• Restorative Dentistry and Endodontics
• /
• 제23권1호
• /
• pp.443-460
• /
• 1998

The purpose of this study was to estimate the changes of tensile bond strength according to the difference in lining materials and lining area. Seventy non-carious extracted human molars were used in the present study, and they were randomly assigned into 2 experimental groups according to the difference in lining materials. Each experimental group was subdivided into 3 groups according to the difference in lining area. Circular cavities were prepared on the dentin surface to a diameter of 1.5mm, 2.0mm, 2.5mm and the prepared cavities were filled with Fuji II LC( Glass Ionomer Cement : GIC) or Dycal. Dentin specimens without circular cavity were used as control group. The primer and bonding agent of All-Bond 2 and composite resin (Z-100, 3M Dental Products, U. S. A.) were applied to the exposed dentin surface with or without lining. Tensile bond strengths for the experimental specimens were then measured. To examine the interface between dentin and liner & between liner and composite resin, two specimens from each group were fabricated and observed under the SEM. The results were as follows. 1. Tensile bond strength for the specimens lined with GIC was higher than that for specimens lined with Dycal. However, there was no significant difference between two groups(p>0.05). 2. Tensile bond strength for the specimens lined with GIC in a diameter of 1.5mm(GIC-1.5mm lining group) was statistically higher than that for the GIC-2.0mm lining group and GIC-2.5mm lining group(p<0.05). 3. Tensile bond strength for the specimens lined with Dycal in a diameter of 2.5mm (Dycal-2.5mm lining group)was statistically lower than that for Dycal-1.5mm lining group and Dycal-2.0mm lining group(p<0.05). 4. It was possible to observe the good adhesion of the resin composite to the GIC and the presence of a fissure between GIC and dentin all along the interface. Interfacial gaps of 7.2-$72.2{\mu}m$ between GIC and dentin were observed. The interfacial gap between GIC and dentin at the cavity base was greater. However, the gap was gradually decreased toward the occlusal portion. 5. It was possible to observe the poor adhesion of the resin composite to the Dycal. The detachment of Dycal was occurred all along the composite resin-Dycal interface, and the gaps of 2.0-$30.1{\mu}m$ were formed. In all the specimens, polymerization shrinkage of resin composite caused the detachment of Dycal from the body of Dycal. At a Dycal-dentin interface. it was possible to observe the good adhesion. but poor adhesion with interfacial gap of 2.9-$26.8{\mu}m$ was observed partially.

• 대한소아치과학회지
• /
• 제27권1호
• /
• pp.54-61
• /
• 2000

아말감은 널리 사용되어 온 대표적 치과재료이지만 치질과의 접착성이 없어 와동의 형태에 의해 유지되는 단점을 가진다. 아말감 수복물은 산화물에 의한 변연봉쇄가 일어나기 전까지 초기에 큰 미세누출을 보이며 수복초기에 이를 적절하게 예방하지 않으면 타액이나 미생물이 와동내에 침투하게 되고 이로 인해 수복 후의 과민반응, 충전물의 용해 및 파괴, 변연 변색과 2차 우식이 유발되어, 결과적으로 수복물의 수명이 단축되며 치수 병변이 발생될 수도 있다. 최근 기존 아말감 수복의 장점을 그대로 유지하면서 치질삭제를 줄이고 변연을 봉쇄하며 소와열구에 예방적 처치를 함께 할 수 있는 수복법이 제안되었는데 이를 이른바 sealed amalgam이라 한다. 이 술식은 예방적 확대 없이 병소만을 제거한 뒤 수복물 변연과 인접 소와열구에 치면열구전색재를 도포함으로서 소와열구의 예방적 충전은 물론 수복물 변연과 치질사이의 틈을 봉쇄하여 미세누출을 감소시킬 수 있다고 하였다. 이에 저자는 아말감 수복후 수복물의 마무리 처리와 전색재 적용시점을 달리 하여 sealed amalgam 수복과 기존의 아말감 수복과의 미세누출의 차이를 비교하고자 30개의 상, 하악 소구치를 준비하여 V급 와동을 소구치의 협, 설측에 형성하고 통상적 아말감 수복을 시행한 후 다음의 각 군으로 나누어 처리하였다. 제 1 군 : 24시간 후 연마 (대조군) 제 2 군 : 연마하지 않음, 즉시 전색재 적용 제 3 군 : 연마하지 않음, 열순환(thermocycling) 500회 후 전색재 적용 위의 처리 후 각 군을 $5^{\circ}C$와 $55^{\circ}C$의 온도변화를 30초씩 번갈아 주며 총 500회의 열순환을 실시한 후 1% methylene blue 용액에 침윤시켜서 100% 습도가 유지된 $37^{\circ}C$ 항온기에 24시간 보관하였다. 치아를 레진에 매몰한 후 협설측으로 치아 장축에 평행하게 절단하여 stereomicroscope를 사용해 색소침투도를 관찰하여 다음과 같은 결론을 얻었다. 1. 평균 미세누출은 연마하지 않고 바로 치면열구전색재를 도포한 2군이 가장 낮았고, 연마만 시행한 1군이 가장 높았다. 2. 실험군간의 미세누출 비교에서 연마만 시행한 1군은 2군에 비해 미세누출이 켰으며 통계적으로 유의성 있는 차이를 보였다(p<0.05). 3군은 1군보다 평균미세누출이 작았으나 통계적으로 유의한 차이가 없었다(p>0.05). 2군은 3군보다 평균 미세누출이 작았으나 통계적으로 유의한 차이가 없었다(p>0.05).