• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• v.50 no.7
• /
• pp.455-463
• /
• 2022

As the need for R&D for high reliability cameras, such as satellite cameras, increases, the reliability of the bonding strength properties between an opto-mechanical structure and an optical component has been secured through specimen tests. However, the widely used specimen shape is not suitable for the application of glass and glass-ceramic material, which is fragile, making it difficult to obtain accurate bonding properties due to stress concentration in glass parts before reaching the bonding strength limit. In this study, the stress distribution characteristics in the shear test condition for various specimen shapes were studied analytically, based on the test results of the glass material's own fracture. Through this, the shape characteristics capable of relieving the stress concentration of the glass part were derived, and the range of the bonding shear strength verifiable by the specimen test was improved.

• The Journal of Korean Academy of Prosthodontics
• /
• v.43 no.5
• /
• pp.599-610
• /
• 2005

Purpose: The success of the bonding between electroformed gold and ceramic is dependent on the surface treatment of the pure gold coping. The purpose of this study was to evaluate the bonding strength between the electroformed gold and ceramic with varying surface treatment. Materials and methods: A total of 32 disks,8 were using conventional ceramometal alloy, 24 were using electroforming technique as recommended by manufacturer, were prepared. 24 electroformed disks were divided 3 groups according to surface treatment, i.e. 50 microns aluminium oxide sandblasting(GES-Sand), gold bonder treatment(GES-Bond) and $Rocatec^{TM}$ system(GES-Rocatec). For control group of conventional alloy 50 microns aluminium oxide treatment was done(V-Supragold). Energy dispersive x-ray analysis and scanning electron microscope image were observed. Using universal testing machine, shear bond strength and bonding failure mode at metal-porcelain interface were measured. Results and Conclusion: The following conclusions were drawn: 1. In the energy dispersive x-ray analysis, the Au was main component in electroformed gold(99.9wt%). After surface treatment, a little amount of $Al_2O_3(2.4wt%)$ were found in GES-Sand, and $SiO_2(4wt%)$ in GES-Bond. In GES-Rocatec, however, a large amount of $SiO_2(17.4wt%)$ were found. 2. In the scanning electron microscopy, similar pattern of surface irregu larities were observed in V-Supragold and GES-Sand. In GES-Bond, surface irregularities were increased and globular ceramic particles were observed. In GES-Rocatec, a large amount of silica particles attached to metal surface with increased surface irregularities were observed. 3. The mean shear bond strength values(MPa) in order were $22.9{\pm}3.7(V-Supragold),\;22.1{\pm}3.8(GES-Bond),\;20.1{\pm}2.8(GES-Rocatec)\;and\;13.0{\pm}1.4(GES-Sand)$. There was no significant difference between V-Supragold, GES-Bond, and GES-Rocatec. (P>0.05) 4. Most bonding failures modes were adhesive type in GES-Sand. However, in V-Supragold, GES-Bond and GES-Rocatec, cohesive and combination failures were commonly observed. From the result, with proper surface treatment method electroformed gold may have enough strength compare to conventional ceramometal alloy.

• The Journal of Korean Academy of Prosthodontics
• /
• v.19 no.1
• /
• pp.61-73
• /
• 1981

The effects of the opaque porcelain firing temperature, the bonding agent and the degassing prior to the opaque firing On the bond strength were investigated by means of the tensile shear stIe$. The diffusional behaviours at the interface of the porcelain and the alloy, and .the microstructures of the ceramic and metal composite were studied for understanding the bonding mechanism. The results obtained in this experiment were summarizd as follow; 1. With no application of bonding agent, the tensile shear strength of the specimen firing at $1840^{\circ}F$ was higher than that of the specimen firing at $1760^{\circ}F$. 2. The highest bond strength was obtained by application of bonding agent without degassing prior to the opaque firing. 3. Application of bonding agent after the degassing showed the lowest bond strength. 4. The greater number of pores were observed at the firing temperature of $1840^{\circ}F$ than that of $1760^{\circ}F$ in the porcelain and the interface respectively.

• The korean journal of orthodontics
• /
• v.46 no.6
• /
• pp.364-371
• /
• 2016

Objective: With the introduction of third-generation light-emitting diodes (LEDs) in dental practice, it is necessary to compare their bracket-bonding effects, safety, and efficacy with those of the second-generation units. Methods: In this study, 80 extracted human premolars were randomly divided into eight groups of 10 samples each. Metal or polycrystalline ceramic brackets were bonded on the teeth using second- or third-generation LED light-curing units (LCUs), according to the manufacturers' instructions. The shear bond strengths were measured using the universal testing machine, and the adhesive remnant index (ARI) was scored by assessing the residual resin on the surfaces of debonded teeth using a scanning electron microscope. In addition, curing times were also measured. Results: The shear bond strengths in all experimental groups were higher than the acceptable clinical shear bond strengths, regardless of the curing unit used. In both LED LCU groups, all ceramic bracket groups showed significantly higher shear bond strengths than did the metal bracket groups except the plasma emulation group which showed no significant difference. When comparing units within the same bracket type, no differences in shear bond strength were observed between the second- and third-generation unit groups. Additionally, no significant differences were observed among the groups for the ARI. Conclusions: The bracket-bonding effects and ARIs of second- and third-generation LED LCUs showed few differences, and most were without statistical significance; however, the curing time was shorter for the second-generation unit.

• Journal of Technologic Dentistry
• /
• v.38 no.2
• /
• pp.69-77
• /
• 2016

Purpose: This study was to evaluate the shear bond strength of ceramic fused to Ni-Cr alloy(Alophaloy) by heat treatment. Methods: The specimens were divided into 5 groups according to heat treatment conditions prior to porcelain application. Eighteen specimens from each group were subjected to the shear load a universal testing machine using a 0.1mm/min cross-head speed and two specimens from each group were observed with SEM and EDX line profile. Results: The observation of the oxide film on the metal surface by SEM photograph showed a coarsening with an increasing degassing hold time. The diffusion of metal oxide was observed farther from the opaque layer in the heat treated specimen than no heat treated specimen. The shear bond strength measured highest to A5(55.23MPa) in the 10min holding group and measured lowest from A1(24.38MPa) in the no heat treated group, and there was a significant difference(p<0.05). Conclusion: The shear bond strength of Ni-Cr alloy improved in the heat treatment compared to the no heat treatment specimen.

• The Journal of Advanced Prosthodontics
• /
• v.8 no.5
• /
• pp.339-344
• /
• 2016

PURPOSE. Pre-surface treatments of coping materials have been recommended to enhance the bonding to the veneering ceramic. Little is known on the effect on shear bond strength, particularly with new coping material. The aim of this study was to investigate the shear bond strength of veneering ceramic to three coping materials: i) metal alloy (MA), ii) zirconia oxide (ZO), and iii) lithium disilicate (LD) after various pre-surface treatments. MATERIALS AND METHODS. Thirty-two (n = 32) discs were prepared for each coping material. Four pre-surface treatments were prepared for each sub-group (n = 8); a) no treatment or control (C), b) sandblast (SB), c) acid etch (AE), and d) sandblast and acid etch (SBAE). Veneering ceramics were applied to all discs. Shear bond strength was measured with a universal testing machine. Data were analyzed with two-way ANOVA and Tukey's multiple comparisons tests. RESULTS. Mean shear bond strengths were obtained for MA ($19.00{\pm}6.39MPa$), ZO ($24.45{\pm}5.14MPa$) and LD ($13.62{\pm}5.12MPa$). There were statistically significant differences in types of coping material and various pre-surface treatments (P<.05). There was a significant correlation between coping materials and pre-surface treatment to the shear bond strength (P<.05). CONCLUSION. Shear bond strength of veneering ceramic to zirconia oxide was higher than metal alloy and lithium disilicate. The highest shear bond strengths were obtained in sandblast and acid etch treatment for zirconia oxide and lithium disilicate groups, and in acid etch treatment for metal alloy group.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.20 no.2
• /
• pp.51-57
• /
• 2021

The quality of the ceramic sintered coating on a metal surface through laser surface treatment is affected by the laser irradiation pattern. Depending on the laser irradiation pattern, the amount of residual stress and heat applied or accumulated on the surface increases or decreases, affecting the thickness attained in the ceramic sintering area. When the heat energy accumulated in the sintering area is high, the ceramic and the metal alloy melt and sufficiently mix to form a homogeneous and thick bonding interface. In this study, the thermal energy accumulation in the region sintered with zirconia was controlled using four types of laser processing patterns. The thickness of the diffusion region is analyzed by laser-induced breakdown spectroscopy of Mg-ZrO2 generated by laser sintering zirconia powder on the magnesium alloy surface. On the basis of the analysis of the Mg and Zr present in the sintered region through LIBS, the effect of the irradiation pattern on the sintering quality is confirmed by comparing and analyzing the heat and mass transfer tendency of the diffusion layer and the degree of diffusion according to the irradiation pattern. The derived diffusion coefficients differed by up to 9.8 times for each laser scanning pattern.

• Journal of Advanced Marine Engineering and Technology
• /
• v.19 no.3
• /
• pp.50-61
• /
• 1995

In recent years, many ceramic researchers have discoved various methods of joining ceramic to metal. However, most of these joining methods are perfomed under vacuum and pressured circumstances. So, when we join ceramic to metal,the proceedings are very complicated and require a very high cost. The purpose of this study is to develop a new joining method of an alumina ceramic to an aluminum metal in air atmosphere. The joining condition, such as copper metallizing, nickel plating, brazing, etc. was investigated through the shear strength test of the trial joint. The results obtained from the above experimenta are summarized as follows : 1) In the case of the $Al_2O_3$/$Al_2O_3$joint, the shear strength of the joint was affected by the various foctor such as kaolin content, copper metallizing thickness, firing temperature, firing time. 2) The better shear strength of the $Al_2O_3$/Al joint was obtained when Ni plating was conducted under higher current density than existing plating condition. 3) The shear strength of the $Al_2O_3$/Al joint increases with the Ni plating thickness is confined to the range of this paper. 4) The shear strength of the thermal-shocked specimen($Al_2O_3$/Al joint) was far more deteriorated than that of the as-bonded specimen.

• The Journal of Advanced Prosthodontics
• /
• v.1 no.3
• /
• pp.129-135
• /
• 2009

STATEMENT OF PROBLEM. Zirconia-based restorations have the common technical complication of delamination, or porcelain chipping, from the zirconia core. Thus the shear bond strength between the zirconia core and the veneering porcelain requires investigation in order to facilitate the material's clinical use. PURPOSE. The purpose of this study was to evaluate the bonding strength of the porcelain veneer to the zirconia core and to other various metal alloys (high noble metal alloy and base metal alloy). MATERIAL AND METHODS. 15 rectangular ($4\times4\times9mm$) specimens each of zirconia (Cercon), base metal alloy (Tillite), high noble metal alloy (Degudent H) were fabricated for the shear bond strength test. The veneering porcelain recommended by the manufacturer for each type of material was fired to the core in thickness of 3mm. After firing, the specimens were embedded in the PTFE mold, placed on a mounting jig, and subjected to shear force in a universal testing machine. Load was applied at a crosshead speed of 0.5mm/min until fracture. The average shear strength (MPa) was analyzed with the oneway ANOVA and the Tukey's test ($\alpha$= .05). The fractured specimens were examined using SEM and EDX to determine the failure pattern. RESULTS. The mean shear strength ($\pm\;SD$) in MPa was 25.43 ($\pm\;3.12$) in the zirconia group, 35.87 ($\pm\;4.23$) in the base metal group, 38.00 ($\pm\;5.23$) in the high noble metal group. The ANOVA showed a significant difference among groups, and the Tukey' s test presented a significant difference between the zirconia group and the metal group. Microscopic examination showed that the failure primarily occurred near the interface with the residual veneering porcelain remaining on the core. CONCLUSION. There was a significant difference between the metal ceramic and zirconia ceramic group in shear bond strength. There was no significant difference between the base metal alloy and the high noble metal alloy.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.30 no.5
• /
• pp.208-213
• /
• 2020

In this research, design optimization was investigated using the finite element analysis and the optimal design technique based on the PQRSM algorithm to minimize the thermal deformation of IGZO oxide in a target module in which IGZO oxide and a copper backplate are bonded to each other. In order to apply the optimal design technique in conjunction with finite element analysis, the x-coordinate of lower supports and upper fixed boards used as design valuables, and the optimal design was performed to minimize the thermal displacement of IGZO materials as the objective function. After the optimization process, the thermal displacement within IGZO oxide could be reduced to 42 % comparing with the initial model. The result is thought to be useful in the industry as it can reduce the thermal deformation of target oxides materials only by changing the position of the subsidiary materials during the bonding process.