• Journal of the Korean Ceramic Society
• /
• v.36 no.4
• /
• pp.372-379
• /
• 1999

Hihg-toughened ceria-stabilized tetragonal zirconia ceramics with irregular grain shape and undulated grain boundary was prepared by ceria doping. Irregularity of grain shapes was increased with the amount of doped ceria. But in case of the large amount of doped ceria grain boundary was migrated to the reverse direction of DIGM. Ceria-stabilized zirconia ceramics annealed at 1650$^{\circ}C$ for 2h after twice dippings into cerium nitrate solu-tion of 0.2M and sintering at 1500$^{\circ}C$ for 2h showed the highest grain boundary length with a value of 23.6$\mu\textrm{m}$ Ceria concentration difference between convex and concave sides in irregular grains was observed over 1 mol% but not observed in normal grains, Specimens with normal grain shape showed intergranular fracture mode whereas the specimens with irregular grain shape showed transgranular fracture mode.

• Journal of the Korean Ceramic Society
• /
• v.35 no.12
• /
• pp.1294-1300
• /
• 1998

Yttria-stabilized zirconia ceramics with irregular grain shapes and curved grain boundaries was prepared by ceria doping. The amount of ceria doped into zirconia compacts by a dipping method were at range of 2 to 20 mol% Irregular grain shapes and curved grain boundaries were formed only inspecimens doped with more than 8mol% cerial. Ceria-doped specimens showed large grain size and low sintered density compared with pure yttria-stabilized zirconia which was due to the increase in the contents of stabilizer and cubic phase. The amount of doped ceria was larger on the surface than the inside regions and therefore mi-crostructure and phase on the surface were different from those in the inside regions. Transgranular frac-ture mode was observed ion ceria doped specimens due to irregular large grain sizes.

• Journal of the Korean Ceramic Society
• /
• v.26 no.6
• /
• pp.789-794
• /
• 1989

The high-temperature strength of Ce-TZP was measured at 200, 650 and 100$0^{\circ}C$ by 4-point bending test. And its fracture behavior was observed by SEM. Below $650^{\circ}C$ of the temperature, where monoclinic fraction was almost zero, the decreasing rate of bending strength was relatively slow, but above this temperature, high temperature strength was largely decreased as a result of the decrease of stress-induced transformation of zirconia. The observation of fracture surface bended at 100$0^{\circ}C$ indicated that the fracture mode changed from intergranular-into transgranular-form with regardless of ceria contents.

• Korean Journal of Materials Research
• /
• v.20 no.7
• /
• pp.379-384
• /
• 2010

The usual ceramic process of mixing and milling in state of oxides $ZrO_2$ and $CeO_2$ was adopted in this study in a wet process to manufacture Ce-TZP. $CeO_2$-$ZrO_2$ ceramics containing 8~20 mol% $CeO_2$ were made by heat treatment at $1250\sim1500^{\circ}C$ for 5hr. The maximum dispersion point of every slurry manufactured with a mixture of $ZrO_2$ and $CeO_2$ was neat at pH10. A stable slurry with average particle size of 90 nm can be manufactured when it is dispersed with the use of ammonia water and polycarboxylic acid ammonium. The sintered Ce-TZP ceramics manufactured with the addition of $CeO_2$ in a concentration of less than 10 mol% progressed to the fracture of the specimen due to the existence of a monoclinic phase of more than 30% at room temperature. More than 99% of the tetragonal phase was created for the sintered body with the addition of $CeO_2$ beyond 18 mol%, but the degradation of the mechanical properties on the entire specimen was brought about due to the $CeO_2$ existing in a percentage above 3%. Consequently, the optimal Ce-TZP level combined in the oxide state was identified to be 16 mol% of $CeO_2$ contents.

• The Korean Journal of Ceramics
• /
• v.4 no.2
• /
• pp.103-113
• /
• 1998

By using a gas-tight electrochemical cell, we can perform high-temperature coulometric titration and measure electronic transport properties to determine the elecronic defect structure of metal oxides. This technique reduces the time and expense required for conventional thermogravimetric measurements. The components of the gas-tight coulometric titration cell are an oxygen sensor, Pt/yttria stabilitized zirconia(YSZ)/Pt, and an encapsulated metal oxide sample. Based on cell design, both transport and thermodynamic measurements can be performed over a wide range of oxygen partial pressure ($pO_2=10^{-35}$ to 1 atm). This paper describes the high-temperature gas-tight electrochemical cells used to determine electronic defect structures and transport properties for pure and doped-oxide systems, such as YSZ, doped and pure ceria $(Ca-CeO_2 \;and\; CeO_2)$, copper oxides and copper-oxide-based ceramic superconductors, transition metal oxides, $SrFeCo_{0.5}O_x,\; and \;BaTiO_2$.

• Journal of Powder Materials
• /
• v.21 no.3
• /
• pp.222-228
• /
• 2014

Much research into fuel cells operating at a temperature below $800^{\circ}C$. is being performed. There are significant efforts to replace the yttria-stabilized zirconia electrolyte with a doped ceria electrolyte that has high ionic conductivity even at a lower temperature. Even if the doped ceria electrolyte has high ionic conductivity, it also shows high electronic conductivity in a reducing environment, therefore, when used as a solid electrolyte of a fuel cell, the powergeneration efficiency and mechanical properties of the fuel cell may be degraded. In this study, gadolinium-doped ceria nanopowder with $Al_2O_3$ and $Mn_2O_3$ as a reinforcing and electron trapping agents were synthesized by ultrasonic pyrolysis process. After firing, their microstructure and mechanical and electrical properties were investigated and compared with those of pure gadolinium-doped ceria specimen.

• Journal of the Korean Ceramic Society
• /
• v.32 no.1
• /
• pp.95-105
• /
• 1995

Ceria(CeO2) stabilized zirconia(CeSZ) sol was synthesized with zirconium n-butoxide Zr(OC4H9)4 and cerium nitrate hexahydrate Ce(NO3)3.6H2O as precursors and ethylacetoacetate(EAcAc) as a chelating agent under atmosphere. CeSZ films were deposited on AISI 304 stainless steel using the prepared polymeric sol by dipcoating and the coating characteristics were investigated by XRD, ellipsometry, scratch test and SEM. The CeSZ film began to crystallize from amorphous to tetragonal phase at 40$0^{\circ}C$ and it was not converted into monoclinic phase up to 100$0^{\circ}C$ by the addition of 16mol% CeO2 as a stabilizer which could suppress phase transformation of zirconia. The CeSZ films were prepared by varying the EAcAc contents and the cncentration of CeSZ sol and measured the thickness and refractive index. From these results, it was found that the EAcAc contents and concentration of CeSZ coating sol evidently affect the densification of CeSZ film. The CeSZ film coated with 0.4M CeSZ sol and heat-treated at $600^{\circ}C$ for 10min had thickness of 50nm and 17% porosity. The CeSZ film on 304 stainless steel effectively acted as a protective layer against oxidation up to 80$0^{\circ}C$ and had superior corrosion resistance in 25% H2SO4 solution for 4.5 hrs.

• New & Renewable Energy
• /
• v.5 no.1
• /
• pp.11-17
• /
• 2009

To improve the performance of the anode-supported Solid Oxide Fuel Cell (SOFC) which can be operated at an intermediate temperature, the functional layer (FL) is introduced on a anode substrate. And the scandia-stabilized zirconia (ScSZ) and samaria-doped ceria (SDC) which have higher ionic conductivity and better chemical stability than yttria-stabilized zirconia (YSZ) are used as material for the anode FL with the Ni, The fabrication process of anode-supported single cell with the anode FL was established and the power density of those was evaluated. As a result, the sample with anode FL (Ni-YSZ) has higher power density than normal cell. The single cell which was composed of the FL (Ni-YSZ) and electrolyte (YSZ) showed about $550mW/cm^2$ of the maximum power density at $650^{\circ}C$ and $1430mW/cm^2$ at $750^{\circ}C$ respectively, In case of the single cell using the ScSZ and SDC as anode FL, the performance of samples decreased rapidly and those showed unstable voltage during long-term test. In case of using methane as a fuel, the cell performance with each FL decreased comparing with $H_2$ fuel. In the region of a high current density, there are large concentration polarizations.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.10 no.2
• /
• pp.122-127
• /
• 2000

Microstructural evolutions in ceria-stabilized zirconia (Ce-TZP) and alumina-dispersed Ce-TZP ceramics were investigated as functions of doping and annealing conditions. All of sintered specimens showed the relative density over 99 %. Sintered specimens had linear grain boundaries and normal grain shapes, but ceria-doped specimens had irregular grain shapes and nonlinear grain boundaries due to the diffusion-induced grain boundary migration during annealing at $1650^{\circ}C$ for 2 h. Mean grain boundary length of Ce-TZP with irregular grain shapes was higher than that of normal grain shapes, and was a value of 23pm at the maximum. Alumina particles dispersed in Ce-TZP inhibited the grain growth of zirconia particles. $Al_2O_3$Ce-TZP doped with ceria and annealed at $1650^{\circ}C$ for 2 h showed irregular grain shapes as well as small grain size. Added alumina particles showed the grain growth during sintering or annealing, and they changed the position from grain boundary to inside of the grains during the annealing. The specimens with normal grain shapes showed an intergranular fracture mode, whereas the specimens with irregular grain shapes showed a transgranular fracture mode during the crack propagation.

• Journal of the Korean Ceramic Society
• /
• v.26 no.5
• /
• pp.719-727
• /
• 1989

By using commercial zirconia powder CeO2-ZrO2 ceramics containing 8~16mol% CeO2 was made by heat treatment at 1350~155$0^{\circ}C$ for 1~10hr. The minimum amount of CeO2 for obtaining complete tetragonal phase was 12mol%, and in the tetragonal phase region fracture toughness of Ce-TZP was decreased with increasing CeO2 content and the maximum value was obtained when 12mol% CeO2 was added. The bending strength goes through maximum at 14mol% CeO2. Fracture mode of Ce-TZP transformed from intergranular to transgranular fracture with increasing CeO2 content, so the morphology of fracture surface of 16mol% Ce-TZP was wholly transgranular and this tendency was independent on grain size. The crystal structure of the 12mol% Ce-TZP was monoclinic with fringes along the grain boundaries which are lying in the particular plane from the TEM observation. The chemical composition of the sintered body was homogeneous as a whole and some amorphism or air pocket was observed at the triple junction.