• Journal of the Korean Ceramic Society
• /
• v.45 no.7
• /
• pp.387-394
• /
• 2008

The Physical property changes of calcined clay by carburization were investigated studied. The carburization mechanism is the penetration of carbon which occurred during incomplete fuel combustion into crevice of clay structure. The experiments for elasticity and freeze-thaw resistance were conducted, and the results can be summarized as follows: Dynamic modulus of elasticity and also freeze-thaw resistance of calcined clay by carburization treatment increased more than 92% after testing 300 cycle, which was more improved than 88% of calcined clay. Therefore, it can decrease the possibility of winter-sowing, which is one the weakness of calcined clay. It is on the basis of the fact that the porosity of calcined clay by carburization treatment is about 12%, which indicates smaller pore spaces comparing with the 14% of porosity of calcined clay and those values were calculated by apparent porosity show and also supported by SEM images. Infrared emissivity of calcined clay by carburization treatment and calcined clay were respectively 0.92 and 0.9l at $80^{\circ}C$. However, those values were 0.91 and 0.88 at $200^{\circ}C$, which means infrared emissivity of calcined clay by carburization treatment shows 3.6% higher than the calcined clay. Moreover, within the wavelength range from 3 to $7\;{\mu}m$, while the calcined clay had low infrared emissivity, the calcined clay by carburization treatment had increased infrared emissivity. It is inferred that it was affected by carbon element that has high infrared absorptivity within this wavelength range.

• Journal of the Korean Society for Heat Treatment
• /
• v.20 no.2
• /
• pp.65-71
• /
• 2007

Microstructural changes and hardness variations in STS 304 steel have been investigated during the processes of carbide dispersion (CD) carburization; carburization, austenitization, subzero treatment and tempering. The carbon content of the surface layer increased up to maximum 4.0% after carburization, and the content was homogenized with the value of 2.3% to the $95{\mu}m$ from the surface after austenitization. The carbide appeared during CD carburization process was $Cr_7C_3$ type, which was composed network carbides along the austenite grain boundaries, square type carbides in the interior of the grain and fine nano-sized carbides. The fine nano-sized carbides precipitated at the austenitization stage and possibly subzero treatment stage were coarsened after tempering at $200^{\circ}C$, resulting the hardness decrease. The tempered steel without subzero treatment increased hardness with increasing time due to the continuous precipitation of fine carbides during tempering. The nano-sized carbide appeared square type morphology.

• Journal of the Korean institute of surface engineering
• /
• v.41 no.2
• /
• pp.63-68
• /
• 2008

Traditionally and generally used calcined clay was carburized, and its characteristics were studied. Carburization treatment was performed by the thermally decomposed carbon and the deposit carbon which occur in a so called 'Boudouard reaction $(2CO{\rightarrow}CO_2+C)'$ at fuel combustion process in a closed-type furnace. The color of the carburized calcine clay changed from yellow to black, and the carbon component revealed as crystalline graphite by the X-ray diffraction test. The weight of the carburized calcine clay decreased to about 4 wt.% by the 1st heating to $1400^{\circ}C$ in air but it does not decreased by the 2nd heating of the same conditions. By the carburization treatment, the water absorption changed from 13 wt.% to 6 wt.%, and the contact angle for water drop changed, too, from 0 to $87^{\circ}$ which was tested by the photograph of one minute after a water drop contact. It means the carburized calcine clay does not absorb water drop so it has a hydrophobic characteristic.

• Journal of the Korean Society for Heat Treatment
• /
• v.15 no.6
• /
• pp.279-280
• /
• 2002

• Journal of the Korean Society for Heat Treatment
• /
• v.13 no.1
• /
• pp.21-26
• /
• 2000

This study deals with effects of heat-treatment on the fatigue strength of SNC815 spur gears. The test gears are heat-treated by two different treatments. After carburization, one group of the test gears is quenched directly, while the other group is fumace cooled, reheated then quenched. The fatigue test at a constant stress amplitude is performed by using an electrohydraulic servo-controlled pulsating tester. The S-N curves are obtained and illustrated. By comparing the estimated strength with the experimental results, the validity of the previous experimental formula, presented by the author for estimating the fatigue strength of carburized gears, was discussed on these tested gears.

• Korean Journal of Materials Research
• /
• v.14 no.8
• /
• pp.558-564
• /
• 2004

In order to improve the low hardness and low wear resistance of Ti-6Al-4V alloy, plasma carburization treatment and CrN film coating were carried out. Effects of the plasma carburization and CrN coating were analyzed and compared with the non-treated alloy by mechanical and creep tests. After plasma carburization and CrN coating treatments, the carburized layer was about 150 ${\mu}m$ in depth and CrN coated layer was about 7.5 ${\mu}m$ in thickness. Hardness value of about $H_{v}$ 402 of the non-treated alloy was improved to $H_{v}$ 1600 and 1390 by plasma carburization and CrN thin film coating, respectively. Stress exponent(n) was decreased from 9.10 in CrN coating specimen to 8.95 in carburized specimen. However, the activation energy(Q) was increased from 242 to 250 kJ/mol. It can be concluded that the static creep deformation for Ti-6Al-4V alloy is controlled by the dislocation climb over the ranges of the experimental conditions.

• 한국연소학회:학술대회논문집
• /
• 2004.11a
• /
• pp.231-237
• /
• 2004

Vacuum carburizing continues to gain acceptance as an alternative to atmosphere carburizing particularly in the car industry. The advantages of low-pressure carburization over atmospheric gas carburization is not only the creation of a surface entirely free of oxide and the environmentally friendly nature of these methods but also an improvement in deformation behaviour achieved by combining carburization with gas quenching, a reduction in batch times by increasing the carburization temperature, low gas and energy consumption and the prevention of soot to a large extent. In present study, an improved vacuum carburizing method is provided which is effective to deposit carbon in the surface of materials and to reduce cycle time. Also LPC process simulator was made to optimize to process controls parameters such as pulse/pause cycles of pressure pattern, temperature, carburizing time, diffusion time. The carburizing process was simulated by a diffusion calculation program, where as the model parameters are proposed with help the experimental results and allows the control of the carburizing process with good accordance to the practical results. Thus it can be concluded that LPC process control method based on the theoretical simulation and experimental datas appears to provide a reasonable tool for prototype LPC system.

• Korean Journal of Metals and Materials
• /
• v.50 no.7
• /
• pp.517-522
• /
• 2012

In this study, a super carburizing treatment was applied to improve roller pitting fatigue life. It produced excellent properties of surface hardness and temper softening resistance by forming precipitation of fine and spherodized carbides on a tempered marstensite matrix through the repeated process of carburization and diffusion after high temperature carburizing step 1. The cycle II performed two times carburizing/diffusion cycle (process) after super carburization at $1,000^{\circ}C$ had fine and spherodized carbides to subsurface $200{\mu}m$. In this case, the carbide was $(Fe,Cr)_3C$ and there was not any massive carbides. In the case of Cycle II, the roller pitting fatigue life had a 6.15 million cycles. It was improved 48% compared to normal gas carburizing treatment.

• Journal of the Korean Society for Heat Treatment
• /
• v.17 no.2
• /
• pp.94-100
• /
• 2004

In order to improve the wear resistance of Ti-6Al-4V alloy, plasma carburization treatment was newly carried out without consumption of its good specific strength and fatigue life over the temperature. Effect of the plasma carburization was analyzed and compared with the non-treated alloy by microstructural observation, structure characterization and mechanical test. The plasma treated alloy formed a carburized layer of about $150{\mu}m$ in depth from the surface, where a fine and hard particles of TiC and $V_4C_3$ were homogeneously dispersed through the layer. The steady-static creep behaviors of Ti-6Al-4V alloy, using the constant stress creep tester, were investigated over the temperature range of $510{\sim}550^{\circ}C$(0.42~0.44Tm) and the stress range of 200~275 MPa. Stress exponent(n) was decreased from 9.32 of non-treatment specimen to 8.95 of carburized, however, the activation energy(Q) increased from 238 to 250 kJ/mol with the same condition as indicated above. From the above results, it can be concluded that the static creep deformation for Ti-6Al-4V alloy was controlled by the dislocation climb over the ranges of the experimental conditions.

• Journal of Advanced Marine Engineering and Technology
• /
• v.25 no.2
• /
• pp.357-364
• /
• 2001

This study deals with the effect on non-martensitic layer on the fatigue strength in carburized gear. The test gears are carburized, then treated by the combination of chemical polishing and electro-polishing. Carburization treatment is used widely on parts of power transmission system like surface hardened layer to improve fatigue strength. Carburized gears are observed using a scanning electron microscope(SEM) to determine the characteristics of crack initiation mechanism in the surface layer. The constant street amplitude fatigue test is performed by using and electro-hydraulic servo-controlled pulsating tester. The S-N curves are obtained and illustrated. The effect of non-martensitic layer on the fatigue strength is clarified.