlo Simulation, the probabilities of penetration depth and durability failure were calculated.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.6 no.1
• /
• pp.205-212
• /
• 2002

The deterioration rate of concrete structures in urban area is accelerated due to rapid urbanization and environmental pollution. Repair materials and methods newly introduced in Korea should be investigated whether they are appropriate for the urban environment in Korea. The creek concrete structures are exposed in severe environmental condition than others. Based on these background in mind, the study is focused on evaluation of performance on repair materials used to rehabilitate creek concrete structures. To evaluate the performance of repair materials, four kinds of repair materials were selected based on polymer emulsion. This experimental study was conducted on fundamental performance such as setting time, compressive strength, bending strength, bonding strength, thermal expansion coefficient, and durability performance such as chloride diffusion, carbonation, chemical attack, and steel corrosion rate. On the basis of this study, the optimal repair material which is proper to the environment condition can be selected and service life of creek concrete structures can be extended. As a result, the life cycle cost can be reduced and the waste of material resources will be cut down.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2019.11a
• /
• pp.147-148
• /
• 2019

Lack of fine aggregate is adversely affecting the quality of concrete. Due to lack of land sand, EZZ sea sand has been used. However, the use of sea sand is also difficult because of the opposition of fishermen. The purpose of this study was to analysis the effect of slag fine aggregate to durability and compressive strength of concrete. The concrete compressive strength and durability were assessed to derive a proper mix ratio of fine aggregate.

• Journal of the Korea Concrete Institute
• /
• v.16 no.4 s.82
• /
• pp.485-492
• /
• 2004

In this study, ASTM C 1202 which is most commonly used for evaluating the penetration resistance into the concrete is reviewed. The test results by ASTM C 1202 showed that the passed charge could be underestimated as the $OH^-$ ion concentration in the concrete is lowered when the concrete is mixed with the admixtures. Therefore, the modified method using the distilled water was proposed in the paper. According to the test results, the modified method is not susceptible to $OH^-$ ion and temperature rise. In addition, the long term emersion test for the concrete mixed with the admixtures in the NaCl solution showed that the chloride diffusion coefficient tested by the modified method have higher correlation compared to the conventional ASTM method.