• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2013.05a
• /
• pp.85-85
• /
• 2013

A ceramic coating material with nano-sized silicon oxide on AISI 4340 steel for a thermal conductor at a high temperature was analyzed to find an optimum coating process. Average surface roughness of the coating layers prepared by dipping process was about $5.26{\mu}m$. Potassium silicate addition as a binder of the coating material tended to improve its hardness. A pencil scratch hardness testing showed that a loading more than 800 g made fragments of the coating layer.

• Journal of the Korean Ceramic Society
• /
• v.43 no.1 s.284
• /
• pp.28-32
• /
• 2006

Diarylethene in photochromic materials was doped in organic-inorganic hybrid low-melting glasses were synthesized through a nonaqueous acid-base reaction process, which consists of network units including a small number of bridging oxides. The organic phase is a dichlorodimethylsilane while the inorganic phase is a tin(II) chloride. Diarylethene was incorporated into the glasses without any degradation of its functionality. The open form of diarylenthene, which is converted from the opening one upon UV-irradiation, is change to the closed form visible light-irradiation. The rate constant of the photochemical reaction is $31.78\times10^{-3}s^{-1}$ with 400 W UV lamp irradiation.

• Journal of the Korean Ceramic Society
• /
• v.24 no.6
• /
• pp.579-585
• /
• 1987

The effects of flux KCl and dopant Nb2O5 on the PTCR characteristics of BaTiO3 prepared by molten salt synthesis method have been investigated. As the amount of dopant Nb2O5 is over the solubility limit in BaTiO3, the room-temperature resistivity increases, and the PTCR effect and the grain size decrease. The variation of the amount of flux KCl slightly influences on the room-temperature resistivity, PTCR effect and grain size in Nb2O5 doped BaTiO3, but BaTiO3 ceramics prepared by the method of molten salt synthesis show larger PTCR effect than those of conventional calcining of mixed oxides.

• Journal of the Korean Ceramic Society
• /
• v.33 no.8
• /
• pp.871-876
• /
• 1996

It is believed that fly ash could be suitable for preparing the sialon by carbothermal reduction method because the total amount of SiO2 and Al2O3 is above 80% and the unburned residual carbon is above 5% within the fly ash. The effects of reaction temperature (1350, 1400, 145$0^{\circ}C$) reaction time (1, 5, 10 hours) and the amount of carbon additions (C/SiO2=2, 3, 4 mole) on the $\beta$-sialon synthesis were obserbed, It was conformed that $\beta$-sialon (Z=2.15~2.18) was formed as major phase under all of the synthesis conditions and small amount of Si2ON2 SiC, AlN and Si3N4 was formed depending on the synthesis conditions. FeSix intermetal-lic compound was formed above 140$0^{\circ}C$ reaction temperature due to the large amount of iron oxides within the raw fly ash.

• Journal of the Korean Ceramic Society
• /
• v.30 no.2
• /
• pp.123-130
• /
• 1993

Dispersed type Al2O3-SiC composite powders were synthesized from Al-isopropoxide (Al(i-OC3H7)3) and Si(OC2H5)4 precursors by hydrolysis of mixed alkoxides and carbothermal reaction method. The characteristics of the synthesized (dispersed type) Al2O3-SiC composite powders were investigated using XRD, SEM, TEM, BET and particle size analyzer. Carbothermal reaction to produce Al2O3-SiC composite was completed in 10h at 135$0^{\circ}C$ on 3~4㎤/s (0.21~0.28cm/s) of H2 flow rate and about 1/1 of carbon/oxides(=SiO2＋Al2O3) molar ratio. The synthesized powders were observed to have the mean particle size range of 0.4~1.26${\mu}{\textrm}{m}$ and showed finer particle size with increasing SiC content.

• Journal of the Korean Ceramic Society
• /
• v.41 no.2
• /
• pp.102-105
• /
• 2004

ZnO-In$_2$O$_3$ films were fabricated on Corning 1737 glass substrate by an electron beam evaporation technique and their characteristics were investigated. The composition of ZnO-In$_2$O$_3$ films had a marked effect on the electrical properties of the films. The ZnO-In$_2$O$_3$ films showed superior transparent-conducting characteristics with increase of Zn content. The resistivity and carrier concentration of the film having Zn content of 45 at% are 4.45${\times}$10$^{-3}$ cm and 3.1${\times}$10$^{19}$ cm$^{-3}$ , respectively. Also, the transmittance was higher than 80% throughout the visible range. The average roughness of the film was 14.6 $\AA$ in terms of root mean square.

• Journal of the Korean Ceramic Society
• /
• v.23 no.6
• /
• pp.71-75
• /
• 1986

The forming reaction processes of magnesium aluminate spinel by a thermal decomposition of sulfate hydrate were studied with DTA, TG. SEM and X-ray powder diffraction methods. The hydrous salt composed of the mixture of the two compounds of $MgSO_4$ $6H_2O$ and ${AL_2}({SO_4})_17H_2O_3$ in which both sulfates were crystalline. On heating the hydrous slat the crystalline magnesium and aluminum sulfate anhydride to amorphous alumina magnesium sulfate anhydride decomposed to amorphous magnesia and these amorphous oxides reacted completely each other to form a spinel at $1000^{\circ}C$ The apparent activation energy of forming reaction of spinel was 36.5 kcal/mole($900^{\circ}C$~$1000^{\circ}C$) The crystallite size of spinel obtained at $1000^{\circ}C$ after 1 h was 380$\AA$.

• Journal of the Korean Ceramic Society
• /
• v.47 no.1
• /
• pp.47-53
• /
• 2010

Ceramics with perovskite-type structure are interesting functional materials for several energy conversion processes due to their flexible structure and a variety of properties. Prominent examples are electrode materials in fuel cells and batteries, thermoelectric converters, piezoelectrics, and photocatalysts. The very attractive physical-chemical properties of perovskite-type phases can be modified in a controlled way by changing the composition and crystallographic structure in tailor-made soft chemistry synthesis processes. Improved thermoelectric materials such as cobaltates with p-type conductivity and n-type manganates are developed by following theoretical predictions and tested to be applied in oxidic thermoelectric converters.

• Journal of the Korean Ceramic Society
• /
• v.37 no.2
• /
• pp.158-163
• /
• 2000

Six different SiC ceramics with SiO2-Re2O3 (Re=Yb, Er, Y, Dy, Gd, Sm) as sintering additives have been fabricated by hot-pressing the SiC-Re2Si2O7 compositions at 1850$^{\circ}C$ for 2 hr under a pressure of 25 MPa. The room temperature strneth and the fracture toughness of the hot-pressed ceramics were characterized and compared with those of the ceramics sintered with YAG (Y3Al5O12). Five SiC ceramics (Re=Yb, Er, Y, Dy, Gd) investigated herein showed sintered densities higher than 94% of theoretical. Tthe SiC-Re2Si2O7 compositions showed lower strength and comparable toughness to those from SiC-YAG composition, owing to the chemical reaction between SiO2 and SiC during sintering. SiC ceramics fabricated from a SiC-Y2Si2O7 composition showed the best mechanical properties of 490 MPa and 4.8 MPa$.$m1/2 among the compositions investigated herein.

• Journal of the Korean Ceramic Society
• /
• v.23 no.1
• /
• pp.13-20
• /
• 1986

Zirconia soild electrolytes containing 4~10mol% of yttria were prepared by wet-blending of oxides and rea-ction-sintering, Sinterbility and degree of stabilization were optimized for the development of oxygen sensor. Fracture strength thermal expansion coefficient electrical conductivity and galvanic potential were measured and discussed with respect to the amount of ytria addition phase transformation microstructure and degree of stabilization. It was found that sintering and stabilization occurred when the composition was designed to be near the boundary region of $ZrO_2-Y_2O_3$ binary system. In such away a good zirconia solid electrolyte suitable for oxygen sensor could be developed.