• Journal of Korea Foundry Society
• /
• v.32 no.6
• /
• pp.269-275
• /
• 2012

Al-Mg-Si/Al hybrid alloy was prepared by Duo-casting and the mechanical behavior was evaluated based on their microstructure and mechanical properties. The hybrid aluminum alloy included the Al-Mg-Si alloy with fine eutectic structure, pure Al with the columnar and equiaxed crystals, and the macro-interface existing between Al-Mg-Si alloy and pure Al. The growth of columnar grains in pure Al occurred from the macro-interface. The tensile strength, 0.2% proof stress and bending strength of the hybrid aluminum alloy were almost similar to those of pure Al, and the elongation was much higher than the Al-Mg-Si alloy. The fracture of the hybrid alloy took place in pure Al side, indicating that the macro-interface was well bonded and the mechanical behavior strongly depends on the limited deformation in pure Al side.

• Korean Journal of Metals and Materials
• /
• v.50 no.7
• /
• pp.503-509
• /
• 2012

We report on the feasibility of producing 6xxx series Al alloy sheets using a combination of twin-roll strip casting and asymmetric rolling. The Al alloy sheets produced in this study exhibited an excellent formability ($\bar{r}=1.2$, ${\Delta}r=0.17$) and mechanical properties (${\sigma}_{TS}{\sim}260MPa$, ${\varepsilon}>30%$), which cannot be feasibly obtained via the conventional technique based on ingot casting and conventional rolling. The enhanced formability as evaluated in terms of $\bar{r}$ and ${\Delta}r$ was clarified by examining the evolution of textures associated with strip casting and subsequent thermo-mechanical treatments. The evaluation of the formability leads us to conclude that the combined technique based on strip casting and asymmetric rolling is a feasible process for enhancing the formability of Al alloy sheets to a level beyond which the conventional technique can reach.

• Journal of Korea Foundry Society
• /
• v.22 no.4
• /
• pp.174-183
• /
• 2002

Twin-roll process is a relatively new continuous casting process which can produce high-quality strip products directly, and solidification rate can reach $10^3$ to $10^4$ K/s, leading to fine and uniform microstructures with enhanced mechanical properties. The strip casting condition for producing fine Al-Sn alloy strip was obtained experimentally, and defects appearing on the strip was examined. Crack formation and surface quality of the strip was found to depend mainly on process parameters such as melt temperature, roller gap and rolling speed. Sn structure of network type was observed in Al-20Sn and Al-40Sn alloy strips, and cell spacing of Al-40Sn alloy was smaller than that of Al-20Sn. Banding strength of the heat treated specimens increased with increasing of soaking time and temperature, and bonding strength of Al-20Sn alloy was more superior than that of Al-40Sn alloy. However wear resistance of Al-40Sn alloy contained large amount of soft Sn which possess good anti-friction characteristics was superior than that of Al-20Sn alloy.

• Journal of Korea Foundry Society
• /
• v.21 no.2
• /
• pp.127-134
• /
• 2001

Misch metal (rare earth element, Ce, La, Nd, Pr) which has large influence on high-temperature stability and toughness was added to the Al-5%Ni-5%Mg alloy, and squeeze casting was used for Al-5%Ni-5%Mg-(Mm) alloys. The effect of applied pressure and misch metal additions on mechanical properties in Al-5%Ni-5%Mg alloy by direct squeeze casting has been investigated. The applied pressure were 0 MPa(gravity casting), 25, 50 and 75 MPa. Squeeze-cast Al-5%Ni-5%Mg-(Mm) alloys had better mechanical properties than those of non-pressurized cast alloys because of the increased cooling rate by the application of pressure during solidification. By the addition of misch metal in Al-5%Ni-5%Mg alloy, better combination of strength and elongation was obtained. The addition of 0.3%Mm in Al-5%Ni-5%Mg alloy improved the heat resistant property due to the formation of fine eutectic phases.

• Journal of Korea Foundry Society
• /
• v.17 no.4
• /
• pp.385-392
• /
• 1997

The main objective of this study is to investigate the microstructure and tensile strength of $SiC_p$/Al alloy composites fabricated by die casting method. Die casting was performed using the preheated mold at the pouring temperature range of $620{\sim}750^{\circ}C$ under the pressure of $1,039 kgf/cm^2$. The low speed and a following high injection speed were 0.4 and 2.1 m/s, respectively. The microstructure of $SiC_p$/Al alloy composites fabricated by die casting method was found to be finer than that of composites fabricated by gravity casting. Also, SiC particulates were homogeneously distributed in refined Al matrix due to rapid solidification. The tensile strength of $SiC_p$/Al alloy composites fabricated by die casting method was found to be varied with cast temperature. The maximun tensile strength of $SiC_p$(10 vol.% and 20 vol.%)/Al alloy composites showed 380 MPa at the cast temperature of $750^{\circ}C$ and 363 MPa at the cast temperature of $700^{\circ}C$, respectively.

• Journal of Korea Foundry Society
• /
• v.13 no.6
• /
• pp.532-539
• /
• 1993

The effect of casting variables for making pure Al and Al-5wt%Si alloy rods free from any surface and inside defects was studied by adopting the horizontal continuous casting method with heated mold. The rods were cast under the casting conditions such as the mold temperature of $670{\sim}690^{\circ}C$, water flow rate of $0.2{\sim}0.6{\ell}/min$, and rod diameter of $4{\sim}8mm$, when the melt temperature and mold to cooler distance was fixed at $700^{\circ}C$ and 20mm, respectively. The results represented that the casting speed for good quality rod increased as the water flow rate increased, whereas, the casting speed decreased as the rod diameter or mold temperature increased. The statistical analysis of $2^3$ factorial design was also applied and the results represented that the averaged optimum casting speed for pure Al(302mm/min) was higher than that of Al-5wt%Si alloy(273mm/min) resulting from the difference of superheat applied. The effect of rod diameter on the optimum casting speed was the highest for pure Al as well as Al-5wt%Si alloy. The effect of water flow rate and mold temperature on the optimum casting speed was in decreasing order.

• Journal of Korea Foundry Society
• /
• v.24 no.3
• /
• pp.165-174
• /
• 2004

The pore formation characteristic of Mg alloy during Lost Foam Casting(LFC) was investigated with reduced pressure test and real casting, which was compared with the results of previous work for Al alloy. Cast Mg alloys in LFC had much lower porosities in comparison with those of Al alloys. Also, the proper pouring temperature gave the minimum porosity like Al alloy although it was higher than that of Al alloys due to the worse fluidity of Mg alloy. The pore formation mechanism of Mg alloy in LFC was similar to that of AI alloy but the critical temperature showing the different mechanism is higher than that of Al alloy as much as $30{\sim}50^{\circ}C$. The result that Mg alloy in LFC had the lower porosity comparing with Al alloy was due to the extra solubility of hydrogen gas although the solubility of Al alloy was easily exceeded by the external sources like pyrolyzed polystyrene products. The mold evacuation gave the lower porosity due to the removal of polystyrene pyrolysis products, and reduced shrinkage defects. Also, there was a proper evacuation pressure that gave a porosity of almost 0vol%. But much higher vacuum degree than this proper pressure caused the severe entrapment of polymer pyrolysis products that gave the large porosity.

• Journal of Korea Foundry Society
• /
• v.22 no.2
• /
• pp.75-81
• /
• 2002

The main objectives were to investigate the suitability of CaO crucible for melting TiAl alloys and to develop investment mold for investment casting of TiAl alloys. TiAl alloy specimen were prepared by plasma arc furnace under argon atmosphere. After melting of TiAl alloy using CaO crucible, the results showed that there is little contamination of oxygen in the TiAl bulk. Conventional vacuum induction furnaces can be readily adaptable to produce cast parts of TiAl without high skilled techniques. The determination of optical metallography and microhardness profiles in investment cast TiAl alloy rods has allowed the gradation of the relative thermal stability of the oxides examined. The molds used for the present study were $ZrO_2$, $Al_2O_3$, CaO stabilized $ZrO_2$ and $ZrSiO_4$. Even although high temperature of mold preheating, $Al_2O_3$ mold is a promising mold material for investment casting of TiAl alloys in terms of thermal stability, cost and handling strength. It is important to take thermal stability and preheating temperature of mold into consideration for investment casting of TiAl alloys.

• Journal of Power System Engineering
• /
• v.7 no.4
• /
• pp.44-48
• /
• 2003

Alumium alloys casting are gaining increased acceptance in the automotive and electronic industeries and squeeze casting is the most efficient method of manufacturing such mass produced parts. This study has been investigated the microstructures and mechanical properties of Al-7.0Si-0.4Mg(AC4C)alloy fabricated by squeeze casting process for development of Engine Mountain Bracket. The microstructure of squeeze casted specimen were composed of eutectic structure Alumimim solid solution and $Mg_2Si$ precipitates. The tensile strength of as-solid solution treatment Al-7.0Si-0.4Mg alloy revealed 2985MPa. It was found that Al-7.0Si-0.4Mg alloy have good aging hardening effect results are presented to show the validity of the control method.

• Korean Journal of Metals and Materials
• /
• v.49 no.3
• /
• pp.243-249
• /
• 2011

This study describes the feasibility of producing high-strength Al alloy sheet with a high solute content using a combined technique of twin-roll strip casting and asymmetric rolling. The Al sheet produced in this study exhibited excellent formability ($\overline{r}$ =1.0, $\Delta$r=0.16) and mechanical properties ($\sigma_{TS}$~305 MPa, $\epsilon$~33%), that, cannot be feasibly obtained via the conventional technique based on ingot casting and rolling. The structural origin of the observed properties, especially enhanced formability, was clarified by examining the evolution of textures associated with strip casting and subsequent thermo-mechanical treatments. Our evaluation of the mechanical properties and formability leads us to conclude that the combination of strip casting and asymmetric rolling is a feasible process for enhancing the formability of Al alloy sheets to the level beyond what the conventional techniques can reach.