• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.556-560
• /
• 2002

The rheological characteristics of PNN-PZT ceramics with high electromechanical coupling factor and electricstrictive constant was investigated. Green sheets of piezoelectric PNN-PZT ceramics were made by tape-casting method with controlling the mixing ratio of a dispersant, an organic binder, and a plasticizer. When the dispersant content was 1 wt.%, the slurry showed the best rheological characteristics for tape casting. The amounts of the plasticizer and the binder was simultaneously varied in the ranges of 1.5~18 and 3~9 wt.%, respectively. When both the plasticizer and binder of 6 wt.% mixed in the solution, respectiveley, the highest green density of the sheet was obtained without macrodefects. Multilyered structures of PNN-PZT/Ag-Pd were successfully fabricated using the optimized tape casting condition. The polarization behavior of these actuators seemed to similar to typical electricstrictive polarization behavior. The multilayer ceramic actuator is about $0.6{\times}10^{-3}$ of strain.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2003.10a
• /
• pp.261-264
• /
• 2003

Semi-solid processing is now becoming of great interest for the production of various parts by pressure die casting. Many advantages are associated with this forming process at the condition that the forming operation is performed under appropriate conditions. The thixoforming process, which needs a suspension of a globular, non-dendritic solid phase in the liquid phase, is characterized by three major steps. The first step is casting of billets with a microstructure suited for thixoforming. The second step is reheating of slugs cut from these billets. The third step is injection of the semi-solid slugs into a die. In this paper, the horizontal reheating machine to obtain the optimal conditions suitable for semiu-solid die casting process was used and applied to extrusion material. It is estimated the possibility of application on semi-solid die casting with extrusion material through various results.

• Korea-Australia Rheology Journal
• /
• v.21 no.2
• /
• pp.135-141
• /
• 2009

Effect of activation energy and crystallization kinetics of polyethylenes (PEs) on the dynamics and stability has been investigated by changing rheological properties and crystallization rate in film casting process. The effect of changes of these properties has been shown using a typical example of short-chain branching (SCB) in linear polyethylenes. SCBs in linear polymers generally lead to the increase of the flow activation energy, and to the decrease of the crystallization rate, making polymer viscosity lower in the case of equivalent molecular weight. In general, the increment of the crystallinity of polymers under partially crystallized state helps to enhance the process stability by increasing tension, and lower fluid viscoelasticity possesses the stabilizing effect for linear polymers. It has been found that the fluid viscoelasticity plays a key role in the control of process stability than crystallization kinetics which critically depends on the cooling to stabilize the film casting process of short-chain branched polymers operated under the low aspect ratio condition.

• Journal of the Korean Ceramic Society
• /
• v.30 no.10
• /
• pp.845-851
• /
• 1993

Low firing temperature substrate were synthesized through tape casting and sintering of glass with cordierite composition and then their properties were investigated. Even though the dielectric properties and XRD patterns of substrates, obtained by tape casting and sintering at 900~100$0^{\circ}C$ for various periods, were similar to those of substrates obtained by dry pressing, the sinterability was enhanced. The substrates were thin and the size was 0.6$\times$50$\times$50mm. From the results of dielectric properties, the sinterability and X-ray diffraction pattern, the proper condition for cofiring process with conductor, Cu, was 90$0^{\circ}C$ for 1h. The properties of the substrate are as follows; the dielectric constant was 5.31(at 1MHz), the dissipation factor was 0.0028, the apparent porosity was 0.28% and the main crystalline phase was $\alpha$-cordierite.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2001.05a
• /
• pp.120-123
• /
• 2001

The semi-solid casting will have a higher internal integrity, mechanical properties and dimensional accuracy than the conventional castings. This process can reduce the manufacturing costs and finished weight for critical components. The semi-solid casting are capable of greater dimensional repeatbility, this supplies considerable savings when extensive machining, salvage and scrap are key variables in the current automotive product. One of the most important factor regarding the semi-solid die casting process are the reheating method of the raw materials to the semi-solid state. Therefore, in this present work, the horizontal type induction heating system to obtain the optimal reheating conditions suitable for semi-solid die casting process was designed and manufactured. And the microstructure of reheated materials was investigated.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1997.10a
• /
• pp.180-183
• /
• 1997

The forming process of metal matrix composites by the die casting and squeeze casting process are limited in size and dimension in term of final parts without machining. The thixoforming process for metal matrix composites has numerous advantages compared to die casting, squeeze casting and compocasting. The characteristics of thixoforming process can decrease the liquid segregation because of he improvement in fluidity in a globular microstructure state and utilizes flow without air entrapment. Therefore, in order to obtain the sound parts of metal matrix composites by using thixoforming process which as co-existing solidus-liquidus pahse, it si very important to obtain reheating condition. However, for he thixoforming process, the billet with the desired volume fraction must be heated to obtain a uniform temperature distribution over the entire cross-sectional areas. To obtain the reheating conditions of composites, the particulate reinforced metal matrix composites for thixoforming were fabricated by combined stirring process which is simultaneously performed with electro-magnetic stirring process which is simultaneously performed with electro-magnetic stirring and mechanical stirring process.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.17 no.7 s.94
• /
• pp.1751-1760
• /
• 1993

The squeeze casting process is considered as an attractive way to form the primary product of near net shape metal matrix composites for wide use in automobile industry. To understand for infiltration limit in squeeze casting processes, the SAFFIL short fiber preform of volume fraction $10%{\sim}23%$ were fabricated by vaccum pumping and speed control press, and the optimal condition for fiber preform fabrication had been experimentally obtained. The composite materials were fabricated by forced infiltration of molten metals such as Al6061, Al7075, pure Al, AC8A, and Al2024. The infiltration distance and deformation of fiber preform are observed, and tensile strength were measured from at the room temperature.

• Journal of Korea Foundry Society
• /
• v.25 no.2
• /
• pp.80-87
• /
• 2005

The microstructure and mechanical property of the Ni and Ni-Cr porous metal reinforced AC4C matrix composites fabricated by squeeze casting were investigated. In this study Ni, Ni-Cr porous metals which are estimated to be easy to fabricate by squeeze casting are used as strengtheners for composite materials. As a matrix material, Al-7wt.%Si-0.3wt.%Mg(AC4C) has been used. In case of Ni/AC4C and Ni-Cr/AC4C composite, $750^{\circ}C$ melt temperature and minimum 25MPa squeezing pressure are needed to produce sound composite materials. The observation of interfacial reaction zone at various heat treatment condition shows that atsolutionizing temperature of above $520^{\circ}C$, the interfacial reaction zone increases proportionally with heat treatment time and the reaction products formed by interfacial reactions are mainly composed by $Al_{3}Ni$ and $Al_{3}Ni_{2}$ phases.

• Journal of Korea Foundry Society
• /
• v.28 no.1
• /
• pp.25-30
• /
• 2008

To develop a functionally graded microstructure of cylindrical liner, effect of centrifugal casting parameters such as pouring temperature of hyper-eutectic Al-Si alloy melt, mold pre-heating temperature, and rotational frequency of mold on distribution of primary Si particles across wall thickness were investigated. Segregation tendency of Si particles toward inner side of cylindrical liner increased as the increase of rotational frequency of mold, pouring temperature of melt and mold pre-heating temperature. Especially, distribution density of primary Si particles within 1.5 mm from inner surface of cylindrical liner was above 35% under the centrifugal casting condition of $750^{\circ}C$ melt pouring temperature, $300^{\circ}C$ mold pre-heating temperature, and 2500 rpm mold rotational frequency.

• Journal of Korea Foundry Society
• /
• v.29 no.5
• /
• pp.198-203
• /
• 2009

In order to manufacture copper ultra fine wire used for bonding wire in integrated circuit package, continuous casting process, which can produce high purity copper rod with small cross section, and wiredrawing process have to be optimized to prevent wire brakeage during entire manufacturing process of fine wire. The optimum condition for producing copper rod with mirror surface has to established by investigation of the effects of several parameters such as withdrawal speed, superheat and rod diameter on grain morphology of the cast rod and on its drawing characteristics to fine wire. The purpose of this study is to propose the optimized process parameters in continuous casting process in order to produce cast rod without internal defects, and to predict microstructure orientation suitable for wire drawing process.