• 한국세라믹학회지
• /
• 제47권5호
• /
• pp.450-456
• /
• 2010

During the process of synthesizing green celsian pigments, attempts were made to replace a given amount of $BaCO_3$ with $SrCO_3$ to accelerate the hexagonal to monoclinic celsian phase transition, which was assumed to promote color development. Monoclinic celsian have been synthesized from Hongkong-Kaolin, $BaCO_3$, $SrCO_3$, $Al(OH)_3$, $SiO_2$ and $SrCO_3$ with 1 to 1.5 wt% of LiF as a mineralizer from 1100 to $1300^{\circ}C$. It was found that replacing $BaCO_3$ with $SrCO_3$ allowed monoclinic celsian to be formed at a lower temperature. While the pigments containing 1 mole of $BaCO_3$ were difficult to synthesize monoclinic celsian with absence of the mineralizer, the formation of monoclinic celsian was successfully achieved even without mineralizer by using 0.25 mole of $SrCO_3$ at $1250^{\circ}C$ for 1 h. The color development was improved from yellowish green to green with increasing amount of $SrCO_3$ being replaced.

• 한국세라믹학회지
• /
• 제39권5호
• /
• pp.438-445
• /
• 2002

본 연구에서는 $PbO-TiO_2-SiO_2-BaO-ZnO-Al_2O_3-CaO-B_2O_3-Bi_2O_3-MgO$계의 유리를 $1,400{\circ}C$에서 용융시킨 후, 급랭, 분쇄하여 glass frit을 제조하였다. Glass frit 분말을 일축가압성형한 후 $750~1,000{\circ}C$의 온도범위에서 2시간 동안 소성 및 결정화 하였다. Glass frit의 결정화는 $750{\circ}$ 전후의 온도에서 시작되었고, 저온에서의 주된 결정상은 $Al_2O_3$와 hexagonal celsian($BaAl_2Si_2O_8$)이었다. 소성온도가 높아지면서 monoclinic celsian, $ZnAl_2O_4,\;Zn_2SiO_4,\;CaTi(SiO_4)O,\;TiO_24 등이 주된 결정상으로 나타났고, 특히 celsian은 hexagonal에서 monoclinic으로 상전이가 발생하였다. 그리고 15wt%의 PbO를 첨가한 glass frit에만 $PbTiO_3-CaTiO_3$ 고용체가 나타났다. 1MHz 대역에서 유전특성을 살펴본 결과 유전상수는 11~16이었고, 유전손실은 0.020 미만이었다. 그러나 15wt%의 PbO를 첨가한 glass frit의 경우는 $PbTiO_3-CaTiO_3$ 고용체 결정상의 존재로 유전상수가 17~26으로 높았고, 유전손실은 0.010~0.015로서 다른 조성들에 비하여 우수한 특성을 나타내었다.

• 한국세라믹학회지
• /
• 제31권9호
• /
• pp.981-988
• /
• 1994

Crystallizable glasses with precipitation of celsian were prepared for the purpose of insulating dielectric layers for the devices such as integrated circuit substrates. Crystallization behavior of these glasses were studied by DTA, SEM, XRD analysis and by the measurement of dielectric properties. The base composition of the glass-ceramic consists in weight percent of 30% SiO2, 10% Al2O3, 26% BaO, 10% CaO, 10% ZnO, 8%TiO2 and 6% B2O3. 2-6 wt% Y2O3 were selected as the nucleating agent to promote monoclinic celsian formation. As a result, in barium-rich glasses containing 4~6wt% Y2O3 , monoclinic celsian was developed as major crystalline phase in the temperature range of 850~90$0^{\circ}C$. Also, the dielectric constant and quality factor of these glass-ceramics were about 9 and more than 1000, respectively.

• 한국결정성장학회지
• /
• 제7권3호
• /
• pp.428-436
• /
• 1997

0.8$\mu$의 평균입자크기와 63$m^2/g$의 비표면적을 갖는 소질성이 뛰어난 hexacelsian분말이 so;ution-polymerization 방법에 의해 제조되어졌다. polymerization 경정을 통한 분말합성을 위하여 PVA 용액이 사용되었다. 소결후 치밀화된 hexacelsian은 $\alpha$,$\beta$,$\gamma$ 간의 상전이 거동을 보였고, 상대밀도 98.5% 의 치밀화ㄱ된 celsian 소결체가 $1600^{\circ}C$에서 72시간의 서냉공정을 거쳐hexacelsian의 상전이에 의하여 얻어졌다.

• The Korean Journal of Ceramics
• /
• 제4권4호
• /
• pp.323-330
• /
• 1998

Mixed oxide compounds of potential usefulness for fibre coatings (hexagonal celsian, $BaAl_2Si_2O_8$ and lanthanum hexaluminate, $LaAl_{11}O_{18}$) or for matrix materials (yttrium aluminium garnet, $Y_3Al_5O_{12}$) were prepared by hybrid sol-gel synthesis and their thermal crystallisation was monitored by thermal analysis, X-ray diffraction and multinuclear solid state MAS NMR. All the gels convert to the crystalline phase below about $12200^{\circ}C$, via amorphous intermediates in which the Al shows and NMR resonance at 36-38 ppm sometimes ascribed to Al in 5-fold coordination. Additional information about the structural changes during thermal treatment was provided by $^{29}Si$, $^{137}Ba$ and $^{89}Y$ MAS NMR spectroscopy, showing that the feldspar framework of celsian begins to be established by about $500^{\circ}C$ but the Ba is still moving into its polyhedral lattice sites about $400^{\circ}C$ after the sluggish onset of crystallization. Lanthanum hexaluminate and YAG crystallise sharply at 1230 and $930^{\circ}C$ respectively, the former via $\gamma-Al_2O_3$, the latter via $YAlO_3$. Yttrium moves into the garnet lattice sites less than $100^{\circ}C$ after crystallisation.

• E2M - 전기 전자와 첨단 소재
• /
• 제8권1호
• /
• pp.95-101
• /
• 1995

Crystallizable glasses with precipitation of celsian, anorthite, wollastonite and gahnite were prepared for the purpose of insulating dielectric layers in devices such as integrated circuit substrates. The starting glasses were prepared by melting the batches for 1 hour at 1450.deg. C and then Quenching to a distilled water. And crystallization behavior of these glasses were studied by DTA, TMA, XRD analysis and by the measurement of dielectric properties. The overall composition of the glass-ceramic consists in weight percent of 30-35% A1$_{2}$O$_{3}$, 13-26% BaO, 5-21% CaO, 10-24% ZnO, 4.5-9.0% TiO$_{2}$ and 4-8% B$_{2}$O$_{3}$. As a result, in barium-rich glasses only celsian phase was developed in the range of 850-900.deg. C. Also, the thermal expansion coefficient, dielectric constant and quality factor of these glass-ceramics were 68*10$^{-7}$ /.deg. C, about 9 and more than 1000, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2006년도 하계학술대회 논문집 Vol.7
• /
• pp.272-273
• /
• 2006

LTCC(low temperature co-fired ceramics)용 glass/ceramic 복합체를 제조하기 위해 4 종류의 borosilicate계 glass를 선정하고 filler로 $Al_2O_3$ ceramics를 filler 사용하여 30~50 vol% glass frit에 따른 소결 및 유전 특성에 대하여 조사하였다. Glass frit은 $SiO_2$와 $B_2O_3$ 함량비를 고정한 후 R(CaO, BaO, ZnO, $Bi_2O_3$)에 따라 유리 연화온도(Ts)와 함량이 소결에 미치는 영향 및 유전 특성 변화를 고찰한 결과, CaO-$B_2O_3-SiO_2$ glass의 경우 다량의 2 차상이 형성되었고, 이에 $900^{\circ}C$ 이하에서 완전 소결이 이루어지지 않았으며, BaO-$B_2O_3-SiO_2$ glass는 celsian($BaAl_2Si_2O_8$) 결정이 형성되면서 소결성의 저하를 갖고 왔으며, ZnO-$B_2O_3-SiO_2$ glass는 소결이 진행됨에 따라 주상이 $Al_2O_3$에서 gahnite($ZnAl_2O_4$) 결정이 형성되면서 품질계수가 크게 증가하였으며, $Bi_2O_3-B_2O_3-SiO_2$ glass는 45 vol%일 때 $900^{\circ}C$에서부터 일정한 선수축율 특성을 나타내었지만, 다량의 액상으로 인하여 유전 특성의 저하를 나타내었다.