• The Journal of Advanced Prosthodontics
• /
• 제4권3호
• /
• pp.162-169
• /
• 2012

PURPOSE. Fracture of the veneering material of zirconia restorations frequently occurs in clinical situations. The purpose of this in vitro study was to compare the fracture strengths of zirconia crowns veneered with various ceramic materials by various techniques. MATERIALS AND METHODS. A 1.2 mm, $360^{\circ}$ chamfer preparation and occlusal reduction of 2 mm were performed on a first mandibular molar, and 45 model dies were fabricated in a titanium alloy by CAD/CAM system. Forty-five zirconia copings were fabricated and divided into three groups. In the first group (LT) zirconia copings were veneered with feldspathic porcelain by the layering technique. In the second group (HT) the glass ceramic was heat-pressed on the zirconia coping, and for the third group (ST) a CAD/CAM-fabricated high-strength anatomically shaped veneering cap was sintered onto the zirconia coping. All crowns were cemented onto their titanium dies with Rely $X^{TM}$ Unicem (3M ESPE) and loaded with a universal testing machine (Instron 5583) until failure. The mean fracture values were compared by an one-way ANOVA and a multiple comparison post-hoc test (${\alpha}$= 0.05). Scanning electron microscope was used to investigate the fractured interface. RESULTS. Mean fracture load and standard deviation was $4263.8{\pm}1110.8$ N for Group LT, $5070.8{\pm}1016.4$ for Group HT and $6242.0{\pm}1759.5$ N for Group ST. The values of Group ST were significantly higher than those of the other groups. CONCLUSION. Zirconia crowns veneered with CAD/CAM generated glass ceramics by the sintering technique are superior to those veneered with feldspathic porcelain by the layering technique or veneered with glass ceramics by the heat-pressing technique in terms of fracture strength.

• 대한치과기공학회지
• /
• 제33권3호
• /
• pp.193-202
• /
• 2011

Purpose: The aim of this study was to evaluate the effect of pre-treatment of core and hydrothermal treatment on the bond strength and flexural strength of ceramic veneered zirconia. Methods: 3Y-TZP specimens(KaVo Zr, $25mm{\times}3mm{\times}1mm$)were prepared by five pre-treatment methods and divided into seven groups including control two groups, subsequently the specimens veneered with the E-MAX ceram according to manufacturer's information(total specimen thickness 1.5mm). Two groups from ceramic-zirconia specimens(n=105, n=15 per group)were assigned into two experimental fatigue conditions, namely storage in an autoclave at $134^{\circ}C$ for 5h, thermo-cycling(3,000cycles, between 5 and $55^{\circ}C$, dwell time 45s, transfer time 2s). A flexural strength test was performed in a universal testing machine(crosshead speed: 0.5mm/min). Data were statistically analyzed using one-way ANOVA and Tukey's test(${\alpha}$=0.05). Results: The ceramic-zirconia bond strength value for liner application group(LLW, $27.3{\pm}3.8$) were significantly lower than those of the pre-treatment groups($30.72{\pm}5.3$). The ceramic-zirconia bond strength and zirconia flexural strength was not affected by thermo-cycling(p>0.05), whereas it was affected by storage in an autoclave at $134^{\circ}C$ for 5h(p<0.05). Conclusion: The results indicated that the ceramic-zirconia bond strength and zirconia flexural strength was affected by low temperature degradation.

• 구강회복응용과학지
• /
• 제24권1호
• /
• pp.113-127
• /
• 2008

이 연구의 목적은 지르코니아 도재 표면의 전단 결합 강도에서 $ZirLiner^{(R)}$와 블라스팅 처리의 적용 효과를 평가하기 위한 것이다. 60개의 무색의 지르코니아 판과 30개의 색이 있는 지르코니아 판이 규격화되고 연마, 글래스블라스팅, 알루미나블라스팅, 그리고 zirliner 같은 블라스팅 처리를 적용시키는 것에 따라 10개씩 9개의 그룹으로 나누어졌다. 시편을 고정대에 위치하고 만능시험기로 전단력을 측정하였다. 파절된 견본의 파절 표면은 SEM으로 검사되었다. 각 군별 시편을 통계처리하여 그 결과를 비교하였다.

• The Journal of Advanced Prosthodontics
• /
• 제11권5호
• /
• pp.297-304
• /
• 2019

PURPOSE. This in vitro study investigated the repair bond strength of the zirconia ceramic after different aging conditions. MATERIALS AND METHODS. In order to imitate the failure modes of veneered zirconia restorations, veneer ceramic, zirconia, and veneer ceramic-zirconia specimens were prepared and were divided into 4 subgroups as: control ($37^{\circ}C$ distilled water for 24 hours ) and 3000, 6000, 12000 thermal cycling groups (n=15). Then, specimens were bonded to composite resin using a porcelain repair kit according to the manufacturer recommendation. The repair bond strength (RBS) test was performed using a universal testing machine (0.5 mm/min). Failure types were analyzed under a stereomicroscope. Two-way ANOVA and Bonferroni test were used for statistical analysis. RESULTS. The RBS values of zirconia specimens were statistically significant and higher than veneer ceramic and veneer ceramic-zirconia specimens in control, 3000 and 6000 thermal cycling groups (P<.05). When 12000 thermal cycles were applied, the highest value was found in zirconia specimens but there was no statistically significant difference between veneer ceramic and veneer ceramic-zirconia specimens (P>.05). Veneer ceramic specimens exhibited cohesive failure types, zirconia specimens exhibited adhesive failure types, and veneer ceramic-zirconia specimens exhibited predominately mixed failure types. CONCLUSION. Thermal cycling can adversely affect RBS of composite resin binded to level of fractured zirconia ceramics.

• 대한치과기공학회지
• /
• 제31권2호
• /
• pp.45-52
• /
• 2009

Esthetic restorations have been widely used in dental practice, although many studies have focused on the development and improvement of all ceramic restorations. The success of esthetic restorations depends primarily on an optimal bond strength between various veneered ceramics and core materials for esthetic restorations. The purpose of this study was to compare the shear bond strength between various veneered ceramics and core materials for esthetic restorations. 30 metal cores and 20 zirconia cores were fabricated and divided into five groups according to veneered ceramic materials such as Creation porcelain powder, Cercon Ceram Kiss, and IPS e.max ZirPress. Thirty spacimens were prepared using Creation porcelain powder, veneered 3mm height and 3mm in diameter, over the metal cores (n=10). Twenty specimens were prepared using Cercon Ceram Kiss and Zirpress, veneered 3mm height and 3mm in diameter, over the zirconia cores (n=10). The shear bond strength test was performed in a universal testing machine with a crosshead speed of 1mm/min. Ultimate shear bond strength data were analyzed with One-way ANOVA and the Scheffe's test (p=.05). Within the limits of this study, the following conclusions were drawn: The mean shear bond strengths (MPa) were: 18.44 for Uni metal VH/Creation (NCUC); 18.72 for Heraenium/Creation (NCHC); 16.23 for Wirobond C/Creation (NCWC); 13.88 for Zirconia core/$110{\mu}m$ $Al_2O_3$ sandblasting/Cercon Ceram Kiss (ZS110P); 14.61 for Zirconia core/No surface treatment/IPS e.max ZirPress (ZNTH). The mean shear bond strength for NCUC (Uni metal VH/Creation), NCHC (Heraenium/Creation) and NCWC (Wirobond C/Creation) were significantly superior to ZS110P (Zirconia core/$110{\mu}m$ $Al_2O_3$ sandblasting/Cercon Ceram Kiss) and ZNTH(Zirconia core/No surface treatment/IPS e.max ZirPress) (p<0.05).

• The Journal of Advanced Prosthodontics
• /
• 제10권4호
• /
• pp.259-264
• /
• 2018

PURPOSE. The purpose of this study was to evaluate the effect of the zirconia surface architecturing technique (ZSAT) on the bond strength between veneering porcelain and zirconia ceramic. MATERIALS AND METHODS. 20 sintered zirconia ceramic specimens were used to determine the optimal surface treatment time, and were randomly divided into 4 groups based on treatment times of 0, 1, 2, and 3 hours. After etching with a special solution, the surface was observed under scanning electron microscope, and then the porcelain was veneered for scratch testing. Sixty 3 mol% yttria-stabilized tetragonal zirconia polycrystal ceramic blocks were used for tensile strength testing; 30 of these blocks were surface treated and the rest were not. Statistical analysis was performed using ANOVA, the Tukey post-hoc test, and independent t-test, and the level of significance was set at ${\alpha}=.05$. RESULTS. The surface treatment of the zirconia using ZSAT increased the surface roughness, and tensile strength test results showed that the ZSAT group significantly increased the bond strength between zirconia and veneering porcelain compared to the untreated group (36 MPa vs. 30 MPa). Optimal etching time was determined to be 2 hours based on the scratch test results. CONCLUSION. ZSAT increases the surface roughness of zirconia, and this might contribute to the increased interfacial bond strength between zirconia and veneering porcelain.

• The Journal of Advanced Prosthodontics
• /
• 제6권5호
• /
• pp.415-422
• /
• 2014

PURPOSE. The purpose of this study was to evaluate and compare the translucency of shaded zirconia allceramic systems. MATERIALS AND METHODS. Translucency of 3 different zirconia all-ceramic systems colored by different techniques was compared with a lithium disilicate glass-ceramic (IPS e.max Press). Square-shaped specimens with 0.5 mm thickness were fabricated from In-Ceram YZ, ICE Zirkon and Katana systems in A1, A2 and A3.5 shades according to Vitapan Classical shade tab (n=11). Specimens were then veneered and glazed with corresponding veneer ceramic recommended by each zirconia system manufacturer and the total thickness was set to 1.5 mm. Translucency measurements were performed with VITA Easyshade Compact spectrophotometer after each stage and translucency parameter was calculated. Data were statistically analyzed with repeated measures ANOVA and Tukey multiple comparison test. RESULTS. The control group was significantly more translucent than the zirconia systems (P<.05). ICE Zirkon cores showed the least translucency; neither In-Ceram YZ nor Katana systems were superior to each other in terms of translucency. Translucency of all specimens was decreased after veneering, and the translucency rankings were changed. CONCLUSION. Coloring technique did not have a significant effect on translucency of zirconia cores. Although zirconia systems were less translucent than lithium disilicate glass ceramic, they had partial translucency and there were translucency differences among the zirconia systems. Chroma affected the translucency of precolored zirconia cores.

• The Journal of Advanced Prosthodontics
• /
• 제6권6호
• /
• pp.451-455
• /
• 2014

PURPOSE. The most common failure seen in restorations with a zirconia core is total or layered delamination of the ceramic veneer. In the present study, the shear bond strengths between veneering ceramics and colored zirconia oxide core materials were evaluated. MATERIALS AND METHODS. Zirconia discs ($15{\times}12{\times}1.6mm$) were divided into 11 groups of 12 discs each. Groups were colored according to the Vita Classic scale: A3, B1, C4, D2, and D4. Each group was treated with the recommended shading time for 3 s, or with prolonged shading for 60 s, except for the control group. Samples were veneered with 3 mm thick and 3.5 mm in diameter translucent ceramic and subjected to shear test in a universal testing machine with a crosshead speed of 1 mm/min. One-way analysis of variance (ANOVA) and Tukey's HSD tests were used for comparisons of the groups having the same shading times. A paired t-test was used for groups of the same color (3 s/60 s). RESULTS. Among the 11 groups investigated C4 (3 s) had the highest bond strength with a value of 36.40 MPa, while A3 (3 s) showed the lowest bond strength with a value of 29.47 MPa. CONCLUSION. Coloring procedures can affect zirconia/ceramic bond strength. However, the results also showed that bond strengths of all the investigated groups were clinically acceptable.

• 대한치과기공학회지
• /
• 제32권4호
• /
• pp.351-356
• /
• 2010

Purpose: The purpose of this study was to evaluate the fracture strength between the core and veneering ceramic according to 2 core materials, In-Ceram Alumina and In-Ceram Zirconia, fabricated by electro ceramic layering technique. 2 different fixed partial denture cores of three units were veneered by veneering ceramic(Ceranion, Noritake) (n=10). Methods: The fracture strengths between the core and veneering ceramic were measured through the 3 point bending test. The interfaces between the core and veneering ceramic were observed with the X-ray dot mapping of EPMA. Results: The result of fracture strength was observed that IZP group, In-Ceram Zirconia core, had higher fracture strength. IPA group, In-Ceram Alumina core, had fracture strength of 359.9(${\pm}$86.2) N. IZP group, In-Ceram Zirconia core, had fracture strength of 823.2(${\pm}$243.0) N. X-ray dot mapping observation showed that a major element in the core and veneering ceramic of IPA group was alumina and silica, respectively. No binder was observed in interfaces between the core and veneering ceramic, and no ion diffusion or transition was observed between the core and veneering ceramic. However, apparent ion diffusion or transition was observed between the core and veneering ceramic of IZP group.

• The Journal of Advanced Prosthodontics
• /
• 제7권5호
• /
• pp.368-374
• /
• 2015

PURPOSE. The aim of the study was to evaluate the effect of abutment shade, ceramic thickness, and coping type on the final shade of zirconia all-ceramic restorations. MATERIALS AND METHODS. Three different types of disk-shaped zirconia coping specimens (Lava, Cercon, Zirkonzahn: ${\phi}10mm{\times}0.4mm$) were fabricated and veneered with IPS e.max Press Ceram (shade A2), for total thicknesses of 1 and 1.5 mm. A total of sixty zirconia restoration specimens were divided into six groups based on their coping types and thicknesses. The abutment specimens (${\phi}10mm{\times}7mm$) were prepared with gold alloy, base metal (nickel-chromium) alloy, and four different shades (A1, A2, A3, A4) of composite resins. The average $L^*$, $a^*$, $b^*$ values of the zirconia specimens on the six abutment specimens were measured with a dental colorimeter, and the statistical significance in the effects of three variables was analyzed by using repeated measures analysis of variance (${\alpha}$=.05).The average shade difference (${\Delta}E$) values of the zirconia specimens between the A2 composite resin abutment and other abutments were also evaluated. RESULTS. The effects of zirconia specimen thickness (P<.001), abutment shade (P<.001), and type of zirconia copings (P<.003) on the final shade of the zirconia restorations were significant. The average ${\Delta}E$ value of Lava specimens (1 mm) between the A2 composite resin and gold alloy abutments was higher (close to the acceptability threshold of 5.5 ${\Delta}E$) than th ose between the A2 composite resin and other abutments. CONCLUSION. This in-vitro study demonstrated that abutment shade, ceramic thickness, and coping type affected the resulting shade of zirconia restorations.